• Transactions of the Korean Society of Mechanical Engineers
• /
• v.7 no.1
• /
• pp.28-35
• /
• 1983

Quantitative analysis have been carried out on the micro-cracks on the surface and into the depth of unnotched smooth mild steel specimen under cyclic stains by rotating bending fatigue tests. Some of the results are; (1) Cracks initiate at the early stage of fatigue life N$_{I}$/ N$_{f}$=10 to 20%, and propagate during the rest of fatigue life. (2) Coalescence of highly crowded small fatigue cracks of random distribution seems to induce the final fracture at higher stress level. (3) The curves of crack initiation and the equal crack length on the graph of stress versus number of cycles are parallel to the S-N curve. (3) The curves of crack initiation and the equal crack length on the graph of stress versus number of cycles are parallel to the S-N curve. (4) The distributions of micro-surface crack length and depth show the composite Weibull distributions which are approximated to two straight lines separated by the value of transient region between stage I and stage II crack.k.k.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.16 no.4
• /
• pp.63-68
• /
• 2008

The fatigue characteristics of bevel gear used for differential gear of automobile was investigated in this paper. From the A-N(Almen intensity-Number of fracture)curve of bevel gear it was shown that there was a specific time that have a maximum fatigue life. Optimal peening condition was 65m/s of project velocity and 8min of project time. Fatigue life was also investigated from the S-N curve between optimal peened specimen and unpeened specimen. Another very significant point is that the crack initiation of bevel gear by shot peening was generated in the subsurface from fractography. This paper shows that shot peening process tremendously improve fatigue characteristics of bevel gear.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.47 no.2
• /
• pp.63-72
• /
• 2005

In this study, the physical and mechanical properties of steel fiber reinforced lightweight polymer concrete were investigated experimentally with various steel fiber contents. All tests were performed at room temperature, and stress-strain curve and load-deflection curve were plotted up to failure. The unit weight of steel fiber reinforced lightweight polymer concrete was in the range of $1,020{\sim}1,160\;kg/m^3$, which was approximately $50\%$ of that of the ordinary polymer concrete, The compressive strength, splitting tensile strength, flexural toughness and flexural load-deflection curves after maximum load were shown with increase of steel fiber content. The stress-strain curves of steel fiber reinforced lightweight polymer concrete were bilinear in nature with a small transition zone, Based on these results, steel fiber reinforced lightweight polymer concrete can be widely applied to the polymer composite products.

• Journal of the Korean Operations Research and Management Science Society
• /
• v.10 no.1
• /
• pp.65-78
• /
• 1985

In this paper, the approach getting a total demand by forecasting the new demand and the replacement demand separately and adding them is used for long term forecasting of durable goods. Cross country analysis using the income as an independent variable and S-shaped growth curve as a fitting model is developed as a method of forecasting new demand. To get the replacement demand the methods using the number of ownership and the replacement rate and the methods using the past demand and the distribution of the product life are proposed. And the theoretical explannation for product life cycle's diversity, which is the one of the major considerations in the long term forecasting, is attempted by the combination of the new demand and the replacement demand patterns. This is applicated the long term forecasting of Korean passenger cars.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.27 no.6
• /
• pp.987-996
• /
• 2003

The structural integrity of the reactor vessel with the approaching end of life must be assured for pressurized thermal shock. The regulation specifies the screening criteria for this and requires that specific analysis be performed for the reactor vessel which is anticipated to exceed the screening criteria at the end of plant life. In case the screening criteria is exceeded by the deterministic analysis, probabilistic analysis must be performed to show that failure probability Is within the limit. In this study, probabilistic fracture mechanics analysis of the reactor vessel for pressurized thermal shock is performed and the effects of residual stress and master curve on the failure probability are investigated.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.199-204
• /
• 2001

