• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2023년도 가을학술발표대회논문집
• /
• pp.93-94
• /
• 2023

This study evaluated the mechanical properties and microstructure of calcium silicate cement based paste according to carbonation curing conditions. As a result, both compressive strength and carbonation depth increased with the carbonation curing period.

• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.618-619
• /
• 2006

The binder phase for TiC reinforced steel matrix composite was added in the form of elemental powders and master alloy powders. The microstructures, binder phase variation with TiC content and mechanical properties were evaluated. The addition of a type of binder phase largely effects the microstructure and mechanical properties. The binder phase variation from starting composition was observed with increase in wt% TiC content and this variation was higher when the master alloy powders were used as a binder. The response to heat treatment was decreased with an increase in TiC content due to the shift of binder phase from the starting composition.

• 한국세라믹학회지
• /
• 제50권3호
• /
• pp.212-217
• /
• 2013

Ultra hard TiN coatings were fabricated by DC and ICP (inductively coupled plasma) magnetron sputtering techniques. The effects of ICP power, ranging from 0 to 300 W, on the coating microstructure, crystallographic, and mechanical properties were systematically investigated with FE-SEM, AFM, HR-XRD and nanoindentation. The results show that ICP power has a significant influence on the coating microstructure and mechanical properties of TiN coatings. With an increasing ICP power, the film microstructure evolves from an apparent columnar structure to a highly dense one. Grain sizes of TiN coatings decreased from 12.6 nm to 8.7 nm with an increase of the ICP power. A maximum nanohardness of 67.6 GPa was obtained for the coatings deposited at an ICP power of 300 W. The crystal structure and preferred orientation in the TiN coatings also varied with the ICP power, exerting an effective influence on film nanohardness.

• 한국재료학회지
• /
• 제27권12호
• /
• pp.652-657
• /
• 2017

The use of continuous welded rail is increasing because of its many advantages, including vibration reduction, enhanced driving stability, and maintenance cost savings. In this work, two different types of continuous welded rails were examined to determine the influence of repeated wheel-rail contact on the crystal structure, microstructure and mechanical properties of the rails. The crystal structure was determined by x-ray diffraction, and the microstructure was examined using optical microscopy and scanning electron microscopy. Tensile and microhardness tests were conducted to examine the mechanical behaviors of prepared specimens taken from different positions in the cross section of both newly manufactured rail and worn rail. Analysis revealed that both the new and worn rail had a mixed microstructure consisting of ferrite and pearlite. The specimens from the top position of each rail exhibited decreased lamella spacing of the pearlite and increased yield strength, ultimate tensile strength and hardness, as compared with those from other positions of the rail. It is thought that the enhanced mechanical property on the top position of the worn rail might be explained by a mixed effect resulting from a directional microstructure, the decreased lamella spacing of pearlite, and work hardening by the repeated wheel-rail contact stress.

• 대한전기학회:학술대회논문집
• /
• 대한전기학회 1994년도 하계학술대회 논문집 C
• /
• pp.1351-1353
• /
• 1994

High strengh pocelain insulators with 35wt% alumina were manufactured by wet produce technique. The microstructure and crystalline phases of this samples and the effect of CaO addition to insulator bodies were studied. Electrical and mechanical properties (permittivity, dissipation factor, modulus of rupture, Young's modulus etc,) were studied. The relation between microstructure and electrical, mechanical properties were analyzed.

• 대한기계학회논문집A
• /
• 제32권12호
• /
• pp.1107-1114
• /
• 2008

This paper is aimed to understand the effect of different galvannealing temperatures on the frictional properties and Fe-Zn intermetallic phases of the galvannealed (GA) coatings on steel sheets. Their galvannealing treatments were conducted at 465, 505, 515 and $540^{\circ}C$ for about 10s in the additional heating furnace of an industrial continuous hot-dip galvanizing line. The mechanical and the frictional properties of the coatings were estimated using nanoindentation, nanoscratch, micro vickers hardness tests and flat friction tests, which were performed at contact pressures of 4, 20 and 80MPa. Also, the correlation between the microstructure and the frictional properties of the GA coatings were investigated by SEM observation for the cross-section of the GA coating after and before flat friction tests. The results showed that the mechanical and the frictional properties of the coatings are strongly dependent on their phase distributions and microstructure. Especially, in low contact pressure of 4MPa the frictional properties of the coatings were dependent on the surface phases and morphology, while in high contact pressure of 80MPa it was influenced by their mechanical properties based on the dominant phase distributions.

