• 한국재료학회지
• /
• 제13권4호
• /
• pp.228-232
• /
• 2003

The effects of$ Nd_2$$O_3$addition on the properties of Mn-Zn ferrite were investigated in the doping concentration range from 0.05 to 0.25 wt%. All samples were prepared by standard fabrication of ferrite ceramics. With increasing the Neodymium oxides, specific density and initial permeability increased on the whole. But, the tendencies such as upper result had the measured value on limitation and characteristics saturated or decreased properties after that. With increasing the content of Neodymium oxides. both the real and imaginary component of complex permeability and the magnetic loss(tan$\delta$) increased. Because reason that magnetic loss increases is high ratio that a real department increases than imaginary department. Magnetic loss increased none the less for increasing the real department related with magnetic permeability. But, the magnetic loss of ferrite doped with the Neodymium oxides were lower than that of none doped Mn-Zn ferrite. The small amount of percent Neodymium oxides in Mn-Zn ferrite composition led to enhancement of resistivity in bulk, and more so in the grain boundary.

• 자원리싸이클링
• /
• 제17권1호
• /
• pp.66-72
• /
• 2008

폐알칼리망간전지로부터 침출과 공침반응을 이용하여 Mn-Zn ferrite 분말을 제조하기 위한 기초실험을 수행하였다. 100g/L 광액 농도 3.0M $H_2SO_4$, $60^{\circ}C$ 및 교반속도 200 rpm의 조건에서 과산화수소 30ml를 첨가하여 얻어진 아연과 망간의 침출율은 각각 97.9%, 93.9% 이상이었으며, 침출용액을 가지고 반응시간, 반응온도, $O_2$ 가스량을 조절하며 공침반응을 진행하였다. 공침반응 결과 pH 12, $80^{\circ}C$, $O_2$ 1.3L/min, 교반속도 400 rpm의 조건에서 Mn-Zn ferrite를 저온 합성할 수 있었다. 합성된 Mn-Zn ferrite분말은 $0.143{\mu}m$의 구형 ferrite로서 80 emu/g의 포화자화값을 가지고 있었다.

• 한국세라믹학회지
• /
• 제36권3호
• /
• pp.255-259
• /
• 1999

높은 투자율과 낮은 손실특성을 지닌(Mn, Zn)ferrite의 전자기적 특성은 소결공정과 소결분위기에 따라 상당히 다양하게 나타난다. 본 연구에서는(Mn, Zn)ferrite를 소결시킬 때의 승온속도와 냉각속도에 따른 초투자율 특성과 미세구조의 관계에 관하여 고찰하였다. 승온속도의 영향을 고찰하기 위하여 spinel ferrites 생성 및 결정입 성장 거동에 가장 중요한 온도인 800~120$0^{\circ}C$의 범위에서 속도를 변화시켰고, 냉각속도 영향을 살펴보기 위하여 1100~80$0^{\circ}C$ 온도범위를 택하였다. 열처리 온도범위 800~120$0^{\circ}C$에서 승온속도가 증가함에따라 초투자율이 7$^{\circ}C$/min까지는 증가했으나 그 이상의 승온속도에서는 오히려 초투자율이 감소하였다. 또한 1100~80$0^{\circ}C$ 온도범위에선 냉각속도가 증가될수록 초투자율이 감소하는 경향을 나타내었다. 치밀화 및 투자율을 높이기 위하여 첨가된 CaO, SiO2, V2O5의 분포상태를 분석한 결과, 이들 첨가물들은 입자와 입계를 따라 균일하게 분포하는 것으로 나타났다.

