• 한국세라믹학회지
• /
• 제34권6호
• /
• pp.583-590
• /
• 1997

The effects of Mn2O3 and Y2O3 additives on the microstructure and dielectric properties of Sr(Zr, Ti)O3 have been investigated. Powders with Sr(Zr1-xTix)O3(0$\leq$x$\leq$0.1) composition were prepared by the conventional solid state processing from commercial TiO2 and precipitation-processed ZrO2. The powders containing sintering additives of Mn2O3 and Y2O3 were compacted and then sintered at 1,55$0^{\circ}C$ for 4 h to get>97% relative density. Mn2O3 suppressed the grain growth and Y2O3 enhanced the density of sintered body. The oxidation state of Mn ions were determined by a chemical wet method and EPR spectroscopy. Mn ions were present as Mn2+ and Mn4+ in SrZrO3, while as Mn3+ and Mn4+ in Ti-substituted Sr(Zr, Ti)O3. With the substitution of Ti, the lattice parameters of SrZrO3 decreased and its dielectric constant increased with remarkable decrease in Q value. The dielectric constant of Sr(Zr, Ti)O3 was in the range of 30 to 40, Q values 1,200~5,400 at 6 GHz and temperature coefficient of resonant frequency -67~100 ppm/K.

• 공업화학
• /
• 제25권5호
• /
• pp.474-480
• /
• 2014

본 연구에서는, $Mn/TiO_2$ 촉매를 이용하여 일산화질소의 산화반응 특성에 따른 연구가 수행되었다. $TiO_2$의 물리 화학적 특징 및 활성금속인 Mn과 담체인 $TiO_2$의 interaction에 따라 일산화질소의 산화반응이 서로 다르게 나타남을 관찰하였다. 우수한 NO oxidation 반응을 나타낸 $Mn/TiO_2(A)$의 경우, Mn의 함량이 10 wt%에서 30 wt%로 증가할수록, 공간속도가 낮아질수록, 반응활성이 증가함을 확인하였다. 이러한 결과를 바탕으로 SCR 전단에 $Mn/TiO_2$ 촉매를 사용함으로써, fast-SCR을 유도하여 SCR반응활성이 증진될 수 있을 것으로 판단된다.

• 공업화학
• /
• 제23권2호
• /
• pp.190-194
• /
• 2012

다양한 상용 $TiO_2$ 담체를 이용한 10 wt%의 Mn계 촉매를 습윤함침법으로 제조하여 $NH_3$에 의한 NO의 저온 선택적 촉매환원법(SCR) 반응 특성을 연구하였다. 촉매의 특성은 BET, XRD, XPS 그리고 TPR과 같은 물리화학적 분석을 통해 수행되었다. MnOx/$TiO_2$ 촉매의 MnOx 표면밀도는 비표면적에 영향을 받는다. 고분산된 망간산화물에 의한 낮은 MnOx surface density로 저온 SCR 활성이 증가하고 망간산화물의 $MnO_2$에서 $Mn_2O_3$로 환원되는 온도가 감소되었다. 우수한 SCR활성을 위해서는 망간산화물을 높은 비표면적을 가진 $TiO_2$에 담지되어야 하고 고분산된 비정질종이 존재해야 한다.

• 한국세라믹학회지
• /
• 제34권2호
• /
• pp.123-130
• /
• 1997

본 연구에서는 유전상수가 크고, 유전체 손실이 적으며, 사용온도 범위에서 정전용량 변화율(TCC : tem-perature coefficient of capacitance)이 작고, 고압에 견딜 수 있는 재료를 개발하기 위하여 중고압용 capacitance의 기본재료로써 (Sr.Pb.Ca)TiO3-xBi2O3.3TiO2 계에서 Bi2O3.3TiO2의 mol.%를 5, 6, 7, 8, 9 mol.%로 변화시켰으며, 그 결과 고용한계 함량이 6mol.%이며, 6mol.%이상에서는 침상구조의 증가에 기인하여 유전율이 다시 감소하는 경향을 보였다. dopant로써 SiO2, Nb2O3, MnO2를 선정하여 첨가한 결과, MnO2를 첨가한 것이 유전성질이 가장 우수하였으며, MnO2의 함량이 0, 0.15, 0.3, 0.45 wt.% 증가함에 따라서 유전율의 감소와 동시에, TOC특성의 급격한 향상을 가져왔다.

• 한국산학기술학회논문지
• /
• 제17권7호
• /
• pp.713-719
• /
• 2016

암모니아를 환원제로 사용하는 선택적 촉매 환원법에서 Mn-Cu-$TiO_2$ 촉매와 $V_2O_5$/$TiO_2$ 촉매를 사용하여 반응 조건에 따른 질소 산화물 전환 특성을 연구하였다. 반응 온도와 공간 속도를 변경시키면서 촉매의 질소 산화물 전환 효율 변화를 측정하였다. Mn-Cu-$TiO_2$ 촉매의 질소 산화물 제거 활성은 반응 온도와 공간 속도가 증가할수록 감소하였으나, $V_2O_5$/$TiO_2$ 촉매의 경우 반응 온도 증가에 따라 촉매의 질소 산화물 제거 활성 또한 증가하였다. Mn-Cu-$TiO_2$ 촉매의 경우 $200^{\circ}C$ 이하의 온도에서 저온 활성이 우수하였으며, 이를 $H_2$-TPR 및 XPS 분석 실험을 통해 확인할 수 있었다. 초기 반응 온도의 변경 실험을 통해 Mn-Cu-$TiO_2$ 촉매의 경우 고온에서 열적 쇼크를 일부 받으나, $V_2O_5$/$TiO_2$ 촉매의 경우는 거의 영향을 받지 않음을 확인할 수 있었다. 공간 속도에 따른 질소 산화물 전환 효율 변화는 C 촉매의 경우 전 구간에 걸쳐 공간 속도가 증가할수록 질소 산화물 전환 효율도 감소하는 경향을 보였다. 그러나 D 촉매의 경우 공간 속도가 증가할수록 질소 산화물 전환 효율은 감소하였으나, 감소 정도가 C 촉매 보다는 훨씬 적었다.

