• Journal of the Korean Vacuum Society
• /
• v.8 no.3B
• /
• pp.262-268
• /
• 1999

Polycarbonate (PC) and Polymethylmethacrylate (PMMA) surface was modified by ion assisted reaction (IAR) technique to obtain the hydrophilic functional groups and improve the wettability. In conditions of ion assisted reaction, ion beam energy was changed from 500 to 1500eV, and ion dose and oxygen gas blown rate were fixed $1\times10^{16}$ ions/$\textrm{cm}^2$ and 4ml/min, respectively. Wetting angle of water on PC and PMMA surface modified by $Ar^+$ ion without blowing oxygen at 4ml/mon showed $5^{\circ}$ and $10^{\circ}$. Changes of wetting angle with oxygen gas and $Ar^+$ ion irradiation were explained by considering formation of hydrophilic group due to a reaction between irradiated polymer chain by energetic ion irradiation and blown oxygen gas. X-ray photoelectron spectroscopy analysis shows that hydrophilic groups such as -C-O, -(C=O)- and -(C=O)-O- are formed on the surface of polymer by chemical interaction. The polymer surface modification using ion assisted reaction only changed the surface physical properties and sept the bulk properties. In comparison with other modification methods, the surface modification by IAR treatment was chemically stable and enhanced the adhesion between metal and polymer surface. The applications of various kinds of polymer surface modification methods, metal and polymer surface. The applications of various kinds of polymer surface modification could be appled to the new materials about hydrophilic surface properties by IAR treatment. The adhesion between metal film and polymer measured by Scotch tape test whether the hydrophilic surfaces could improve the adhesion strength or not.

• Bulletin of the Korean Chemical Society
• /
• v.34 no.12
• /
• pp.3715-3721
• /
• 2013

In this study, the behavior of cells on the modified surface, and the correlation between the modified substrates and the response of cells is described. A close-packed layer of nano-sized silica beads was prepared on a coverslip, and the adhesion, proliferation, and migration of BALB/3T3 fibroblast cells on the silica layer was monitered. The 550 nm silica beads were synthesized by the hydrolysis and condensation reaction of tetraethylorthosilicate in basic solution. The amine groups were introduced onto the surfaces of silica particles by treatment with 3-aminopropyltrimethoxysilane. The close-packed layer of silica beads on the coverslip was obtained by the reaction of the amine-functionalized silica beads and the (3-triethoxysilyl)propylsuccinic anhydride treated coverslip. BALB/3T3 fibroblast cells were loaded on bare glass, APTMS coated glass, and silica bead coated glass with the same initial cell density, and the migration and proliferation of cells on the substrates was investigated. The cells were fixed and stained with antibodies in order to analyze the changes in the actin filaments and nuclei after culture on the different surfaces. The motility of cells on the silica bead coated glass was greater than that of the cells cultured on the control substrate. The growth rate of cells on the silica bead coated glass was slower than that of the control. Because the close-packed layer of silica beads gave an embossed surface, the adhesion of cells was very weak compared to the smooth surfaces. These results indicate that the adhesion of cells on the substrates is very important, and the actin filaments might play key roles in the migration and proliferation of cells. The nuclei of the cells were shrunk on the weakly adhered surfaces, and the S1 stage in which DNA is duplicated in the cell dividing processes might be retarded. As a result, the rate of proliferation of cells was decreased compared to the smooth surface of the control. In conclusion, the results described here are very important in the understanding of the interaction between implanted materials and biosystems.

