• Journal of the Korean Physical Society
• /
• 제73권12호
• /
• pp.1873-1878
• /
• 2018

We have investigated the ionic conductivity and dielectric relaxation in $Li_2B_4O_7$ (LBO) and $Li_2O-B_2O_3-Ta_2O_5$ (LBTO) glasses. The sample was synthesized by using the melt quenching method. The frequency dependence of the electrical data from the LBO and LBTO glasses has been analyzed in the frameworks of the impedance Cole-Cole formalism and the universal power-law representation driven by the modified fractional Rayleigh equation. The potential barriers in the LBO and the LBTO glasses turn out to be the same. Comparing with the dc and ac activation energies of the LBO glass, these energies of the LBTO glass decrease due to the increasing Coulomb interaction of inter-cationic interaction.

• 폴리머
• /
• 제31권6호
• /
• pp.532-537
• /
• 2007

본 연구에서는 poly(vinyl alcohol)(PVA)를 dimethyl sulfoxide(DMSO)에 녹여 이 용액의 유변학적 특성에 미치는 PVA의 분자량분포의 영향에 관하여 고찰하였다. 동일 평균분자량인 경우에도 수지 혼합(resin blending)에 의해 분자량분포가 넓어지면 점도와 손실탄성률이 더 낮아짐을 알 수 있었다. 이것은 동일 평균 분자량의 경우 분자량분포가 넓은 PVA/DMSO 용액계의 자유체적이 증가되기 때문이라고 생각된다. 분자량 분포가 저장탄성률에 미치는 영향은, 14 wt%용액의 경우에는, 1.3 rad/sec보다 낮은 진동수 영역에서는 동일 평균분자량의 경우 분자량분포가 넓은 PVA/DMSO 용액계가 탄성이 더 크고, 1.3 rad/sec보다 높은 진동수 영역에서는 분자량분포가 좁은 PVA/DMSO 용액계가 탄성이 더 크게 측정되었다. 14 wt% 용액의 경우에 Modified Cole-Cole plot에서의 기울기는 분자량분포가 넓어지면 진동수에 따른 상전이 현상이 더 뚜렷해졌다.

• Korea-Australia Rheology Journal
• /
• 제20권2호
• /
• pp.73-77
• /
• 2008

The rheological properties of polar solutions are very sensitive to preparative methods as well as measuring conditions. The effects of dissolution temperature on the rheological properties of the solutions of polyvinyl alcohol (PVA) in dimethyl sulfoxide were investigated over the range of dissolution temperatures $70-130^{\circ}C$. Viscosity was increased as dissolution temperature was increased. PVA solutions prepared at 120 and $130^{\circ}C$ showed Bingham behavior, which became less noticeable with decreasing dissolution temperature. The modified Cole-Cole plot of the solutions gave slope less than 2, suggesting the solutions were a heterogeneous system irrespective of optical transparency. Further, the slope was decreased with increasing dissolution temperature, indicating that the solid character got more prominent as dissolution temperature was increased. However, the relaxation time of the solutions was little dependent on dissolution temperature.

• Korea-Australia Rheology Journal
• /
• 제19권1호
• /
• pp.1-5
• /
• 2007

By combining ultrasonic energy which is essential for the chain scission of polymer molecules and a multifunctional agent (MFA) having double bonds at its ends, we were able to modify the molecular structure of polycarbonate (PC) from linear to a branched structure during melt processing. The three double bonds in chain ends of MFA were expected to act as sites for trapping macroradicals of PC during the course of ultrasound-assisted mixing process. The transformation of molecular structure of PC was confirmed by the measurements of rheological properties of the modified PC. After the ultrasonic irradiation of PC together with MFA, increase in complex viscosities and shear-thinning behavior were observed. The Cole-Cole plot and measurement of extensional viscosities revealed the characteristic features of branched structure with well-defined extensional behavior which is comparable to that of a commercial branched PC.

• 폴리머
• /
• 제31권3호
• /
• pp.269-272
• /
• 2007

본 연구는 생분해성 고분자인 폴리락틱에시드(Poly(lactic acid; PLA)의 가공성을 향상시키는 연구의 일환으로 순수 PLA, 반응압출법에 의한 화학적으로 개질된 PLA 및 기능성 단량체를 함유한 PLA에 전자선을 조사하여 PLA를 개질한 후 유변학적 특성을 조사하였다. 유변학적 특성은 복합점도와 log G' vs. log G" 선도를 이용하여 해석 분석 비교하였다. 그 결과 전자선 조사로 개질된 순수 PLA 및 화학적으로 개질된 PLA의 복합점도는 전자선 조사량에 따라 감소하는 경향을 보였지만, 기능성단량체가 첨가된 PLA는 전자선 조사에 의해 복합점도가 증가하다가 감소하는 경향을 보였다.

• Korean Chemical Engineering Research
• /
• 제46권1호
• /
• pp.124-130
• /
• 2008

높은 용융강도가 요구되는 용도로 사용하기 위하여, 기능성 단량체인 glycidyl methacrylate(GMA)가 첨가된 poly(lactic acid)(PLA)를 전자선 조사로 개질하였다. GMA의 양과 전자선량을 조절하여 다양하게 개질된 PLA를 제조한 후 열적 특성, 용융 점탄성 성질 및 겔화도를 조사하였다. GMA를 첨가하지 않고 전자선 조사로만 개질한 PLA의 복합점도와 저장 탄성률은 원래의 PLA의 값보다 더 낮았고 조사량이 증가하면 더욱 낮아졌다. GMA을 0.1 phr 또는 0.3 phr로 첨가하여 개질한 PLA의 물성의 조사량에 따른 변화 경향은 GMA를 첨가하지 않고 개질한 PLA와 비슷하지만, 0.5 phr GMA를 함유하며 전자선 조사량 5 kGy로 개질된 PLA는 원래의 PLA보다 낮은 주파수 영역에서 3배나 큰 복합점도와 10배나 큰 저장탄성률을 보였다.

• 폴리머
• /
• 제34권5호
• /
• pp.485-489
• /
• 2010

본 연구에서는 폴리락트산(PLA)의 용융강도를 높이기 위하여 PLA에 글리시딜 메타크릴레이트(GMA)를 PLA에 첨가한 후 전자선을 조사하여 PLA를 개질하였다. GMA는 5 phr(parts per hundred parts of resin)로 고정하고 전자선 조사량을 변화시키며 개질 PLA을 제조하였으며, 이후 열적, 유변학적 특성 및 젤화도를 조사하였다. 주파수 0.1 rad/s에서 조사량 300 kGy로 개질된 PLA와 순수 PLA의 유변학적 물성을 서로 비교해보면 복합점도는 약 210배, 탄성률은 약 14500배 상승하는 예외적으로 아주 큰 변화를 보였다. 젤화도의 결과로 조사량 200 kGy 이하로 조사된 시료에서 일어난 분자반응은 가교화 반응보다는 가지화 반응이 우세하다는 것을 알 수 있었다.