• Journal of Welding and Joining
• /
• 제14권6호
• /
• pp.81-92
• /
• 1996

This study is to compare the weldability of Zircaloy-4 end cap of nuclear fuel pin using by GTA and Nd :YAG LB. The welding parameters which affect bead width and penetration depth have been investigated. The effect of joint geometry of end cap for GTAW and LBW has been studied and optimum conditions of Zircaloy-4 endcap welding have been found. Microstructures and microhardness of GTA and LB welded zones have been also compared.

• 한국세라믹학회지
• /
• 제30권8호
• /
• pp.643-650
• /
• 1993

NdAl3(BO3)4 have been developed for miniature solid state laser material. Single crystals of NdAl3(BO3)4 were grown by TSSG technique using BaB4O7 flux. The effects of growth conditions such as cooling rate, seed orientation and rotation speed on crystal quality and the morphology were studied. At the cooling rate of 2.4$^{\circ}C$/day and the crystal rotation speed of 30~40rpm with the seed orientation in <201> or <100> directions, transparent and light violet colored crystals in size of 10$\times$15$\times$20㎣ with well developed {010}, {111}, {111}, {021}, {001}, {102}, {112}, {021} faces were obtained. By X-ray diffraction analysis, the space group was determined as C2/c, and the X-ray powder data was obtained.

• 한국초전도저온공학회:학술대회논문집
• /
• 한국초전도저온공학회 2002년도 학술대회 논문집
• /
• pp.346-350
• /
• 2002

The effect of Ca-doping on the superconducting properties of Nd-Ba-Cu-O bulk superconductors, fabricated by the oxygen-controlled melt growth process, has been systematically investigated. Various c-axis textured bulk samples were grown using precursors with the nominal compositions of N $d_{1.8-x}$C $a_{x}$B $a_{2.4}$C $u_{3.4}$ $O_{y}$ (x = 0.00, 0.02, 0.05, 0.10, 0.15) in a reduced oxygen atmosphere of 1% $O_2$ in Ar. Magnetization measurements revealed that the critical temperatures( $T_{c}$) were almost linearly depressed from 95K to 86K with increasing the Ca dopant from x = 0.0 to 0.15, respectively, and thus critical current densities( $J_{c}$) at 77K and for H//c-axis of specimens were gradually degraded with increasing x. Compositional analyses revealed that although the amounts of the Ca dopant both in NdB $a_2$C $u_3$ $O_{y}$(Nd123) and N $d_4$B $a_2$C $u_2$ $O_{10}$(Nd422) were increased with increasing x, only less than half of the initial Ca compositions were detected in melt-grown Ca-doped Nd-Ba-Cu-O bulk crystals. The supression of $T_{c}$ is attributed to an increased Nd substitution for the Ba site in the Nd123 superconducting matrix with increasing the amount of the Ca dopant.t.opant.t.t.t.t.t.

• 한국자기학회지
• /
• 제6권2호
• /
• pp.80-85
• /
• 1996

$Nd_{2}Fe_{14}B/Fe_{3}B$ 복합자성상을 근간으로 한 급냉제조된 합금을 외부 자장중에서 열처리를 함으로써 자기특성이 월등하게 좋아짐을 확인하였다. $Nd_{4}Fe_{73.5}Co_{3}(Hf_{1-x}-Ga_{x})B_{18.5}$ 조성 합금을 1~5 kOe 자장중에서 열처리함으로써 연자성의 기지상$(Fe_{3}B)$ 및 강자성상$(Nd_{2}Fe_{14}B)$의 결정입도가 20% 감소하였고, 그 결과 잔류자속밀도 $(B_{r})$ 및 최대자기에너지적, ${(B.H)}_{max}$가 30% 이상 증가하였다. 이러한 증가는 입도의 감소 뿐만 아니라 미세입도의 고른 분포에도 기인한 것으로 판단되었다. 보자력의 극대점은 잔류자속밀도와는 달리 특정결정입도에서 발생하며, 이러한 기구를 교환상호작용변수 와 연관하여 설명한다. $Nd_{4}Fe_{73.5}Co_{3}Hf_{0.5}Ga_{0.5}B_{18.5}$ 합금을 자장중 열처리한 결과 ${(B.H)}_{max}=15.8$ MGOe의 고에너지적을 얻을 수 있음을 확인하였다.

