• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.29 no.5
• /
• pp.298-302
• /
• 2016

In this work, $LiMn_2O_4$ and $LiNi_{1/3}Mn_{1/3}Co_{1/3}O_2$ cathode materials are mixed by some specific ratios to enhance the practical capacity, energy density and cycle performance of battery. At present, the most used cathode material in lithium ion batteries for EVs is spinel structure-type $LiMn_2O_4$. $LiMn_2O_4$ has advantages of high average voltage, excellent safety, environmental friendliness, and low cost. However, due to the low rechargeable capacity (120 mAh/g), it can not meet the requirement of high energy density for the EVs, resulting in limiting its development. The battery of $LiMn_2O_4-LiNi_{1/3}Mn_{1/3}Co_{1/3}O_2$ (50:50 wt%) mixed cathode delivers a energy density of 483.5 mWh/g at a current rate of 1.0 C. The accumulated capacity from $1^{st}$ to 150th cycles was 18.1 Ah/g when the battery is cycled at a current rate of 1.0 C in voltage range of 3.2~4.3 V.

• Journal of Electrochemical Science and Technology
• /
• v.7 no.2
• /
• pp.139-145
• /
• 2016

The electrochemical performance of carbon-coated LiMn₂O₄ nanoparticles was reported. The polydopamine layer was introduced as a new organic carbon source. The carbon layer was homogeneously coated onto the surface of the LiMn₂O₄ nanoparticles because the polymerization process from the dopamine solution (in a buffer solution, pH 8.5) easily and uniformly formed a polydopamine layer. The phase integrity of LiMn₂O₄ deteriorated during the carbon-coating process due to oxygen loss, although the main structure was maintained. The carbon-coated sample led to improved rate capability because of the effect of the conductive carbon layer. Moreover, the carbon coating also enhanced the cyclic performance. This indicates that the carbon layer may suppress unwanted side reactions with the electrolytes and compensate for the low electronic conductivity of the pristine LiMn₂O₄.

• Applied Chemistry for Engineering
• /
• v.10 no.6
• /
• pp.832-837
• /
• 1999

Stability of a cathode material was determined by Tafel plot in 1 M LiOH solution. The stabilized $LiM_xMn_{2-x}O_4$ (x=0.05~0.1) electrode resulted in overpotential of 0.13~0.15 mV at 100 mA. This overpotential was 0.05 mV lower than that of the spinel structured $LiMn_2O_4$ electrode. Conductivity test at various potentials showed that the conductivity of $LiM_xMn_{2-x}O_4$ was higher than that of the spinel structured $LiMn_2O_4$ and the bulk resistance of $LiM_xMn_{2-x}O_4$ due to the dissolution of $Mn^{2+}$ was lowered.

• Applied Chemistry for Engineering
• /
• v.9 no.5
• /
• pp.774-780
• /
• 1998

For the stabilization of the spinel structured $LiMn_2O_4$, a fraction of manganese was substituted with various metals such as Mg, Fe, V, W, Cr, Mo with Mn that had a similar ionic radii ($LiM_xMn_{2-x}O_4(0.05{\leq}x{\leq}0.02)$). The $LiM_xMn_{2-x}O_4$ showed a substantial improvement as lower capacity loss than that of the spinel structured $LiMn_2O_4$ when it was used as a cathode material. And with the partial substitution, the chemical diffusion coefficient for $LiMg_{0.05}Mn_{1.9}O_4$ and $LiCr_{0.1}Mn_{1.9}O_4$ was increased by and order of magnitude compared to that of the $LiMn_2O_4$ with spinel structure. The results showed that significant improvement can be made on the electrochemical characteristics as the structure of the $LiMn_2O_4$ electrode material was stabilized by the partial substitution.

• Journal of Electrochemical Science and Technology
• /
• v.13 no.2
• /
• pp.177-185
• /
• 2022

Electrochemical properties of LiMn₂O₄ cathode were investigated in three types of Zn-containing electrolytes: lithium-zinc sulfate electrolyte (1M ZnSO₄ / 2M Li₂SO₄), zinc sulfate electrolyte (2MZnSO₄) and lithium-zinc-manganese sulfate electrolyte (1MZnSO₄ / 2MLi₂SO₄ / 0.1MMnSO₄). Cyclic voltammetry measurements demonstrated that LiMn₂O₄ is electrochemically inactive in pure ZnSO₄ electrolyte after initial oxidation. The effect of manganese (II) additive in the zinc-manganese sulfate electrolyte on the electrochemical performance was analyzed. The initial capacity of LiMn₂O₄ is higher in presence of MnSO₄ (140 mAh g^-1 in 1 M ZnSO₄ / 2 M Li₂SO₄ / 0.1 M MnSO₄ and 120 mAh g^-1 in 1 M ZnSO₄ / 2MLi₂SO₄). The capacity increase can be explained by the electrodeposition of MnO_x layer on the electrode surface. Structural characterization of postmortem electrodes with use of XRD and EDX analysis confirmed that partially formed in pure ZnSO₄ electrolyte Zn-containing phase leads to fast capacity fading which is probably related to blocked electroactive sites.

