• Proceedings of the Optical Society of Korea Conference
• /
• 2001.08a
• /
• pp.110-111
• /
• 2001

• Korean Journal of Metals and Materials
• /
• v.46 no.7
• /
• pp.420-426
• /
• 2008

By using electrodeposition, we developed a new method to produce Ni/Invar bimetal sheets, which have been used for the present study to investigate the texture evolution during annealing. The grains of electrodeposited Ni were columnar, while those of electrodeposited Fe-Ni alloy were nanocrystalline. These different parts of the bimetal underwent different evolution of textures and microstructures during annealing. In the nanocrystalline Invar, the as-deposited textures were of fiber-type characterized by strong <100>//ND and weak <111>//ND components, and the occurrence of grain growth resulted in the strong development of the <111>//ND fiber texture with the minor <100> // ND components. On the other hand, in the columnar-structured Ni part, the as-deposited <110>//ND fiber texture transformed to the <112>//ND fiber texture due to recrystallization occurring above $550^{\circ}C$. The development of microtextures which took place during annealing in the Ni/Invar interfacial regions was investigated by using the OIM analysis, and discussed in terms of the effect of atomic diffusion across the interfaces.

• Journal of Food Hygiene and Safety
• /
• v.18 no.1
• /
• pp.30-32
• /
• 2003

This study was performed to investigate the contents of nitrites in 450 meat products in Seoul from Jan. to Dec. in 2002. Sorbic acid contents of the samples were determined by Gas Chromatography. 67 samples of 450 (14.9%) were detected in sorbic acid contents. In each meat products, 65,6% (21/32) in dried meats, 17.6% (3/17) in bacon, 11.7% (27/231) in hams, 11.7% (13/111) in sausages, and 11.5% (3/26) in meat cu. The concentration range of Sorbic acid and its average content in each of the meat products are as follows: ND-1.21 g/ Kg and 0.34 g/kg in dried meat, ND-0.84 g/Kg and 0.12 g/Kg in bacon, ND-1.27 g/Kg and 0.074 g/Kg in ham, ND- 0.90 g/Kg and 0.077 g/Kg in sausage, and ND-0.20 g/Kg, 0.015 g/Kg in can meat. Together, these results demonstrated that the processed market meat products must be reinforced to supply for the citizens as safe foods.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.10 no.2
• /
• pp.152-158
• /
• 2000

The crystallographic grain orientation of {{{{ { ZrB}_{2 } }}}}-ZrC composite sintered by pressureless a sintering(PLS) and spark plasma sintering (SPS) was analysed by the SEM-EBSP technique. In the case of PLS, (160) plane of {{{{ { ZrB}_{2 } }}}} was oriented to ND direction, (101) and (111) plane of ZrC were oriented to ND direction. In the case of SPS, (0001) plane of {{{{ { ZrB}_{2 } }}}} was strongly oriented to ND direction. Only (001) plane of ZrC was oriented to ND direction. The PLS specimen had weakly oriented grain structure and interface between {{{{ { ZrB}_{2 } }}}} and ZrC was found to be more stable than that of SPS but the SPS specimen had a preferentially oriented grain structure.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2004.06a
• /
• pp.110-111
• /
• 2004

• Journal of the Korean Ceramic Society
• /
• v.37 no.10
• /
• pp.1014-1020
• /
• 2000

RF 마크네트론 스퍼터법으로 Ce의 일부를 희토류 원소로 치환한 Ce$_{1-x}$RE$_{x}$O$_{2-y}$(0.1$\leq$x$\leq$0.4, RE=Y, Nd) 박막을 Si(111), $Al_2$O$_3$(1012) 기판 위에 1450~1$600^{\circ}C$로 소결한 target을 이용하여 성장시켰다. Ce$_{1-x}$RE$_{x}$O$_{2-y}$ 박막의 성장시 기판온도 및 증착시간 등을 변화시켜 성장시켰으며, 성장된 박막의 특성분석은 XRD, SEM, TEM으로 행하였다. 증착된 박막의 방향성 및 결정성장 거동은 증착온도 및 시간에 따라 차이를 보였다. Si(111) 기판 위에 증착된 Ce$_{1-x}$Y$_{x}$O$_{2-y}$(x=0.3) 박막의 경우, 80$0^{\circ}C$에 비해 7$50^{\circ}C$에서 증착 시간에 따른 (111) 우선배향성의 정도가 나은 결과를 보였으며, $Al_2$O$_3$(1012) 기판 위에 증착한 Ce$_{1-x}$Nd$_{x}$O$_{2-y}$(x=0.3) 박막 또는 (111) 우선배향성을 나타내었다.을 나타내었다.

