• 대한치과기공학회지
• /
• 제30권2호
• /
• pp.79-86
• /
• 2008

The purpose of this study was to investigate the effect retention element formed by metal surface treatment method on the bond strength of indirect composite resin and metal. The metal specimens were cast from Ni-Cr alloy($Rexillium^{(R)}$ III). They were divided into 5 groups by applied retention element: $50{\mu}m$ aluminium oxide sandblasting group, $250{\mu}m$ aluminium oxide sandblasting group, 0.2mm retention crystal group, 10% $H_{2}SO_{4}$ solution etching group, $110{\mu}m$ $Rocatec^{TM}$ Plus system group. Total 50 metal specimens were veneered with Sinfony indirect composite resin system. Specimens were tested for shear bond strength on an Instron universal testing machine and fracture mode of fractured specimens were analyzed by SEM and EDS. 1. 0.2 mm retention crystals were most effective in improving the resin-metal shear bond strength (p<0.05). 2. Sandblasting by $250{\mu}m$ aluminium oxide were more effective than sandblasting by $50{\mu}m$ aluminium oxide in improving the resin-metal shear bond strength(p<0.05). 3. Fracture mode of resin-metal fractured surface were cohesive failure mode in 0.2mm retention crystal, mixed failure mode in sandblasted specimens, etched specimens and the specimens sandblasted with $110{\mu}m$ $Rocatec^{TM}$ Plus system.

• 한국분말재료학회지
• /
• 제12권2호
• /
• pp.112-116
• /
• 2005

In the present study, the focus is on the analysis of carbothermal reduction of oxide powder prepared from waste WC/Co hardmetal by solid carbon under a stream of argon for the recycling of the WC/Co hard-metal. The oxide powder was prepared by the combination of the oxidation and crushing processes using the waste $WC-8 wt.\%Co$ hardmetal as the raw material. This oxide powder was mixed with carbon black, and then this mixture was carbothermally reduced under a flowing argon atmosphere. The changes in the phase structure and gases discharge of the mixture during carbothermal reduction was analysed using XRD and gas analyzer. The oxide powder prepared from waste $WC-8wt.\%Co$ hardmetal has a mixture of $WO_{3} and CoWO_{4}$. This oxide powder reduced at about $850^{\circ}C$, formed tungsten carbides at about $950^{\circ}C$, and then fully transformed to a mixed state of tungsten carbide (WC) and cobalt at about $1100^{\circ}C$ by solid carbon under a stream of argon. The WC/Co composite powder synthesized at $1000^{\circ}C$ for 6 hours from oxide powder of waste $WC-8wt.\%Co$ hardmetal has an average particle size of $0.3 {\mu}m$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2002년도 하계학술대회 논문집 Vol.3 No.2
• /
• pp.1125-1128
• /
• 2002

Electrochemical capacitor made with metal oxide electrode uses rapid and reversible protonation/deprotonation of metal oxide material under the aqueous acidic solution, generally. Electrochemical stability window of aqueous electrolyte-type capacitor is narrow compared to that of organic electrolyte-type capacitor. Electrochemical characteristics of electrochemical capacitor made with metal oxide electrode and lithium cation based organic electrolyte were evaluated. Electrochemical capacitor based on $RuO_2$ electrode material and 1M $LiPF_6$ in mixed solvents of EC, DEC, and EMC has anodic and cathodic specific capacitance of 145 and 142 F/g-$RuO_2{\cdot}nH_2O$, respectively, by using cyclic voltammetry with scan rate of 2 mV/sec g-$RuO_2$ in potential range of 2.0~4.2V(Li|$Li^+$).

