• Bulletin of the Korean Chemical Society
• /
• v.30 no.7
• /
• pp.1598-1602
• /
• 2009

The particle size of Li[$Ni_{0.2}Li_{0.2}Mn_{0.6}]O_2$ cathode powder was controlled effectively by dispersion using lauric acid as a surfactant. The samples treated by lauric acid showed smaller particles of approximately half the original size compared to the particles of a pristine sample. A structural change due to the dispersion of Li[$Ni_{0.2}Li_{0.2}Mn_{0.6}]O_2$ powder was not detected. The rate performance of the Li[$Ni_{0.2}Li_{0.2}Mn_{0.6}]O_2$ cathode was improved by dispersion using lauric acid, which was likely due to the decrease of the particle size. In particular, a sample dispersed pristine powder using lauric acid (L2) presented a greatly enhanced discharge capacity and capacity retention at a high C rate. The discharge capacity of a pristine sample was only 133 m$Ahg^{-1}$ (3C rate) and 96 m$Ahg^{-1}$ (12C rate) at the tenth cycle. In contrast, the L2 electrode delivered higher discharge capacities of 160 m$Ahg^{-1}$ (3C rate) and 129 m$Ahg^{-1}$ (12C rate) at the tenth cycle. The capacity retention at a rate of 12C/2C was also enhanced from ~ 45% (pristine sample) to 57% (L2) by treatment with lauric acid.

• The Korean Journal of Ceramics
• /
• v.5 no.3
• /
• pp.250-254
• /
• 1999

Synthesis of the spinel $LiMn_2O_4$ by emulsion method was investigated. $LiOH.H_2O \;and \;Mn(NO_3)_2.6H_2O$ were used as starting materials to prepare mixed aqueous solution (0.5 mol/$\ell$ for the $LiMn_2O_4$). Kerosene, paraffin oil and span 80 were used for organic phase. The aqueous solutioin and organic phase were mixed in the ratio of 2:1 and emulsified at the speed of 4000 rpm for 5 min. The prepared emulsions were dropped into the petroleum heated at $170^{\circ}C$ to evaporate water in the silicon oil bath, dried at $120^{\circ}C$ in the oven the remove petroleum and calcined at temperature ranges from 600 to $900^{\circ}C$ for 48 hrs. The characteristics of powders were investigated by XRD, SEM, BET and electrochemical properties of synthesized cathode materials were measured with Galvanostatic system. $Li_{1.05}Mn_2O_4$ calcined at $800^{\circ}C$ for 48 hrs showed initial discharge capacity of 125.9mAH/g.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.3
• /
• pp.249-254
• /
• 2008

Ag doping effect on $Li[Ni_{0.2}Li_{0.2}Mn_{0.6}]O_2$ cathode material was studied. Specially, we focused on rate performance of Ag doped samples. The $Li[Ni_{0.2}Li_{0.2}Mn_{0.6}]O_2$ powder was prepared by simple combustion method and the Ag was doped using $AgNO_3$ during gelation process. Based on X-ray diffraction analysis, there was no structural change by Ag doping, but the 'metallic' form of Ag was included in the doped powder. Both bare and Ag 1 wt.% doped sample showed similar discharge capacity of 242 mAh/g at 0.2C rate. However, as the increase of charge-discharge rate to 3C, Ag 1 wt.% doped sample showed higher discharge capacity (172 mAh/g) and better cyclic performance than those of bare sample. The discharge capacity of Ag 5 wt.% doped sample was relatively low at all rate condition. However it displayed better rate performance than other samples.

• Journal of Electrochemical Science and Technology
• /
• v.2 no.2
• /
• pp.97-102
• /
• 2011

Different amounts of excess lithium in the range of x = 0~0.3 were added to $Li_{1+x}[Mn_{0.720}Ni_{0.175}Co_{0.105}]O_2$ cathode materials synthesized using the co-precipitation method to investigate its microstructure and electrochemical properties. Pure layered structure without impurities was confirmed in the XRD pattern analysis and increasing peak intensity of $Li_2MnO_3$ was observed along with the addition of over 0.2 mol Li. The initial discharge capacity of the stoichiometric composition was determined to be 246 mAh/g, while the discharge capacity of the addition of 0.1 mol Li was obtained to be 241 mAh/g, which was not significantly different from that of the stoichiometric composition. However, the discharge capacities decreased dramatically after the addition of 0.2 and 0.3 mol Li to 162 mAh/g and 146 mAh/g, respectively. In the rate capability test, the active $Li_{1+x}[Mn_{0.720}Ni_{0.175}Co_{0.105}]O_2$ cathode material of the stoichiometric composition showed a dramatic decrease in its discharge capacity with increasing C-rate, as evidenced by the result that the discharge capacity at 5C was 13% compared with 0.1C. On the other hand, the discharge capacity of compositions containing excess lithium was improved at higher current rates. The cycling test showed that the composition containing an excess of 0.1 mol Li had the most outstanding capacity retention.

