• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2008년도 추계학술대회A
• /
• pp.83-84
• /
• 2008

The primary water stress corrosion cracking (PWSCC) of dissimilar metal weld based on Alloy 82/182 is one of major issues in material degradation of nuclear components. It is well known that the crack initiation and growth due to PWSCC is influenced by material's susceptibility to PWSCC and distribution of welding residual stress. Therefore, modeling the welding residual stress is of interest in understanding crack formation and growth in dissimilar metal weld. Currently in Korea, a numerical round robin study is undertaken to provide guidance on the welding residual stress analysis of dissimilar metal weld. As a part of this effort, the present paper investigates distribution of welding resisual stress of a ferritic low alloy steel nozzle with dissimilar metal weld using Alloy 82/182. Two-dimensional thermo-mechanical finite element analyses are carried out to simulate multi-pass welding process on the basis of the detailed design and fabrication data. The present results are compared with those from other participants, and more works incorporating physical measurements are going to be performed to quantify the uncertainties relating to modelling assumptions.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.390-395
• /
• 2002

The experimental and numerical study has been conducted on the sleeve repair welding of API 5L X65 pipeline. SMA W and GTAW were applied to weld the sleeve. The macrostructure and hardness of repair welds have been examined. The [mite element analysis of the multi-pass sleeve-fillet welding has been conducted to validate the experiment and investigate the effects of in-service welding conditions. The effect of gas flow rate on the hydrogen cracking was investigated. The effect of internal pressure on residual stresses and plastic strain was investigated. The allowable heat input was predicted considering the maximum temperature of inner surface of pipe and cooling rate at CGHAZ.

• International Journal of Korean Welding Society
• /
• 제2권2호
• /
• pp.36-41
• /
• 2002

The experimental and numerical study has been conducted on the sleeve repair welding of API 5L X65 pipeline. SMAW and GTAW were applied to weld the sleeve. The macrostructure and hardness of repair welds have been examined. The finite element analysis of the multi-pass sleeve-fillet welding has been conducted to validate the experiment and investigate the effects of in-service welding conditions. The effect of gas flow rate on the hydrogen cracking was investigated. The effect of internal pressure on residual stresses and plastic strain was investigated. The allowable heat input was predicted considering the maximum temperature of inner surface of pipe and cooling rate at CGHAZ.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.430-434
• /
• 2001

To perform the integrity evaluation of RPV more realistically, it is necessary to evaluate the metallurgical microstructure and residual stress considering more real phenomena such as multi-pass welding process and PWHT. Accordingly, firstly, this paper proposes the integrated assessment methodology systematically developed for residual stress on weldment of RPV by using thermodynamics, diffusion theory, finite element method and validation experiment. Also, the residual stress on circumferential weldment of reactor pressure vessel is calculated considering multi-pass welding process by the commercial finite element package, ABAQUS.

• 대한조선학회논문집
• /
• 제39권3호
• /
• pp.81-88
• /
• 2002

용접구조물의 루트부는 외력에 의한 응력 집중에 의해 파손되기 쉽다. 따라서 구조물의 안전성 및 신뢰성 측면에서 홈 가공한 그루브 용접에 의한 완전용입 용접이 일반적으로 요구되어진다. 하지만 필릿 T-이음부 용접은 루트부의 갭과 같은 불완전 용입부를 만들어내기 쉬움에도 불구하고 홈 가공 시간 및 용접봉 소모량을 줄이기 위해 이러한 필릿용접이 자주 행해지고 있다. 따라서, 본 연구에서는 필릿 용접구조물의 플래이트(또는 플랜지)와 웨브 부분에 발생하는 용접잔류 응력과, 특히 불완전 용입에 의한 루트부 갭을 갖는 양면 T-이음부의 노치부분에 발생하는 잔류응력 분포를 해석하고자 하였다. 해석을 위해서 서브머지드 아-크 용접에 의한 단층 및 다층패스용접 모델을 선정하였으며, 열전도 및 열탄소성 이론을 고려한 유한요소 프로그램을 사용하였다.

• Journal of Welding and Joining
• /
• 제28권4호
• /
• pp.18-25
• /
• 2010

Super-duplex stainless steels (SDSS) have a good balance of mechanical property and corrosion resistance when they consist of approximately equal amount of austenite and ferrite. The SDSS needs to avoid the detrimental phases such as sigma(${\sigma}$), chi(${\chi}$), secondary austenite(${\gamma}2$), chromium carbide & nitride and to maintain the ratio of ferrite & austenite phase as well known. However, the effects of the subsequent weld thermal cycle were seldom experimentally studied on the micro-structural variation of weldment & pitting corrosion property. Therefore, the present study investigated the effect of the subsequent thermal cycle on the change of weld microstructure and pitting corrosion property at $40^{\circ}C$. The thermal history of root side was measured experimentally and the change of microstructure of weld root & the weight loss by pitting corrosion test were observed as a function of the thermal cycle of each weld layer. The ferrite contents of root weld were reduced with the subsequent weld thermal cycles. The pitting corrosion was occurred in the weld root region in case of the all pitted specimen & in the middle weld layer in some cases. And the weight loss by pitting corrosion was increased in proportional to the time exposed at high temperature of the root weld and also by the decrease of ferrite content. The subsequent weld thermal cycles destroy the phase balance of ferrite & austenite at the root weld. Conclusively, It is thought that as the more subsequent welds were added, the more the phase balance of ferrite & austenite was deviated from equality, therefore the pitting corrosion property was deteriorated by galvanic effect of the two phases and the increase of 2nd phases & grain boundary energy.

