• Korea-Australia Rheology Journal
• /
• v.19 no.1
• /
• pp.17-25
• /
• 2007

In liquid composite molding (LCM), composites are produced by impregnation of a dry preform with liquid resin. The resin flow through the preform is usually described by Darcy's law and the permeability tensor must be obtained for filling analysis. While the resin flow in the thickness direction can be neglected for thin parts, the resin flow in the transverse direction is important for thicker parts. However, the transverse permeability of the preform has not been investigated frequently. In this study, the transverse permeability was measured experimentally for five different fiber preforms. In order to verify the experimental results, the measured transverse permeability was compared with numerical results. Five different fiber mats were used in this study: glass fiber woven fabric, aramid fiber woven fabric, glass fiber random mat, glass fiber braided preform, and glass/aramid hybrid braided preform. The anisotropic braided preforms were manufactured by using a three dimensional braiding machine. The pressure was measured at the inlet and outlet positions with pressure transducers.

• Elastomers and Composites
• /
• v.55 no.4
• /
• pp.289-299
• /
• 2020

Highly aromatic (HA) oils are common processing aids used in tire tread compounds. However, they often bleed and evaporate from the vulcanizates during tire use. Thus, the mechanical and dynamical properties of the tire decrease. To overcome this problem, we investigated nonfunctionalized liquid butadiene rubber (LBR-305, Kuraray) and center-functionalized liquid butadiene rubber (C-LqBR), polymerized by anionic polymerization. In addition to the liquid butadiene rubbers, p-tert-octylphenol (P-Resin) and C5 hydrocarbon (H-Resin) tackifier resins, which can induce entanglement of rubber compounds, were researched as a processing aid to solve the bleeding problem. Liquid butadiene rubbers have significantly reduced extraction loss by crosslinking with the main rubber chain. They have also increased the abrasion resistance and showed similar or better mechanical and dynamical properties against HA oils. However, resin compounds did not show differences in extraction loss compared to HA oil compounds; instead, they showed increased wet traction.

• Journal of the Korea Furniture Society
• /
• v.21 no.2
• /
• pp.126-132
• /
• 2010

High wear resistances are obtained with an additional coating of the surface of the decor film in the same operation of impregnating with low viscosity melamine resin by liquid overlay system. The cellulosic fibers have a good adhesion to the corundum particles and keep them sufficiently homogeneous in the blend with the resin. The amount of these fibers in nearly as big as it is in a common overlay in relation to the resin. Therefore these fibers keep the resin inside during the press process and consequently very the surface of the decor print of the film. That means that the corundum particles are equally dissipated throughout the entire layer over the decor. The change of the color of the print is nearly not visible as the particles are almost equally dissipated. Looking to the flooring purposes of liquid overlay one can see that by the lesser exposure of the corundum particles on the very surface, there is no longer an abrasive surface but a feeling like a normal melamine surface.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.05a
• /
• pp.371-376
• /
• 2001

The purpose of this study is to investigate toughening of unsaturated polyester resin by addition of polyuretane liquid rubber. In general, unsaturated polyester resin has strong brittleness in spite of its high strength Therefore; it is difficult to use unsaturated polyester mortar for the place where impact resistance is demanded. In this study, it was evaluated strength and Gf by using to polyurethane liquid rubber. As a result, the toughness of unsaturated polyester mortar was increased by polyuretane liquid rubber.

• Journal of agriculture & life science
• /
• v.46 no.2
• /
• pp.43-48
• /
• 2012

This study was investigated on the properties of board made from Miscanthus sinensis var. purpurascens particles differed in density of board and mixed ratio of powder type- and liquid type-phenolic resin. As the board density increase, thickness swelling and bending strength increased while water absorption decreased. With increasing the resin content, water absorption and thickness swelling decreased while MOR and internal bond strength increased. The board made of liquid type phenol-formaldehyde resin was low in water absorption and thickness swelling, and there were similar bending strengths between power type- and liquid type-phenol resin in resin cont of 11% and 13% at the board density $0.4g/cm^3$ and internal bond strength was higher with liquid type-phenolic resin in its bending strength.

• Applied Chemistry for Engineering
• /
• v.18 no.5
• /
• pp.527-530
• /
• 2007

The binary liquid type fire retardant paint of polyurethane (alkyd resin) lacquer is developed to cover the defect of one liquid type white paint of chlorinated rubber used generally but which has weak surface and poor adhesive strength to the wood as well as generating much black smoke when it is firing. The properties of the composition of binary liquid type of white paint of polyurethane lacquer developed in this study for using to wood has shown that the better suppressed smoke generation and enhanced the adhesive strength to the wood than that of fire retardant white paint used.

