• Transactions on Electrical and Electronic Materials
• /
• v.8 no.3
• /
• pp.121-124
• /
• 2007

The $Zn_2SiO_4:Mn$ phosphors were prepared using polymer matrix technique in order to improve the performance of green emitting phosphors for plasma display panel(PDP). $Zn_2SiO_4:Mn$ phosphor exhibits a strong green emission around 520-530 nm. The emission intensity and particle size of powders were controlled by sintering temperature and raw material composition. The zinc silicate $Zn_2SiO_4:Mn$ single phase were obtained at lower temperature than prepared by solid-state reaction method. PL luminance of $Zn_2SiO_4:Mn$ phosphor was similar to the commercial material.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.11a
• /
• pp.93-96
• /
• 2000

In this study, we investigated the electromagnetic properties of Mn-Zn ferrite doped with rare earth oxide (Dy$_2$O$_3$, Er$_2$O$_3$). The main composition is 52mo1% ${\alpha}$-Fe$_2$O$_3$, 25mol% Mn$_3$O$_4$ 23mo1% ZnO and doped with them(0.05wt% ∼ 0.25wt%, step:0.05wt%). An experimental process has advanced by conventional ferrimagnetism manufacturing that was prepared by standard ceramic techniques. The XRD pattern of all doped sample were observed spinel and secondary phase. The density of sample were measured nearly constant value. As increased the additive, resistivity, initial permeability and real component of the series complex permeability increased with setting limits each other. In case of Mn-Zn ferrite excess doped with them, resistivity, initial permeability and real component of the series complex permeability decreased and magnetic loss increased in proportion to increasing the additive.

• Journal of the Korean Magnetics Society
• /
• v.5 no.4
• /
• pp.269-274
• /
• 1995

The basic composition of Mn-Zn ferrite was $Mn_{0.631}Zn_{0.316}Fe_{2.053}O_{4}$(specimen A), $Mn_{0.584}Zn_{0.312}Fe_{2.104}O_{4}$(specimen B) and $Mn_{0.538}Zn_{0.308}Fe_{2.154}O_{4}$(specimen C) with additional 0.1 mol % $CaCo_{3}$ and 0.04 mol % $V_{2}O_{5}$. For high per¬meability and acceleration of grain growth, $CaCo_{3}$ and $V_{2}O_{5}$. was added. The mixture of the law materials was calcinated at $950^{\circ}C$ for 3 hours and then milled. The compacts of toroidal type were sintered at different temperature($1250^{\circ}C$, $1300^{\circ}C$, $1350^{\circ}C$) for 2 hours in $N_2$ atmosphere. The effects of the various raw material composition and sintered temperature on the physical properties of Mn-Zn ferrite have been investigated. They turned out to be spinel structure by X-ray diffraction and the size of grain from SEM was from $18\;\mu\textrm{m}\;to\;23\;\mu\textrm{m}$. As the sintering temperature was increased from $1250^{\circ}C$ to $1350^{\circ}C$, the initial permeability and magnetic induction has increased and the both of Q factor and coercive force has decreased. The coercive force and curie temperature were almost the same at each specimen Their values were about 0.45 Oe and $200^{\circ}C$. The frequency of specimen will used in the range from 200 kHz to 2 MHz. The basic composition of $Mn_{0.584}Zn_{0.312}Fe_{2.104}O_{4}$(specimen B) sintered at $1300^{\circ}C$ shows the best results at magnetic induction (Br & Bm).