• 한국표면공학회지
• /
• 제32권6호
• /
• pp.686-694
• /
• 1999

Insoluble anodes of the Ta/Ir mixed metal oxide for electrodeposition of Ni-W alloy in ammoniacal citrate bath were prepared by thermal decomposition method. Ti plate was etched in boiling oxalic acid solution and coated with ethanol solution of $TaCl_{5}$ and $IrCl_4$ mixed in a fixed ratio, followed by drying and treating at various temperatures. The coating layer of these insoluble anode was characterized by SEM, EDX, XRD and DSC. The decomposition rate of citric acid in plating bath was determined by measuring the $CO_2$ gas evolved at the anodes with Gas Chromatography. Evolution of $CO_2$ gas from Ta/Ir oxide anodes decreased about 5% compared with that of Pt. The $CO_2$ gas evolution was increased with the amount of Ir-oxide in the coatings. The coatings which have more than 40% ratio of Ta content and heat-treated at the temperature higher than $400^{\circ}C$ showed better efficiency

• Journal of Welding and Joining
• /
• 제9권4호
• /
• pp.17-27
• /
• 1991

The direct brazing technology which could be used for the simplification of brazing process and the improvement of brazed joint quality was studied with $Al_2O_3$ and stainless steels. The brazing of $Al_2O_3$ to STS304 or STS430 was performed under different brazing conditions such as brazing filler metal, temperature, heating rate and brazing time. Microstructural observation and chemical analysis be SEM/EPAM were carried out to verify the quality of brazed joints. 4-point bending strength of brazed joints was also measured to find the optimal brazing conditions. The results showed that, in brazing of $Al_2O_3$, the mixed oxide layer resulted from the reaction between Ti in filler metal and oxide layer on the material surface to be brazed was found to be bery important for the joint quality. The width of oxide layer varied with the brazing conditions such as brazing time, heating rate and chemical composition of filler metals. The strength of brazed joints was more affected by the type of materials and their thermal properties than by brazing heat cycle.

• 자원리싸이클링
• /
• 제21권1호
• /
• pp.75-81
• /
• 2012

선탄경석을 환경개선물질로 순환자원화하기 위해 철산화물과 혼합하여 중금속 불용화제를 제조하고 이의 적정제조 조건과 중금속에 대한 불용화 성능을 평가하였다 선탄경석을 분쇄한 후 철산화물의 분말을 혼합하여 구형의 펠릿을 제조하고 이를 가열하여 중금속 불용화제를 제조하였다. 온도별로 가열한 결과, $1100^{\circ}C$부터 선탄경석에 함유된 탄질분에 의해 영가철이 생성되었다. 제조된 불용화제는 구형의 다공체로서 공극률은 34.63%, 겉보기 밀도는 1.31 g/mL, 공극의 평균크기는 9.82 ${\mu}m$로 측정되었다. 불용화제를 비소(V), 구리(II), 크롬(VI), 카드뮴(II)이 함유된 각각의 중금속 용액과 반응시킨 결과, 영가철이 생성된 $1100^{\circ}C$에서 제조된 펠릿이 중금속 불용화도가 높고 pH를 더 높이는 것으로 나타났다. 중금속농도 10 ppm의 용액을 99.9%이상 불용화하기까지 비소의 경우 1시간, 크롬의 경우 2시간, 구리의 경우 4시간이 필요하였다. 그러나 카드뮴의 경우 불용화도가 낮게 나타났고 중금속농도가 높을수록 불용화도가 더 낮아지는 것으로 나타났다.

• 한국수소및신에너지학회논문집
• /
• 제17권1호
• /
• pp.21-30
• /
• 2006

[ $M/Fe_2O_3$ ] (M=Rh, Ce and Zr) mixed oxides were prepared using urea method to develop a medium for chemical hydrogen storage by their redox cycles. And their redox behaviors by repeated cycles were studied using temperature programmed reaction(TPR) technique. Additives such as Rh, Ce and Zr were added to iron oxides in order to lower the reaction temperature for reduction by hydrogen and re-oxidation by water-splitting. From the results, concentration of urea used as a precipitant had little effect on particle size and reduction property of iron oxide. TPR patterns of iron oxide consisted of two reduction peaks due to the course of $Fe_2O_3\;{\rightarrow}\;Fe_3O_4\;{\rightarrow}\;Fe$. The results of repeated redox tests showed that Rh added to iron oxide have an effect on lowering the re-oxidation temperature by water-splitting. Meanwhile, Ce and Zr additives played an important role in prevention of deactivation by repeated cycles. Finally, Fe-oxide(Rh, Ce, Zr) sample added with Rh, Ce and Zr showed the lowest re-oxidation temperature by water-splitting and maintained high $H_2$ recovery in spite of the repeated redox cycles. Consequently, it is expected that Fe-oxide(Rh, Ce, Zr) sample can be a feasible medium for chemical hydrogen storage using redox cycle of iron oxide.

