• Bulletin of the Korean Chemical Society
• /
• v.29 no.4
• /
• pp.758-760
• /
• 2008

Nanoporous AAO (Anodic Aluminum Oxide) membranes have many advantages as a template for variety of magnetic materials. Materials can be embedded into the pores by electrodeposition, sputtering or magnetic-field-assisted infiltration of magnetic nanoparticles. This work focuses on the fabrication of the magnetic structures in the AAO templates by electrodeposition. Our method allows the controlled growth of Co nanostructures within the porous alumina membrane in the form of dots, rods and long wires. The shape of Co nanostructures has been investigated by field emission scanning electron microscope (FESEM). The magnetic hysteresis loops of Co nanostructures were measured using SQUID at 5 K and 300 K. The magnetic properties of the Co nanostructures are proportional to their aspect ratios and can be controlled by changing the aspect ratios.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.17 no.8
• /
• pp.882-887
• /
• 2004

The new magnetic porcelain materials have been studied by mixing magnetic St-ferrite powders with traditional porcelain materials before forming process. For the maintenance of magnetic characteristics after glaze firing process, the Sr-ferrite grains with the size of 1∼2 ${\mu}{\textrm}{m}$ were agglomerated as the isotropic granules with the size of 0.5∼2 mm. The high characteristics of magnetic porcelain materials were achieved at the following conditions; isotropic Sr-ferrite granules of 30 wt%, granule size of 1.4∼2 mm, and glaze firing temperature of $1250^{\circ}C$ in air The magnetic porcelain materials indicated the high magnetic properties, such as the remanent flux density of 240 G, the intrinsic coercivity of 3910 Oe, and the surface flux density of 178 G. The extraction properties of the magnetic tea cups were high compared to that of the traditional tea cups.

• Journal of Magnetics
• /
• v.6 no.2
• /
• pp.73-76
• /
• 2001

A double rectangular spiral type inductor has been fabricated by using FeTaN films. The inductor is composed of internal coils sandwiched by magnetic layers. Characteristics of inductor performance are investigated with an emphasis on planarization of magnetic films. In the absence of the planarization process, the grating topology of the upper magnetic films over the coil arrays degrades the soft magnetic properties and the inductor performance. It also induces a longitudinal magnetic anisotropy with the easy axis aligned to the magnetic flux direction. This alignment prevents the upper magnetic films from contributing to the total induction. Glass bonding is a viable method for achieving a completely planar inductor structure. The planar inductor with glass bonding shows excellent performance: inductance of 1.1 $\mu H$, Q factor of 7 (at 5 MHz), and the current capability up to 100 mA.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.5
• /
• pp.249-255
• /
• 2017

Using a magnetic separation process, pond ash generated in thermoelectric power plants was separated into magnetic materials and nonmagnetic materials in order to make it into a raw material of geopolymers and unburned carbon; screening characteristics according to the particle sizes and magnet strength levels of the pond ash were observed. Based on the results of magnetic separation into fine particle (0.15~0.84 mm) and rough particle (0.84~2.4 mm) pond ash using 3000 G magnets, the weight fraction and ignition loss of nonmagnetic materials were found to be higher than those of magnetic materials, regardless of the particle size. In the case of fine particle pond ash, when the magnet strength was increased from 3000 G to 10000 G, even those materials that were weakly magnetic were separated into magnetic materials, leading to drastic increases in the weight fraction of magnetic materials, such that the ignition loss accounted for 66.9 % (22.8 wt%) of the entire ignition loss of 32.6 wt%, despite of the low ignition loss. Based on the results of measurement of the compressive strength levels of geopolymers made of magnetic-separated rough particle pond ash, the compressive strength of geopolymers made of magnetic materials containing small amounts of unburned carbon was found to be 20 MPa.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2008.12a
• /
• pp.128.1-128.1
• /
• 2008

• Proceedings of the Korean Magnestics Society Conference
• /
• 2008.12a
• /
• pp.234.1-234.1
• /
• 2008

• Proceedings of the Korean Magnestics Society Conference
• /
• 2005.06a
• /
• pp.26-26
• /
• 2005

• Journal of Powder Materials
• /
• v.28 no.3
• /
• pp.233-238
• /
• 2021

Iron-based amorphous powder attracts increasing attention because of its excellent soft magnetic properties and low iron loss at high frequencies. The development of an insulating layer on the surface of the amorphous soft magnetic powder is important for minimizing the eddy current loss and enhancing the energy efficiency of high-frequency devices by further increasing the electrical resistivity of the cores. In this study, a hybrid insulating coating layer is investigated to compensate for the limitations of monolithic organic or inorganic coating layers. Fe₂O₃ nanoparticles are added to the flexible silicon-based epoxy layer to prevent magnetic dilution; in addition TiO₂ nanoparticles are added to enhance the mechanical durability of the coating layer. In the hybrid coating layer with optimal composition, the decrease in magnetic permeability and saturation magnetization is suppressed.

• Proceedings of the Korean Magnestics Society Conference
• /
• 2008.12a
• /
• pp.146.1-146.1
• /
• 2008

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.04a
• /
• pp.83-87
• /
• 2002

In order to improve the capability of magnetic circuit, magnetic materials are used for all kinds of electromagnetic energy-conversion devices. This paper presents the analysis method considering magnetic properties of the magnetic material and analyzes that the effects of magnetic materials. In addition, it is described that the requirements of magnetic materials for the improvement of electric machines. Several application examples using a metal powder in electromagnetic energy conversion devices is introduced.