• 한국항해항만학회:학술대회논문집
• /
• 한국항해항만학회 2000년도 추계학술대회논문집
• /
• pp.93-96
• /
• 2000

In this study, we investigated the electromagnetic properties of Mn-Zn ferrite doped with rare earth oxide (Dy$_2$O$_3$, Er$_2$O$_3$). The main composition is 52mo1% $\alpha$-Fe$_2$O$_3$, 25mo1% Mn$_3$O$_4$23mo1% ZnO and doped with them(0.05wt%~0.25wt%, step:0.05wt%). An experimental process has advanced by conventional ferrimagnetism manufacturing that was prepared by standard ceramic techniques. The XRD pattern of all doped sample were observed spinel and secondary phase. The density of sample were measured nearly constant value. As increased the additive, resistivity, initial permeability and real component of the series complex permeability increased with setting limits each other. In case of Mn-Zn ferrite excess doped with them, resistivity, initial permeability and real component of the series complex permeability decreased and magnetic loss increased in proportion to increasing the additive.

• Journal of Welding and Joining
• /
• 제8권2호
• /
• pp.27-39
• /
• 1990

The effect of silicon and manganese, in the ranges of 0.3% to 1.0wt% Si and 0.7 to 2.6wt%Mn, on the microstructure and mechanical properties of flux cored arc welded deposits have been investigated for the purpose of improving mechanical properties. Microstructure of weld metals was mainly influenced by manganese content, and manganese increased the volum fraction of acicular ferrite and refined the microstructure. Also, tensile properties were governed by manganese content, ultimate tensile strength and yield strength were increased by approximately 82MPa and 58MPa per 1% Mn addition to the deposit. Toughness was improved by increasing Mn content and lowering Si content. Optimal impact properties were obtained at above 1.8wt% Mn and below 0.5wt% Si. Acicular ferrite was predominant factor in improving mechanical properties. Formation of acicular ferrite was promoted by manganese and no direct relationship between AF(acicular ferrite) proportion and oxygen in weld metal was found.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2000년도 추계학술대회 논문집
• /
• pp.93-96
• /
• 2000

In this study, we investigated the electromagnetic properties of Mn-Zn ferrite doped with rare earth oxide (Dy$_2$O$_3$, Er$_2$O$_3$). The main composition is 52mo1% ${\alpha}$-Fe$_2$O$_3$, 25mol% Mn$_3$O$_4$ 23mo1% ZnO and doped with them(0.05wt% ∼ 0.25wt%, step:0.05wt%). An experimental process has advanced by conventional ferrimagnetism manufacturing that was prepared by standard ceramic techniques. The XRD pattern of all doped sample were observed spinel and secondary phase. The density of sample were measured nearly constant value. As increased the additive, resistivity, initial permeability and real component of the series complex permeability increased with setting limits each other. In case of Mn-Zn ferrite excess doped with them, resistivity, initial permeability and real component of the series complex permeability decreased and magnetic loss increased in proportion to increasing the additive.

• 자원환경지질
• /
• 제36권5호
• /
• pp.381-385
• /
• 2003

본 연구는 폐산화철을 이용한 폐수 중금속 제거 가능성을 알아보고자 시도되었다. 실제 폐수와 폐산화철을 적용하기에 앞서 상업적으로 구입가능한 Mn-ferrite를 이용하여 실내 회분식 시험을 통한 흡착실험을 실시하여 pH, 접촉시간, 중금속 농도 및 온도 등과 같은 다양한 흡착 조절인자들을 이용하여 페라이트에 의한 Cd과 Pb의 흡착 및 제거특성을 알아보았다. 접촉시간을 1에서 360분까지 변화하여 흡착속도를 측정하였으며 일정온도에서 Cd와 Pb의 농도를 변화시켜 흡착등온선을 구하였다. 또한 온도(15∼35$^{\circ}$)와 pH(4∼10) 변화에 따른 흡착특성 변화를 고찰하였다. Cd과 Pb는 Freundlich 식에 잘 맞았으며 Cd에 비하여 Pb가 더 흡착이 잘 되었다. pH가 높을수록 Cd와 Pb가 더 잘 흡착되었으며 이는 pH증가에 따라 수소이온 농도가 감소하고 결과적으로 표면의 흡착가용 장소가 증가하기 때문인 것으로 생각된다. 같은 pH에서 원소의 농도가 증가할 때 흡착이 더 잘 일어났다. 온도 역시 Pb와 Cd의 흡착능에 영향을 미쳤으며 Pb의 경우 온도가 증가할수록 흡착정도가 높아지는 반면 Cd의 경우 덜 흡착이 되었다. Cd는 Pb에 비하여 더 온도에 영향을 받으며 이러한 Cd와 Pb의 흡착특성 차이는 Cd에 비하여 Pb가 더 hard한 특성 때문인 것으로 생각된다. 본 연구는 폐산화철을 이용하여 각종 폐수 중금속을 제거하는 공정에 사용될 수 있음을 시사한다.

