• Steel and Composite Structures
• /
• 제39권4호
• /
• pp.401-417
• /
• 2021

This study experimentally reveals the influence of welding on grade S690Q high strength steel (HSS) butt joints from both micro and macro levels. Total eight butt joints, taking plate thickness and welding heat input as principal factors, were welded by shielded metal arc welding. In micro level, the microstructure transformations of the coarse grain heat affected zone (CGHAZ), the fine grain heat affected zone (FGHAZ) and the tempering zone occurred during welding were observed under light optical microscopy, and the corresponding mechanical performance of those areas were explored by micro-hardness tests. In macro level, standard tensile tests were conducted to investigate the impacts of welding on tensile behaviour of S690Q HSS butt joints. The test results showed that the main microstructure of S690Q HSS before welding was tempered martensite. After welding, the original microstructure was transformed to granular bainite in the CGHAZ, and to ferrite and cementite in the FGHAZ. For the tempering zone, some temper martensite decomposed to ferrite. The performed micro-hardness tests revealed that an obvious "soft layer" occurred in HAZ, and the HAZ size increased as the heat input increased. However, under the same level of heat input, the HAZ size decreased as the plate thickness increased. Subsequent coupon tensile tests found that all joints eventually failed within the HAZ with reduced tensile strength when compared with the base material. Similar to the size of the HAZ, the reduction of tensile strength increased as the welding heat input increased but decreased as the thickness of the plate increased.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2009년도 추계학술대회 논문집
• /
• pp.225-225
• /
• 2009

In this study, Nano and micro-filler mixture composites were fabricated by fixed value of $SiO_2$ nano-filler 0.4 [wt%] according to increase of $SiO_2$ micro-filler [wt%] from 1 to 10. Composites with a good dispersion of mixed $SiO_2$ Nano and micro-particles in the epoxy resins were prepared and experiments were performed to measure the dielectric breakdown strength properties with various temperature and thickness. The dielectric strength properties are compared and analyzed with respect to nano/micro-composites filled with $SiO_2$ fillers less than properties obtained for nanocomposites.

• 소성∙가공
• /
• 제11권7호
• /
• pp.575-580
• /
• 2002

To evaluate elastic and micro-failure properties of MEMS materials, the electro-statically operated test devices were designed and fabricated by micro machining technology. The test structures consist or comb drives for loading and suspending beams in testing. From the analysis of beam displacement based on elastic beam theory, elastic modulus and yield strength of Al film were measured. And, by introducing the micro notch and cyclic loading, the micro-failure was Induced and the micro-fracture toughness of Si film was evaluated. Moreover, the cycles to failure were estimated from the degradation of resonant frequency. Finally, the effects of notch on micro failure were discussed.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2003년도 춘계학술대회 논문집
• /
• pp.593-598
• /
• 2003

Ceramic plates containing many micro-holes are used in diverse applications such as MCP (Microchannel Plate). catalytic converters, filters, electrical insulators in integrated circuits, and so on. One of the efficient methods for machining many holes in ceramic plates is wet drilling of ceramic green bodies followed by sintering them. Since the strength of ceramic green bodies is much lower than the strength of sintered ceramic plate, ceramic green bodies can be drilled with high feed rate. The axial force during micro-drilling of ceramic green bodies increases rapidly at high feed rate, which induces the crack in workpiece. Therefore, the tool lift of micro-drill with respect to feed rate may be determined by the predicting increase of axial force. In this work, the axial force during micro-drilling was calculated using the chip flow model on the micro-drill tip. from which the tool life of diamond abrasive micro-drill during micro-drilling of ceramic green bodies was calculated.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.240-245
• /
• 2004

Tensile properties of hard coating material, TiN, were evaluated using micro-tensile testing system. TiN has been known as a hard coating material commonly used today. Micro-tensile testing system consisted of a micro tensile loading system and a micro-ESPI(Electronic Speckle Pattern Interferometry) system. Micro-tensile loading system had a maximum load capacity of 500mN and a resolution of 4.5 nm in stroke. TiN thin film $1{\mu}m$ thick was deposited on the Si wafer pre-deposited of $Si_3N_4$ film substrate by the closed field unbalanced magnetron sputtering (CFUBMS) process. Three kinds of micro-tensile specimen with the respective width of $50{\mu}m$, $100{\mu}m$ and $500{\mu}m$ were fabricated by MEMS process. The mechanical properties including tensile strength and elastic modulus were determined using the micro-tensile testing system and compared by those obtained by nano-indentation

• 오토저널
• /
• 제11권1호
• /
• pp.51-56
• /
• 1989

This study was performed to investigate the effect of defect on fatigue strength under the stress of rotary bending. The specimens were made of low carbon steel having artificial microholes, namely, single micro-hole and two adjacent micro-holes as natural defects, and the effects of the diameter of hole and the distance between the holes on fatigue strength have been investigated. The obtained result can be summarized as follows: 1, The critical defect means the largest size of defect that does not affect fatigue limit, and correspondes to the size of defect leading to final fracture under fatigue limit of smooth specimen. The size of defect which has an effect on fatigue limit is larger than that of critical defect. 2, The defect larger than the critical defect affects fatigue strength for as a kind of size effect, and the physical meaning of size effect of defect is considered same as the one of notch effect.

