• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.08a
• /
• pp.268-268
• /
• 2012

Atmospheric pressure microwave induced plasmas are used to excite and ionize chemical species for elemental analysis, for plasma reforming, and for plasma surface treatment. Microwave plasma differs significantly from other plasmas and has several interesting properties. For example, the electron density is higher in microwave plasma than in radio-frequency (RF) or direct current (DC) plasma. Several types of radical species with high density are generated under high electron density, so the reactivity of microwave plasma is expected to be very high [1]. Therefore, useful applications of atmospheric pressure microwave plasmas are expected. The surface characteristics of SUS304 stainless steel are investigated before and after surface modification by microwave plasma under atmospheric pressure conditions. The plasma device was operated by power sources with microwave frequency. We used a device based on a coaxial transmission line resonator (CTLR). The atmospheric pressure plasma jet (APPJ) in the case of microwave frequency (880 MHz) used Ar as plasma gas [2]. Typical microwave Pw was 3-10 W. To determine the optimal processing conditions, the surface treatment experiments were performed using various values of Pw (3-10 W), treatment time (5-120 s), and ratios of mixture gas (hydrogen peroxide). Torch-to-sample distance was fixed at the plasma edge point. Plasma treatment of a stainless steel plate significantly affected the wettability, contact angle (CA), and free energy (mJ/$m^2$) of the SUS304 surface. CA and ${\gamma}$ were analyzed. The optimal surface modification parameters to modify were a power of 10 W, a treatment time of 45 s, and a hydrogen peroxide content of 0.6 wt% [3]. Under these processing conditions, a CA of just $9.8^{\circ}$ was obtained. As CA decreased, wettability increased; i.e. the surface changed from hydrophobic to hydrophilic. From these results, 10 W power and 45 s treatment time are the best values to minimize CA and maximize ${\gamma}$.

• Bulletin of the Korean Chemical Society
• /
• v.35 no.3
• /
• pp.905-907
• /
• 2014

The plasma and microwave surface treatments of carbon nanotubes that loaded on plastic substrates were carried out with expecting a change of carbon nanotube dispersion by increasing treatment time. The microwave treatment process was undergone by commercial microwave oven (800 W). The electrical property was measured by hall measurement and resistance was increased by increasing $O_2$ flow rate of plasma, suggesting an improvement of carbon nanotube dispersion and a possibility of controlling the resistances of carbon nanotubes by plasma surface treatment. The resistance was increased in both polyethylene terephthalate and polyimide substrates by increasing $O_2$ flow rate. Resistance changes only slightly with different $O_2$ flow treatment in measure rho for all polyimide samples. Sheet resistance is lowest in polyimide substrate not due to high carbon nanotube loading but due to tendency to remain in elongated structure. $O_2$ or $N_2$ plasma treatments on both polyethylene terephthalate and polyimide substrates lead to increase in sheet resistance.

• Journal of the Korea Furniture Society
• /
• v.18 no.4
• /
• pp.275-281
• /
• 2007

This study was carried out to know bending process property of bentwood by treatment methods such as microwave and ammonia solution treatment. Bentwood processing was operated on bending-jig form with 60mm and 100mm radius of curvature (ROC). The species was used to Korean red pine (Pinus densiflora). No significant difference was shown in bentwood processing method on ROC. In treatment method, ammonia solution treatment for bentwood was better in dimensional stability and working ability than that of microwave treatment. However, bentwood stress was reduced with ammonia solution treatment. Color of bentwood surface appearance has a dark tendency in ammonia solution treatment. But it seems to beautiful effect of apparent annual ring is rising esthetically by ammonia solution treatment. To utilize wood as a exterior material for living amenity, it has to be closely examined from various angles including surface property, degree of swelling and shrinkage, drying state, retaining strength, durability, safety, and insect damage.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2005.07b
• /
• pp.1534-1535
• /
• 2005

Highly luminescent efficiency phosphors have been successfully produced by surface modification and microwave irradiation treatment. The SEM image and XRD analysis reveal that the surface morphology of the white-light phosphors can be notably modified by microwave irradiation and exhibit with better crystalline property. The VUV PL spectra show that the microwave irradiation treatment can effectively enhance the luminescent efficiency by a factor of 1.5 times for intensity compared to that without microwave treatment. A further improvement in all visible emission can be made by modifying surface composition through MgO coating on the phosphor powder. These results demonstrate that such a simple approach can provide for improving luminescent efficiency of phosphors for the optoelectronic devices.