Big accidents of flyings, vessel, subways, gas equipments, buildings and bridge happens frenquently. Therefore many people are suffering harm of property. The destruction cause of macaine components is almost accused by fatigue. This study is test for STS304 specimen using pure and cantilever bending state. Rounded specimen and notched specimen including fracture surface investigation was comparatively experimented, fatigue life according to degree of surface finishing was examined. Fatigue fracture probability of notched canilever specimens were predicted by P-S-N curve, median rank and Weibull distribution. And at the relation with the rotational speed and stress, the fatigue life of the test specimen was higher at high speed than low speed.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.129-134
• /
• 2000

Recently, HIPS(High Impact Polystyrene) materials are spot-lighted as office equipment, home electronics, electronics appliances housing, packing containers, etc. But its using are occur to problem caused by fatigue fracture. However, its strength is larged affected by environmental conditions. So, in this paper it tried to analyze the effect of temperature by tensile test and fatigue test. It was observed that yield strength and ultimate strength, fatigue life of same stress decreased relatively with increase temperature. Further, this paper predict S-N curve using the result of tensile test and micro vickers hardness test. For this purpose, the management in the engineering department is able to design the fatigue life of HIPS(HR-1360) materials.

• Journal of the Korean Society of Safety
• /
• v.17 no.4
• /
• pp.38-44
• /
• 2002

The application of fractal concept provides an useful method in the study for the quantitative analysis of irregular variations like the fracture surfaces and crack profiles. Fractal curves have characteristics that represents a self-similarity based on the fractal dimension. The fractal dimensions were obtained by the box counting method. In this report, we obtained the nearly stable fractal dimensions of fracture crack profiles for STS316 with CT specimen as the crack advances and the relationships between crack length and fractal dimension. Moreover fractal fracture parameter that corresponds to J-R curve is shown by the relationships between fractal dimension and crack extension. From the results, we concluded that crack extension of high toughness material also shows the fractal characteristics, which can be used in order to evaluate the crack life precisely.

• Structural Engineering and Mechanics
• /
• v.83 no.1
• /
• pp.109-121
• /
• 2022

Twelve push-out test specimens were conducted with various parameters to study the static and fatigue performance of a new through-bolt shear connector transferring the shear forces of interface between prefabricated hybrid fiber reinforced concrete (HFRC) slabs and steel girders. It was found that the fibers could improve the fatigue life, capacity and initial stiffness of through-bolt shear connector. While the bolt-hole clearance reduced, the initial stiffness, capacity and slippage of through-bolt shear connector increased. After the steel-concrete interface properties were improved, the initial stiffness increased, and the capacity and slippage reduced. Base on the test results, the equation of the load-slip curve and capacity of through-bolt shear connector with prefabricated HFRC slab were obtained by the regression of test results, and the allowable range of shear force under fatigue load was recommended, which could provide the reference in the design of through-bolt shear connector with prefabricated HFRC slabs.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.6 no.1
• /
• pp.50-56
• /
• 2010

Fatigue has been known as a major degradation mechanism of ASME class 1 components in nuclear power plants. Fatigue damage could be accelerated by combined interaction of several loads and environmental factors. However, the environmental effect is not explicitly addressed in the ASME S-N curve which is based on air at room temperature. Therefore many studies have been performed to understand the environmental effects on fatigue behavior of materials used in nuclear power plants. As a part of efforts, we performed low cycle fatigue tests under various environmental conditions and analyzed the environmental effects on the fatigue life of SA508 Gr. 1a low alloy steel by comparing with higuchi's model. Test results show that the fatigue life depends on water temperature, dissolved oxygen and strain rate. But strain rate over 0.4%/s has little effect on the fatigue life. To find the cause of different fatigue life with ANL's and higuchi's model, another test performed with different heat numbered and heat treated materials of SA508 Gr. 1a. On a metallurgical point of view, the material with bainite microstructure shows much longer fatigue life than that with ferrite/pearlite microstructure. And the characteristics of crack propagation as different microstructure seem to be the main cause of different fatigue life.