• 한국정밀공학회지
• /
• 제30권3호
• /
• pp.271-277
• /
• 2013

Inconel 718 super alloy was aging heat treated at the temperature range from $675^{\circ}C$ to $785^{\circ}C$ for 5~40 hours after solution annealing at $1025^{\circ}C$ for 1 hour. The aging treated specimens were investigated microstructure, mechanical properties and thermal expansion/contraction. Precipitates appeared for a long time aging treatment were niobium carbide and also ${\gamma}^{\prime}$ phase. For the aging treatment time of 10 hours, the changes in strength and hardness with increasing aging treatment temperature showed the maximum value at the temperature of $725^{\circ}C$. This maximum value is to be related with the precipitation of ${\gamma}^{\prime}$ and ${\gamma}^{{\prime}{\prime}}$ phases. The decrease in strength, elongation and hardness during long time aging at $725^{\circ}C$ were thought to be induced from the coarsening of the grain size and the transformation of ${\gamma}^{{\prime}{\prime}}$ phase to ${\gamma}^{\prime}$ phase. For the specimens treated for 10 hours, impact energy showed constant value of ~105 J with increasing the aging temperature, however this value continuously decreased with elapsing time at the aging temperature of $725^{\circ}C$. It was found that the decrease in impact value was induced from the coarsening of grain size and the carbide coarsening. The coefficient of thermal expansion of aging treated Inconel 718 alloy increased with raising test temperature, and the coefficient was appeared $11.57{\sim}12.09{\mu}m/m{\cdot}^{\circ}C$ and $14.28{\sim}14.39{\mu}m/m{\cdot}^{\circ}C$, respectively, after heating to $150^{\circ}C$ and $450^{\circ}C$.

• 해양환경안전학회지
• /
• 제29권5호
• /
• pp.479-487
• /
• 2023

최근 지구 온난화의 영향으로 태풍의 파괴력이 증가함에 따라 부유식 해상풍력발전기의 막대한 유실과 붕괴에 대한 우려가 깊어지고 있다. 부유식 해상풍력발전기의 안전한 운영을 위해 새로운 형태의 탈착형 계류 시스템 개발이 요구되고 있다. 본 연구에서 고려한 새로운 반잠수식 계류 풀리는 기존의 탈착형 계류 장치에 비해 계류 라인으로 부유식 해상풍력 터빈을 보다 쉽게 탈부착할 수 있도록 고안되었다. 8MW급 부유식 해상풍력발전기에 적용 가능한 반잠수식 계류 풀리의 초기 설계에 대한 구조적 안전성을 검토하기 위해 3D 프린터를 이용하여 축소구조모형을 제작하고, 이 모형에 대한 구조시험을 수행하였다. 축소 모형의 구조시험을 위해 3D 프린팅에 사용된 ABS 소재의 인장 시편을 제작하고 인장시험을 수행하여 소재의 물성을 평가하였다. 인장시험에서 얻은 재료 특성과 축소모형 구조 시험과 동일한 하중 및 경계 조건을 적용하여 반잠수식 계류 풀리의 유한요소해석을 수행하였다. 유한요소해석을 통해 반잠수식 계류 풀리의 구조적 취약 부분을 검토하였다. 반잠수식 계류 풀리의 주요 하중조건을 고려하여 구조모형시험을 수행하였으며, 재료의 최대인장응력 이상이 발생하는 위치에 대해 유한요소해석과 시험 결과를 비교하였다. 유한요소해석과 모형시험의 결과로부터 작동조건에서는 Body와 Wheel의 연결부 구조가 취약한 것으로 파악되었고, 계류조건에서는 Body와 Chain stopper의 연결부 구조가 취약한 것으로 검토되었다. 축소모형 구조시험에서 나타난 SMP의 구조 취약부는 구조해석의 결과와 일치하는 것으로 나타났다. 연구 결과를 통해 반잠수식 계류 풀리의 초기 설계에 대한 구조적 안전성을 실험적으로 검증할 수 있었다. 또한, 본 연구 결과는 상세설계 단계에서 반잠수식 계류 풀리의 구조 강도를 향상시키는데 유용하게 활용될 수 있을 것으로 판단된다.

