• Polymer(Korea)
• /
• v.34 no.2
• /
• pp.126-132
• /
• 2010

A cation-exchange nanofiber poly(vinylidene fluoride) (PVdF) membrane was prepared by a radiation-induced graft polymerization (RIGP) of sodium styrene sulfonate (NaSS) in the presence of the polymerizable access agents in methanol solution. The used polymerizable access agents include styrene, acrylic acid, and vinyl pyrrolidone. The anion-exchange nanofiber PVdF membrane was also prepared by RIGP of glycidyl methacrylate (GMA) and its subsequent chemical modification. The successful preparations of cation- and anion-exchange PVdF membranes were confirmed via SEM, XPS and thermal analysis. The content of the grafting yield, ion-exchange group, and water uptake was in the range of 30.0~32.3%, 2.81~3.01 mmol/g and 66.6~147%, respectively. The proton conductivity at 20$^{\circ}C$ was in the range of 0.020~0.053 S/cm. From the result, the prepared ionexchange PVdF membrane can be used as a separator in battery cells.

• Journal of the Korean Ceramic Society
• /
• v.22 no.5
• /
• pp.23-28
• /
• 1985

A model for degradation of $eta$-$Al_2O_3$ is derived from sress generated by Poiseuille pressure capillary effect and effulent flux in charging process of Na-S Battery. Critical current density for degradation increase with increasing the crack length and crack tip radius. radius 10-7cm and crack length 10-5cm Dependence of crack growth velocity on crack lengh is seperated two regions that is for a large crack length it is predominated by Poiseuille pressure and effulent fluex but in the case of small crack length it is controlled by capillary effect.

• Korean Journal of Metals and Materials
• /
• v.49 no.11
• /
• pp.839-844
• /
• 2011

We examined the effects of alloying elements such as Fe, Ga, In, Sn, Mg, and Mn on the electrochemical characteristics of Al-based alloys for Al-air batteries by potentiodynamic polarization tests and electrochemical impedance spectroscopy. The corrosion potential of an Al anode was lowered by the addition of Ga and Sn, resulting in an increase in the cell voltage compared with a pure Al electrode. Fe was not beneficial to improve the electrochemical properties of the Al anode in that it caused a decrease in the cell voltage and reduced corrosion rate slightly. In, Mn, Sn, and Mg decreased the corrosion rate of the Al alloys, while Ga enhanced corrosion significantly and accelerated consumption of the anode.

• Current Photovoltaic Research
• /
• v.11 no.2
• /
• pp.58-65
• /
• 2023

The expanding significance of energy storage (ES) technology is increasing the acceptability of power systems by augmenting renewable energy supply. To deploy such ES technologies, we must select the optimal technology that meets the requirements of the system and confirm the technical and economic feasibility of the business model based on it. Herein, we propose a method and tool for selecting the optimal ES technology and service suitable for meeting the requirements of the system, based on its performance characteristics. The method described in this study can be used to discover and apply various ES technologies and develop business models with excellent economic feasibility.

• Journal of the Korean Electrochemical Society
• /
• v.4 no.4
• /
• pp.139-145
• /
• 2001

Various compositions of iron oxide based materials as a cathode of lithium secondary battery have been fabricated and tested with electrochemical method. A layered form of $LiFeO_2$ was synthesized by mixing and heating the initial materials of $FeCl_3\;6H_2O,\;LiOH$ and NaOH at low temperature. The effect of changing the precursors composition was investigated. As a result, when increasing the additive amount of NaOH, the capacity of the electrode is decreased but the performance and declining rate of capacity became smaller. $LiFeO_2$ synthesized with the weight ratio of $NaOH/FeCl_3/LiOH,\;2/1/7$ showed the largest capacity, but the discharging efficiency was sharply decreased after 30 cycles. Charge-discharge tests of lithium cells with $LiFeO_2$ cathode having the layer structure were performed. This cell showed the reversibility in the range of 1.5-4.5V of cell voltage. By using CPR method, chemical diffusion coefficients were measured in 1M $LiPF_6/EC/DEC$ solution. The value of chemical diffusion coefficient decreased with increasing the lithium content x, In 0.5$10^{-11}^cm^2/s$.

• Resources Recycling
• /
• v.33 no.3
• /
• pp.21-29
• /
• 2024

Globally, the demand for electric vehicles (EVs) is surging due to carbon-neutral strategies aimed at decarbonization. Consequently, the demand for lithium-ion batteries, which are essential components of EVs, is also rising, leading to an increase in the generation of spent batteries. This has prompted research into the recycling of spent batteries to recover valuable metals. In this study, we aimed to selectively leach and recover lithium from the cathode material of spent LFP batteries. To enhance the reaction surface area and reactivity, the binder in the cathode material powder was removed, and the material was subjected to heat treatment in both atmospheric and nitrogen environments across various temperature ranges. This was followed by a mechanochemical process for aqueous leaching. Initially, after heat treatment, the powder was converted into a soluble lithium compound using sodium persulfate (Na₂S₂O₈) in a mechanochemical reaction. Subsequently, aqueous leaching was performed using distilled water. This study confirmed the changes in the characteristics of the cathode material powder due to heat treatment. The final heat treatment in a nitrogen atmosphere resulted in a lithium leaching efficiency of approximately 100% across all temperature ranges.

