• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.18 no.6
• /
• pp.543-549
• /
• 2005

The electrical and dielectric properties of $ZnO-Pr_6O_{11}-CoO-Cr_2O_3-based$ varistors were investigated in the sintering time range of $1\~3$ h. Increasing sintering time improved the densification of ceramics, whereas deteriorated the nonlinearity, in which the nonlinear exponent greatly decreased from 55.3 to 38.2 and the leakage current increased from 0.1 to $1.1\;{\mu}A$. The donor concentration and density of interface states increased in the range of $(1.06\~1.60)\times10^8/cm^3\;and\;(3.15\~3.67)\times10^{12}/cm^2$ with increasing sintering time, respectively. while, in dielectric properties, the increase of sintering time increased in the range of $0.0228\~0.0505$ in tans and $1.32\~1.36\;{\mu}s$ in relaxation time.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2004.04b
• /
• pp.18-21
• /
• 2004

An alkoxide-based sol-gel method was used to fabricate $Ba_{0.6}Sr_{0.4}TiO_3$ thin films doped by Bi from 5 to 20 mol% on a $Pt/Ti/SiO_2/Si$ substrate. The structural and dielectric properties of BST thin films were investigated as a function of Bi dopant concentration. The dielectric properties of the Bi doped BST films were strongly dependent on the Bi contents. The dielectric constant and dielectric loss of the films decreased with increasing Bi content. However, the leakage current density of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin film showed the lowest value of $5.13{\times}10^{-7}\;A/cm^2$ at 5 V. The figure of merit (FOM) reached a maximum value of 32.42 at a 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin films. The dielectric constant, loss factor, and tunability of the 10 mol% Bi doped $Ba_{0.6}Sr_{0.4}TiO_3$ thin films were 333, 0.0095, and 31.1%, respectively.

• Proceedings of the KIEE Conference
• /
• 1997.11a
• /
• pp.291-293
• /
• 1997

In this study, Sol-Gel derived $(Ba_{0.7}Sr_{0.3})TiO_3$ thin films were fabricated and investigated. The stock solution was synthesized and spin-coated on Pt/Ti/$SiO_2$/Si substrate at 4000(rpm] and then, annealed at $650{\sim}750[^{\circ}C]$. Crystallization condition, microstructural properties and interfacial structure were observed by XRD, AFM, SEM and TEM. It was found that the BST thin films were completely crystallized at 750[$^{\circ}C$] and showed nano-sized grains. The dielectric constant and loss of the BST thin films were 220, 0.01 at 1[kHz] respectively. Increasing the temperature, the dielectric constant and loss characteristics were not varied widely. At the applied voltage of 1.5[V], the leakage current density was under the $10^{-9}[A/cm^2]$.

• Journal of Advanced Marine Engineering and Technology
• /
• v.30 no.8
• /
• pp.894-900
• /
• 2006

The electrical characteristics associated with crystal structure changes as a function of La content for $(Pb_{1-x}La_x)(Zr_{0.5}Ti_{0.5})O_3$ thin films were investigated for applications in memory capacitors. Tetragonality of PLZT films decreased with increasing La content. Thin films with La $\geq$ 20 mol% were found to be cubic. Films with La $\geq$ 12 mol% exhibited broader dielectric peaks compared to those of bulk ceramics and behaved as relaxer ferroelectrics. Tetragonal PLZT film with 12 mol% La had a dielectric constant maximum of 1330 at room temperature and a charge storage density of ${\sim}18{\mu}C/cm^2$ at 5 V. Decrease in coercive field and remnant polarization with increase in La content were resulting from less dipolar response caused by the decreased crystal anisotropy. The leakage current densities $<10^{-8}A/cm^2$ up to 5 V bias voltage were observed for the films with La $\geq$ 14 mol%.

• Applied Science and Convergence Technology
• /
• v.26 no.5
• /
• pp.133-138
• /
• 2017

We investigated the interface defect engineering and reaction mechanism of reduced transition layer and nitride layer in the active plasma process on 4H-SiC by the plasma reaction with the rapid processing time at the room temperature. Through the combination of experiment and theoretical studies, we clearly observed that advanced active plasma process on 4H-SiC of oxidation and nitridation have improved electrical properties by the stable bond structure and decrease of the interfacial defects. In the plasma oxidation system, we showed that plasma oxide on SiC has enhanced electrical characteristics than the thermally oxidation and suppressed generation of the interface trap density. The decrease of the defect states in transition layer and stress induced leakage current (SILC) clearly showed that plasma process enhances quality of $SiO_2$ by the reduction of transition layer due to the controlled interstitial C atoms. And in another processes, the Plasma Nitridation (PN) system, we investigated the modification in bond structure in the nitride SiC surface by the rapid PN process. We observed that converted N reacted through spontaneous incorporation the SiC sub-surface, resulting in N atoms converted to C-site by the low bond energy. In particular, electrical properties exhibited that the generated trap states was suppressed with the nitrided layer. The results of active plasma oxidation and nitridation system suggest plasma processes on SiC of rapid and low temperature process, compare with the traditional gas annealing process with high temperature and long process time.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.05c
• /
• pp.58-62
• /
• 2002