• Journal of Magnetics
• /
• 제16권3호
• /
• pp.229-233
• /
• 2011

Phase evolution during the hydrogen-assisted disproportionation of $Nd_{12.5}Fe_{80.6}B_{6.4}Ga_{0.3}Nb_{0.2}$ alloy was investigated mainly by using a magnetic balance-type thermomagnetic analyser (TMA). In order to avoid any undesirable phase change in the course of heating for TMA, a swift TMA technique with very high heating rate (around 2 min to reach $800^{\circ}C$ from room temperature) was adopted. The hydrided $Nd_{12.5}Fe_{80.6}B_{6.4}Ga_{0.3}Nb_{0.2}$ alloy started to be disproportionated in hydrogen from around $600^{\circ}C$, and the alloy after the early disproportionation (from 600 to $660^{\circ}C$) has been partially disproportionated. The partially disproportionated alloy consisted of a mixture of $NdH_x$, $Fe_3B$, ${\alpha}$-Fe, and the remaining undisproportionated $Nd_2Fe_{14}BH_x$-phase. During the subsequent heating to $800^{\circ}C$ in hydrogen, two additional phases of $Fe_{23}B_6$ and $Fe_2B$ were formed, and the material consisted of a mixture of $NdH_x$, $Fe_{23}B_6$, $Fe_3B$, $Fe_2B$, and ${\alpha}$-Fe phases. During the subsequent isothermal holding at $800^{\circ}C$ for 1 hour, the phase constitution was further changed, and one additional unknown magnetic phase was formed. Eventually, the fully disproportionated $Nd_{12.5}Fe_{80.6}B_{6.4}Ga_{0.3}Nb_{0.2}$ alloy consisted of $NdH_x$, $Fe_{23}B_6$, $Fe_3B$, $Fe_2B$, ${\alpha}$-Fe, and one additional unknown magnetic phase.

• 한국광학회:학술대회논문집
• /
• 한국광학회 1998년도 제15회 광학 및 양자전자 학술발표회 논문집
• /
• pp.72-73
• /
• 1998

• Journal of Animal Science and Technology
• /
• 제46권6호
• /
• pp.937-946
• /
• 2004

Duroc 품종은 돼지 사육에 있어 산육성과 육질 향상을 위해 이용되고 있다. 본 연구는 육종에 많이 이용되는 Duroc 품종의 모계 특이적인 서열의 검색과 계통유전학적 유연관계의 정립을 위하여 미토콘드리아 유전체의 전체 염기서열을 결정하고 집단 내 다형성을 조사하였다. mtDNA 전체 서열의 길이는 16,584-bp 이고, D-loop과 tRNA, rRNA 유전자 영역에서는 삽입/결실이 확인되었다. 4개의 coding gene (COⅡ, COⅢ, ND3, ND4)에서 불완전한 종결코돈을, ND4L과 ND2 유전자는 선택적 개시코돈 양상을 보였다. Duroc 집단에 대한 분석 결과 조절영역에서의 특이적인 11-bp 중복 단위가 일부 개체(15.2%)에서 발견되었고, ND2의 개시코돈과 CYTB 유전자에서도 다형현상을 보였다. 각각의 유전자 영역에서의 다형성은 서로 연관되어 있었고, 그 결과 Duroc 집단은 크게 두 가지 haplotype으로 구분되었다. 계통수에서 Duroc mtDNA 서열은 유럽계열 cluster에 위치하였으나, haplotype 분석과 기존에 연구결과들을 종합해 보면 Duroc 품종은 여러 모계선조 집단에서 기원한 것으로 보이며, 유럽과 아시아 계열 모두가 품종 형성에 이용된 것으로 사료된다된 것으로 사료된다.

• 한국자기학회지
• /
• 제5권1호
• /
• pp.64-70
• /
• 1995

$ThMn_{12}$ 구조를 갖는 $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$의 결정학적 및 자기적 성질을 X선 회절법과 VSM, $M\"{o}ssbauer$분광법으로 연구하였다. $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$합금은 알곤가스 분위기의 아크 용해로에서 제조하였다. $NdFe_{10.7}TiM_{0.3}$의 결정구조는 순수 단일상의 tetragonal구조를 갖고 있으며 $a_{0}=8.587\;{\AA},\;c_{0}=4.788\;{\AA}$의 격자상수를 결정하였다. $M\"{o}ssbauer$ spectrum은 13 K 부터 770 K 영역까지 취하였으며 Curie 온도는 $NdFe_{10.7}TiM_{0.3}$의 경우 $570{\pm}3\;K$로 결정하였다. $NdFe_{10.7}TiM_{0.3}(M=B,\;Ti)$은 $8i_{1},\;8i_{2},\;8j_{1},\;8j_{2}$ 및 8f의 5 set의 Fe 이온의 subspectra로 분석하였다. $NdFe_{10.7}TiM_{0.3}$의 실온에서 Fe-site $8i_{1},\;8i_{2},\;8j_{1},\;8j_{2}$ 및 8f는 16.4, 8.2, 14.8, 21.3 및 39.3%의 면적비를 각각 가지고 있었다. 초미세자기장은 $H_{hf}(8i)>H_{hf}(8j)>H_{hf}(8f)$비로 감소함을 알았다.