• 한국결정성장학회지
• /
• 제13권2호
• /
• pp.63-67
• /
• 2003

Synthesis of $PbLaTiO_{3}$ : Mn powders containing La and Mn was carried out using $PbO,\;TiO_{2},\;La_{2}O_{3}\;and\;MnO_{2}$ as starting materials by hydrothermal method. In the synthesis of single phase $PbLaTiO_{3}$ : Mn powder containing La and Mn, the optimal x value corresponding to La substitution was 0.01 which corresponds to $0.99(Pb_{1-x}La_{2x/3}TiO_{3})+0.01MnO_{2}$. The optimal conditions for the preparation of the powder synthesis were 8 M-KOH solvent of hydrothermal solvent, $270^{\circ}C$ of reaction temperature and 24 hrs of run time. It was found that the synthesized powders had spherical morphology with average particle size of 70 nm and specific surface area of $5.5\;m^{2}/g$.

• Bulletin of the Korean Chemical Society
• /
• 제35권8호
• /
• pp.2295-2298
• /
• 2014

To effectively destruct 2-chlorophenol, a representative sterile preservative, nanometer-sized Mn (0.5, 1.0, 3.0 mol %)-incorporated $TiO_2$ powders were synthesized by a solvothermal method. XRD result demonstrated that the Mn ingredients were perfectly inserted into $TiO_2$ framework. The Mn-$TiO_2$ particles exhibited an anatase structure with a particle size of below 20 nm. The absorbance was shifted to the higher wavelength on Mn-$TiO_2$ compared to that of $TiO_2$. Otherwise, the PL intensities which has a close relationship for recombination between holes and electrons significantly decreased on Mn-$TiO_2$. The photodecomposition for 2-chlorophenol in a liquid system was enhanced over Mn-doped $TiO_2$ compared with pure $TiO_2$: 2-chlorophenol of 50 ppm was completely decomposed after 12 h when 1.0 mol % Mn-$TiO_2$ was used. Consequently, the core of this paper is as follows. introducing Mn into $TiO_2$ framework reduced the band-gap, moreover, it played as an electron capture resulted to lower recombination between electrons and holes during photocatalytic reaction for removal of 2-cholophenol.

• 한국세라믹학회지
• /
• 제27권2호
• /
• pp.187-194
• /
• 1990

Effects of MnO2 addition ranged from 0.0wt% to 5.0wt% on the microstructure and dielectric and piezoelectric properties of the Pb(Zr0.52 Ti0.48)O3 Ceramics have been investigated. The solubility limit of MnO2 in Pb(Zr0.52 Ti0.48)O3 is about 0.5wt%, and MnO2 as a valence state of Mn3+ is substituted for (Zr, Ti) lattice site in PZT solid-solution. The addition of MnO2 up to 0.5wt% in Pb(Zr0.52 Ti0.48)O3 brings increase of density, but decreased of grain size and tetragonality. Dielectric constant slightly decreases, but both coupling factor(Kp) and mechanical quality factor(Qm) increase with the addition of MnO2. However, excess amount of MnO2 addition more than 0.75wt% results in rapid decrease of resistance. Dielectric constant and tan $\delta$ increase due to the second phase and inhomogeneous Mn distribution.

• 한국환경과학회지
• /
• 제15권4호
• /
• pp.333-340
• /
• 2006

A (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ catalyst were prepared by co-precipitation method and used for low-temperature selective catalytic reduction (SCR) of $NO_x$ with ammonia in the presence of oxygen. The properties of the catalysts were studied by X-ray diffraction (XRD), temperature programmed reduction (TPR) and scanning electron microscope-energy dispersive X-ray spectroscopy (SEM-EDS). The experimental results showed that (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ catalyst yielded 81% NO conversion at temperature as low as $150^{\circ}C$ and a space velocity of $2,400\;h^{-1}$. Crystalline phase of $Mn_{2}O_3$ was present at ${\ge}\;15%$ Mn on $V_{2}O_{5}/TiO_{2}$. XRD confirmed the presence of manganese oxide ($Mn_{2}O_{3}$) at $2{\theta}=32.978^{\circ}(222)$. The XRD patterns presented of (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ did not show intense or sharp peaks for manganese oxides and vanadia oxides. The TPR profiles of (5 wt.%)Mn-(1 wt.%)$V_{2}O_{5}/TiO_{2}$ catalyst showed main reduction peat of a maximum at $595^{\circ}C$.

• 공업화학
• /
• 제23권1호
• /
• pp.119-123
• /
• 2012

본 연구는 Mn/$TiO_2$ 촉매를 이용한 저온 $NH_3$-SCR 반응에서 산소의 역할에 대한 영향을 기술하였다. 촉매의 격자산소는 저온 SCR 반응에 참여하며, 기상의 산소는 환원된 촉매를 재산화 시키는 역할을 한다. 이러한 산소의 redox 특성은 SCR 반응활성에 중요한 요소로 작용하며, 격자산소의 이용능력은 표면에 노출된 망간의 산화상태에 큰 영향을 받는다. $TiO_2$ 담체 표면에 존재하는 Mn이 $MnO_2$의 망간산화물 형태로 존재할 때가 $Mn_2O_3$의 형태로 존재할 때보다 우수한 redox 특성을 가지며, 이러한 망간의 산화상태는 $TiO_2$의 비표면적에 큰 영향을 받는다.