• Proceedings of the Korea Concrete Institute Conference
• /
• 2002.10a
• /
• pp.757-762
• /
• 2002

This study focused on the investigation of durability of latex modified concrete in the points of surface scaling resistance as cement types variated and latex content variated such as 5%, 10%, 15%, and 20%. An increasing the amount of latex produced concrete with increased flexural strength, but with slightly lower compressive strength. The increase in flexural strength might be attributed to the latex films between the hydrated cement and aggregates, and the decrease in compressive strength to the flexibility of the latex component named by Butadiene. The surface scaling resistance test was used to evaluate the durability of latex-modified concretes and rapid setting latex-modified concretes. The surface scaling resistance of LMC was quite good comparing to conventional concrete. Further, surface scaling resistance of RSLMC was improved with increasing the latex content.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2000.10a
• /
• pp.191-196
• /
• 2000

This study was focused on the investigation of permeability of latex modified concrete as the latex content variated such as 5%, 10%, 15%, and 20%. The rapid chloride permeability test was used to evaluate the relative permeability of latex-modified concretes and conventional concretes. The results showed that the permeability of latex-modified concretes was considerably lower than conventional concretes tested, which may be due to the latex filled in voids and interconnections of hydrated cement and aggregates by a film of latex particles.

• Journal of Industrial Technology
• /
• v.22 no.A
• /
• pp.177-184
• /
• 2002

Reinforced concrete(R/C) is commonly used to structures because they have many merits that compressive strength, economy and so on. However, reinforced concrete has a crack at the tensile section which is due to the relatively lower tensile strength than its compressive strength Latex modified concrete(LMC) has higher tensile and flexural strength than the ordinary portland cement, due to the interconnections of hydrated cement and aggregates by a film of latex particles. The purpose of this study was to investigate the flexural behavior of reinforced concrete beam with latex modified concrete, having the main experimental variables such as concrete types(ordinary portland cement concrete, latex modified concrete), latex contents(0%, 15%), flexural steel ratios(0.012, 0.0235), and with/without shear reinforcement. The beam of LMC showed considerably higher initial cracking loads and ductility than that of OPC, but, similar to ultimate strength and deflection. This might be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic, and colloidal properties of the latexes resulting in reduced water evaporation. The beam with latex modified concrete could be adopted at field for controlling and reducing the tensile crack due to its higher tensile strength.

• Journal of Industrial Technology
• /
• v.21 no.B
• /
• pp.301-306
• /
• 2001

Drying shrinkage cracking which may be caused by the relatively large specific surface is a matter of grave concern for latex modified concrete(LMC) overlay and rapid-setting cement latex modified concrete(RSLMC) overlay. Therefore, the purpose of this dissertation was to study the drying shrinkage properties of LMC and RSLMC with the main experimental variables such as cement types(ordinary portland cement, rapid setting cement), latex contents(0, 5, 10, 15, 20%), W-C ratios, and curing days at a same controlled environment of 60% of relative humidity and $20^{\circ}C$ of temperature. Test results revealed that the drying shrinkage of latex modified concrete(LMC), rapid-setting cement latex modified concrete(RSLMC) was considerably lower than that of ordinary portland cement concrete(OPC), rapid-setting cement concrete(RSC), respectively. This may be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic and colloidal properties of the latexes, resulting in reduced water evaporation.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2001.11a
• /
• pp.1023-1028
• /
• 2001

This study focused on the investigation of strength development and permeability of LMC(latex modified concrete) and RSLMC(rapid-setting cement latex modified concrete) as the latex content, cement types and w/c ratio variated. The compressive strength of latex modified concrete decreased slightly and the flexural strength increased quitely at the latex content of 15%. This may due to the flexibility of latex filled in voids and interconnections of hydrated cement and aggregates by a film of latex particles, respectively. The permeability test results showed that the permeability of LMC was considerably lower than that of conventional concrete. In the RSLMC's tests of permeability to chloride ion indicated very low permeability at an early age, which nay be due to the early formation of needle-shape ettringites and latex film.

