• Applied Chemistry for Engineering
• /
• v.27 no.1
• /
• pp.74-79
• /
• 2016

The effects of scale formation of hardness material caused by electrode reactions on the desalination performance of the membrane capacitive deionization (MCDI) were investigated. During the repeated adsorption and desorption process for the influent containing $Ca^{2+}$ ion, changes in effluent concentration and cell potential with respect to the number of adsorption were analyzed. It was found that $OH^-$ generation at the cathode was initiated at about 0.8 V or more of cell potential. In addition, the scale of $Ca(OH)_2$ was formed on the surface of cathode carbon electrode by combining adsorbed $Ca^{2+}$ ions and $OH^-$ ions generated from electrode reaction. As the scale was forming, the electrical resistance of carbon electrode was increasing, which resulted in the decrease of the adsorption amount. In the case of the operation at 1.5 V cell potential, the adsorption was reduced to 58% of the initial adsorption amount due to the scale formation.

• Membrane Journal
• /
• v.27 no.3
• /
• pp.240-247
• /
• 2017

In this study, the heterogeneous ion exchange membranes prepared by the combination of the carbon electrode and mixed the cation and anion exchange polymers and polyvinylidene fluoride as the basic polymer together were made to recognize the efficiency of the salt removal for the application of the membrane capacitive deionization process. The mixing weight ratio of the solvent, basic polymer and ion exchange resin was 7 : 2 : 1 and this mixed solution was directly cast on the electrode. As for the operating conditions of the adsorption voltage and time, feed flow rate, desorption voltage and time of the feed solution NaCl 100 mg/L, the salt removal efficiencies (SRE) were measured. Apart from this NaCl, the $CaCl_2$ and $MgSO_4$ solutions were investigated in terms of SRE as well. Typically, SRE for NaCl 100 mg/L solution under the conditions of adsorption voltage/time, 1.5 V/3 min, desorption voltage/time -0.1 V/3 min, was shown 98%. And for the $CaCl_2$ and $MgSO_4$ solutions, the SREs of 70 and 59% were measured under the conditions of adsorption voltage/time, 1.2 V/3 min, desorption voltage/time -0.5 V/5 min, respectively.

• Membrane Journal
• /
• v.27 no.1
• /
• pp.84-91
• /
• 2017

In this study, heterogeneous ion exchange membranes were prepared by mixing cation or anion exchange resins and commercial polyvinylidene fluoride (PVDF) for MCDI process. The mixing ratios of PVDF and ion exchange resins were 1 : 1, 1.4 : 1, 2 : 1, and 3 : 1. We characterized SEM, water content, ion exchange capacity, methanol permeability, and ion conductivity. In the viewpoint of membrane characterization, the blending ratio of 2 : 1 showed the best. For the blending ratio of 2 : 1, heterogeneous cation exchange membrane showed the water content 34%, ion exchange capacity 1.54 meq/g, ion conductivity 0.019 S/cm, and methanol permeability $2.28{\times}10^{-7}{\sim}8.86{\times}10^{-7}cm^2/s$ while In the case of heterogeneous anion exchange membrane, the result showed 37%, 2.18 meq/g, and 0.034 S/cm and $1.46{\times}10^{-7}{\sim}8.66{\times}10^{-7}cm^2/s$.

• Korean Chemical Engineering Research
• /
• v.56 no.3
• /
• pp.361-369
• /
• 2018

A manufacturing method has been devised to prepare novel heterogeneous cation exchange membranes by mixing ethylene vinyl acetate (EVA) copolymers with a commercial cation exchange resin. Optimum material characteristics, mixture ratios and manufacturing conditions have been worked out for achieving favorable membrane performance. Ion exchange capacity, electrical resistance, water uptake, swelling ratio and tensile strength properties were measured. SEM analysis was used to monitor morphology. Effects of vinyl acetate (VA) content, melt index (MI) and ion exchange resin content on properties of heterogeneous cation exchange membranes have been discussed. An application test was carried out by mounting a selected membrane in a membrane capacitive deionization (MCDI) system to investigate its desalination capability. 0.92 meq/g of ion exchange capacity, $8.7{\Omega}.cm^2$ of electrical resistance, $40kgf/cm^2$ of tensile strength, 19% of swelling ratio, 42% of water uptake, and 56.4% salt removal rate were achieved at best. VA content plays a leading role on the extent of physical properties and performance; however, MI is important for having uniform distribution of resin grains and achieving better ionic conductivity. Overall, manufacturing cost has been suppressed to 5-10% of that of homogeneous ion exchange membranes.