Glass-ceramics based on lithium disilicate($Li_2Si_2O_5$) are prepared by heat-treatment of glasses in a system of $SiO_2-Li_2O-K_2O-Al_2O_3$ with different compositions. The crystallization heat-treatment was conducted at the temperature range of $700{\sim}900^{\circ}C$ and samples were analyzed by XRD and SEM. Mechanical properties were determined by a Vicker's hardness and 4 point bending strength. When $SiO_2/Li_2O$ ratio increased, cristobalite and tridymite crystals showed more predominate than lithium disilicate crystals. Increase in $Al_2O_3$ contents in the glass suppressed crystallzation of lithium disilicate crystals. Increase in ZnO, $B_2O_3$ contents in the glass decreased crystallization temperature of lithium disilicate crystals, and increased mechanical properties because of the reduction of the lithium disilicate crystal size.

• 한국세라믹학회지
• /
• 제18권3호
• /
• pp.163-170
• /
• 1981

The crystallization of $Li_2O-SiO_2$ system glasses and the effect of phase separtion to crystal nucleation were studied. The crystallization temperatures of various glasses were determined by DTA and glasses were nucleation heat treated at the temperatures ranging from 45$0^{\circ}C$ to 5$25^{\circ}C$. These glasses were thengown at $700^{\circ}C$ to observable size in the optical microscope. Crystal nucleation rates of various glasses were obtained by estimating the number of crystals per unit volume. The main crystal phase of these glasses identified by X-ray diffraction was lithium disilicate ($Li_2O$.$2SiO_2$). It was found that the crystal nucleation rate of glass (19.5% $Li_2P$-80.5% $SiO_2$), the nearest composition to lithium disilicate, was higher than other glasses. The opalescence caused by phase separation was observed in the nucleation heat treated glass (16.3% $Li_2O$-83.7% $SiO_2$). The result from nucleation density measurement of this glass indicated that the nucleation was enhanced during early stage of phase separation. The molphologies of crystals in glasses and crystal growth rate at $600^{\circ}C$ were also discussed.

• 구강회복응용과학지
• /
• 제38권2호
• /
• pp.71-80
• /
• 2022

다양한 치과용 도재가 개발되고 있으나 현재 단일구조 보철물로 사용할 수 있는 수준의 기계적, 광학적 성질을 보이는 도재는 반투명 지르코니아와 리튬디실리케이트 결정화유리가 대표적이다. 기계적 성질의 경우 지르코니아가, 광학적 성질은 리튬디실리케이트가 상대적으로 더 우수하다고 알려져 있으나 물성개선을 통해 보다 다양한 증례에 보철물을 적용할 수 있게 되었다. 그 결과 반투명 지르코니아와 리튬디실리케이트 보철물의 적응증이 서로 중복되는 경우가 발생하고 있다. 그러나 두 도재는 유리질(glass matrix) 포함여부뿐만 아니라 강화기전, 탄성계수 등이 서로다르다. 이에 본 문헌고찰에서는 두 단일구조 치과용 도재의 물성을 평가한 다양한 연구결과들을 살펴보고 특히 가공치가 포함된 고정성 보철물의 디자인 시 고려사항에 대해 알아보고자 한다.

• 한국세라믹학회지
• /
• 제41권2호
• /
• pp.143-150
• /
• 2004

본 연구에서는 치아 수복에 사용되는 상용 글라스 세라믹들을 디스크 모양으로 열가압 성형하여 ball-on-3-bal에 의한 이축강도와 압입시험에 의한 파괴인성을 측정하였다. 시편들로부터 XRD, SEM, TEM을 이용하여 결정상과 미세구조를 분석하였다. 글라스 세라믹내의 결정들은 균열의 진행에 대하여 효과적인 저지를 하지 못하였으나 높은 결정화도가 기계적 성질의 향상에 기여하는 것으로 판단된다. Lithium disilicate결정의 글라스 세라믹은 상대적으로 결정함량이 낮은 leucite 세라믹에 비하여 유의하게 높은 이축강도와 파괴인성을 나타내어 치과용 글라스 세라믹으로서 높은 신뢰성이 기대된다.

• 한국세라믹학회지
• /
• 제24권3호
• /
• pp.227-234
• /
• 1987

With the content of ZnO varing from 10.5 to 47.4 wt%, the crystallization of lithium zinc silicate glass was investigated by DTA, XRD, and SEM. In this work P2O5 was used as nucleation agent. The crystallization temperature was found to increase with the content of ZnO and the microstructure of formed crystalling phases was studied through the scanning electron microscopy. According to the XRD analysis, the crystal phases formed are summarized as follows. 1) The major phases are lithium orthosilicate, lithium disilicate and quartz at 10.5 wt% ZnO. 2) Lithium zinc silicate polymorphous and cristobalite occur in the composition varying 21.3 to 30.8 wt% ZnO. 3) At composition containing 47.4wt% ZnO some quantity of willemite is formed.

