• 소성∙가공
• /
• 제30권1호
• /
• pp.5-15
• /
• 2021

The effects of heat treatments (T6 and T73) on the microstructure, mechanical properties, and high cycle fatigue behavior of modified AA7075 alloys were investigated. A modified 7075 alloy was manufactured using modified-Mg (Mg-Al2Ca) instead of the conventional element Mg. Based on the microstructure, the average grain size was 4.5 ㎛ (T6) and 5.2 ㎛ (T73). Regardless of heat treatment, the modified AA7075 alloys consisted of Al matrix containing homogeneously distributed Al2CuMg and MgZn2 phases with reduced Fe-intermetallic compound. Room temperature tensile tests showed that the properties of modified 7075-T6 (Y.S.: 622MPa, T.S: 675MPa, elongation: 15.4%) were superior to those of T73 alloy (Y.S.: 492MPa, T.S: 548MPa, elongation: 12.8%). Experimental data show that the fatigue life of T6 was 400 MPa, about 64% of its yield strength. However, the fatigue life of T73 alloy was 330 MPa and 67%. Irrespective of the stress level, all crack initiation points were located on the specimen surface, and no inclusions acting as stress concentrators were seen. Superior mechanical properties and high cycle fatigue behavior of modified AA7075-T6 alloy are attributed to the fine grains and homogeneous distribution of small second phases such as MgZn2 and Al2CuMg, in addition to reduced Fe-intermetallic compounds.

• 한국주조공학회지
• /
• 제41권6호
• /
• pp.528-534
• /
• 2021

본 연구는 Al-Mg-Si 합금에서 Cu가 첨가 후 자연시효와 인공시효에 따른 제2상 석출 반응이 합금의 열확산도 및 경도에 미치는 영향을 연구하였다. 연구에 사용된 Al-0.4Mg-0.2Si 합금과 Cu를 0.6 wt%, 1.0wt% 추가한 Al-Mg-Si-Cu 합금을 각각 중력 주조로 제작하고 열확산도 경도를 측정하고 석출 반응을 확인하기 위해 열량 분석을 실시 하였다. Al-Mg-Si 합금에 첨가된 Cu는 Q'상 및 θ'상과 같은 강화상 형성에 참여하여 합금의 경도와 고온 열확산도를 향상시켰다. 한편, 자연시효 시간 증가는 Al-Mg-Si-Cu 합금의 열확산도에는 큰 영향을 미치지 않았으나, 경도를 하락시키는 것으로 확인되었다.

• 한국주조공학회지
• /
• 제27권3호
• /
• pp.126-130
• /
• 2007

Oxidation behavior of CaO added Mg and Mg-5Al alloys was investigated. At $500^{\circ}C$, oxidation rate of pure Mg was abruptly increased, while that of CaO added Mg was remarkably reduced with increasing CaO content. As a result of surface analysis by AES, there was the thin oxide layer mixed with MgO and CaO in CaO added Mg. Oxidation behavior of CaO added Mg was similar to that of Ca added Mg. Oxidation rate of 0.6CaO added Mg-5Al alloy was much lower than that of Mg-5Al alloy at $500^{\circ}C$ and both alloys showed the linear weight change at $400^{\circ}C$.

• 소성∙가공
• /
• 제31권5호
• /
• pp.253-260
• /
• 2022

In this study, the microstructural characteristics of a high-speed-extruded Mg-5Bi-3Al (BA53) alloy and its tensile, compressive, and high-cycle fatigue properties are investigated. The BA53 alloy is successfully extruded at a die-exit speed of 16.6 m/min without any hot cracking using a large-scale extruder for mass production. The homogenized BA53 billet has a large grain size of ~900 ㎛ and it contains fine and coarse Mg₃Bi₂ particles. The extruded BA53 alloy has a fully recrystallized microstructure with an average grain size of 33.8 ㎛ owing to the occurrence of complete dynamic recrystallization during high-speed extrusion. In addition, the extruded BA53 alloy contains numerous fine lath-type Mg₃Bi₂ particles, which are formed through static precipitation during air cooling after exiting the extrusion die. The extruded BA53 alloy has a high tensile yield strength of 175.1 MPa and ultimate tensile strength of 244.4 MPa, which are mainly attributed to the relative fine grain size and numerous fine particles. The compressive yield strength (93.4 MPa) of the extruded BA53 alloy is lower than its tensile yield strength, resulting in a tension-compression yield asymmetry of 0.53. High-cycle fatigue test results reveal that the extruded BA53 alloy has a fatigue strength of 110 MPa and fatigue cracks initiate at the surface of fatigue test specimens, indicating that the Mg₃Bi₂ particles do not act as fatigue crack initiation sites. Furthermore, the extruded BA53 alloy exhibits a higher fatigue ratio of 0.45 than other commercial extruded Mg-Al-Zn-based alloys.

