In this study, in order to develop the composition ceramics for low loss and low temperature sintering multilayer piezoelectric actuator, PMN-PZN-PZT ceramics were fabricated using two stage calcination method and $Li_2CO_3$, $Bi_2O_3$ and CuO as sintering aids and their piezoelectric characteristics were investigated according to the 2nd calcination and sintering temperature. At the calcination temperature of $750^{\circ}C$ and sintering temperature of $930^{\circ}C$, density, electromechanical coupling factor ($k_p$), mechanical quality factor ($Q_m$), Dielectric constant (${\varepsilon}_r$) and piezoelectric constant ($d_{33}$) of specimen showed the optimum value of $7.94g/cm^2$ 0.581, 1554, 1555 and 356pC/N, respectively for multilayer piezoelectric actuator application.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.12
• /
• pp.1039-1043
• /
• 2007

In this paper, in order to develop low temperature sintering ceramics for multilayer piezoelectric actuator application, PMN-PZN-PZT ceramics were fabricated using $LiCO_3,\;Bi_2O_3$ and CuO as sintering aids. And also, their piezoelectric and dielectric properties were investigated according to the milling time. All the specimens sintered at $930\;^{\circ}C$ showed tetragonal phases without secondary phases. With increasing milling time, piezoelectric and dielectric characteristic of specimens increased up to 60 hours milling time and then decreased due to the agglomeration of fine particle. Accordingly, it seems that 60 hour is optimum milling condition. At the sintering temperature of $930\;^{\circ}C$ and milling time of 60 hour, density, dielectric constant(${\varepsilon}_r$), electromechanical coupling factor (kp), mechanical quality factor (Qm), piezoelectric d constant showed the optimum value of $7.95\;g/m^3$, 1382, 0.546, 1749, 330 pC/N, respectively for multilayer piezoelectric actuator application.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.20 no.9
• /
• pp.766-770
• /
• 2007

In this study, in order to develop low temperature sintering ceramics for multilayer piezoelectric actuator, $0.07Pb(Mn_{1/3}Nb_{2/3})O_3-xPb(Ni_{1/3}Nb_{2/3})O_3-(0.93-x)Pb(Zr,Ti)O_3$ ceramics system were fabricated using $Li_2CO_3-Bi_2O_3-CuO$ sintering aids and the specimens were sintered at $930^{\circ}C$. Thereafter, their piezoelectric and dielectric characteristics were investigated according to the amount of PNN substitution. At 9 mol% PNN substitution, density, electromechanical coupling factor ($k_p$), dielectric constant, mechanical quality factor ($Q_m$) and piezoelectric constant ($d_{33}$) showed the optimum value of $7.86g/cm^3$, 0.60, 1640, 1323 and 387 pC/N, respectively. It is considered that these values are suitable for piezoelectric divece application such ad multilayer piezoelectric actuator and ultrasonic vibrator with pure Ag internal electrode.

• Analytical Science and Technology
• /
• v.6 no.2
• /
• pp.231-238
• /
• 1993

The thermal behavior of binder in multi-layer actuator has an effect on the properties of actuator. Binder burn-out process and thermal degradation mechanism of PNN-PZT/Acrylic binder were analyzed by FTIR, DSC, TGA. Binder was burnt out by two step. In oxygen atomsphere, thermal degradation was activated and final residue was minimized to 5%.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.11a
• /
• pp.290-291
• /
• 2007

In this study, in order to develop low temperature sintering ceramics for multilayer piezoelectric actuator, sensers, transducers, PMN-PNN-PZT ceramics were manufacrtured with the sintering temperature, and their piezoelectric and dielectric properties were investigated. At the composition ceramics sintered at $900^{\circ}C$, desity, dielectric constant$({\varepsilon}_r)$, electromechanical coupling factor(kp), piezoelectric constant$(d_{33})$ and mechanical quality factor(Qm) showed the optimal value of $7.86g/cm^3$, 1417, 0.634, 410pC/N and 1138, respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.11 no.11
• /
• pp.963-968
• /
• 1998

The stress distribution in multilayer piezoelectric ceramic actuators was investigated by Finite element analysis. The y direction stress was concentrated at electrode tip. The y direction maximum stress was decreased to 4.9$\times10^ 7 N/m^2$ with internal electrode gap(a) until 0.4 mm and was not much difference with external electrode thickness(c). The stress distribution with internal layers was almost same and the stress distribution of load condition was higher than that of no load condition The y direction maximum stress increased with the number of layer and saturated at 260 layers. In the case of defective actuator, the stress distribution was disconnected around the defect and larger than that of normal actuator.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.1
• /
• pp.35-39
• /
• 2006