• Journal of The Korean Society of Grassland and Forage Science
• /
• v.23 no.4
• /
• pp.237-246
• /
• 2003

This pot experiment was conducted in order to find out the effects of application of combined micronutrients(T$_1$: control. T$_2$; Fe, T$_3$; Fe+Mn, T$_4$； Fe＋Mn＋Cu, T$_{5}$; Fe+Mn+Cu＋Zn, T$_{6}$；Fe+Mn+Cu＋Zn+Mo, T$_{7}$； Fe+Mn+Cu+Zn+Mo+B) on forage performance of pure and mixed cultures of orchardgrass and white clover The 2nd part was concerned with the changes in the forage yields and concurrence index. The results obtained are summarized as follows: 1. The effects of combined micronutrient applications on the forage yields were different according to the forage species, whether it was a pure or mixed cultures, and additional fertilization(especially N). The effects of them on the forage productivity and botanical composition were more obvious in white clover, especially in mixed culture, than in orchardgrass. By the significant role of B as a regulator, the yields of both forages were best in the T$_{7}$, respectively. 2. In the pure culture, the high yields of both forages were obtained by the T$_{7}$ and T$_2$, whereas the T$_{6}$ and T$_3$resulted in the low yields. The best yields of both forages were obtained by the T$_{7}$ with relatively optimum ratios among the micronutrients as follows; Fe/Mn/Cu/Zn, Fe/Mo, Mo/B, and ∑ cation/∑anion. It was observed the multiple interaction of Fe${\times}$Mn${\times}$Mo${\times}$B, and the significant role of B as a regulator. The effects of them on white clover were more distinct at no additional fertilization than at the additional fertilization(especially N). 3. In mixed culture, the optimum applications of them resulted in the positive increase of yield and botanical composition of white clover, whereas orchardgrass tended to be inversely except the T$_{7}$.X> 7/. 7/.

• Journal of Korean Vacuum Science & Technology
• /
• v.4 no.3
• /
• pp.68-72
• /
• 2000

We have deposited Mn on Pd(oon) at RT up to 30 ML. LEED pattern changed from p($1{\times}1$) to c($2{\times}2$) order below 0.5 ML Mn deposition. During Mn deposition, we have not found any changes in the peak position and the intensity of LEED I/V curve. Using LEED I/V curve analysis for each coverage, we found atomic structure and surface composition of c($2{\times}2$) ordered Mn alloy on Pd(001) surface. Above 1 Ml Mn, in the first layer the Mn subplane lies above the Pd subplane by 0.32 ${\AA}$. This result is very different from the earlier result of Jona et al., who contended that after annealing at 200 for 2 min, a buckled first layer with the Mn subplane lower than the Pd subplane by 0.2 ${\AA}$.

• Korean Journal of Human Ecology
• /
• v.9 no.3
• /
• pp.69-79
• /
• 2006

The previous studies on the intake of trace elements performed in Korea were only concerned about major elements like Fe, Zn or Cu. There is little data about the intake of minor elements like Mn, Se, Mo or Cr. And most of the data were obtained by calculation using Food Composition Tables or by analysis using atomic absorption spectrophotometers (AAS). The purpose of this study, therefore, was to evaluate the dietary intake of seven trace elements, Fe, Zn, Cu, Mn, Se, Mo, and Cr of Korean adult wonmen and to compare the data between analyzed using ICP-MS (or ICP-AES) and calculated by the CAN-Pro (or Food Composition Table). A total of nineteen adult women participated voluntarily in this study and collected one-tenth of the foods that they consumed for three consecutive days. Analyzed intake of Fe of the subjects was $6.94{\pm}2.18$ (calculated, $18.87{\pm}4.50$) mg/day, that of Ze was $9.35{\pm}4.95$ (calculated, $8.35{\pm}2.87mg/day$), that of Cu was $1.18{\pm}0.26\;(1.11{\pm}0.32mg/day)$, that of Mn was $3.69{\pm}0.69\;(2.83{\pm}1.68mg/day)$, that of Se was $41.93{\pm}9.28$ (calculated, $27.58{\pm}6.97{\mu}g/day$), that of Mo was $134.0{\pm}49.1{\mu}g/day$, and that of Cr was $136.5{\pm}147.9{\mu}g/day$. The analyzed Fe intake of the subjects did not meet Estimated Average Requirement (EAR) nor Recommended Intakes (RI) for Korean women aged 20-29 years old. However, the analyzed intakes of the other six elements, Zn, Cu, Mn, Se, Mo, and Cr, seemed to meet each of the respective RIs. The analyzed Fe intake was significantly lower than the calculated one, in fact by 2.72 times, however, the analyzed intakes of the other elements, Mn and Se, were significantly higher and those of Zn and Cu were similar than each of the calculated ones. The difference of the data between analyzed and calculated intakes indicates that it is necessary to set up database on trace element contents of foods of the Food Composition Table and the CAN-Pro so as to have accuracy.