• 대한환경공학회지
• /
• 제37권7호
• /
• pp.412-417
• /
• 2015

본 연구는 하수처리장에서 발생하는 하수슬러지 소각재와 Geobond를 이용한 응용 블록의 개발을 위하여 수행하였다. 실험은 무소성 공정으로 진행하였으며, Sewage Sludge Ash (SSA)를 Geobond(무기바인더)와 특수시멘트인 초조강 시멘트 마이크로 시멘트, 모래 등의 바인더를 혼합한 각각의 페이스트 시편을 성형 후 건조 및 양생과정을 거친 시편을 단기 압축강도를 측정한 후 28일 장기 양생한 결과 압축 강도가 64.6 MPa로 발현하였다. 이는 KS기준치 22.54 MPa ($229.7kg/cm^2$)을 훨씬 상회하는 고강도의 압축강도를 나타내었다. 하수슬러지 소각재(SSA) 첨가율은 각 바인더 별 약 10~40%까지 혼합 가능한 것으로 나타났다. 따라서 SSA를 무기바인더인 Geobond와 특수시멘트(HESPC, MC)의 대체 물질로의 사용이 가능함을 입증하였다.

• 한국재료학회지
• /
• 제18권11호
• /
• pp.604-609
• /
• 2008

The sintering behavior of zircon with silica was investigated. Zircon with 5 vol% of sedimentation $SiO_2$ resulted in the apparent density of $4.45\;g/cm^3$, the diametral tensile strength of $12.125\;kgf/cm^2$, and the micro Vickers hardness of 1283 HV. The dissociation temperature and mechanical characteristics of the $ZrSiO_4$ were changed with different kinds of $SiO_2$. $SiO_2$ addition prevented dissociation of $ZrSiO_4$. Zircon with 5 vol% of sedimentation $SiO_2$ and with 5 vol% of fused $SiO_2$ resulted in increased diametral tensile strength and increased micro Vickers hardness by suppression of $ZrSiO_4$ dissociation and low temperature liquid $SiO_2$ formation. Zircon with fumed $SiO_2$ and quartz $SiO_2$ resulted in decreased diametral tensile strength and decreased micro Vickers hardness because of cristobalite and quartz phase formation and high temperature liquid $SiO_2$ formation. Zircon with 10 vol% of $SiO_2$ resulted in decreased diametral tensile strength and decreased micro Vickers hardness because of weak particle coupling due to excess formation of liquid $SiO_2$.

• Advances in concrete construction
• /
• 제10권5호
• /
• pp.431-441
• /
• 2020

For the purpose of improving the properties of UHPC as well as the economic efficiency in production of the material, Availability of river sands as fine aggregate instead of micro silica sand were investigated. Four different sizes of river sands were considered. Using river sand instead of micro silica sand increased the flowability, and decreased the yield stress and plastic viscosity in rheological properties, and the effect was higher with larger particle size of river sand. It was demonstrated by analyses based on the packing density. In the results of compressive strength and elastic modulus, even though river sand was not as good as micro silica sand, it could provide high strength of over 170 MPa and elastic modulus greater than 40 GPa. The difference in compressive strength depending on the size of river sand was explained with the concept of maximum paste thickness based on the packing density of aggregate. The flexural performance with river sand also presented relatively lower resistance than micro silica sand, and the reduction was greater with larger particle size of river sand. The flexural performance was proven to be also influenced by the difference in the fiber orientation distribution due to the size of river sand.

• Restorative Dentistry and Endodontics
• /
• 제29권4호
• /
• pp.339-345
• /
• 2004

The aim of this study was to measure and compare the micro shear bond strengths of the following dentin bonding systems to the dentin surfaces under simulated pulpal pressure: All Bond $2^{\circledR},{\;}Second^{\circledR},{\;}AdheSE^{\circledR}$, Adper Prompt $L-Pop^{\circledR}$. The occlusal surfaces of 180 extracted human molars were prepared so the dentin bonding surfaces could be exposed. The teeth were randomly assigned to 3 equal groups of 60 each and subdivided. The dentin surfaces were treated with the above mentioned bonding system and resin composite cylinders were built up under a simulated pulpal pressure when saline (Group II) or diluted bovine serum (Group III) was used as the pulpal fluid. As a control. the same procedures were performed in the dried dentin surfaces (Group I). After one day of storage in water. the micro shear bond strengths were measured using an EZ tester. Group II and III showed significantly lower shear bond strength than Group I statistically (p < 0.05). $SEbond^{\circledR}{\;}and{\;}AdheSE^{\circledR}$ showed no difference among the different dentin condition. In the Adper Prompt $L-Pop^{\circledR}$. a simulated pulpal pressure were applied to the specimens using diluted bovine serum. which showed a higher strength than the specimens in which saline was used (p < 0.05).