• 한국항해학회지
• /
• 제22권3호
• /
• pp.65-72
• /
• 1998

최근에는 고장력강의 사용증대와 함께 구조부재가 경량화추세에 있으며 이상부식이 발생한 구조부재는 강도가 크게 저하되리라 예상되지만 지금까지 이에 관한 연구가 거의 없는 상태이다. 본 연구에서는 단소성대변형유한요소법을 적용하여 국부이상부식을 가진 판이 면내압축하중을 받을 경우에 압축최종강도에 미치는 부식부영역의 크기. 부식부의 판두께 감소량 및 세장비의 영향에 대하여 연구하였다.

• 한국해양공학회:학술대회논문집
• /
• 한국해양공학회 2006년 창립20주년기념 정기학술대회 및 국제워크샵
• /
• pp.230-232
• /
• 2006

Failure behaviors of thin cylinder with corrosion are very important for the integrity of boiler and pressure vessel system. In this study, FEM with internal pressure are conducted on 1000 mm diameter (length 3000 mm and thickness, 5.9 mm) SS400 carbon steel. Failure behaviors of locally wall thinned cylinders were calculated by elasto-plastic analysis using finite element method. The elasto-plastic analysis was performed by FE code ANSYS. We simulated various types of local wall thinning that can be occurred at cylinder surface due to corrosion. Locally wall thinned shapes were machined to be different in size along the circumferential or axial direction of straight cylinder. In case of local wall thinned length 30 mm, internal pressure, when the crack initiation and the plastic collapse occur, didn't decrease dramatically even though local wall thinned depth was deep. In 400 mm, the more local wall thinned depth is deep, the more internal pressure decreased dramatically. In degraded materials, crack is easily initiation but plastic collapse was difficult.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 추계학술대회
• /
• pp.7-12
• /
• 2004

A lifetime prediction of holddown spring screw in nuclear fuel assembly was performed using fracture mechanics approach. The spring screw was designed such that it was capable of sustaining the loads imposed by the initial tensile preload and operational loads. In order to investigate the cause of failure and to predict the stress corrosion cracking life of the screw, a stress analysis of the top nozzle spring assembly was done using finite element analysis. The elastic-plastic finite element analysis showed that the local stresses at the critical regions of head-shank fillet and thread root significantly exceeded than the yield strength of the screw material, resulting in local plastic deformation. Normalized stress intensity factors for PWSCC life prediction was proposed. Primary water stress corrosion cracking life of the Inconel 600 screw was predicted by using integration of the Scott model and resulted in 1.78 years, which was fairly close to the actual service life of the holddown spring screw.

• 한국강구조학회 논문집
• /
• 제20권2호
• /
• pp.313-321
• /
• 2008

최근 일본에서 하로식 트러스교의 콘크리트 상판을 관통하는 사재가 콘크리트 상판의 상부 또는 하부에서 심한 부식손상 에 의해 파단 된 사례가 보고되었다. 이는 도장막의 노화에 따른 콘크리트와의 경계부에 있어 사재의 국부부식에 기인한 것으로 추정되고 있다. 그러므로 이와 같이 콘크리트와 강재의 경계부에 있어서의 국부 부식손상 대책수립 및 이를 기점으로 발생될 수 있는 피로손상에 대한 검토가 필요하다. 본 실험에서는 인장시험편에 부분적으로 콘크리트 블록을 설치한 콘크리트-강재의 모델시험체에 대한 부식환경촉진실험을 실시하여, 경계부의 부식감소량을 측정하였으며, 부식실험 후의 모델시험체를 이용한 피로실험을 실시하였다. 부식촉진실험의 조건으로는 실제대기환경에의 적용성이 검토된 S6사이클(JIS K5621)을 사용하였으며, 부식촉진실험기간은 150일, 300일, 450일, 600일로 각 5개의 모델시험체를 사용하였다. 부식촉진실험결과를 근거로 실험기간에 따른 최대 및 평균 부식깊이를 정량화하였으며, 부식실험 후의 부식 손상된 모델시험체의 피로실험결과를 근거로 실험기간의 증가에 따른 피로강도 감소량을 명확히 하였다.

• Nuclear Engineering and Technology
• /
• 제56권8호
• /
• pp.3067-3075
• /
• 2024

Static corrosion tests in LBE under oxygen-saturated and -depleted conditions at 500 ℃ for 1000 h were conducted to investigate the corrosion-induced diffusion layers on T91 and SS316L steels subject to dissolution and oxidation corrosion. Following nano-indentation experiments examined the variations of local mechanical properties within the corrosion layers. Under the present conditions, T91 steel showed better resistance to dissolution corrosion while higher susceptibility to oxidation corrosion against SS316L. For both steels, nano-indentation results showed a gradual decrease in mechanical properties from steel matrix to the corrosion side after dissolution corrosion. When subject to oxidation corrosion, the oxide scale formed on T91 steel showed lower Er-modulus and enhanced hardness in comparison with those of the steel matrix. An obvious decrease in both modulus and hardness was found at the interface between steel matrix and oxide scale.

