• Journal of Powder Materials
• /
• v.15 no.5
• /
• pp.371-377
• /
• 2008

This paper deals with the phase analysis of $MgB_2$ bulk using spark plasma sintering process after ball milling. Mg and amorphous B powders were used as raw materials, and milled by planetary-mill for 9 hours at argon atmosphere. In order to confirm formation of $MgB_2$ phase, DTA and XRD were used. The milled powders were fabricated to $MgB_2$ bulk at the various temperatures by Spark Plasma Sintering. The fabricated $MgB_2$ bulk was evaluated with XRD, EDS, FE-SEM and PPMS. In the DTA result, reaction on formation of $MgB_2$ phase started at $340^{\circ}C$. This means that ball milling process improves reactivity on formation of $MgB_2$ phase. The $MgB_2$ MgO and FeB phases were characterized from XRD result. MgO and FeB were undesirable phases which affect formation of $MgB_2$ phase, and it's distribution could be confirmed from EDS mapping result. Spark Plasma Sintered sample for 5 min at $700^{\circ}C$ was relatively densified and it's density and transition temperature showing super conducting property were $1.87\;g/cm^3$ and 21K.

• Progress in Superconductivity and Cryogenics
• /
• v.24 no.4
• /
• pp.36-39
• /
• 2022

Since the MgB₂ superconductor is simply composed of two constituents of Mg and B, its performance can be monitored easily with the change of one ingredient compared to the other. With the powder size of B less than 100 nm, two different sizes of Mg powders are used to investigate the reaction temperature dependence of MgB₂ bulk samples. In the range of 630-700℃ for the duration of 30 min., the un-reacted Mg is seen only at 630℃ with Mg powder size of <5 ㎛, whereas Mg traces are detected at all the temperature range with Mg powder size of <45 ㎛. The reaction temperature dependence of MgB₂ superconducting transition temperature, T_c, shows little difference whether Mg powder size is large or small in this range except for the 630℃. It is worthy of notice that the critical current densities of MgB₂ show higher performance with the small size of Mg compared to the large one at all field ranges. With the Mg powder size of <45 ㎛, flux pinning is enhanced with decreasing the reaction temperature, whereas flux pinning properties is quite similar in the Mg powder size of <5 ㎛ except for the 630℃, where Mg is left behind after the reaction.

• Journal of the Korean Applied Science and Technology
• /
• v.36 no.4
• /
• pp.1119-1127
• /
• 2019

This study analyzes the content of niacin, B1, and B2, which are among the water-soluble vitamin B group, in cultivars of the commonly consumed agricultural products of apples, peaches, nectarines and strawberries to compare content differences and to use results as base material for the Korean Food Composition Table. While the vitamin B1 content of apples according to different cultivars was found to be within the ranges of 0.063-0.208 mg/100g, and the content of vitamin B2 was found to be within the value ranges of 0.006-0.031 mg/100g, no niacin was found. The vitamin B1 content of peaches and nectarines according to different cultivars was found to be within the value ranges of 0.014-0.276 mg/100g, the content of vitamin B2 was found to be within he value ranges of 0.019-0.042 mg/100g, and niacin content was found to be within the value ranges of 0.298-1.096 mg/100g. The vitamin B1 content of strawberries according to cultivars was found to be within the value ranges of 0.112-0.394 mg/100g, the content of vitamin B2 was found to within the value ranges of 0.001-0.027 mg/100g, and niacin content was found to be within the value ranges of 0.388-0.809 mg/100g. Therefore, when nutrient composition analysis databases for the fruits of apples, peaches, and strawberries are constructed, cultivar factors must be put into consideration. In addition, differences can be found according to fruit harvest times, cultivation methods, and environmental factors, so related additional is needed.

• Progress in Superconductivity and Cryogenics
• /
• v.13 no.4
• /
• pp.5-9
• /
• 2011

We have fabricated the superconducting $MgB_2$/carbon fiber by physical vapor deposition method. Mg (Magnesium) and B (Boron) were simultaneously deposited on the carbon fiber using the RF-sputtering and thermal evaporation, respectively. To ensure the relatively high vapor pressure of Mg at the growth region and the subsequent phase stability of $MgB_2$ at the deposition temperature, inverted funnel-like guide made of Mg-foil was employed while one side of the guide were open for the sputtered B flux. Mg vapor pressure should be controlled precisely to secure the complete reaction. The $MgB_2$/carbon fiber showed a uniformly deposited thin layer with dense and well-formed grains. The $MgB_2$/carbon fibers in this study showed $T_c$~37.5K, $J_c$ ~ $2{\times}10^4\;A/cm^2$ in the 20K, 0T.

• Progress in Superconductivity
• /
• v.13 no.3
• /
• pp.184-188
• /
• 2012

$MgB_2$ superconducting sheets have been fabricated by powder rolling method using mixture of Mg and B powders. Sheet-type $MgB_2$ bulk samples of ~10 mm width and 50-100 mm long were squeezed out after compacted by two rotating rolls of 130 mm diameter with gap distance of 0.5 mm and speed of ~40 cm/min (~1 rpm). The nominal composition of Mg, which is ductile metal, was added up to 30% to facilitate forming the $MgB_2$ sheets. The annealed samples at $900^{\circ}C$ and 3 hrs showed superconducting transition temperature of ~32 K and critical current densities at zero fields were ${\sim}10^5A/cm^2$ at 5 K and ${\sim}5{\times}10^4A/cm^2$ at 20 K.

