• Korean Journal of Materials Research
• /
• v.10 no.5
• /
• pp.375-381
• /
• 2000

Aluminium foil for electrolytic capacitors was anodized at the voltage of 100V and 140V for 10 minutes in ammonium adipate solution to form aluminum oxide layer on aluminum substrate as an dielectric film. The thickness, the stoichiometry and the crystal structure of the layer were investigated by using RBS and TEM . In addition EIS technique was employed to study the effects of addition of sulfuric acid on the increment of the foil surface area. It was found that the thickness values of the layers anodized at 100V and 140V were about 130 nm and 190 nm respectively and the stoichiometry of the elements of aluminum and oxygen was 2:3. The anodic oxide layer was shown to be amorphous. but the structure irradiated with electron beam resulted in the transformation into crystalline structure of $${\gamma}$-Al_2$$O_3$ . From a comparison of the impedance results and the capacitance variation to investigate the ef- fects of sulfuric acid addition to the etching bath of hydrochloric acid, the EIS techinque could be useful to analyze the capacitance variation.

• Journal of the Korean Magnetics Society
• /
• v.2 no.3
• /
• pp.251-256
• /
• 1992

Artificial superlattices of Co/Pd were prepared by RF magnetron sputtering Multilayered structure and compositional modulation were analyzed with a side angle x-ray diffractometer. It has been found that expansion of Co lattice occured in this artificial superlattice due to the lattice mismatch between Co and Pd. Perpendicular magnetic anisotropy could be observed when the Co layer thickness became less than 8${\AA}$ and maximum coercivity of 2350 Oe could be obtained in [Co(2.5 ${\AA}$)/Pd(9.3 ${\AA})]_{50}$/Pd$(200\;{\AA})$ with a perfect squareness of magnetic hysteresis loop. Characteristic of perpendicular magnetic anisotropy in Co/Pd superlattices could be related to the expansion of Co lattice caused by Pd layer and it turned out that as the thickness of Pd layer increased, perpendicular magnetic anisotropy increased. The interface anisotropy energy and volume anisotropy energy were calculated to be 0.29 ergs/$cm^2$ and -$6.9{\times}10^6$ ergs/$cm^3$ respectively, which are consistent with the values reported elsewhere.

• Journal of Korea Foundry Society
• /
• v.35 no.5
• /
• pp.120-127
• /
• 2015

The effects of Ti, B and Zr on grain refinement and castability were investigated in Al-4wt%Mg-0.9wt%Si-0.3wt%Mn-0.15wt%Fe alloy. Measurement of cooling curve and micro-structure observation were performed to analyze the effects of the addition of minor elements Ti, B and Zr during solidification. The prominence of effect on grain refinement was in increasing order for Ti, Zr and B element. Fine grain size and an increase of the crystallization temperature for ${\alpha}$-Al solution were evident as the amount of addition elements increased in this study. Addition of 0.15wt% Ti was most effective for grain refinement, and the resulting grain size of ${\alpha}$-Al solution for shell mold and steel mold were $72.3{\mu}m$ and $23.5{\mu}m$, respectively. Fluidity and shrinkage tests were perform to evaluate the castability of the alloy. Maximum fluidity length and minimum ratio of micro shrinkage were recorded for 0.15wt% Ti addition due to the effect of the finest grain size.

• Journal of Korean Society of Steel Construction
• /
• v.24 no.1
• /
• pp.73-80
• /
• 2012

The adoption of a composite beam system is regarded as a simple but effective solution because it improves the overall stiffness, strength and stability of the structure by welding shear studs. However, welding shear studs poses problems including electric shock and weld defects. Mechanical methods have emerged as an alternative to metallurgical methods for connecting the H-beam and shear connector. Four specimens were tested in order to compare the structural behavior of the proposed composite beams with that of the classical composite beam given the condition of horizontal loading. With the original composite beam (FCB-SB specimen) using stud bolts, hysteresis loops are stable, but its strength decreased with the crashing of the concrete slab around the column. The suggested composite beams using shear connectors also yielded stable hysteresis loops. Consequently, use of the suggested composite beams instead of the original composite beam are recommended.

• Korean Journal of Materials Research
• /
• v.11 no.7
• /
• pp.569-574
• /
• 2001

The crystal structure, surface morphology and preferred orientation of the copper electrodeposit were investigated by the using sulfate bath with $SiO_2$suspensions and the cathode substrate Au sputtered. As by the addition of colloidal silica in copper electrolytic bath and Au pre-coating on substrate, the crystal particles of deposits was fined-down, made uniform and the account of particles were increased. Hardness of copper electrodeposits with colloidal silica increased about 15% in comparison with that of pure copper deposit film and (111), (200) and (311) plane of X-ray diffraction patterns were almost swept away, so preferred orientation of the copper deposits changed from (111) to (110) plane by codeposit $SiO_2$ and precoating the substrate.

• Korean Journal of Materials Research
• /
• v.11 no.7
• /
• pp.550-555
• /
• 2001

A diamond-like carbon(DLC) films were deposited on the borosilicate glass substrate by radio frequency plasma enhanced chemical deposition(rf-PECVD). The $methane(CH_4)-hydrogen(H_2)$ gas mixture was used as precursor gas. The morphologies, the structure and the optical properties of the DLC films were investigated by SEM, Raman and UV spectrometer. The deposition rate was slightly increased with the hydrogen concentration in the gas mixture and it maintained constant at over 25 sccm of the gas flow rate. The optical band gap calculated by UV spectra decreased with increase of deposition time and DC self bias, but that were not effected by hydrogen content. Most effective parameter on the transmittance of film was bias voltage, especially in the range of ultra violet and visible light.