• 농업과학연구
• /
• 제13권1호
• /
• pp.90-102
• /
• 1986

본(本) 연구(硏究)는 물-시멘트비(比)와 감수제(減水劑) 첨가량(添加量)에 따른 콘크리트의 제성질(諸性質)을 보통(普通)시멘트 콘크리트와 비교(比較) 구명(究明)함으로써 콘크리트의 효과적(效果的)인 사용(使用)을 위(爲)한 기초자료(基礎資料)를 마련하는데 있으며, 이 연구(硏究)에서 얻어진 결과(結果)를 요약(要約)하면 다음과 같다. 1. 적량(適量)의 감수제(減水劑)를 첨가(添加)하면 보통(普通)시멘트 콘크리트에 비(比)하여 감수표준제(減水標準劑)인 WR-LG는 12.9%, 고류동화제(高流動化劑)인 HF-SP는 8.6%, 감수조강제(減水早强劑)인 AH-WR은 17.2%의 단위수량(單位水量)이 감소(減少)되었으며, 이의 첨가량(添加量)이 증가(增加)함에 따라 단위수량(單位水量)은 더욱 감소(減少)하였다. 2. 최대강도(最大强度)를 나타내는 감수제(減水劑)의 첨가율(添加率) WR-LG는 0.2%, HF-SP와 AH-WR은 0.4%로 나타났으며, 강도(强度)의 증가율(增加率)은 보통(普通)시멘트 콘크리트에 비(比)하여 WR-LG 콘크리트는 24.1%, HF-SP 콘크리트는 41.8%, AH-WR 콘크리트는 43.6%로 나타났다. 3. 감수제(減水劑)를 첨가(添加)한 콘크리트의 압축강도(壓縮强度)와 인장강도간(引張强度間)에는 각각(各各) 직선형(直線形)으로써 그 상관계수(相關係數)는 고도(高度)의 유의성(有意性)이 인정(認定)되었고, 콘크리트의 재령(材齡)과 감수제(減水劑) 첨가량(添加量)에 따라 압축(壓縮)과 인장강도(引張强度)를 추정(推定)할 수 있는 다중회귀방정식(多重回歸方程式)을 유도(誘導)하였으며 각(各) 방정식(方程式)은 높은 유의성(有意性) 인정(認定)되었다. 4. 적량(適量)의 감수제(減水劑)를 첨가(添加)하였을 때의 물-시멘트비(比)와 압축강도(壓縮强度)와의 관계(關係)는 직선형(直線形)으로써 모두 유의성(有意性)이 인정(認定)되었으며, 강도(强道)의 증가율(增加率)은 물-시멘트비(比) 감소율(減少率)보다 높게 나타났다.

• 콘크리트학회논문집
• /
• 제23권2호
• /
• pp.135-144
• /
• 2011

최근 PS 강연선의 대체재로서 높은 인장강도와 훌륭한 내부식을 가진 FRP(fiber rienforced polymer)를 이용한 조사가 활발히 진행되어지고 있다. 따라서, 이 연구는 FRP 긴장재를 이용한 프리스트레스트 콘크리트 보를 제작하여 반복 하중에 따른 피로거동의 특성을 분석함으로써 프리스트레스트 콘크리트 보의 안전성을 평가하고자 하였다. 또한 기존 PS 강연선을 이용한 프리스트레스트 콘크리트 보를 제작하여 피로 성능을 비교하였다. 반복 하중은 정적 실험을 통해서 얻은 극한 하중의 40%를 최소 하중으로 일정하게 고정하고 최대 하중은 극한 하중의 60%, 70%, 80%로 결정하였다. 반복 하중은 4점 재하방식으로 sine파를 이용한 1~3 Hz의 속도 재하하였다. 피로한계는 100만회로 하였다. 40~60% 범위의 시험체는 100만회까지 피로 파괴가 나타나지 않았지만, 반복 횟수가 증가함에 따라 콘크리트와 긴장재 사이의 부착력이 저하되었고, 수평방향의 균열이 나타났다. FRP 긴장재를 이용한 프리스트레스트 콘크리트 보의 피로 실험 결과 사용 하중 상태에서의 반복 하중에 대해서 안전한 것으로 나타났다. 피로한계 100만회에 대한 피로 강도는 FRP 긴장재를 이용한 프리스트레스트 콘크리트 보의 경우 69.2%, PS 강연선을 이용한 프리스트레스트 콘크리트 보는 59.8%에 해당함을 알 수 있었다.