• 대한금속재료학회지
• /
• 제47권2호
• /
• pp.121-128
• /
• 2009

The strain, microstructure and mechanical properties through thickness of an oxygen free copper(OFC) processed by differential speed rolling(DSR) were investigated in detail. The OFC sample with thickness of 1 mm was rolled to 35% reduction at ambient temperature without lubrication changing the differential speed ratio from 1.0:1 to 2.2:1. The shear strain introduced by the conventional rolling showed positive values at positions of upper roll side and negative values at positions of lower roll side. However, it showed zero or positive values at all positions for the samples rolled by the DSR. The effects of strain distribution through thickness of the coper sheets on microstructure, texture and mechanical properties are discussed in the present study.

• International Journal of Precision Engineering and Manufacturing-Green Technology
• /
• 제5권5호
• /
• pp.605-612
• /
• 2018

This work investigates the relationships between the static mechanical properties of Ti-6Al-4V manufactured through selective laser melting (SLM) and post-process heat treatments, namely stress relieve, annealing and hot isostatic pressing (HIP). In particular, Ti-6Al-4V parts were fabricated in three different build orientations of X, Z, and $45^{\circ}$ to investigate the multi-directional mechanical properties. The results showed that fully densified Ti-6Al-4V parts with densities of up to 99.5% were obtained with optimized SLM parameters. The microstructure of stress relieved and mill annealed samples was dominated by fine ${\alpha}^{\prime}$ martensitic needles. After HIP treatment, the martensite structure was fully transformed into ${\alpha}$ and ${\beta}$ phases (${\alpha}+{\beta}$ lamellar). Within the realm of tensile properties, the yield and ultimate strength values were found statistically similar with respect to the built orientation for a given heat treatment. However, the ductility was found orientation dependent for the HIP samples, where a lower value was observed for samples built in the X direction.

• Nuclear Engineering and Technology
• /
• 제31권6호
• /
• pp.561-571
• /
• 1999

Microstructure and mechanical properties of five Cr-Mo steels for nuclear industry applications have been investigated. Transmission electron microscopy, energy dispersive spectrometer, differential scanning calorimeter, hardness, tensile, and impact test were used to evaluate the Cr and W effect on the microstructure and mechanical properties. Microstructures of Cr-Mo steels after tempering are classified into three types : bainitic 2.25Cr-lMo steel, martensitic Mod.9Cr-lMo, HT9M, and HT9W steels, and dual phase HT9 steel. The majority of the precipitates were found to be M$_{23}$C$_{6}$ carbides. As minor phases, fine needle-like V(C,N), spherical NbC, fine needle-like Cr-rich Cr$_2$N, and Cr-rich M$_{7}$C$_3$were also found. Addition of 2wt.% W in Cr-Mo steels retarded the formation of subgrain and dissolution of Cr$_2$N precipitates. Hardness and ultimate tensile strength increased with increasing Cr content. Though Cr content of HT9W steel was lower than that of HT9 steel, the hardness of HT9W was higher due to the higher W content. W added HT9W steel had the highest ultimate tensile strength above $600^{\circ}C$. But impact toughness of W added steel (HT9W) and high Cr steel (HT9) was low.w.w.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2008년도 추계학술대회 논문집
• /
• pp.207-210
• /
• 2008

The effects of boron additions in steels have long been recognized as very important, mainly with respect to hardnability of heat treatable steels. we investigated the effect of the microstructure and mechanical properties with cooling condition after heat treatment of the boron-treated(${\fallingdotseq}8{\sim}18ppm$) low carbon(${\fallingdotseq}0.2%C$) low alloy steel. The specimens were austenitised for 10 min at $910^{\circ}C$, cooled for the various periods of time from 10 sec to 30 sec or with water after forming for 15 sec. After cooling, mechanical properties were measured by tensile test and hardness test. For analysis of microstructure, Optical were carried out.