• Journal of the Korean Ceramic Society
• /
• v.41 no.10 s.269
• /
• pp.735-741
• /
• 2004

$LiMn_{1.92}Co_{0.08}O_4$ and $LiNi_{0.7}Co_{0.3}O_2$ synthesized by a simplified combustion method had good electrochemical properties. Mixtures $LiMn_{1.92}Co_{0.08}O_4$-x wt$\%$ $LiNi_{0.7}Co_{0.3}O_2$ (x=9, 23, 33, 41, and 47) were prepared by milling for 30 min and their electrochemical properties were investigated. The electrode with x=9 had a relatively large first discharge capacity (109.9 mAh/g at 0.1 C) and good cycling performance. The decrease in the discharge capacity of the mixture electrodes with cycling is considered to result mainly from the degradation of $LiNi_{0.7}Co_{0.3}O_2$, caused by coating of $LiNi_{0.7}Co_{0.3}O_2$ with Mn dissolved from $LiMn_{1.92}Co_{0.08}O_4$.

• Korean Journal of Metals and Materials
• /
• v.46 no.3
• /
• pp.174-181
• /
• 2008

The stability of the cathode materials for Li secondary battery is an important factor for its cyclability. The present paper focuses on the structural stability of $LiNi_{0.5}Mn_{1.5}O_4$ during lithiation/delithiation of Li ions and compared to that of $LiMn_{2}O_4$. $LiMn_{2}O_4$ and $LiNi_{0.5}Mn_{1.5}O_4$ powders are synthesized using a solgel method and their structural and electrochemical properties are investigated by XRD, SEM, and charge-discharge tests. $Li_xMn_2O_4$ and $Li_xNi_{0.5}Mn_{1.5}O_4$(x = 0.9,0.5,0.1) specimens are obtained after charge/discharge tests by controlling the cut-off voltage for XRD and TEM investigation. The charge-discharge tests shows that initial capacity of $LiNi_{0.5}Mn_{1.5}O_4$ is 125 mAh/g and that of LiMn2O4 is around 100 mAh/g. The capacity of $LiNi_{0.5}Mn_{1.5}O_4$ is maintained 95% of its initial capacity whereas the capacity of $LiMn_{2}O_4$ is maintained 65% of its initial capacity.

• Transactions of the Korean hydrogen and new energy society
• /
• v.15 no.1
• /
• pp.62-71
• /
• 2004

$LiMn_{1.92}Co_{0.08}O_4-x\;wt.%LiNi_{0.7}Co_{0.3}O_2$를 단순화한 연소법에 의하여 합성하고, 그것들의 전기화학적 특성을 조사하였다. 또한 30분동안 밀링하여 준비한 $LiMn_{1.92}Co_{0.08}O_4-x\;wt.%LiNi_{0.7}Co_{0.3}O_2$ (x=9, 23, 33, 41 and 47) 혼합물 전극의 전기화학적 특성을 조사하였다. x=33 조성의 전극이 가장 큰 초기방전용량(132.0mAh/g at 0.1C)을 나타내었다. x=9조성의 전극은 비교적 큰 초기방전용량(109.9mAh/g at 0.1C)과 우수한 싸이클 특성을 나타내었다. 싸이클링에 따른 혼합물 전극의 방전용량의 감소는 주로 $LiNi_{0.7}Co_{0.3}O_2$의 퇴화에 기인한다고 생각된다. 그런데 $LiNi_{0.7}Co_{0.3}O_2$의 퇴화는 $LiMn_{1.92}Co_{0.08}O_4$로부터 용해된 Mn이 $LiNi_{0.7}Co_{0.3}O_2$를 둘러쌈(coating)으로써 야기되는 것으로 생각된다.

• Applied Chemistry for Engineering
• /
• v.10 no.1
• /
• pp.80-84
• /
• 1999

$Li_{4/3}Mn_{5/3}O_4$ having a defect structure was prepared by sol-gel process using lithium acetate and manganese acetate as starting materials, and their electrode characteristics in the lithium secondary battery was investigated. The reaction mole ratio was determined as $AA/Mn(OAc)_2$ of 0.2 and $NH_4OH/Mn(OAc)_2$ to $H_2O/Mn(OAc)_2$ of 0.4. The product was obtained through heat treatment at $350^{\circ}C$ for 12hrs after 1'st heat treatment at $150^{\circ}C$ of xerogel under oxygen atmosphere. When the charge and discharge cycles were performed between 2.0 V and 3.2 V, $Li/Li_{4/3}Mn_{5/3}O_4$ cell showed the dicharge capacity of 84.23 mAh/g and the good cycleability was obtained in the plateau region.

• Journal of the Korean Ceramic Society
• /
• v.43 no.9 s.292
• /
• pp.588-593
• /
• 2006

Spinel phase $LiMn_2O_4$ is of great interest as cathode materials for lithium-ion batteries. In this study, SHS (Self propagating High-temperature Synthesis) method to synthesize spinel $LiMn_2O_4$ directly from lithium nitrate, manganese oxide, manganese and sodium chloride were investigated. The influence of Li/Mn ratio, the heat-treated condition of product have been explored. The resultant $LiMn_2O_4$ synthesized under the optimum synthesis conditions shows perfect spinel structure, uniform particle size and excellent electrochemical performances.