• Corrosion Science and Technology
• /
• 제14권5호
• /
• pp.226-231
• /
• 2015

In spite of highly advanced paint coating techniques, corrosion damage of marine metal and alloys increase more and more due to inherent micro-cracks and porosities in coatings formed during the coating process. Furthermore, flowing seawater conditions promote the breakdown of the protective oxide of the materials introducing more oxygen into marine environments, leading to the acceleration of corrosion. Various corrosion protection methods are available to prevent steel from marine corrosion. Cathodic protection is one of the useful corrosion protection methods by which the potential of the corroded metal is intentionally lowered to an immune state having the advantage of providing additional protection barriers to steel exposed to aqueous corrosion or soil corrosion, in addition to the coating. In the present investigation, the effect of flow velocity was examined for the determination of the optimum corrosion protection current density in cathodic protection as well as the corrosion rate of the steel. It is demonstrated from the result that the material corrosion under dynamic flowing conditions seems more prone to corrosion than under static conditions.

• Corrosion Science and Technology
• /
• 제2권1호
• /
• pp.26-29
• /
• 2003

This study determined that the four corrosive characters of carbon steel in the marine splash zone (MSZ) in China's four sea areas. It has a range and a corrosion peak value. The rust in the MSZ plays the role of "depolarizer" in the cathodic process of corrosion. The growth law of the rust layer in MSZ has a character of "annual ring". In addition the reasons causing serious corrosion of carbon steel in the marine splash zone has been discussed in this paper.

• Journal of Advanced Marine Engineering and Technology
• /
• 제40권10호
• /
• pp.883-887
• /
• 2016

This study aims to evaluate the corrosion behavior of a newly developed high-strength steel in marine environments. Metals used in seawater are easily deteriorated because of the presence of corrosive species such as chloride ions in it. Seawater causes much higher corrosion than fresh water. Thus, the corrosion of steel in marine environment has been recognized as a crucial problem in designing structures which cannot be cathodically protected. In this study, the corrosion resistance of a newly developed high-strength steel was evaluated. Four different specimens were tested to confirm the corrosion resistance. The exposure corrosion test was carried out by exposing the specimens to different marine environments such as atmospheric, tidal, splash, and submerged zones for two years. The specimens taken out from each location were cleaned ultrasonically and chemically prior to the evaluation of their corrosion resistance by the weight loss method. Finally, the pitting depth of the specimens was also measured to evaluate their pitting corrosion. The conditions used for the corrosion test were similar to the environmental conditions. The corrosion test results revealed that the corrosion rate and pitting corrosion of the newly developed high-strength steel was lower than that of the other carbon steels.

• Journal of Advanced Marine Engineering and Technology
• /
• 제23권5호
• /
• pp.695-701
• /
• 1999

Thermal sprayed Ni-Cr alloy coating on the carbon steel was carried out erosion-corrosion test and electrochemical corrosion test in the marine environment. THe erosion-corrosion behavior and electrochemical corrosion characteristics of substrate(SS400) and thermal sprayed Ni-Cr coating was investigated, The erosion-corrosion control efficiency of Ni-Cr coating to substrate was also estimated quantitatively.

• Corrosion Science and Technology
• /
• 제14권5호
• /
• pp.232-238
• /
• 2015

Corrosion is of greatest concern for metallic materials exposed to corrosive seawater or aggressive marine atmospheres. Marine structures and components made of metallic materials incur an initial cost and additional large costs for corrosion control and maintenance. There have been worldwide efforts to minimize marine corrosion and extend service life of the materials. It is believed that various factors are associated with corrosion of marine grade metallic materials, particularly the temperature of the solution affecting the corrosion rate by changing dissolved oxygen solubility and concentrations of chloride. In the present study, the electrochemical characteristics of S355ML steel are investigated to identify corrosion acceleration tendencies with changes in solution temperature under marine environments. It was found that increasing seawater temperature, promoted not only activation of chloride ion transfer, but also the formation of porous $Fe(OH)_3$ or $Fe_2O_3$, leading to the acceleration of corrosion.