• Progress in Superconductivity
• /
• v.10 no.1
• /
• pp.40-44
• /
• 2008

A combined process of a mechanical ball milling and liquid glycerin ($C_{3}H_{8}O_3$) treatment of boron (B) powder has been conducted to enhance the superconducting properties of $MgB_2$. The individual aims of the mechanical milling and the glycerin treatment were to reduce the grain size of the $MgB_2$ and to achieve homogeneous carbon (C) incorporation into the $MgB_2$, respectively. Four kinds of B powders of as-received, glycerin treated, 2 h milled, and 2 h milled + glycerin treated were prepared. $MgB_2$ bulks were fabricated by in situ process using the prepared B powders. The mechanical ball milling was effective for a grain refinement, and a lattice disorder was easily achieved by glycerin addition. It was found that the critical current density ($J_c$) values were enhanced in the samples with milled B or glycerin treated B only. In the $MgB_2$ bulk prepared with both milled and glycerin treated B, the $J_c$ was further increased due to a higher grain boundary density and a greater C substitution.

• Progress in Superconductivity and Cryogenics
• /
• v.19 no.2
• /
• pp.19-24
• /
• 2017

Cryogenic milling which is a combined process of low-temperature treatment and mechanical milling was applied to fabricate high critical current density $(J_c)MgB_2$ bulk superconductors. Liquid nitrogen was used as a coolant, and no solvent or lubricant was used. Spherical Mg ($6-12{\mu}m$, 99.9 % purity) and plate-like B powder (${\sim}1{\mu}m$, 97 % purity) were milled simultaneously for various time periods (0, 2, 4, 6 h) at a rotating speed of 500 rpm using $ZrO_2$ balls. The (Mg+2B) powders milled were pressed into pellets and heat-treated at $700^{\circ}C$ for 1 h in flowing argon. The use of cryomilled powders as raw materials promoted the formation reaction of superconducting $MgB_2$, reduced the grain size of $MgB_2$, and suppressed the formation of impurity MgO. The superconducting critical temperature ($T_c$) of $MgB_2$ was not influenced as the milling time (t) increased up to 6 h. Meanwhile, the critical current density ($J_c$) of $MgB_2$ increased significantly when t increased to 4 h. When t increased further to 6 h, however, $J_c$ decreased. The $J_c$ enhancement of $MgB_2$ by cryogenic milling is attributed to the formation of the fine grain $MgB_2$ and a suppression of the MgO formation.

• Progress in Superconductivity and Cryogenics
• /
• v.19 no.1
• /
• pp.42-46
• /
• 2017

The effects of the heat treatment temperature ($600^{\circ}C-1050^{\circ}C$) on the formation of $MgB_2$ and the superconducting properties have been examined. The self-synthesized $MgB_4$ and commercial Mg powders were used as raw materials for the formation of $MgB_2$. The superconducting critical temperatures ($T_cs$) of $MgB_2$ bulk superconductors prepared at $600^{\circ}C-850^{\circ}C$ were as high as 37-38 K regardless of the heat treatment temperature. However, because $MgB_4$ is more stable than $MgB_2$ at above $850^{\circ}C$, no superconducting signals were detected in the susceptibility-temperature curves of the samples prepared above $850^{\circ}C$. As for the critical current density ($J_c$), the sample heat-treated at a low temperature ($600^{\circ}C$) for a prolonged period (40 h) showed a Jc higher than those prepared at $650^{\circ}C-850^{\circ}C$ for a short period (1 h). The FWHM (full width at half maximum) result showed that the grain size of $MgB_2$ of the $600^{\circ}C$ sample was smaller than that of the other samples. The high $J_c$ of the $600^{\circ}C$sample is attributed to the presence of large numbers of grain boundaries, which can act as flux pinning centers of $MgB_2$.

• Progress in Superconductivity and Cryogenics
• /
• v.10 no.1
• /
• pp.19-23
• /
• 2008

Spherical $MgB_2$ powders was synthesized with the ultrasonic spray pyrolysis(USP) process using aqueous solutions of boron and magnesium ion. The properties of synthesized $MgB_2$ powder were characterized by XRD, SEM and EDS. A small amount of MgO was detected as the secondary phase out of the synthesized powder and the ratios of $MgB_2$ to MgO increased with increasing furnace temperature. The particle size and morphology of $MgB_2$ powder were investigated with varying molar concentration of the boron and magnesium solution and furnace temperature between $600^{\circ}C$ and $1000^{\circ}C$ in $Ar/H_2$. The average particle size of $MgB_2$ showed narrow distribution ranging from 300nm to 400nm. The morphology of particles exhibited mostly spherical shapes and uniform distribution.

• Progress in Superconductivity and Cryogenics
• /
• v.15 no.2
• /
• pp.12-15
• /
• 2013

The pure and carbon (C)-doped $MgB_2$ thin films were fabricated on $Al_2O_3$ (0001) substrates at a temperature of $650^{\circ}C$ by using hot-filament-assisted hybrid physical-chemical vapor deposition technique. The $T_c$ value for pure $MgB_2$ film is 38.5 K, while it is between 30 and 35 K for carbon-doped $MgB_2$ films. Expansion in c-axis lattice parameter was observed with increase in carbon doping concentration which is in contrast to carbon-doped $MgB_2$ single crystals. Significant enhancement in the critical current density was obtained for C-doped $MgB_2$ films as compared to the undoped $MgB_2$ film. This enhancement is most probably due to the incorporation of C into $MgB_2$ and the high density of grain boundaries, both help in the pinning of vortices and result in improved superconducting performance.