• Transactions of Materials Processing
• /
• v.14 no.6 s.78
• /
• pp.553-558
• /
• 2005

A study on the microstructure, the texture and the formability of the samples after ECAPed and subsequent heat-treated AA 1050 aluminum alloy sheet have been carried out. The specimens after the ECAP showed a very fine grain size, a decrease of <100> // ND, and an increase of <111> // ND textures. The $\{111\}<112>,\;\{123\}<634>,\;\{110\}<001>,\;\{112\}<111>,\;\{110\}<111>,\;and\;\{013\}<231>$ texture components were increased in the specimens after the ECAP and subsequent heat-treatment at $400^{\circ}C$ for 1 hour. One of the most important properties in sheet metals is formability. The r-value or plastic strain ratio has was as a parameter that expressed the formability of sheet metals. The change of the plastic strain ratios after the ECAP and subsequent heat-treatment conditions were investigated and it was found that they were two times higher than those of the initial Al sheets. This could be attributed to the formation above texture components through the ECAP and subsequent heat-treatment of AA 1050 Aluminum alloy sheet.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2005.05a
• /
• pp.148-151
• /
• 2005

A study on the microstructure and the texture of the samples after ECAP and subsequent heat treatment has been carried out. The specimens after ECAP showed a very fine grain size, a decrease of <100> // ND, and an increase of <111> // ND textures. The $\{111\}<112>,\;\{123\}<634>,\;\{110\}<001>,\;\{112\}<111>,\;\{110\}<111>,\;and\;\{013\}<231>$ texture components were increased in the specimens after the ECAP and subsequent heat-treatment at $400^{\circ}C$ for 1 hour. One of the most important properties in sheet metals is formability. The r-value or plastic strain ratio has been used as a parameter that expresses the formability of sheet metals. The change of the plastic strain ratios after the ECAP and subsequent heat-treatment conditions has been investigated and it was found that they were two times higher than those of the initial Al sheets. This could be attributed to the formation above texture components through the ECAP and subsequent heat-treatment.

• Korean Journal of Crystallography
• /
• v.5 no.2
• /
• pp.51-66
• /
• 1994

Y3Al5O2 and Nd: Y3Al5012 single crystals were grown by Czochralskl technique. The effectt of pulling rate rotation rate, and doping level of Nd3+ ion on the crystal quality were studied Various types of defects were analysed by photo-elastic effect and chemical etching method Finally, spectroscopic and laser poputies of grown crystal were measured. Optirmum pulling rate for good quality was dependant on the doping level of Nd3+ ion. It was found that the suitable pulling rates for pure Y3Al5O12 for 3.0∼3.5 a/o Nd3+ ion doped Y3Al5012 and for more than 40 a/o Nd3+ ion doped Y3Al5012 were 2∼4mm/hr, 0.6∼0.5mm/hr, and less than 0.4mm/hr respectively. Solid-liquid interface was convex at the rotation rate of 27∼60rpm, and concave at the rotation rate of 80∼100rpm. Growth axis was confired to <111> direction and lattice parameter was measured to 12.017A. Core (211) facets,striations, inclusions of metal particles, dislocations and optical inhonngeneities were detected. Four level laser transition of Nd3+ion in YIAls012 single crystal were identified by the spectroscopic measurements. Laser rod with tam diameter and 63mm length was fabricated from grown Nd3+ Y3Al5012 sin91e crystals. 1.8lJ of lasing threshould and 0.49% of soope efficiency were measured by the Pulsed laser action.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.1 no.1
• /
• pp.5-16
• /
• 1991

It was grown Cubic $ZrO_2(10 mol% Y_2O_3)$ single crystals doped with 1 wt% rare earth metal oxides (RE=Ce, Pr, Nd, Eu, Er) by Skull method. It was investigated electrical properties on (111) plane of grown single crystals by Impedance Spectroscopy. It was potted relation between temperature and electrical conductivities and observed the transition at $약300-400^{\circ}$ It was obtained activation energy on the migration of oxygen vacancy between low temperature (before the transition) and high temperature (after the transition till ${\11}500^{\circ}$) and its difference can be seen the activation energy of the formation of oxygen vacancies by break up defect complexes. It was obtained the activation energy according as add yttria and rare earth metal oxides and discussed ionic conduction mechanism. Grown single crystals showed Ce: orange - red, Pr: golden - yellow, Nd: lilac, Eu: light pink, Er: pink due to dopant effect from the light absorption data in the visible range.