• 한국표면공학회지
• /
• 제44권3호
• /
• pp.105-116
• /
• 2011

Ships and offshore structures are exposed to harsh marine environments, and maintenance and repair are becoming increasingly important to the industry and the economy. The major corrosion phenomenons of metals and alloys in marine environment are pitting corrosion, stress corrosion cracking, crevice corrosion, fatigue corrosion, cavitation-erosion and etc. due to the effect of chloride ions and is quite serious. Methods of protection against corrosion can generally be divided into two groups: anodic protection and cathodic protection. Anodic protection is limited to the passivity characteristics of a material in its environment, while cathodic protection can apply methods such as sacrificial anode cathodic protection and impressed current cathodic protection. Sacrificial anode methods using Al and Zn alloys are widely used for marine structures and vessels intended for use in seawater. Impressed current cathodic protection methods are also widely used in marine environments, but tend to generate problems related to hydrogen embrittlement caused by hydrogen gas generation. Therefore, it is important to the proper maintenance and operation of the various corrosion protection systems for ship in the harsh marine environment.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.133-138
• /
• 2002

Microbiologically Influenced Corrosion (MIC) was suspected in a corrosion failure of cooling system of stainless piping welded joint, carrying marine water. Marine water which is used for cooling water in a plant was transferred to the laboratory and used for experiment. In the first experiment, weld metal samples were exposed to the test solution for 56 days (marine water and sterilized marine water (control)). Surface condition of experimental coupons was observed using a Scanning Electron Microscope (SEM). In another experiment, free corrosion potential of these material was monitored for 56 days. Pitting corrosion was found in the coupons exposed to marine water. Free corrosion potential ennoblement was found to be significant compared to control. It was suspected that this corrosion case was MIC. In the second experiment, coupons were exposed to diluted nutrient medium containing single culture of microbes isolated from the MIC causing marine water sample used for the first experiment. After exposure test, surface condition of experimental coupon was observed using SEM. Pitting corrosion was found in coupons exposed to some of the isolates. The results indicate that they contribute to the corrosive effect of the SUS316L welds.

• Journal of Advanced Marine Engineering and Technology
• /
• 제25권6호
• /
• pp.1336-1340
• /
• 2001

Due to increase of air pollution substance, such as $SO_2$,$SO_3$, H2S ,CO, HCI, $Cl_2$ and so on, the operating environment of mechanical equipment and facilities like generating plants, ships, metal structure etc., are acidified and corroded. In these environments, the crevice corrosion of marine facilities frequently occurs at crevice like jointed bolt, gasket or sealant, riveted plates, contact of metal with non-metallic solids etc. Therefore, this paper was studied on the crevice corrosion behavior of mild steel(SS 400) in marine environment. In a variety of NaCl solutions, the aspect of he .crevice corrosion and polarization behavior under the crevice corrosion was investigated. The main results obtained are as follows: 1) Under crevice corrosion, the open circuit potential become less treble as the concentration of NaCl solution increased. 2) The corrosion current density of mild steel was high drained as the concentration of NaCl solution increased by 3.5%, but in the concentration increased over 3.5%, the corrosion current density was low drained. 3) The crevice corrosion is more sensitive to the synergy effect of dissolved oxygen and NaCl.

• 수산해양교육연구
• /
• 제10권1호
• /
• pp.69-78
• /
• 1998

Thermal sprayed Cu-Ni alloy coating on the carbon steel was carried out impingement erosion-corrosion test and electrochemical corrosion test in the marine environment. The impingement erosion-corrosion behavior and electrochemical corrosion characteristics of substrate(SS400) and thermal sprayed Cu-Ni coating was investigated, and the corrosion control efficiency of Cu-Ni coating to substrate was estimated quantitatively. Main results obtained are as follows : 1) The weight loss rate of Cu-Ni coating layer by the impingement erosion-corrosion compared with substrate was smaller in high specific resistance solution than in low specific resistance solution. 2) The corrosion potential of Cu-Ni coating layer spray coating in the marine environment became more noble than that of substrate. 3) With the lapse of time, corrosion current density of Cu-Ni coating layer became stable, but that of substrate was increased. 4) As the corrosion control efficiency of Cu-Ni coating layer in the marine environment was over 90%, its anti-corrosion characteristics was excellent.

• Corrosion Science and Technology
• /
• 제10권3호
• /
• pp.101-107
• /
• 2011

Marine ships have played an important role as a carrier, transporting much more than 80% of all international trading, and marine transportation is an internationally competitive, strategic, and great national important industry. However, those marine ships have the characteristics such as voyage of long distance, large-volume and lower speed than the other carry system. Therefore, it is important to manufacture a larger and faster ship, however, the steel plates which are consisted with most of those ships has brought about many corrosion problems in sea water such as general corrosion, localized corrosion, cavitation and erosion corrosion etc.. Most hulls of the ships have been protected with paintings, sacrificial anode, marine growth prevention system, and impressed current cathodic protection methods against numerious corrosion problems mentioned above. However, these conventional methods are not very effective because the rudder of ships stern are exposed to very severe corrosive environment such as tides, speeds of ships, cavitations and erosion corrosion, etc.. In this study, electrochemical and cavitation characteristics was investigated for the rudder material of ship which is exposed to serious corrosive environment. As a result, it is considered that the optimum cathodic protection potentials of rudder material is the range of -0.6 V ~ -0.8 V(Ag/AgCl) in static seawater.