• 한국해양공학회지
• /
• 제20권4호
• /
• pp.17-23
• /
• 2006

Monotonic four-point bending tests were conducted on straight pipe specimens, 102 mm in diameter with local wall thinning, in order to investigate the effects of the depth, shape, and location of wall thinning on the deformation and failure behavior of pipes. The local wall thinning simulated natural erosion/corrosion metal loss. The deformation and fracture behavior of the straight pipes with local wall thinning was compared with that of non wall-thinning pipes. The failure modes were classifiedas local buckling, ovalization, or crack initiation, depending on the depth, shape, and location of the local wall thinning. Three-dimensional elasto-plastic analyses were carried out using the finite element method. The deformation and failure behavior, simulated by finite element analyses, coincided with the experimental results.

• Corrosion Science and Technology
• /
• 제16권3호
• /
• pp.151-159
• /
• 2017

The MA8 alloy (formula Mg-Mn-Се) has been shown to have greater corrosion stability than the VMD10 magnesium alloy (formula Mg-Zn-Zr-Y) in chloride-containing solutions by Scanning Vibrating Electrode Technique (SVET) and by optical microscopy, gravimetry, and volumetry. It has been established that the crucial factor for the corrosion activity of these samples is the occurrence of microgalvanic coupling at the sample surface. The peculiarities of the kinetics and mechanism of the corrosion in the local heterogeneous regions of the magnesium alloy surface were investigated by localized electrochemical techniques. The stages of the corrosion process in artificial defects in the coating obtained by plasma electrolytic oxidation (PEO) at the surface of the MA8 magnesium alloy were also studied. The analysis of the experimental data enabled us to determine that the corrosion process in the defect zone develops predominantly at the magnesium/coating interface. Based on the measurements of the corrosion rate of the samples with PEO and composite polymer-containing coatings, the best anticorrosion properties were displayed by the composite polymer-containing coatings.

• International Journal of Precision Engineering and Manufacturing
• /
• 제1권2호
• /
• pp.48-54
• /
• 2000

This paper presents the effect of shape of external corrosion in pipeline on failure prediction by using a numerical simulation. The numerical study for the pipeline failure analysis is based on the FEM(Finite Element Method)with an elastic-plstic and large-deformation analysis. Corrosion pits and narrow corrosion grooves in pressurized pipeline were analysed. A failure criterion, based on the local stress state at the corrosion and a plastic collapse failure mechanism, is proposed. The predicted failure stress assessed for the simulated corrosion defects having different corroded shapes along the pipeline axis compared with those by methods specified in ANSI/ASME B31G code and a modified B31G code. It is concluded the corrosion geometry significantly affects the failure behavior of corroded pipeline and categorisation of pipeline corrosion should be considered in the development of new guidance for integrity assessment.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2015년도 춘계학술대회 논문집
• /
• pp.179-180
• /
• 2015

pure Mg and some Mg alloys are relatively rapidly corroded after operation, resulting in the decrease of mechanical strength and change of local ion concentration. In this study, the corrosion mechanism of biodegradable implant materials was investigated by corrosion tests of the Mg alloy in Hank's solution. Particularly, the crystal structures and chemical bonding state of corrosion reactants was systematically examined.

• 설비공학논문집
• /
• 제23권7호
• /
• pp.483-491
• /
• 2011

When pipe components made of carbon steel in nuclear, fossil, and industry are exposed to flowing fluid, wall thinning caused by FAC(flow accelerated corrosion) can be generated and eventually ruptured at the portion of pressure boundary. A study to identify the locations generating local wall thinning and to disclose turbulence coefficient related to the local wall thinning was performed. Experiment and numerical analyses for tee of down scaled piping components were performed and the results were compared. In particular, flow visualization experiment which was used alkali metallic salt was performed to find actual location of local wall thinning inside tee components. To disclose the relationship between turbulence coefficients and local wall thinning, numerical analyses were performed for tee components. The turbulence coefficients based on the numerical analyses were compared with the local wall thinning based on the measured data. From the comparison of the results, the vertical flow velocity component(Vr) flowing to the wall after separating in the wall due to the geometrical configuration and colliding with the wall directly at an angle of some degree was analogous to the configuration of local wall thinning.