• 콘크리트학회논문집
• /
• 제15권4호
• /
• pp.549-556
• /
• 2003

시멘트 모르타르의 내마모성, 여러 피착체에 대한 부착성능, 내화학성, 내수성 등의 많은 성능을 개선시키는 데 폴리머 디스퍼젼은 매우 유용한 재료로서 본 실험에 사용한 SBR은 상업적으로 국내에서 생산되고 있는 시멘트 적용성이 우수한 재료이다. 본 실험에서는 시멘트 모르타르에 높은 유동성을 유도하여 자기 평활성을 가지도록 고유동화제와 SBR을 사용하여 시험체를 제작하였으며 SBR에 의한 시험체의 부착강도의 발현 특성을 파악하고자 하였으며 SBR에 의해 개질된 자기 평활성을 가지는 시멘트 모르타르는 재령의 증가에 따라 부착강도는 증가하는 현상을 보여주었으며 파괴형상을 보면 재령이 증가함에 따라 시험체에서 보다는 계면과 피착체에서 외부 인장력에 대하여 파괴가 일어났다. 현재 사무실, 공장, 주차장 등의 바닥 마감재로 널리 사용되고 있는 합성 고분자계 재료인 에폭시 수지나 폴리우레탄 제품은 연도변화가 심하여 가사시간이 상당히 짧다는 것을 확인할 수 있었으며 이에 반하여 본 연구의 시험체는 충분한 가사시간을 확보할 수 있는 이점을 가진 재료로 여겨진다.

• 한국재료학회지
• /
• 제30권10호
• /
• pp.542-549
• /
• 2020

Effects of Sc addition on microstructure, electrical conductivity, thermal conductivity and mechanical properties of the as-cast and as-extruded Al-2Zn-1Cu-0.3Mg-xSc (x = 0, 0.25, 0.5 wt%) alloys are investigated. The average grain size of the as-cast Al-2Zn-1Cu-0.3Mg alloy is 2,334 ㎛; however, this value drops to 914 and 529 ㎛ with addition of Sc element at 0.25 wt% and 0.5 wt%, respectively. This grain refinement is due to primary Al₃Sc phase forming during solidification. The as-extruded Al-2Zn-1Cu-0.3Mg alloy has a recrystallization structure consisting of almost equiaxed grains. However, the as-extruded Sc-containing alloys consist of grains that are extremely elongated in the extrusion direction. In addition, it is found that the proportion of low-angle grain boundaries below 15 degree is dominant. This is because the addition of Sc results in the formation of coherent and nano-scale Al₃Sc phases during hot extrusion, inhibiting the process of recrystallization and improving the strength by pinning of dislocations and the formation of subgrain boundaries. The maximum values of the yield and tensile strength are 126 MPa and 215 MPa for the as-extruded Al-2Zn-1Cu-0.3Mg-0.25Sc alloy, respectively. The increase in strength is probably due to the existence of nano-scale Al₃Sc precipitates and dense Al₂Cu phases. Thermal conductivity of the as-cast Al-2Zn-1Cu-0.3Mg-xSc alloy is reduced to 204, 187 and 183 W/MK by additions of elemental Sc of 0, 0.25 and 0.5 wt%, respectively. On the other hand, the thermal conductivity of the as-extruded Al-2Zn-1Cu-0.3Mg-xSc alloy is about 200 W/Mk regardless of the content of Sc. This is because of the formation of coherent Al₃Sc phase, which decreases Sc content and causes extremely high electrical resistivity.