• 한국표면공학회지
• /
• 제25권1호
• /
• pp.1-7
• /
• 1992

The formation of manganese ferrite has been performed to investigate some properties according to the variation of compositions, pH, current density by electrolysis. It has been found that the amount of oxidized weight of anode were increased with increasing current density. The amount of oxidized weight of anode were most in pH 10. As the result of X-ray diffraction Mn Fe₂O₄ crystal composition in pH13. When the particles of Mn/sub x/ Fe/sub 3-x/O₄ were heated at 300℃, it has been shown typical Mn Fe₂O₄(JCPDS Card No. 10-319) in X=1 composition. As the result of SEM observation, the size of MnFe₂O₄ particles were about 0.1㎛, the shape of particles were spherical type. According to the above mentioned experimental condition, 0.1-0.5㎛ sub-micron particles of manganese ferrite were formed from the wasted manganese dry cell, through washing → reduction → electrloysis.

• 한국수소및신에너지학회논문집
• /
• 제14권3호
• /
• pp.268-275
• /
• 2003

The water-splitting process by the metal oxides using solar heat is one of the hydrogen production method. The hydrogen production process using the metal oxides (NiFe2O4/NiAl2O4,CoFe2O4/CoAl2O4, CoMnNiFerrite, CoMnSnFerrite, CoMnZnFerrite, CoSnZnFerrite) was carried out by two steps. The first step was carried out by the CH4-reduction to increase activation of metal oxides at operation temperature. And then, it was carried out the water-splitting reaction using the water at operation temperature for the second step. Hydrogen was produced in this step. The production rates of H2 were 110, 160, 72, 29, 17, $21m{\ell}/hr{\cdot}g-_{Metal\;Oxide}$ for NiFe2O4/NiAl2O4, CoFe2O4/CoAl2O4, CoMnNiFerrite, CoMnSnFerrite, CoMnZnFerrite, CoSnZnFerrite respectively in the second step. CoFe2O4/CoAl2O4 had higher H2 production rate than the other metal oxides.

• 한국토양환경학회지
• /
• 제1권2호
• /
• pp.51-60
• /
• 1996

본 연구에서는 산업폐기물로 버려지는 hematite와 ferrite를 이용하여 Mn-EDTA와 불소의 제거에 대한 실험을 행하였다. 제거율을 비교, 평가하기 위하여 무기오염물에 대하여 우수한 흡착능을 가지는 것으로 알려진 Na-bentonite를 실험에 포함하였다. Batch형태의 실험 결과, 망간에 대하여 여러 초기농도에서 ferrite-A는 48∼65 %, ferrite-B는 46∼57 %, hematite 의 경우 17∼26%o의 제거율을 갖는 것으로 나타났으며, Na-bentonite의 경우, 10∼23%의 제거율을 나타냈다. 불소의 경우에는 hematite가 53∼63%의 제거율을, ferrite-A가 54∼63%, ferrite-B는 20∼38%를 보였다. 연구 결과 Hematite와 Ferrite가 가지고 있는 특히 complex ion을 형성하는 무기 오염 물질 제거능이 Na-bentonite 보다 우수한 것으로 나타났다. 결론적으로 이러한 산화 광물과 Na-Bentonite 의 혼합을 통하여 차수재로서의 Na-bentonite의 역할을 증진시킬 수 있을 것이다.