• Bulletin of the Korean Chemical Society
• /
• v.14 no.2
• /
• pp.297-299
• /
• 1993

• Korean Journal of Materials Research
• /
• v.10 no.6
• /
• pp.437-444
• /
• 2000

We investigated the effect of substrate temperature, chemical composition and post-deposition heat-treatment on the crystal structure and electrical transport of $La_{1-x}Sr_xMnO_{3-{\delta}}$(0.19${\leq}x{\leq}$0.31) thin films. As-prepared $La_{1-x}Sr_xMnO_{3-{\delta}}$ films grown at $500^{\circ}C$ by sputter techniques were found to have the pseudo-tetragonal system(a/c=0.97) and a highly preferential <001> orientation. The films were changed to be of the cubic system by post-deposition annealing at around $900^{\circ}C$. A main target of $La_{0.67}Sr_{0.33}MnO_3$ as well as auxliary targets of $La_{0.3}Sr_{0.7}MnO_3$ ceramics were co-sputtered to control the chemical composition of the film. The Sr content(x) of the film ranged from 0.19 to 0.31, depending on the number of the auxiliary target. When x increased from 0.19 to 0.31, the electrical resistivity of the film decreased and the transition temperature between metal and semiconductor shifted to higher temperature. With a magnetic field of 0.18 T, the magneto-resistance ratio (MR(%) = (${\rho}_o-{\rho}_H/{\rho}_H$) of the $La_{0.69}Sr_{0.31}MnO_3$ thin film was about 390%.

• Journal of Powder Materials
• /
• v.4 no.4
• /
• pp.243-251
• /
• 1997

Engine valve-shaped TiAl-Mn intermetallics containing 43.5 to 47.5at%Al (Mn/Al=0.036) are successively fabricated by reactive sintering the elemental powder mixtures near-net shaped by extrusion and die forging. A duplex structure consisted of lamellar grains and equiaxed $\gamma$ grains is developed for all compositions, and the areal fraction of the lamellar grains(or equiaxed $\gamma$ grains) decreases (or increases) with increasing Al content. As Al content increased, the elongation increases with accompanying decrease in yield strength and ultimate tensile strength at both room temperature and 80$0^{\circ}C$. This indicates that the suitable composition is Ti-45at%Al-1.6at%Mn in considering the balance of ambient and elevated tensile properties. The reactive-sintered Ti-45Al-1.6Mn alloy shows superior oxidation resistance not only to the plasma arc melted one but also to the heat resistance steel STR35(representative exhaust valve head material for automotive engine). The reactive-sintered Ti-45Al-1.6Mn alloy coated with an oxidizing scale exhibits a better wear resistance than induction hardened martensitic steel STR11(representative exhaust valve tip material for automotive engine).

• Korean Journal of Materials Research
• /
• v.13 no.9
• /
• pp.619-624
• /
• 2003

This paper describes a method to control Mn and Fe contents in recycled AZ91D ingots, based on the mutual solubility of Mn and Fe in AZ91 alloy melts. For this purpose, Fe solubility with the change of Mn content and temperature was investigated in the homogenized and re-precipitated liquid AZ91 alloy. The increase of the amount of Mn added to the melt resulted in the decrease of Fe content. The data obtained in this study was adopted to the pilot plant for recycling of the scrap. As a result, Mn and Fe contents measured in the recycled ingot were in good agreement with ASTM B93 standard.