• 한국구조물진단유지관리공학회 논문집
• /
• 제18권5호
• /
• pp.41-50
• /
• 2014

본 연구에서는 섬유종류에 따른 인발특성과 섬유보강 콘크리트의 휨특성에 대하여 평가하기 위하여, 섬유의 재질 및 형상 다른 후크형 강섬유, 비정질 강섬유 및 폴리아미드 섬유에 대하여 인발시험과 섬유보강 콘크리트 시험체를 제작하여 휨특성을 평가하였다. 그 결과, 후크형 강섬유의 경우 최대인발하중에서 섬유가 매트릭스로부터 인발되었지만, 비정질 강섬유는 섬유와 매트릭스의 부착강도가 섬유자체의 인장강도보다 높아 섬유가 매트릭스로부터 인발되지 않고 파괴되는 현상을 나타내었다, 한편, 폴리아미드 섬유는 연신율에 의해 최대인발 하중까지 변위가 크게 발생하였으며, 최대하중이후에 섬유가 끊어지는 파괴특성을 나타내었다. 섬유보강 콘크리트의 휨특성에 있어서 비정질 강섬유는 매트릭스와의 부착강도가 높고, 섬유의 혼입개체수가 많아 콘크리트의 최대휨강도는 높았지만, 균열발생 이후 섬유가 매트릭스로부터 인발되지 않고 섬유가 파괴되는 것에 의해 응력의 저하가 급격하게 발생하지만, 후크형 강섬유보강 콘크리트는 균열발생 이후 섬유가 인발되면서 응력의 저하가 완만하게 발생하였다. 폴리아미드 섬유보강 콘크리트는 균열발생이후 섬유의 연신률에 의해 응력이 급격하게 저하하는 구간이 발생하였으며, 섬유와 매트릭스의 부착에 의해 재상승하였다가 섬유가 끊어지면서 파괴되었다. 섬유와 매트릭스의 인발특성은 섬유보강 콘크리트의 휨강도 및 변형 능력에 큰 영향을 미치는 것으로 판단된다.

• 대한의용생체공학회:의공학회지
• /
• 제17권3호
• /
• pp.327-336
• /
• 1996

This study was performed to investigate the effec% of immersion in water and thermal cycling on the mechanical peoperties of light cured restorative composite resins. Five commerically available light-cured composite resins(Photo Clearfil A : CA, Lite-Fil A . LF, Clearril Photo Posterior CP, Prisms AP.H.. PA, 2100 : ZH) were unto The specimens of 12 m in diameter and 0.7 m in thickness were made, and an immersion in $37^{\circ}C$ water for 7 days and a thermal cycling of 1000 cycles at 15 second dwell time each in $5^{\circ}C$ and $55^{\circ}C$ baths were performed. Biaxial flexure test was conducted using the ball-on-three-ball method at the crosshead speed of 0.5mm/min. In order to investigate the deterioration of composite resins during the thermal cycling test, Weibull analysis for the biaxial flexure strengths was done. Fracture surfaces and the surfaces before and after the thermal cycling test were examined by SEM. The highest Weibull modulus value of 10.09 after thermal cycling tests which means the lowest strength variation, was observed in the CP group, and the lowest value of 4.47 was obsered in the LF Group. Biaxial flexure strengths and Knoop hardness numbers significantly decreased due to the thermal cycling ($\textit{p}$< 0.01), however, they recovered when specimens were drie4 The highest biaxial flexure strength of 125.65MPa was observed in the ZH group after the thermal cycling test, and the lowest value of 64.86MPa was observed in the CA group. Biaxial flexure strengths of ZH and CP groups were higher than those of PA, CF, and CA groups after thermal cycling test($\textit{p}$< 0.05). Knoop hardness numbers of CP group after the thermal cycling test was the highest(95.47 $\pm$ 7.35kg/$mm^2$) among the samples, while that of CA group was the lowest(30.73 $\pm$ 2.58kg/$mm^2$). Knoop hardness numbers showed the significant differences between the CP group and others after the thermal cycling test(($\textit{p}$< 0.05). Fracture surfaces showed that the composite resin failure developed along the matrix resin and the filler/resin interface region, and the cracks propagated in the conical shape from the maximum tensile stress zone.