In this study, in order to develop the multilayer piezoelectric actuator and ultrasonic resonator, PMN-PNN-PZT ceramics were fabricated by sintering with $Li_2CO_3-Na_2CO_3$ as sintering aids at $950^{\circ}C$ and their piezoelectric and dielectric characteristics were investigated as a function of PNN substitution. With increasing PNN substitution, dielectric constant(${\epsilon}_r$), electromechanical coupling factor(kp), and piezoelectric d constant($d_{33}$) were increased to $12 mol\%$ PNN substitution and then showed a tendency to decrease rapidly With increasing PNN substitution, crystal structure changed from tetragonal to rhombohedral at $12 mol\%$ PNN substitution and then secondary phase was appeared and its intensity was increased. At the $12 mol\%$ PNN substituted PMN-PZT composition ceramic sintered at $950^{\circ}C$, density, kp, $d_{33}$ and Qm showed the optimum value of $7.79 g/cm^3$, 0.599, 419 pC/N, and 894, respectively for multilayer piezoelectric actuator application.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.2
• /
• pp.126-130
• /
• 2008

In this study, in order to develop low loss multilayer piezoelectric actuator, PZN-PZT ceramics were fabricated using $Li_2CO_3,\;Bi_2O_3$, CuO and ZnO as sintering aids, their structural, piezoelectric and dielectric characteristics were investigated according to the amount of ZnO addition, At the sintering temperature of $870^{\circ}C$, the density, electromechanical coupling factor(kp), mechanical quality factor(Qm), dielectric constant(${\epsilon}_r$) and piezoelectric constant($d_{33}$) of 0.4 wt% ZnO added specimen (sintered at $870^{\circ}C$) showed the optimum value of $7.812g/cm^3$, 0.535, 916, 1399, 335 pC/N respectively. Taking into consideration above piezoelectric properties of the specimen sintered at low temperature, it was concluded that PZN-PZT ceramics using 0.4 wt% ZnO as additive showed the optimum characteristics as the composition ceramics for low loss multilayer piezoelectric actuator application.

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.4
• /
• pp.121-124
• /
• 2009

In this study, in order to develop compositions of ceramics suitable for piezoelectric actuator and ultrasonic vibrator applications using low temperature sintering, multilayer, PMN-PNN-PZT ceramics were fabricated using $Li_2CO_3$ and $Na_2CO_3$ as sintering aids. Their structural, piezoelectric and dielectric characteristics were investigated according to the Zr/Ti ratio. As the Zr/Ti ratio increased, the electromechanical coupling factor $k_p$, and piezoelectric constant $d_{33}$ and the mechanical quality factor $Q_m$ all increased with Zr/Ti ratio and then decreased after the ratio exceeded 50/50. At the ratio of Zr/Ti =49/51 and sintering temperature of $900^{\circ}C$; the density, electromechanical coupling factor $k_p$, dielectric constant ${\varepsilon}_r$ piezoelectric $d_{33}$ constant and mechanical quality factor $Q_m$ all showed the optimum values of 7.900 $g/cm^3$, 0.576, 856, 312 pC/N, 1,326, respectively. These property values are very suitable for multilayer ceramics actuator applications.

• Transactions on Electrical and Electronic Materials
• /
• v.9 no.3
• /
• pp.91-95
• /
• 2008

In this study, in order to develop the composition ceramics for low loss multilayer piezoelectric actuator application, $Pb(Zn_{1/2}W_{1/2})O_3-Pb(Mn_{1/3}Nb_{2/3})O_3-Pb(Zr,Ti)O_3$ (abbreviated as PZW-PMN-PZT)ceramics according to the amount of $MnO_2$ addition were fabricated using two-stage calcinations method. And also, their dielectric and piezoelectric properties were investigated. At the 0.2 wt% $MnO_2$ added PZW-PMN-PZT ceramics sintered at $930^{\circ}C$, density, electromechanical coupling factor $k_p$, dielectric constant ${\varepsilon}_r$, piezoelectric $d_{33}$ constant and mechanical quality factor $Q_m$ showed the optimum value of $7.84g/cm^3$, 0.543, 1,392, 318.7 pC/N, 1,536, respectively for low loss multilayer ceramics actuator application.