• Korean Journal of Materials Research
• /
• v.5 no.7
• /
• pp.775-780
• /
• 1995

Thin films of titanium nitride are formed using the tetrakis-dimethyl-amino-titanium (TDMAT(Ti[N($CH_3$)$_2$]$_4$)) under various conditions. The formation of TiN films has been obtained from the thermal decomposition of the Ti-precursor and the gas phase reaction between TDMAT and ammonia(NH$_3$). The resistivity of the MOCVD film can be attributed to their impurity. Especially the curve fitting graph of XPS data is revealed that main impurities in the films as carbon and oxygen make various interstitial compounds which has influenced physical and electrical properties of the film. In the contact hole with the aspect ratio of 3:1 and the diameter of 0.5${\mu}{\textrm}{m}$, the SEM morphology shows that the step coverage is more decreased in the films formed y flowing ammonia additionally than the films formed by pyrolysis of TDMAT and the phenomenon is probably related with the activation energy.

• New Physics: Sae Mulli
• /
• v.68 no.12
• /
• pp.1281-1287
• /
• 2018

In this study, $Al_xGa_{1-x}N$ films were grown on (0001) sapphire substrates by using metal-organic chemical vapor deposition (MOCVD). The crystallinity of the grown films was examined with X-ray diffraction (XRD) patterns. The surfaces and the chemical properties of the $Al_xGa_{1-x}N$ films were investigated using atomic force microscopy (AFM) and X-ray photoelectron spectroscopy (XPS), respectively. The optical properties of the $Al_xGa_{1-x}N$ film were studied in a wide photon energy range between 2.0 ~ 8.7 eV by using spectroscopic ellipsometry (SE) at room temperature. The data obtained by using SE were analyzed to find the critical points of the pseudodielectric function spectra, $<{\varepsilon}(E)>=<{\varepsilon}_1(E)>+i<{\varepsilon}_2(E)>$. In addition, the second derivative spectra, $d^2<{\varepsilon}(E)>/dE^2$, of the pseudodielectric function for the $Al_xGa_{1-x}N$ films were numerically calculated to determine the critical points (CPs), such as the $E_0$, $E_1$, and $E_2$ structure. For the four samples (x = 0.18, 0.21, 0.25, 0.29) between a composition of x = 0.18 and x = 0.29, changes in the critical points (blue-shifts) with increasing Al composition at 300 K for the $Al_xGa_{1-x}N$ film were observed via ellipsometric measurements for the first time.

• Journal of the Korean Vacuum Society
• /
• v.15 no.3
• /
• pp.294-300
• /
• 2006

We fabricated the distributed feedback (DFB) InP/InGaAs/InP grating structures on InP (100) substrates by metal-organic chemical vapor deposition, and their structural properties were investigated by atomic force microscopy and scanning electron microscopy. Self-assembled InAs/InAlGaAs quantum dots (QDs) were grown on the InP/InGaAs/InP grating structures by molecular beam epitaxy, and their optical properties were compared with InAs/InAlGaAs QDs without grating structure. The duty of the grating structures was about 30%. The PL peak position of InAs/InAlGaAs QDs grown on the grating structure was 1605 nm, which was red-shifted by 18 nm from that of the InAs/InAlGaAs QDs without grating structure. This indicates that the formation of InAs/InAlGaAs QDs was affected by the existence of the DFB grating structures.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.25 no.5
• /
• pp.182-187
• /
• 2015

The growth and characterization of micro sized AlGaN array structures selectively grown by metal organic chemical vapor deposition (MOCVD) on GaN stripes are reported. The shape of the AlGaN array structures depends on the size of exposed area for selective growth. The AlGaN array structures grown selectively on relatively large exposed area have regular shapes resembling those of the GaN stripes on the substrate, while samples selectively grown on relatively small exposed area have irregular shapes. The phonon frequency of the AlGaN array structures increases with increasing Al composition in the AlGaN structure. However, at relatively high Al composition (x = 0.28 in this research), the phonon frequency decreases slightly from the expected value not only because of large tensile strain associated with large differences between the lattice constants of the AlGaN structure and underlying GaN stripes but also changes of crystal facet direction during the selective growth.

• Journal of the Korean Vacuum Society
• /
• v.19 no.4
• /
• pp.275-280
• /
• 2010

The influence of $O_2$-plasma treatment on $H_2$ post-treated BZO (ZnO:B) thin film using MOCVD (Metal-Organic Chemical Vapor Deposition) are investigated. An $O_2$-plasma treatment of the $H_2$ post-treated BZO thin films resulted in XRD peak of (100), (101) and (110). Also, electrical properties resulted in an increase in sheet resistance and work function. The weighted optical transmittance and haze at 300~1,100 nm of BZO thin films with $O_2$-plasma treatment on the $H_2$ post-treatment show approximately 86% and 15%, respectively.

• Journal of the Korean Vacuum Society
• /
• v.19 no.3
• /
• pp.217-223
• /
• 2010

We grew multi-stacked InAs/$In_{0.1}Ga_{0.9}As$ DWELL (dot-in-a-well) structure by metal organic chemical vapor deposition and investigated optical properties by photoluminescence and I-V characteristics by dark current measurement. When stacking InAs quantum dots (QDs) with same growth parameter, the size and density of QDs were changed, resulting in the bimodal emission peak. By decreasing the flow rate of TMIn, we achieved the uniform multi-stacked QD structure which had the single emission peak and high PL intensity. As the growth temperature of n-type GaAs top contact layer (TCL) is above $600^{\circ}C$, the PL intensity severely decreased and dark current level increased. At bias of 0.5 V, the activation energy for temperature dependence of dark current decreased from 106 meV to 48 meV with increasing the growth temperature of n-type GaAs TCL from 580 to $650^{\circ}C$. This suggest that the thermal escape of bounded electrons and non-radiative transition become dominant due to the thermal inter-diffusion at the interface between InAs QDs and $In_{0.1}Ga_{0.9}As$ well layer.