• The Korean Journal of Ceramics
• /
• 제5권4호
• /
• pp.363-367
• /
• 1999

New glass ceramics were investigated for the application as substrates to be used in hard disk devices. The glass system to precipitate lithium di-silicate was studied so as to optimize the composition to realize very high surface flatness. The addition of small amount of several metal oxides with high valences had very drastic effects on the microstructure, because they played a role of crystallization agents, and consequently it determined surface flatness even after the polishing process. The possible mechanism changes of crystal growth due to the addition of metal oxides were discussed in relation to the final micro-texture development. The glass ceramics with very high surface flatness(Ra=7.1 $\AA$) was obtained by the addition of the mixture of $P-2O_5 \;and \;MoO_3$ as crystallization agents.

• 대한치과보철학회지
• /
• 제39권2호
• /
• pp.184-196
• /
• 2001

The objective of this study was to investigate the influence of resin cements and ceramic etching on shear bond strength of Empress 2 ceramic and observe the change of microstructure of ceramic according to etching time. Sixty-six square ceramic specimens($6{\times}6{\times}1.5mm$) were prepared. 6 specimens were etched with different etching times(0, 10, 20, 30, 40 and 60 seconds) and observed by means of a scanning electron microscope(SEM). Other sixty specimens were divided into 6 groups with 10 specimens in each group. 3 groups were etched with 4% hydrofluoric acid and each groups was bonded with 3 resin cements(Variolink II, Super-Bond C&B, Panavia F). Each specimen was subjected to a shear load in an Instron at a cross-head speed of 0.5mm/min and was observed with SEM after mechanical testing to establish modes of failure. The results were as follows : 1. Within etched groups, Variolink II and Super-Bond C&B exhibited significantly greater bonding strengths than Panavia F(p<0.05) 2. Bond strength of etching groups had three to five times greater than that of no-etching groups. 3. All of no-etching groups showed adhesive failure and etching groups mostly showed mixed failure. And, 20-second etching specimen showed the most distinct lithium disilicate crystal. so it is considered that 20-second etching is optimal time for bonding.

• 대한치과의사협회지
• /
• 제58권7호
• /
• pp.435-442
• /
• 2020

치과의사가 수복재료를 선택하고 환자에게 추천할 때는 수복할 치아 위치, 결손 정도, 환자의 심미적 요구도, 저작력, 나이, 경제적 여건 등 여러 가지의 요인을 고려한다. 그렇지만, 수복재료를 선택할 때의 일차적인 기준은 구강 내에서 기능 시 작용하는 교합력을 최우선으로 고려해야 한다. 미국 국립보건원(NIH) 지원으로 조사된 연구 결과에 의하면, 전치부 수복재료로서는 리튬 디실리케이트계 글라스-세라믹이 54%, layered zirconia가 17%, 루사이트 강화 글라스-세라믹이 13% 순을 보여, 전치부 수복재료로서 리튬 디실리케이트계 글라스-세라믹이 가장 많이 사용었다. 또한 구치부 수복재료로서는 단일구조 지르코니아가 32%, 금속-세라믹이 31%, 리튬 디실리케이트계 글라스-세라믹이 21% 순을 나타냈다. 세라믹 수복 재료의 특성을 살펴보면, 단일구조 지르코니아는 강도는 높지만 명도가 높고 저온열화로 인한 강도 저하가 일어날 수 있다. layered zirconia는 심미성은 우수하지만 강도가 낮은 비니어 세라믹의 칩핑과 박리가 문제가 되고 있다. 리튬 디실리케이트계 글라스-세라믹은 심미성은 우수하지만 지르코니아에 비해 강도가 낮으므로 구치부에 적용 시 파절이 일어날 위험성이 있다. 루사이트계 글라스-세라믹은 심미성은 우수하지만 기본적으로 강도가 낮기 때문에 전치부에 한정하여 적용한다. 세라믹 크라운이 구치부 교합력에 저항하기 위해서는 350 MPa 이상의 굴곡강도를 가져야 한다. 리튬 디실리케이트계 글라스-세라믹은 광투과성이 양호한 심미성이 있는 재료이므로 비니어 없이 전치부에 적용할 수 있고, 굴곡강도가 400 MPa 이상이므로 구치부 교합력에 저항할 수 있고, HF에 의한 산부식과 실란(silane) 처리가 가능하므로 레진과 강한 결합력을 얻을 수 있고, 또한 포세린에 비해 대합치의 마모가 적다. 이러한 점들을 고려하면 리튬 디실리케이트계 글라스-세라믹 재료는 전구치부의 단일치 수복에 적합한 성질을 갖고 있음을 알수 있다. 그렇지만 그의 임상 응용이 더욱 증가하기 위해서는 이들 재료에 대한 보다 많은 연구와 이해가 필요하리라고 생각된다.