• Elastomers and Composites
• /
• 제38권3호
• /
• pp.227-234
• /
• 2003

배합고무에 각종 표면처리제로 처리한 수산화 알루미늄을 무게비 100:20, 100:40, 100:60, 100:80 및 100:100으로 배합하여 고압애자용 실리콘 복합체(HVI SC)를 제조하였다. 배합 공정에서 지방산, 아크릴 실란 및 비닐 실란등의 표면처리제로 수산화 알루미늄을 표면처리하였다. 수산화알루미늄의 첨가량 및 표면처리제의 종류에 따른 기계적 특성 및 전기적 특성을 연구하였다. 수산화 알루미늄의 첨가량이 증가하면서 인장강도, 신장율 및 인열강도는 감소하였으며, 비닐 실란으로 표면처리한 수산화 알루미늄을 첨가한 HVI SC의 인장강도 및 탄성율은 지방산 및 아크릴 실란을 사용한 HVI SC 보다 우수하였다. 또한 비닐 실란을 사용한 HVI SC의 체적저항, 절연파괴강도 및 내트래킹 특성이 지방산 및 아크릴 실란을 사용한 HVI SC 보다 우수하였다. 표면처리제의 종류에 따른 실리콘 복합체의 고분자 충전작용은 결합고무 함량으로 검토하였다. 실험의 결과로는 비닐 실란을 표면처리제로 사용한 실리콘 복합체의 결합고무 함량이 다른 표면처리제를 사용한 것 보다 높았다 표면처리제의 종류에 따른 실리콘 복합체의 가교밀도는 Rheometer로 측정하였다 비닐 실란을 표면처리한 수산화 알루미늄을 충진한 실리콘복합체의 최대토크가 다른 표면처리제를 사용한 것들 중에 가장 높았다.

• 한국재료학회지
• /
• 제9권10호
• /
• pp.962-969
• /
• 1999

Ag-Cu-Ti 삽입금속을 이용하여 제조된 AlN/Cu와 AlN/W 활성금속브레이징 접합체의 잔류응력을 유한요소법으로 탄성 및 탄소성 해석을 행하여 그 결과를 접합강도 측정 결과와 파단 거동 관찰 결과와 비교, 분석하였다. 최대 잔류 주응력의 크기는 AlN/W 접합체보다 모재간 열팽창계수 차이가 큰 AlN/Cu 접합체에서 더 크게 나타났으며, 접합계면에 인접한 AlN 세라믹스 자유표면에 인장 성분의 응력집중이 확인되었다. 모재와 삽입금속의 탄소성 변형을 모두 고려할 경우, AlN/Cu 접합체의 경우 연질의 삽입금속에 의해 최대 잔류 주응력이 감소하여 소성변형에 의한 응력완화 효과가 있음을 확인하였으나, 100$\mu\textrm{m}$ 이상으로 삽입금속 두께를 증가시키더라도 잔류 주응력의 크기는 더 이상 크게 감소하지 않았다. 측정된 최대 접합강도는 AlN/Cu와 AlN/W 접합체에서 각각 52 MPa와 108 MPa이었으며, 파단 형태는 AlN/Cu 접합체는 AlN 자유표면으로부터 AlN 내부로 큰 각도를 이루면 진행되는 돔형의 파단이, AlN/W 접합체에서는 접합계면의 삽입금속층을 따라 AlN 측에서 파단이 일어나는 형태를 보였다.