• 한국잠사곤충학회지
• /
• 제45권1호
• /
• pp.10-17
• /
• 2003

최근에 기능성 양잠으로 관심이 높아지고 있는 Nd-s잠, N$d^{H}$잠의 이화학적 특성분석 결과는 다음과 같았다. 1. 처리온도 증가에 따른 용해성에서 Nd-s잠과 N$d^{H}$잠의 경우 용해도가 증가하였지만 백옥잠은 용해도 정도가 미미하였다. 특히, Nd-s잠의 경우 9$0^{\circ}C$에서의 용해성은 낮았으나 10$0^{\circ}C$경우는 높았다 13$0^{\circ}C$이상에서 연감률은 Hd-s잠과 NdH잠은 100%였고, 백옥잠은 24%였다. 효소처리에 의한 연감률이 Nd-s잠과 N$d^{H}$잠의 경우 처리시간이 경과함에 따라 연감률이 증가하였고, 백옥잠은 3% 이하였다. 2. 아미노산조성에서 Nd-s잠은 글리신 29.l mol%로 가장 높았고, N$d^{H}$잠은 세린 32.6 mol%로 가장 높았다. 정련 전 백옥잠은 글리신 40.3mol%, 정련 후 백옥잠은 글리신 46.3 mol%였다. 3 시차 주사 열량 분석은 Nd-s잠, N$d^{H}$잠, 정련 전$.$후 백옥잠에서 10$0^{\circ}C$이하 peak는 수분증발에 의한 흡열 peak로 보여지고, Nd-s잠, N$d^{H}$잠 및 정련 전 백옥잠은 216$^{\circ}C$∼218$^{\circ}C$에서 열변성 peak로 보여지며, 314$^{\circ}C$∼32$0^{\circ}C$부근에서 peak는 열분해 peak로 보였다. 4. 적외선 분광 분석에서 Nd-s 잠은 결정화도가 44.3%, N$d^{H}$잠은 43.7%, 정련 전 백옥잠은 59.9%, 정련 후 백옥잠은 61.8%로서 Nd-s잠과 N$d^{H}$ 잠은 백옥잠보다 결정화도가 낮았다. 5. X-선 결정화도는 정련 전 Nd-s잠은 35.9, 정련 전 N$d^{H}$ 잠은 33.5%, 백옥잠정련 전이 47.2%, 정련 후 백옥잠은 49.8가 나타났다. 6. N$d^{H}$ 잠의 고치를 12$0^{\circ}C$에서 여과하여 동결건조하여 분말로 만들어 수용성만 이용하여 분자량 측정은 1시간 처리의 수평균분자량은 9,417로 분자량이 제일 크고 골고루 넓은 범위에서 분포되어 있으며, 2시간처리시는 3,744, 4시간처리시는 4,944, 6시간처리시는 3,910으로 평균분자량이 처리시간에 따라 저분자화 되는 경향이었으며, N$d^{H}$ 잠의 수평균분자량은 3,744∼9,417범위로 나타났다.은 3,744∼9,417범위로 나타났다.

• Journal of Welding and Joining
• /
• 제15권6호
• /
• pp.85-95
• /
• 1997

This study is to investigate the optimum conditions of Nd:YAG laser beam welding for Zircaloy-4 end cap closure by optical fiber transmission. Laser welding parameters which affect the penetration depth and bead width were experimentally examined using the various beam radius by the beam quality analyzer, joint geometries of end cap and the laser parameters which mean pulse width, repetition rate and pulse energy. Also, an optimum welding speed and the effect of assistant gas with varying the flow rate of He were investigated. We found that the laser average power for the end cap welding will be 230W and rotation speed must not exceed 8 RPM, the best position of focus using optical fiber with 600.mu.m will be 2 to 3mm below the surface of the material.