• Journal of Electrochemical Science and Technology
• /
• v.12 no.2
• /
• pp.272-278
• /
• 2021

In this study, high nickel layered LiNi_0.8Co_0.1Mn_0.1O₂ cathode materials for lithium-ion batteries were modified by yttrium doping and poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) coating. The effects of yttrium doping and PEDOT:PSS coating on the structural and electrochemical properties of the LiNi_0.8Co_0.1Mn_0.1O₂ cathode material were investigated and compared. The substitution of nickel with an electrochemically inert yttrium was confirmed to be successful in stabilizing the layered structure framework. Moreover, coating the surfaces of the LiNi_0.8Co_0.1Mn_0.1O₂ particles with a conductive polymer, PEDOT:PSS, improved the capacity retention, thermal stability, and impedance of the cathode material by increasing its ionic and electric conductivities.

• Proceedings of the Korean Ceranic Society Conference
• /
• 2000.10a
• /
• pp.129.1-129
• /
• 2000

• Journal of Electrochemical Science and Technology
• /
• v.7 no.4
• /
• pp.245-250
• /
• 2016

The layered $Na_{0.6}Li_{0.6}[Mn_{0.72}Ni_{0.18}Co_{0.10}]O_2$ composite with well crystalized and high specific capacity is prepared by molten-salt method and using the substitution of Na for Li-ion battery. The effects of annealing temperature, time, Na contents, and electrochemical performance are investigated. In XRD analysis, the substitution of Na-ion resulted in the P2-$Na_{2/3}MO_2$ structure ($Na_{0.70}MO_{2.05}$), which co-exists in the $Na_{0.6}Li_{0.6}[Mn_{0.72}Ni_{0.18}Co_{0.10}]O_2$ composites. The discharge capacities of cathode materials exhibited $284mAhg^{-1}$ with higher initial coulombic efficiency.

• Journal of Powder Materials
• /
• v.21 no.2
• /
• pp.131-136
• /
• 2014

Cathode materials and their precursors are prepared with transition metal solutions recycled from the the waste lithium-ion batteries containing NCM (nickel-cobalt-manganese) cathodes by a $H_2$ and C-reduction process. The recycled transition metal sulfate solutions are used in a co-precipitation process in a CSTR reactor to obtain the transition metal hydroxide. The NCM cathode materials (Ni:Mn:Co=5:3:2) are prepared from the transition metal hydroxide by calcining with lithium carbonate. X-ray diffraction and scanning electron microscopy analyses show that the cathode material has a layered structure and particle size of about 10 ${\mu}m$. The cathode materials also exhibited a capacity of about 160 mAh/g with a retention rate of 93~96% after 100 cycles.

• Korean Journal of Materials Research
• /
• v.31 no.2
• /
• pp.68-74
• /
• 2021

Zinc-ion Batteris (ZIBs) are recently being considered as energy storage devices due to their high specific capacity and high safety, and the abundance of zinc sources. Especially, ZIBs can overcome the drawbacks of conventional lithium ion batteris (LIBs), such as cost and safety issues. However, in spite of their advantages, the cathode materials under development are required to improve performance of ZIBs, because the capacity and cycling stability of ZIBs are mainly influenced by the cathode materials. To design optimized cathode materials for high performance ZIBs, a novel manganese oxide (MnO2) coated graphite sheet is suggested herein with improved zinc-ion diffusion capability thanks to the uniformly decorated MnO2 on the graphite sheet surface. Especially, to optimize MnO2 on the graphite sheet surface, amounts of percursors are regulated. The optimized MnO2 coated graphite sheet shows a superior zinc-ion diffusion ability and good electrochemical performance, including high specific capacity of 330.8 mAh g-1 at current density of 0.1 A g-1, high-rate performance with 109.4 mAh g-1 at a current density of 2.0 A g-1, and remarkable cycling stability (82.2 % after 200 cycles at a current density of 1.0 A g-1). The excellent electrochemical performance is due to the uniformly decorated MnO2 on the graphite sheet surface, which leads to excellent zinc-ion diffusion ability. Thus, our study can provide a promising strategy for high performance next-generation ZIBs in the near future.

• Bulletin of the Korean Chemical Society
• /
• v.29 no.9
• /
• pp.1695-1698
• /
• 2008