• Applied Chemistry for Engineering
• /
• v.10 no.3
• /
• pp.450-455
• /
• 1999

Unsaturated diol (UD) was prepared from the esterification of maleic anhydride with diethylene glycol (DEG). Unsaturated polyesters modified with rosin (UPMR) or with rosin maleic anhydride adduct (RMA) from 2-hydroxyethylmethacrylate (HEMA) and rosin (UPMRH) were prepared by the reaction of UD with RMA or RMA-HEMA. After crosslinking of UPMR and UPMRH with styrene and methylmethacrylate (MMA), respectively, solvent resistance, tensile strength, and adhesion property of the resins were measured. UPMR crosslinked with styrene or MMA shows an excellent resistance to water and acid. Solvents resistance and tensile strength of UPMR using styrene as crosslinking agent were increased compared with those of UPMR using MMA as crosslinking agent. UPMRH showed better solvents resistance and tensile strength than UPMR. Adhesion strengths of UPMR crosslinked with styrene and MMA were 1.61 and 3.02 MPa, and those of UPMRH were 2.32 and 3.89 MPa, respectively.

• Macromolecular Research
• /
• v.13 no.5
• /
• pp.446-452
• /
• 2005

The interactions between the surface of scaffolds and specific cells play an important role in tissue engineering applications. Some cell adhesive ligand peptides including Arg-Gly-Asp (RGD) have been grafted into polymeric scaffolds to improve specific cell attachment. In order to make cell adhesive scaffolds for tissue regeneration, biodegradable nonporous poly(L-lactic acid) (PLLA) films were prepared by using a solvent casting technique with chloroform. The hydrophobic PLLA films were surface-modified by Argon plasma treatment and in situ direct acrylic acid (AA) grafting to get hydrophilic PLLA-g-PAA. The obtained carboxylic groups of PLLA-g-PAA were coupled with the amine groups of Gly-Arg-Asp-Gly (GRDG, control) and GRGD as a ligand peptide to get PLLA-g-GRDG and PLLA-g-GRGD, respectively. The surface properties of the modified PLLA films were examined by various surface analyses. The surface structures of the PLLA films were confirmed by ATR-FTIR and ESCA, whereas the immobilized amounts of the ligand peptides were 138-145 pmol/$cm^2$. The PLLA surfaces were more hydrophilic after AA and/or RGD grafting but their surface morphologies showed still relatively smoothness. Fibroblast adhesion to the PLLA surfaces was improved in the order of PLLA control

• International Journal of Highway Engineering
• /
• v.3 no.4 s.10
• /
• pp.117-126
• /
• 2001

In this research, evaluation of adhesion in tension property of SBR-modified concrete to ordinary portland cement concrete was conducted with uniaxial direct tensile bond test which was proposed by Kuhlmann. A test set-up was fabricated in order to minimize the eccentric force by introducing a joint which might fully rotate. The main experimental variables were cement-latex ratios, surface preparations and moisture levels. The results obtained were as follows: The LMC specimen at 15% latex-cement ratio increased the adhesion in tension by range of 37% compared to that of conventional cement concrete. This might be due to latex film formed between cement paste and aggregate. The effects of surface preparation on bond of latex modified concrete to conventional concrete were significant at the conditions by sand paper and wire brush. A better bond could be achieved by rough surface rather than smooth. The saturated and surface dry (SSD) condition were considered to be the most appropriate moisture level followed by wet, finally by dry. Thus, a proper surface preparation and moisture level are quite necessity in order to obtain better bonding at LMC overlay.

• Journal of the Korean Vacuum Society
• /
• v.21 no.2
• /
• pp.78-85
• /
• 2012

In order to improve the adhesion between poly-monochloro-para-xylylene (Parylene-C) film and Aluminum thin film, the surface of Parylene-C film was irradiated by ${O_2}^+$ and $Ar^+$ ion beam generated by duoplamatron ion source. The ion dose of $Ar^+$ and ${O_2}^+$ was changed from $5{\times}10^{14}$ to $1{\times}10^{17}/cm^2$ and the ion beam energy was 1 kV. Contact angles of water on Parylene-C modified by $Ar^+$ and ${O_2}^+$ ion irradiation decreased from $78^{\circ}$ to around $17^{\circ}$, and $9^{\circ}$, respectively. X-ray photoelectron spectroscopy analysis shows that the hydrophilic groups were formed on the surface of Parylene-C by chemical reaction between the unstable chains induced by the ion irradiation and oxygen ions or residual oxygen gas. The hydrophilic groups were identified as C-O bond, C=O bond and (C=O)-O bond. The cross cut tape test which was applied to characterize the adhesion between Al thin film and Parylene-C film modified by ${O_2}^+$ ions irradiation shows that the adhesion strength was improved as increasing ion dose.