• Journal of the Semiconductor & Display Technology
• /
• v.9 no.2
• /
• pp.33-39
• /
• 2010

The moisture absorption properties such as diffusion coefficient and moisture content ratio of liquid type epoxy resin systems with the filler were investigated. Bisphenol A type and Bisphenol F type epoxy resin, Kayahard MCD as hardener and 2-methylimidazole as catalyst were used in these epoxy resin systems. The nano-sized spherical type fused silica as filler were used in order to study the moisture absorption properties of these liquid type epoxy encapsulant according to the change of filler size. The temperature of glass transition (Tg) of these epoxy resin systems was measured using Dynamic Scanning Calorimeter (DSC), and the moisture absorption properties of these epoxy resin systems according to the change of time were observed at $85^{\circ}C$ and 85% relative humidity condition using a thermo-hygrostat. The diffusion coefficients in these systems were calculated in terms of modified Crank equation based on Ficks' law. An increase of Tg and diffusion coefficient with filler size in these systems can be observed, which are attributed to the increase of free volume with Tg. The change of maximum moisture absorption ratio according to the filler size and filler content cannot be observed; however, the diffusion coefficients of these systems decreased with filler content. The diffusion via free volume is dominant in the epoxy resin systems with low nano-sized filler content; however, the diffusion with the interaction of absorption according the increase of the filler surface area is dominant in the liquid type epoxy encapsulant with high nano-sized filler content.

• Journal of the Korean Academy of Esthetic Dentistry
• /
• v.29 no.2
• /
• pp.92-102
• /
• 2020

Bond-Fill SB is made of powder/liquid, and the flowability can be controlled by adjusting the amount of liquid in the brush. Thanks to the strong catalyst called TBB, it has the advantage of being able to polymerize even in the presence of water and oxygen. Also, since it contains 4-META, it has the advantage of being able to adhere to metals and ceramics with appropriate surface treatment. If you fully understand these advantages, you can actively utilize them in cases where it is difficult to treat with conventional composite resin.

• Journal of the Korean Wood Science and Technology
• /
• v.42 no.5
• /
• pp.605-614
• /
• 2014

This study investigated microstructural changes of cured urea-formaldehyde (UF) resins mixed with aqueous rubber latex emulsion after intentional acid etching. Transmission electron microscopy (TEM) was used in order to better understand a hydrolytic degradation process of cured UF resins responsible for the formaldehyde emission from wood-based composite panels. A liquid UF resin with a formaldehyde to urea (F/U) molar ratio 1.0 was mixed with a rubber latex emulsion at three different mixing mass ratios (UF resin to latex = 30:70, 50:50, and 70:30). The rate of curing of the liquid modified UF resins decreased with an increase of the rubber latex proportion as determined by differential scanning calorimetry (DSC) measurement. Ultrathin sections of modified and cured UF resin films were exposed to hydrochloric acid etching in order to mimic a certain hydrolytic degradation. TEM observation showed spherical particles and various cavities in the cured UF resins after the acid etching, indicating that the acid etching had hydrolytically degraded some part of the cured UF resin by acid hydrolysis, also showing spherical particles of cured UF resin dispersed in the latex matrix. These results suggested that spherical structures of cured UF resin might play an important role in hindering the hydrolysis degradation of cured UF resin.

• Elastomers and Composites
• /
• v.31 no.1
• /
• pp.13-22
• /
• 1996

In order to Improve the fracture toughness of epoxy resin system, liquid chloroprene rubber(LCR) and liquid butadiene rubber (LBR) which have hydroxy group were used in the brittle epoxy system. Mechanical and toughness characterization of the modified epoxy resins were investigated as a function of liquid rubbers content. Epoxy resins modified with both of the liquid rubbers showed complete phase-separation microstructure : In all of the LCR content, it was observed that the domain size of LCR dispersed in the epoxy matrix ranging from $2{\mu}m\;to\;5{\mu}m$. It was found that fracture toughness, $K_{ic}$, of the modified LCR system was enhanced continuously as increasing LCR content. However around 10phr of LBR system showed maximum fracture toughness. Specifically, when BPA add to the modified LCR system, thermal and mechanical properties increased than neat epoxy. At the same time, fracture toughness was enhanced.