• Journal of the Korean institute of surface engineering
• /
• v.42 no.1
• /
• pp.8-12
• /
• 2009

Electronic structures and chemical bonding of Li-intercalated $LiTiS_2$ and $LiTiO_2$ were investigated by using discrete variational $X{\alpha}$ method as a first-principles molecular-orbital method. ${\alpha}-NaFeO_2$ structure is the equilibrium structure for $LiCoO_2$, which is widely used as a commercial cathode material for lithium secondary battery. The study especially focused on the charge state of Li ions and the magnitude of covalency around Li ions. The average voltage of lithium intercalation was calculated using pseudopotential method and the average intercalation voltage of $LiTiO_2$ was higher than that of $LiTiS_2$. It can be explained by the differences in Mulliken charge of lithium and the bond overlap population between the intercalated Li ions and anions in $LiTiO_2$ as well as $LiTiS_2$. The Mulliken charge, which means the ionicity of Li atom, was approximately 0.12 in $LiTiS_2$ and the bond overlap population (BOP) indicating the covalency between Ti and S was about 0.339. One the other hands, the Mulliken charge of lithium was about 0.79, which means that Li is fully ionized. The BOP, the covalency between Ti and O, was 0.181 in $LiTiO_2$. Because of high ionicity of Li and the weak covalency between Ti and the nearest anion, $LiTiO_2$ has a higher intercalation voltage than that of $LiTiS_2$.

• KEPCO Journal on Electric Power and Energy
• /
• v.1 no.1
• /
• pp.29-32
• /
• 2015

Since the characteristics of Renewable Energy Sources like wind turbine generators are very different from those of existing thermal power generators and their response to the sudden change of the frequency are not as good as that from thermal power generators. Especially when the penetration level of the wind power generation is substantially high, the output from the WTG would be possibly limited to keep the stability of power systems. For this, this paper implements the process for calculating the dynamic penetration limit of WTG and analyze the potential application of BESS for increasing the dynamic penetration limit of WTG.

• Journal of Korean Society of Environmental Engineers
• /
• v.38 no.11
• /
• pp.603-610
• /
• 2016

This work studies the synthesis of birnessite (${\delta}-MnO_2$), a catalyst of oxidative-coupling reactions, from the powder of spent alkaline manganese batteries (SABP, <8 mesh) and evaluate its reactivity for 1-naphthol (1-NP) removals. Manganese oxides using commercial reagents ($MnSO_4$, $MnCl_2$) and the acid birnessite (A-Bir) by McKenzie method were also synthesized, and their crystallinity and reactivity for 1-NP were compared with one another. 96% Mn and 98% Zn were extracted from SABP by acid leaching at the condition of solid/liquid (S/L) ratio 1:10 in $1.0M\;H_2SO_4+10.5%\;H_2O_2$ at $60^{\circ}C$. From the acid leaching solution, 69% (at pH 8) and 94.3% (pH>13) of Mn were separated by hydroxide precipitation. Optimal OH/Mn mixing ratio (mol/mol) for the manganese oxide (MO) synthesis by alkaline (NaOH) hydrothermal techniques was 6.0. Under this condition, the best 1-NP removal efficiency was observed and XRD analysis confirmed that the MOs are corresponding to birnessite. Kinetic constants (k, at pH 6) for the 1-NP removals of the birnessites obtained from Mn recovered at pH 8 (${Mn^{2+}}_{(aq)}$) and pH>13 ($Mn(OH)_{2(s)}$) are 0.112 and $0.106min^{-1}$, respectively, which are similar to that from $MnSO_4$ reagent ($0.117min^{-1}$). The results indicated that the birnessite prepared from the SABP as a raw material could be used as an oxidative-coupling catalyst for removals of trace phenolic compounds in soil and water, and propose the recycle scheme of SAB for the birnessite synthesis.

• Dementia and Neurocognitive Disorders
• /
• v.22 no.3
• /
• pp.100-108
• /
• 2023

Background and Purpose: The efficacy and safety of GV1001 have been demonstrated in patients with moderate-to-severe Alzheimer's disease (AD). In this study, we aimed to further demonstrate the effectiveness of GV1001 using subscales of the Severe Impairment Battery (SIB), which is a validated measure to assess cognitive function in patients with moderate-to-severe AD. Methods: We performed a post hoc analysis of data from a 6 month, multicenter, phase 2, randomized, double-blind, placebo-controlled trial with GV1001 (ClinicalTrials.gov, NCT03184467). Patients were randomized to receive either GV1001 or a placebo for 24 weeks. In the current study, nine subscales of SIB-social interaction, memory, orientation, language, attention, praxis, visuospatial ability, construction, and orientation to name-were compared between the treatment (GV1001 1.12 mg) and placebo groups at weeks 12 and 24. The safety endpoints for these patients were also determined based on adverse events. Results: In addition to the considerable beneficial effect of GV1001 on the SIB total score, GV1001 1.12 mg showed the most significant effect on language function at 24 weeks compared to placebo in both the full analysis set (FAS) and per-protocol set (PPS) (p=0.017 and p=0.011, respectively). The rate of adverse events did not differ significantly between the 2 groups. Conclusions: Patients with moderate-to-severe AD receiving GV1001 had greater language benefits than those receiving placebo, as measured using the SIB language subscale.