• 동력기계공학회지
• /
• 제12권1호
• /
• pp.66-71
• /
• 2008

Alumium alloys hot forging process are gaining increased acceptance in the automotive and electronic industries and hot forging is one of the most efficient manufacturing method for mass product parts. It has been investigated the microstructures and mechanical properties of Al-11.7Si-0.5Mg (KNT40-T6)alloy fabricated by hot forging process for development of connecting rod in this study. The microstructure of hot forged specimen was composed of eutectic structure of alumimum solid solution and $Mg_2Si$ precipitates. The tensile strength of solutionized Al-11.7Si-0.5Mg alloy was 217MPa. This alloy showed a good corrosion resistance using electrochemical polarization test.

• 한국주조공학회지
• /
• 제31권3호
• /
• pp.145-151
• /
• 2011

Metallic foam has been known as a functional material which can be used for absorption properties of energy and sound. The unique characteristics of Al foam of mechanical, acoustic, thermal properties depend on density, cell size distribution and cell size, and these characteristics expected to apply industry field. Al-Zn-Mg-Cu alloy foams was fabricated by following process; firstly melting the Al alloy, thickening process of addition of Ca granule to increased of viscosity, foaming process of addition of titanium hydride powder to make the pores, holding in the furnace to form of cooling down to the room temperature. Metal foams with various porosity level were manufactured by change the foaming temperature. Compressive strength of the Al alloy foams was 2 times higher at 88% porosity and 1.2 times higher at 92% porosity than pure Al foams. It's sound and vibration absorption coefficient were higher than pure Al foams and with increasing porosity.

• 열처리공학회지
• /
• 제20권6호
• /
• pp.293-298
• /
• 2007

Influences of aluminum carbide ($Al_4C_3$) addition on microstructure and damping capacity of Mg-3%Al casting alloy have been investigated based on experimental results of optical micrography, scanning electron microscopy with energy-dispersive spectrometry analysis and damping capacity measurement at RT. The addition of $Al_4C_3$ particles results in an efficient grain refinement. The damping capacity shows an increasing tendency with an increase in $Al_4C_3$ content. The damping value associated with $Al_4C_3$ particles is linearly dependent on the volume fraction of $Al_4C_3$ particles to the 2/3 power, $f_{2/3}$, which corresponds to the total surface area of the particles.

• 한국주조공학회지
• /
• 제19권5호
• /
• pp.433-439
• /
• 1999

Rapidly solidified Mg-Al-Si base alloys containing Ca were obtained by melt spinning. The melt-spun ribbons were aged isochronally or isothermally to investigate age hardening phenomena and microstructural change according to the alloy composition. Age hardening occurred after aging at $200^{\circ}C$ for 1h mainly due to the precipitation of $Al_2Ca$ and $Mg_2Ca$, which have coherent interfaces with the matrix. With the increase of Ca content, the hardness values of the alloy ribbons were increased. Among the alloys, Mg-10Al-2 Si-3Ca alloy showed a good thermal stability at elevated temperature.

• 한국주조공학회지
• /
• 제37권1호
• /
• pp.14-20
• /
• 2017

The microstructure, electrical conductivity and hardness variation of an AZ91-5wt%Sn Mg alloy sample during a solid-solution and aging heat treatment were instigated by optical microscopy, scanning electron microscopy, X-ray diffraction and by Rockwell hardness techniques in this study. The XRD result shows that the main phases in the as-casted alloy are ${\alpha}$-Mg, $Mg_{17}Al_{12}$ and $Mg_2Sn$. From the SEM images of the AZ91-5wt%Sn Mg alloy after the solution treatment, the $Mg_{17}Al_{12}$ phases in the alloy were found to have dissolved into the matrix with an increase in the holding time during the solution treatment, but $Mg_2Sn$ phases were clearly observable. The highest peak hardness of the AZ91-5wt%Sn Mg alloy is 82HRE at an aging temperature of $200^{\circ}C$.

• 한국표면공학회지
• /
• 제49권5호
• /
• pp.454-460
• /
• 2016

Double-layered Al-Mg films have been deposited by using an e-beam deposition method on a cold-rolled steel sheet(CR), which the structure of the film was Al/Mg/CR. The micro-structure, alloy phase, and corrosion resistance of the Al-Mg coated CR were investigated before and after heat treatment at $400^{\circ}C$ for 2, 3, and 10 min in a nitrogen atmosphere. Total thickness of Al-Mg films was fixed at $3{\mu}m$ and the thickness ratio of Al and Mg layers(Al:Mg) has been changed from 5:1 to 1:5. The cross-sectional morphology of the films, which had the thickness ratio of 2:1(Al:Mg), 1:1, and 1:2, was changed after heat treatment from columnar to featureless structure. The x-ray diffraction data for as-deposited films showed only pure Al and Mg peaks. Al-Mg alloy peaks such as $Al_3Mg_2$ and $Al_{12}Mg_{17}$ phase appeared after the heat treatment. The Al-Mg coating with the thickness ratio of 1:1(Al:Mg) showed the best corrosion resistance of up to 500 hours by salt spray test.