• Journal of the Korean Vacuum Society
• /
• v.19 no.2
• /
• pp.134-140
• /
• 2010

We have investigated the contactless electroreflectance (CER) properties of $In_{0.5}(Ga_{1-x}Al_x)_{0.5}P$/GaAs double heterostructures grown by metal-organic chemical vapour deposition (MOCVD). The CER measurements on the sample were studied as a function of temperature, modulation voltage ($V_{ac}$), and dc bias voltage ($V_{bias}$). Five signals observed at room temperature are related to the GaAs, $In_{0.5}Ga_{0.5}P$, $In_{0.5}(Ga_{0.73}Al_{0.27})_{0.5}P$, $In_{0.5}(Ga_{0.5}Al_{0.5})_{0.5}P$, and $In_{0.5}(Ga_{0.2}Al_{0.8})_{0.5}P$ transitions, respectively. From the temperature dependence of CER spectrum, the Varshni coefficients and broadening parameters were determined and discussed. In addition, we found that the behavior of the CER amplitude for the reverse bias is larger than that of the forward.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.31 no.4
• /
• pp.149-153
• /
• 2021

ε-Ga₂O₃ thin films were grown on 4H-SiC substrates by metal organic chemical vapor deposition (MOCVD) and crystalline quality were evaluated depend on growth conditions. It was found that the best conditions of the ε-Ga₂O₃ were grown at a growth temperature of 665℃ and an oxygen flow rate of 200 sccm. Two-dimensional growth was completed after the merge of hexagonal nuclei, and the arrangement direction of hexagonal nuclei was closely related to the crystal direction of the substrate. However, it was confirmed that crystal structure of the ε-Ga₂O₃ had an orthorhombic rather than hexagonal. Crystal phase transformation was performed by thermal treatment. And a β-Ga₂O₃ thin film was grown directly on 4H-SiC for the comparison to the phase transformed β-Ga₂O₃ thin film. The phase transformed β-Ga₂O₃ film showed better crystal quality than directly grown one.

• Korean Journal of Materials Research
• /
• v.11 no.1
• /
• pp.20-26
• /
• 2001

The deposition characteristics of MOCVO Cu using the (hfac)Cu(I) (1,5-DMCOD)(1,1,1,5,5,5-hexafluoro-2,4-pentanedionato Cu(I) 1,5-dimethyl-cyclooctadine) as a precursor have been investigated in terms of the effects of hydrogen and H(hfac) ligand addition with He carrier gas. MOCVD Cu using a Helium carrier gas showed a low deposition rate (20~$125{\AA}/min$) at the substrate temperature range of 180~$230^{\circ}C$. Moreover, the Cu film deposited at 19$0^{\circ}C$ was very thin (~$700{\AA}$) and showed the lowest resistivity value of $2.8{\mu}{\Omega}-cm$. The deposition rate of MOCVD Cu using $H_2$or H(hfac) addition was significantly enhanced especially at the low temperature region (180~$190^{\circ}C$). Furthermore, thinner Cu films (~$500{\AA}$) provided low resistivity (3.6~$2.86{\mu}{\Omega}-cm$). From surface reflectance measurement, very thin films deposited by using different gas system revealed good surface morphology comparable with sputtered Cu film ($300^{\circ}C$, vacuum-anneal). Hence, Cu film using (hfac)Cu(1,5-DMCOD) as a precursor is expected as a good seed layer in the electrochemical deposition process for Cu metallization.

• Korean Journal of Environment and Ecology
• /
• v.22 no.3
• /
• pp.260-267
• /
• 2008

This study was carried out to investigated the relation between air depositions and soil properties in Gyeongsanman province. Soil pH was average 4.40 in regions, and was the highest soil pH value in Miryang-sanne(pH 5.02), the lowest pH value in Namhae-seomyeon(pH4.08). Soil pH, soil organic matter content, avail phosphorus, K, Ca and cation exchange capacity(CEC) were significantly different among regions(p<0.05). Pb in Heavy metal content was 3.86mg/kg average value, and was the highest in Keo-je region(9.87mg/kg), the lowest in Mryang-sanne (0.86mg/kg). Zn, Cd, Cr and Ni were significantly different among regions(p<0.05). Correlation between rainfall pH and soil properties were positive in soil $pH(r=0.7826^{**})$, Ca$(r=0.6278^*)$, Mg$(r=0.5841^*)$, CEC$(r=0.6341^{**})$ and Cd$(r=0.5995^*)$, and were negative in Pb$(r=-0.5283^*)$. Correlation between $SO_2$ concentration and soil properties was negative in soil pH$(r=-0.6796^{**})$, Ca$(r=-0.5810^*)$, Mg$(r=-0.5522^*)$) and CEC$(r=-0.5905^*)$. Correlation between $NO_2$ concentration and soil properties were positive in organic matter $(r=0.6208^*)$, K$(r=0.5380^*)$. It was predicted that rainfall and $SO_2$ concentration would affect soil acidification, and soil heavy metal content related Cd and Pb. Others soil heavy metal were not related.