• Journal of Welding and Joining
• /
• v.29 no.1
• /
• pp.59-64
• /
• 2011

Al6082-T6 is widely used because of its corrosion resistance and excellent strength. HAZ softening occurs in MIG welding process for this aluminium alloys because this aluminium alloy is heated to higher temperature than its aging temperature during welding. Therefore, low heat input and minimum standard deviation of heat input are required for narrow HAZ width and, for higher strength of welds. In this study, Al6082-T6 was used to examine for HAZ softening with various heat input in aluminium MIG welding. For weldments, micro hardness was measured and tensile test was carried out. Minimum hardness was increased at high speed welding such as 80cm/min and 120cm/min in welding speed comparing with 40cm/min. Also, in case of high speed welding such as 80cm/min and 120cm/min, tensile strength of weldments was increased about 10% comparing with low speed welding(40cm/min).

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.15 no.1
• /
• pp.110-115
• /
• 2016

The need for high-strength galvanized steel has recently increased because of the increased number of car consumers who want improved efficiency and exterior quality. High-strength galvanized steel with high corrosion resistance improves the durability of products and exterior quality. Furthermore, the gilt of zinc does not come off during machining because of the fine adhesive property of zinc. When these are welded, zinc has a lower melting temperature than iron, so zinc is more quickly vaporized than iron. Vaporized zinc can stick to electrodes, which increases spatter in welding transportation. Created spatter can enter the molten pool and develop into inner defects or blowholes and pits. Scattered spatter sticks to the product, which leads to the secondary cost of spatter removal. Therefore, in this study, comparisons of amounts of spatter generated are conducted according to the composition of shielding gas in the MIG and CMT processes to find optimal welding parameters.

• Journal of Welding and Joining
• /
• v.14 no.4
• /
• pp.53-61
• /
• 1996

It was attempted to improve the wear resistance of Al alloy under the load condition by making a formation of the thicker surface hardening alloy layers. The thicker surface hardening alloy layers were formed on 6061 Al alloys overlayed by MIG and TIG welding process with Cu powders feeding. The characteristics of hardening and wear resistance have been investigated in relation to the microstructures of alloyed layers, with a selection of optimum alloying conditions for formation of overlaying layer. The results obtained were summarized as follows With increasing feeding rate of Cu powders by MIG welding, the hardness and specific wear of the overlay weld alloys were increased. It is considered that these high hardness and specific wear of overlay weld alloys were due to the formation of Θ($Al_2Cu$) phases. With increasing feeding rate of Cu powders by TIG welding, the hardness and specific wear of the overlay weld alloys were increased in feeding rates 12 and 18g/min. However, the hardness and specific wear were decreased in the powder feeding rate 38g/min. It is considered that considered that decrease of hardness and specific wear in the powder feeding rate 38g/min due to formation of ${\gamma}$($Al_4Cu_9$) phases.

• Journal of Power System Engineering
• /
• v.14 no.3
• /
• pp.58-63
• /
• 2010

A laser beam welding and an electric arc welding were combined, and the positive points of each welding method are drawn such as high speed, low thermal load, deep penetration, and high productivity. The fiber laser-MIG conjugated welding. namely the hybrid welding has been studied mainly for the automation industry of a pipeline welding. In this study, the MIG welding was combined with a fiber laser welding to make up the hybrid welding. The weld shapes, microstructures and mechanical properties for weld zones after the hybrid welding or only fiber laser welding were investigated on the 700 MPa grade Ultra Fine Grained(UFG) high strength steel. The amount of acicular ferrite in weld metals and HAZ(heat affected zone) was observed larger after hybrid welding compared with after only laser welding. The Vickers hardness of the top area of the fusion zone after fiber laser welding was higher compared with after hybrid welding.

• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.59-64
• /
• 2002

Effects of the aging treatments on the microstructure and strength of heat affected zone(HAZ) in the welds of a age-hardened Al-Mg-Si alloy, 5N01-T5, were investigated. The base metal aging treatments before MIG welding were conducted at 423K to 473K for 28.8ks Post weld heat treatment(PWHT) to recover the HAZ strength was performed at 448K for 28.8ks. Microstructure observations, hardness measurements and tensile tests were conducted to study properties of the MIG weld joints. The position of the softest region in HAZ where the hardness insufficiently recovered after natural aging and PWHT was at a distance of approximately 15mm from the center of the fusion zone. Hardness of the softest regions after natural aging and PWHT decreased with increase in the base metal aging temperature. TEM observation clarified that strengthening ${\beta}$"(Mg$_2$Si) precipitates and coarse ${\beta}$′ precipitates affected the hardnes of HAZ. Incomplete recover of hardness in HAZ after PWHT was caused by the precipitating of non-hardening ${\beta}$′ phase during the weld thermal cycle. In order to examine the effects of weldheat input and welding speed, the laser weld joints were also investigated and compared with the MIG weld ones. Laser welding had the narrower width of the softened regions in HAZ compared with MIG welding. The hardness of the softest regions of the laser welds after PWHT was higher than that of the MIG welds. Quantitative relations between hardness of the softest region and base metal aging temperature were obtained for both welding processes. Accordingly, the equations to estimate the strength of the weld joints after PWHT with varying base metal temperatures were proposed for MIG welding and laser welding.

• Journal of Advanced Marine Engineering and Technology
• /
• v.15 no.4
• /
• pp.22-28
• /
• 1991

The crevice corrosion behavior on austenitic AISI 304 and 316L stainless steel welded by TIG, MIG, $CO_2$ and SMA was studied. The results are as follows : In 10% $FeCl_3$ solution and natural sea water sampled near Mokpo port, the base metal of 304 stainless steel showed small amount corrosion, whereas 316L stainless steel did not showed any corrosion in the test periods. The weight loss caused by crevice corrosion increased with increasing weld heat input and residual .delta. ferrite formed in welded part. The corrosion resistance of the welded part was in the order of TIG, MIG, $CO_2$ and SMA. From this tendency, it is proved that the smaller heat input gives the better corrosion resistance.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2001.11a
• /
• pp.88-91
• /
• 2001

New type of vehicles made from thin aluminum alloy are under rapid development and some product are already on the market, but when welding sheet metal joint of aluminum alloy, the main problem are burn-through by the high heat input. The purpose of this study, it is to prevent the burn-through and to shallow penetration that AC pulse welding has diminish the penetration and to lower the droplet temperature at Al sheet metal welding. In this study, we observed the bead appearance and whether it was appeared burn through or not , as the variation of the root gap in the lap and butt-joint welding process.

• Proceedings of the KIPE Conference
• /
• 2002.07a
• /
• pp.665-668
• /
• 2002

Joining thin aluminum alloy is difficult using most wilding techniques. Many of problems associated burn-through by the high heat input Common welding techniques are TIG, MIG, and MIG-PULSE welding. The VP-GMAW provides more control of the heat balance in the voiding arc by taking advantage of the different arc characteristics obtained with each of the two polarities. In this paper, we proposed new VP_GMA Welding method by control DSP 320C32, and the characteristic and experiment result-voltage, current, welding bead. penentraion by this method are presented

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.18 no.11
• /
• pp.124-129
• /
• 2017

In this study, we report characteristics of friction stir welding (FSW) technique applied to Al-6005-T6 extruded sheets, which is a common material for railway car bodies. With the welding speed fixed at 300 mm/min, the revolution per minute (RPM) of the rotating tool was varied from 600 to 1800 RPM, with the aim at evaluating the resultant microstructure and mechanical behaviors. Comparison is also made with the conventional Metal Inert Gas (MIG) welding technique. Unlike MIG, no micro-voids were observed for FSW specimens. Hardness measurement revealed that the increased heat input by increasing RPM results in widened heat affected zone (HAZ) and decreased hardness for HAZ due to grain coarsening. Hardness results for the nugget do no show difference. During tensile tests, specimens fractured at HAZ, and increasing rpm led to decrease of the yield stress and tensile stress for the selected RPM range, which is considered to be due to the grain coarsening for HAZ.

• Proceedings of the Korean Society of Marine Engineers Conference
• /
• 2011.06a
• /
• pp.75-75
• /
• 2011