• Journal of Advanced Marine Engineering and Technology
• /
• 제9권4호
• /
• pp.328-338
• /
• 1985

When the low temperature service steels are used as materials for welded structure, some problems-brittleness and weld cracking, etc.-occur in welded part due to the change of mechanical and metallurgical characteristics resulted from the thermal cycle during the welding procedure. In this study, the experiments were conducted to investigate the change of mechanical and metallurgical characteristics of the welded part for the low temperature and high pressure service steels. Moreover, the Static and Dynamic Implant Test Method was introduced to this study in order to find out the mechnism of weld cracking. In addition, the fracture toughnesses of welded bond were inspected under the various low temperature environments. Main results obtained are as follows; 1) The effect of the hydrogen on the fatigue characteristics of the weld bond can be estimated by the new self-contrived Dynamic Implant Test equipment. 2) The fine micro-structure and low hardness in the heat affected zone can be obtained by the small heat input multi-pass welding. 3) The susceptibility of the delayed cracking is largely affected by the condition of used electrode. 4) The transition temperature of the fracture surface in weld bond appears to be higher 20 .deg. C than that in base metal.

• International Journal of Naval Architecture and Ocean Engineering
• /
• 제10권2호
• /
• pp.129-140
• /
• 2018

A residual stress generated in the steel structure is broadly categorized into initial residual stress during manufacturing steel material, welding residual stress caused by welding, and heat treatment residual stress by heat treatment. Initial residual stresses induced during the manufacturing process is combined with welding residual stress or heat treatment residual stress, and remained as a final residual stress. Because such final residual stress affects the safety and strength of the structure, it is of utmost importance to measure or predict the magnitude of residual stress, and to apply this point on the design of the structure. In this study, the initial residual stress of steel structures having thicknesses of 25 mm and 70 mm during manufacturing was measured in order to investigate initial residual stress (hereinafter, referred to as initial stress). In addition, thermal elastic plastic FEM analysis was performed with this initial condition, and the effect of initial stress on the welding residual stress was investigated. Further, the reliability of the FE analysis result, considering the initial stress and welding residual stress for the steel structures having two thicknesses, was validated by comparing it with the measured results. In the vicinity of the weld joint, the initial stress is released and finally controlled by the weld residual stress. On the other hand, the farther away from the weld joint, the greater the influence of the initial stress. The range in which the initial stress affects the weld residual stress was not changed by the initial stress. However, in the region where the initial stress occurs in the compressive stress, the magnitude of the weld residual compressive stress varies with the compression or tension of the initial stress. The effect of initial stress on the maximum compression residual stress was far larger when initial stress was considered in case of a thickness of 25 mm with a value of 180 MPa, while in case of thickness at 70 mm, it was 200 MPa. The increase in compressive residual stress is almost the same as the initial stress. However, if initial stress was tensile, there was no significant change in the maximum compression residual stress.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2006년 추계학술발표대회 개요집
• /
• pp.128-129
• /
• 2006

To investigate impact property characteristics on the low temperature plate weld metal, the two different plates of the same steel grade were welded and evaluated by Mo bearing and no Mo containing welding consumables. The results are summarized as follows; 1) Multi pass welded Mo bearing weldment was not satisfied with the requirement of tensile strength, while no Mo containing one was satisfied with it 2) In the plate butt weldment, the impact property of weld metal was highly affected by both the welding consumable and plate.

• Journal of Welding and Joining
• /
• 제8권1호
• /
• pp.23-30
• /
• 1990

The robotic welding has been adapted positively in many welding shops forthe purpose of improving the welding efficiency and liberating operators from the severe working atmosphere. But for a large-size structure with thick plates like ship-building and every kind of plants manufacturing, the application of the arc welding robots is not established yet. The reason is assumed that the conventional arc welding robots are not adaptive for multi-pass welding of thick plates whose grooves are not so accurate. As one solution to this problem, a guidance system which uses the welding arc itself as a sensor is largely used. In this study the velocity controller which changes the tip to workpiece distance for regulating the weld proposed. The proportional and integral gain of velocity controller were determined by using the computer simulation of the control system, and the simulation results compared with the experimental ones. It was revealed that the developed control system using the arc sensor principle has a good capability of tracking the weld joint, although some more studies will be needed to refine the model of arc current.