• Korean Chemical Engineering Research
• /
• v.59 no.3
• /
• pp.399-409
• /
• 2021

In order to utilize dolomite as a calcium/magnesium compound material, it was prepared highly reactive calcined dolomite(CaO·MgO) using a microwave kiln (950 ℃, 60 min). The experiment was performed according to the standard of the hydration test (ASTM C 110) and hydration reactivity was analyzed as medium reactivity (max 74.1 ℃, 5 min). Experiments were performed with calcined dolomite and salt (MgCl₂·6H₂O) (a) 1:1, (b) 1:1.5, and (c) 1:2 wt% based on the hydration reaction of calcined dolomite. The result of X-ray diffraction analysis confirmed that MgO of calcined dolomite increased to Mg(OH)₂ as the salt addition ratio increased. After the separating reaction, calcium was stirred at 80 ℃, 24 hr that produced CaCl₂ of white crystal. XRD results, it was confirmed calcium chloride hydrate (CaCl₂·(H₂O)x) and CaO of calcined dolomite and salt additional reaction was separated into CaCl₂. And it was synthesized with Ca(OH)₂ 99 wt% by NaOH adding reaction to the CaCl₂ solution, and the synthesized Ca(OH)₂ was manufactured CaO through the heat treatment process. In order to prepare calcium carbonate, CaCO₃ was synthesized by adding Na₂CO₃ to CaCl₂ solution, and the shape was analyzed in cubic form with a purity of 99 wt%.