• Journal of Microbiology and Biotechnology
• /
• v.27 no.7
• /
• pp.1209-1215
• /
• 2017

Microwave sterilization was performed to inactivate the spores of biofilms of Bacillus cereus involved in foodborne illness. The sterilization conditions, such as the amount of water and the operating temperature and treatment time, were optimized using statistical analysis based on 15 runs of experimental results designed by the Box-Behnken method. Statistical analysis showed that the optimal conditions for the inactivation of B. cereus biofilms were 14 ml of water, $108^{\circ}C$ of temperature, and 15 min of treatment time. Interestingly, response surface plots showed that the amount of water is the most important factor for microwave sterilization under the present conditions. Complete inactivation by microwaves was achieved in 5 min, and the inactivation efficiency by microwave was obviously higher than that by conventional steam autoclave. Finally, confocal laser scanning microscopy images showed that the principal effect of microwave treatment was cell membrane disruption. Thus, this study can contribute to the development of a process to control food-associated pathogens.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.11
• /
• pp.1014-1018
• /
• 2005

The purpose of this study is to obtain strong bond strength at the interface between piezoelectric substrates and semiconductor thin films to be applied for the manufacture of high-performance acoustic wave semiconductor coupled device. For this purpose, we have compared and examined the effects of different surface treatment methods on hydrophile properties at the surface of the piezoelectric substrates. Moreover, we have observed the effect of microwave and laser on the elimination of water molecules at the interface. As for the piezoelectric substrates, dry method for surface treatment was found to be superior in the control of hydrophilicity of the surface compared to wet method. On the other hand, both microwave and laser were found to be effective in the elimination of water molecules in the interface.

• Journal of Electrochemical Science and Technology
• /
• v.12 no.3
• /
• pp.297-301
• /
• 2021

Microbial fuel cells (MFCs) convert chemical energy to electrical energy via electrochemically active microorganisms. The interactions between microbes and the surface of a carbon electrode play a vital role in capturing the respiratory electrons from bacteria. Therefore, improvements in the electrochemical and physicochemical properties of carbon materials are essential for increasing performance. In this study, a microwave and sulfuric acid treatment was used to modify the surface structure of graphite granules. The prepared expandable graphite granules (EGG) exhibited a 1.5 times higher power density than the unmodified graphite granules (1400 vs. 900 mW/m³). Scanning electron microscopy and Fourier transform infrared spectroscopy revealed improved physical and chemical characteristics of the EGG surface. These results suggest that physical and chemical surface modification using sulfuric acid and microwave heating improves the performance of electrode-based bioprocesses, such as MFCs.

• The Journal of Engineering Research
• /
• v.4 no.1
• /
• pp.93-107
• /
• 2002

The active carbon waste which was used in water purification plant was investigated for the improvement of capillary after microwave treatment. The variation of surface area was measured with the various kinds and amounts of active carbon. The water vapor as the activator was verified to improve the capillary but it reacted with the water contained in waste active carbon. In contrast to the water vapor, the $CO_2$ gas improved the surface area about 10-20 % compared to as received one. The best results was observed at the intensity of 2.75 kw microwave. The more effective recovery of active carbon waste was observed at the microwave treatment compared to the rotary kiln treatment. However, the mass production is so difficult in the microwave process.

• Applied Science and Convergence Technology
• /
• v.26 no.4
• /
• pp.62-65
• /
• 2017

Passivation of surface defects by the formation of chemically inert structure at the surface of $TiO_2$ nanocrystals can be potentially useful in enhancing their photocatalytic activity. In this regard, we have studied the surface chemical states of $TiO_2$ surfaces prepared by a treatment in the afterglow of $N_2$ microwave plasma using X-ray photoemission spectroscopy (XPS). We find that nitrogen is incorporated into the surface after the treatment up to a few atomic percent. Interestingly, the surface oxynitride layer is found to be chemically stable when it's in contact with water at room temperature (RT). The surface nitrogen species were also found to be thermally stable upon annealing up to $150^{\circ}C$ in the atmospheric pressure. Thus, we conclude that the treatment of oxide materials such as $TiO_2$ in the afterglow of $N_2$ plasma can be effective way to passivate the surface with nitrogen species.

• Transactions of the Korean hydrogen and new energy society
• /
• v.24 no.2
• /
• pp.142-149
• /
• 2013

Carbon materials are mainly used as catalyst supports for polymer exchange membrane fuel cell (PEMFC). Catalyst supports are required specific characteristics of the carbon materials, such as large surface area and high electrical conductivity. Attempted were to improve electrical conductivity and to maintain high surface area of carbon materials using a microwave treatment. Microwave treatment, as a relatively new technique, takes short reaction time and reduce the consumption of the gases used for carbon treatment compared to a traditional heat treatment. Hybrid carbon (ACF/Graphene) as catalyst supports by microwave-irradiation method for PEMFC increase the cell performance because of increased electrical conductivity resulting in triple-phase contact and reduced the interfacial resistance. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-Ray Diffraction (XRD) were employed to analyze carbon materials. The performance of microwave-treated carbon materials was evaluated by measuring current-voltage (I-V) characteristics and electrode impedance.