• Transactions on Electrical and Electronic Materials
• /
• 제11권1호
• /
• pp.1-10
• /
• 2010

This is an overview paper reporting our most recent work on processing and microstructure of nano-structured oxides and their photoluminescence and photo-catalysis properties. Zinc oxide and related transition metal oxides such as vanadium pentoxide and titanium dioxide were produced by a combination of magnetron sputtering, hydrothermal growth and atmosphere controlled heat treatment. Special morphology and microstructure were created including nanorods arrays, core-brushes, nano-lollipops and multilayers with very large surface area. These structures showed special properties such as much enhanced photoluminescence and chemical reactivity. The photo-catalytic properties have also been promoted significantly. It is believed that two factors contributed to the high reactivity: the large surface area and the interaction between different oxides. The transition metal oxides with different band gaps have much enhanced photoluminescence under laser stimulation. Use of these complex oxide structures as electrodes can also improve the energy conversion efficiency of solar cells. The mixed oxide complex may provide a promising way to high-efficiency photo emitting materials and photo-catalysts.

• Macromolecular Research
• /
• 제16권7호
• /
• pp.659-662
• /
• 2008

A new and useful poly(ethylene oxide)-based pH-sensitive block copolymer is introduced. Poly(ethylene oxide-b-N-phenylmaleimide) was first synthesized by anionic polymerization of N-phenylmaleimide (N-PMI) using mixed alkali metal polymeric alkoxide by sequential monomer addition method in the mixture of benzene/THF/DMSO (10/5/3, v/v/v) at room temperature. Reductive deimidation of the resulting block copolymer was performed using hydrazine monohydrate leading to the formation of the corresponding pH-sensitive poly(ethylene oxide-b-maleic acid).

• 한국응용과학기술학회지
• /
• 제33권2호
• /
• pp.401-410
• /
• 2016

금속 산화물과 혼합한 $Pt-Sn/Al_2O_3$ 촉매의 프로판 탈수소 반응 성능의 향상 가능성에 대해서 연구하였다. 금속 산화물로서 $Cu-Mn/{\gamma}-Al_2O_3$, $Ni-Mn/{\gamma}-Al_2O_3$, $Cu/{\alpha}-Al_2O_3$를 제조하여 $Pt-Sn/Al_2O_3$ 촉매와 혼합하고, 프로판 탈수소 반응 성능을 측정하였다. 이 결과들을 불활성 물질인 glass bead를 혼합한 $Pt-Sn/Al_2O_3$ 촉매를 기준샘플로 삼아 비교하였다. 촉매와 금속산화물을 환원처리하지 않고 반응 실험한 경우, $576.5^{\circ}C$에서 기준샘플의 전환율 8% 대비, $Cu-Mn/{\gamma}-Al_2O_3$를 혼합한 $Pt-Sn/Al_2O_3$ 촉매가 14.9%의 높은 전환율과 96.8%의 선택도를 보였다. 촉매와 금속산화물을 환원 처리하여 반응활성을 측정한 경우, $Cu/{\alpha}-Al_2O_3$과 $Pt-Sn/Al_2O_3$의 혼합촉매가 기준샘플대비 초기에 높은 수율을 보였다. 그러나, 촉매를 환원 처리한 경우 전반적으로 전환율 상승이 크지 않았고, 이것으로 $Cu-Mn/{\gamma}-Al_2O_3$의 격자산소가 탈수소반응의 전환율 증가 영향을 주었음을 알 수 있었다.