• Journal of Powder Materials
• /
• v.20 no.4
• /
• pp.275-279
• /
• 2013

Fe-based oxide dispersion strengthened (ODS) powders were produced by high energy ball milling, followed by spark plasma sintering (SPS) for consolidation. The mixed powders of 84Fe-14Cr-$2Y_2O_3$ (wt%) were mechanically milled for 10 and 90 mins, and then consolidated at different temperatures ($900{\sim}1100^{\circ}C$). Mechanically-Alloyed (MAed) particles were examined by means of cross-sectional images using scanning electron microscopy (SEM). Both mechanical alloying and sintering behavior was investigated by X-ray diffraction (XRD) and high resolution transmission electron microscopy (HR-TEM). To confirm the thermal behavior of $Y_2O_3$, a replica method was applied after the SPS process. From the SEM observation, MAed powders milled for 10 min showed a lamella structure consisting of rich regions of Fe and Cr, while both regions were fully alloyed after 90 min. The results of sintering behavior clearly indicate that as the SPS temperature increased, micro-sized defects decreased and the density of consolidated ODS alloys increased. TEM images revealed that precipitates smaller than 50 nm consisted of $YCrO_3$.

• Journal of Welding and Joining
• /
• v.27 no.2
• /
• pp.38-43
• /
• 2009

In this study, we investigated photocatalytic ability of plasma sprayed $TiO_2$ and Ag sputtering $TiO_2$(Ag-$TiO_2$) coatings. A sputtering processes were adopted to coat the surface of $TiO_2$ with Ag(99.99%). Ag was sputtered at 10mA, 450V for $1{\sim}11$ seconds. $TiO_2$ and Ag-$TiO_2$ coatings were heat-treated at 250, 300, 350, $400^{\circ}C$ for $0{\sim}240$seconds. Photoelectrical conductivity was measured by four-point probe, and photodegradation was calculated by UV-V is spectrometer. Microstructure observation of $TiO_2$ and Ag-$TiO_2$ coatings were investigated by SEM. Crystal structure of $TiO_2$ and Ag-$TiO_2$ coatings were investigated by XRD. Qualitative analyses of $TiO_2$ and Ag-$TiO_2$ coatings were conducted by EDX. When $TiO_2$ coatings were heat-treated at $350^{\circ}C$ for 30 sec, photoelectrical conductivity and photodegradation were best. And in XRD analysis result, (101)/(110) relative intensity ratio of $TiO_2$(rutile) was comparably changed with photoelectrical conductivity. When Ag-$TiO_2$ coatings were heat-treated at $350^{\circ}C$ for 30 [sec] after sputtering Ag for 7 sec, Photoelectrical conductivity and photodegradation are best. Surface of coatings in such condition has very small and uniform Ag particles.

• Korean Journal of Materials Research
• /
• v.7 no.8
• /
• pp.654-659
• /
• 1997

HMDS[Si$_{2}$(CH$_{3}$)$_{6}$]단일 선구체를 이용하여 화학증착 방법으로 성장된 3C-SiC/Si(001) 이종접합박막의 특성을 XRD, 라만 스펙트럼 및 투과전자현미경(TEM)등을 이용하여 조사하였으며 시판되고 있는 상용 3C-SiC/Si 시편을 같은 방법으로 분석하여 특성을 비교검토하였다. $C_{3}$H$_{8}$-SiH$_{4}$-H$_{2}$혼합가스를 선구체로 이용하여 5$\mu\textrm{m}$두께로 성장된 상용 3C-SiC/Si 이종접합박막 시료의 XRD스펙트럼에서는 강한 3C-SiC(002)피크 만이 관찰되었으며, 라만 스펙트럼의 LO피크는 970nm$^{-1}$ 정도에서 강하게 나타났다. TEM 관찰 결과 다수의 전위, 쌍정, 적층결함 및 APB와 같은 결정결함들이 3C-SiC/Si 계면 근처에 집중적으로 분포되어 있었으며 성장된 박막은 단결정임을 확인할 수 있었다. 선구체로 HMDS를 사용하여 0.3$\mu\textrm{m}$ 및 2$\mu\textrm{m}$ 두께로 성장시킨 3C-SiC/Si 박막 시료의 XRD 스펙트럼은 다소 완만한 3C-SiC(002) 피크와 함께 3C-SiC(111)피크가 관찰되었으며, TEM으로 확인한 결과 소경각 결정립들이 약 5˚-10˚ 정도 방위차를 가지고 성장하여 기둥구조(columnar structure)를 이루고 있기 때문임을 알 수 있었다. 라만 스펙트럼 분석 결과 박막의 LO 피크가 967-969nm$^{-1}$정도로 다소 낮은 wavenumber쪽으로 이동되어 박막 내에 상당한 응력이 존재함을 확인할 수 있었다. 이와 같은 HMDS 3C-SiC박막의 특성은 성장 온도가 낮고 박막 성장용 가스로 사용한 HMDS 선구체에서 탄소가 과잉으로 공급되기 때문으로 제안되었다.다.

• Korean Journal of Materials Research
• /
• v.8 no.11
• /
• pp.993-998
• /
• 1998

In this study TiNi/A16061 shape memory composite is introduced as one of new material using a shape memory alloy. High tensile strength of composite due to compressive residual stress in matrix by the shape memory effect of TiNi fiber can be produced. This composite can remove the tensile residual stress by the difference of coefficients of thermal expansion between fiber and matrix. one of the significant weak point of metal matrix composite. In this paper, shape memory composites are made by squeeze casting. And then, microstructure and fatigue properties of the composites by shape memory effect above inverse transformation temperature A, of TiNi alloy are discussed. The results of the fatigue crack control properties of TiNi/A16061 shape memory composite by a squeeze casting are summarized as follows the effect of fatigue crack propagation control at 363K increases according to the increase of volume fraction and prestrain in composites.