Pb($Zr_{0.52}Ti_{0.48}$)$O_3$ (PZT) thin films deposited on the Pt/Ti and Ru/$RuO_2$ bottom electrode by rf magnetron sputtering methode. Ru/$RuO_2$ bottom electrode deposited on the p-type wafer as Ru thickness by in-situ process. Our results show that all PZT films indicated perovskite polycrystalline structure with perferred orientation (110) and no pyrochlore phase is observed. A well-fabricated $RuO_2$/PZT/Ru(100nm)/$RUO_2$ capacitor showed a leakage current density in the order of $2.13{\times}10^{-7}A/cm^2$ as 100 kV/cm, a remanent polarization of 7.20 ${\mu}C/cm^2$, and a coercive field of 58.37 kV/cm. The results show that the new Ru/$RuO_2$ bottom electrodes are expected to reduce the degradation ferroelectric fatigue and excellent ferroelectric properties.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.14 no.5
• /
• pp.370-375
• /
• 2001

PZT thin films (3500${\AA}$) ahve been prepared onto Pt/Ti/corning glass (1737) substrates with a RF magnetron sputtering system using Pb$\sub$1.50/(Zr$\sub$0.52/,Ti$\sub$0.48)O$_3$ ceramic target. We used two-step annealing techniques, PZT thin films were grown at a 300$^{\circ}C$ substrate temperature and then subjected to an RTA treatment. In case of 500$^{\circ}C$ RTA temperature show pyrochlore phase. The formation of Perovskite phase started above 600$^{\circ}C$ and PZT thin films generated (101) preferred orientation. As the RTA time and temperature increased, crystallization of PZT films were enhanced. The PZT capacitors fabricated at 650$^{\circ}C$ for 10 minutes RTA treatment showed remanent polarization 30 ${\mu}$C/$\textrm{cm}^2$, saturation polarization 42${\mu}$C/$\textrm{cm}^2$, coercive field 110kV/cm, leakage current density 2.83x10$\^$-7/A/$\textrm{cm}^2$, remanent polarization were decreased by 30% after 10$\^$9/ cycles.

• Proceedings of the KIEE Conference
• /
• 2002.07c
• /
• pp.1449-1451
• /
• 2002

A developed 800kV class composite hollow insulator for $SF_6$ Gas Insulated Switchgear (GIS) was tested as to insulation with their surfaces contaminated. The wet power frequency withstand voltage of the silicone rubber housing was about 135kV at an equivalent salt deposite density of $5kg/m^2$, to sufficiently satisfy the required performance. According to IEC 60507, the salt fog withstand voltage was measured at 565kV, and the highest measured leakage current was below 0.2mA. Therefore, it was clarified that the composite hollow insulator has sufficient insulation performance even when it is contaminated on the surface.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.13 no.1
• /
• pp.66-74
• /
• 2000

The structural and electrical characteristics of SBT thin films, fabricated on Pt/Ti/SiO\ulcorner/Si substrates by a pulsed laser deposition(PLD), were investigated to develop ferroelectric thin films for capacitor lay-ers of FRAM. EFfects of target composition on the characteristics of SBT thin films were examined. Target were prepared by mixed oxide method, and composition of Sr/Bi/Ta on SBT was changed to 1/2/2, 1/2.4/2, 1/2.8/2, 0.8/2/2 and 1.2/2/2. SBt thin films were fabricated, as a function of substrate temperature and oxygen pressure, by PLD. The optimized ocndition, to fabricate high quality SBT thin films, was 700 $^{\circ}C$ of substrate temperature, 200 mTorr of oxygen pressure, and 2 J/$\textrm{cm}^2$ of laser energy density. Maximum remnant value(2Pr) of 9.0 $\mu$C/$\textrm{cm}^2$, coercive field value(Ec) of 50 kV/cm, dielectric constant value of 166, and leakage current densities of <10\ulcorner A/$\textrm{cm}^2$ were observed for the films with 1/2/2 composition, which was prepared at the above PLD condition.

• Transactions on Electrical and Electronic Materials
• /
• v.4 no.1
• /
• pp.15-20
• /
• 2003

NiCr alloys are prepared onto poly-Si/ $SiO_2$/Si substrates to replace Pt bottom electrode with a new one for integration of high dielectric constant materials. Alloys deposited at Ni and Cr power of 40 and 40 W showed optimum properties in the composition of N $i_{1.6}$C $r_{1.0}$. The grain size of films increases with increasing deposition temperature. The films deposited at 50$0^{\circ}C$ showed a severe agglomeration due to homogeneous nucleation. The NiCr alloys from the rms roughness and resistivity data showed a thermal stability independent of increasing annealing temperature. The 80 nm thick BST films deposited onto N $i_{1.6}$C $r_{1.0}$/poly-Si showed a dielectric constant of 280 and a dissipation factor of about 5 % at 100 kHz. The leakage current density of as-deposited BST films was about 5$\times$10$^{-7}$ A/$\textrm{cm}^2$ at an applied voltage of 1 V. The NiCr alloys are possible to replace Pt bottom electrode with new one to integrate f3r high dielectric constant materials.terials.