• Textile Coloration and Finishing
• /
• v.27 no.1
• /
• pp.18-26
• /
• 2015

para-aramid fibers were treated by atmosphere air plasma to improve the interfacial adhesion. The wettability of plasma-treated aramid fiber was observed by means of dynamic contact angle surface free energy measurement. Surface roughness were investigated with the help of scanning electron microscopy and atomic force microscopy. The tensile test of aramid fiber roving was carried out to determine the effect of plasma surface treatments on the mechanical properties of the fibers. A pull-out force test was carried out to observe the interfacial adhesion effect with matrix material. It was found that surface modification and a chemical component ratio of the aramid fibers improved wettability and adhesion characterization. After oxygen plasma, it was indicated that modified the surface roughness of aramid fiber increased mechanical interlocking between the fiber surface and vinylester resin. Consequently the oxygen plasma treatment is able to improve fiber-matrix adhesion through excited functional group and etching effect on fiber surface.

• Journal of Adhesion and Interface
• /
• v.13 no.1
• /
• pp.1-8
• /
• 2012

The effect of the grafting ratio on the mechanical property and adhesion property of the grafted EPDM modified with methacrylic acid (MA) was investigated. The storage modulus of MA-grafted EPDM was maintained higher than that of cross-linked EPDM vulcanizate by sulfur, but it was observed that the storage modulus was decreased at elevated temperature because of the weakened secondary bonding. When the functional group for hydrogen bonding was introduced in EPDM, it had excellent mechanical properties by the aggregate between grafted EPDM molecules and crystallinity of MA. The bonding strength between EPDM and other rubbers was very low because EPDM has nonpolar property and low molecular interaction to others. The bonding strength was increased as increasing grafting ratio and it was excellent enough to break the rubber during the peel test when the grafting ratio was more than 10%.

• Applied Chemistry for Engineering
• /
• v.16 no.6
• /
• pp.725-730
• /
• 2005

In the development of biomaterials as a substitute of hard tissues, the biocompatibility and osteoconductivity of the biomaterial are considered to be one of the most significant considerations. These biological properties of a material can be greatly improved by the modification of the surface properties by the depositing calcium phosphate thin films on the material since calcium phosphate films possess similar chemical compositions to hard tissues. The success of a material as a biomaterial will be determined by the interaction of the surface of the material with the adhesion molecules which induce cellular adhesion and biological responses of the adherent cells. Depending on the adsorption mechanisms and adsorbed conformation of the adhesion molecules on the surface of the biomaterial, cellular responses, such as adhesion, proliferation and differentiation of osteoblast cells, can be promoted or restricted. It has been reported that materials of which surfaces were modified with thin films of calcium phosphate appeared to be more osteoconductive. Rapid formations of bone nodule in addition to higher differentiations of osteoblast have been observed on the calcium phosphate thin films.

• Proceedings of the Korea Concrete Institute Conference
• /
• 1998.10a
• /
• pp.368-373
• /
• 1998

Prepackaged system consists out of a dry mix which contains cement, sand, redispersible polymer powder and admixtures in the right proportions. The purpose of this study is to evaluate the quality of prepackaged-type polymer-modified mortar products using redispersible poly(ethylene-vinyl acetate)(EVA) powder. Polymer-modified mortars using the redispersible polymer powder with powdered with powdered shrinkage-reducing agent were prepared with cellulose fiber contents of 0, 0.5, 1.0% and shrinkage-reducing agent contents of 0, 4%, and tested for drying shrinkage, strength, adhesion in tension, water absorption. From the test results, the prepackaged-type polymer-modified mortar products with 4% of shrinkage-reducing agent content give good properties. and that their properties largely depends on the shrinkage-reducing agent content rather than the cellulose fiber contents.