• International Journal of Concrete Structures and Materials
• /
• v.19 no.1E
• /
• pp.41-48
• /
• 2007

Addition of latex to concrete is known to increase its durability and permeability. The purpose of this study is to analyze air void systems in latex-modified concretes using a reasonable and objective method of image analysis with such experimental variables as water-cement (w/c) ratios, latex contents (0%, 15%) and cement types (ordinary portland cement (OPC), high-early strength (HES) cement and very-early strength (VES) cement). The results are analyzed by spacing factor, air volume (content) after hardening, air void distribution and structure. Additionally, air void systems and permeability of latex-modified concrete (LMC) are compared by a correlation analysis. The results are as follows. The LMC of the same w/c ratio showed better air entraining (AE) effect than OPC with AE water reducer. The VES-LMC showed that the quantity of entrained air below $100{\mu}m$ increased more than four times. For the case of HES-LMC, microscopic entrained air between the range of 50 to $500{\mu}m$ increased greater than 7 times even in the absence of anti-foamer. Although spacing factor was measured rather low, the permeability of latex-modified concrete was good. It is construed that air void system does not have a considerable effect on the property of latex-modified concrete, but latex film (membrane) has a definite influence on the durability of LMC.

• Journal of Industrial Technology
• /
• v.21 no.B
• /
• pp.317-324
• /
• 2001

This study focused on the investigation of strength development and permeability of LMC(Latex Modified Concrete) and RSLMC(Rapid-Setting Cement Latex Modified Concrete) as the latex content, cement types and w/c ratio changed. The compressive strength of latex modified concrete decreased slightly and the flexural strength increased quitely at 15% of latex content. This may be due to the flexibility of latex filled in voids and interconnections of hydrated cement and aggregates by a film of latex particles, respectively. The permeability test results showed that the permeability of LMC was considerably lower than that of conventional concrete. Results of chloride permeability test, for RSLMC indicated very low at an early age caused by the early formation of needle-shape ettringites and latex film.

• International Journal of Highway Engineering
• /
• v.3 no.3 s.9
• /
• pp.135-146
• /
• 2001

This study focused on the investigation of compressive and flexural strengths development, and bond strength of latex modified concrete in order to validate the feasibility of application into concrete bridge deck overlay. Pull-out bond test was used for evaluating the bond strength of latex modified concrete to substrate. The main experimental variables were latex-cement ratio, surface preparation and moisture levels. The compressive strength of latex modified concrete decreased slightly and the flexural strength increased as the latex content increased from 5% to 20%. This might be due to the flexibility latex filled in voids and interconnections of hydrated cement and aggregates by a film of latex particles, respectively. In general, increasing the amount of latex will produce concrete with increased tensile and flexural strength and lower modulus of elasticity. Significant improvements in bond strength between new and existing concrete were achieved through the modification of the new concrete bridge deck overlay by latex polymers. The effect of surface preparation on bond of latex modified concrete to conventional concrete were significant at the conditions by sand paper and wire brush. A better bond could be achieved by rough surface rather than smooth. The saturated condition of surface is the most appropriate moisture level among the considered followed by dry condition and wet condition.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.50 no.4
• /
• pp.27-37
• /
• 2008

It is most serious problem which is various occurs from the agricultural concrete structure and off shore concrete structure the problem which it comes to think is deterioration of the concrete which is caused with the corrosion of the reinforcing steel which is caused by with permeation of the water and the sea water. Specially the off shore concrete structure has been deteriorated by the steel reinforcement corrosion. The latex modified concrete(LMC) was adds latex in the plain concrete as the latex has increase the durability of concrete. This study were accomplished to the estimate the diffusion coefficient of LMC, and the time dependent constants of diffusion. The average chloride diffusion coefficient was estimated. Also, the average chloride diffusion coefficient was compared with diffusion coefficient test results of 28 curing days. The test results indicated that the average chloride diffusion coefficient could closely estimate the test results of the diffusion coefficient test results of 28 curing days.

• Journal of The Korean Society of Agricultural Engineers
• /
• v.49 no.4
• /
• pp.35-41
• /
• 2007

The most agricultural concrete structures for the irrigation and drainage are exposed to the underwater condition at the irrigation period and they take the influence on very severe cold in the winter. Therefore, it is impossible to use repair materials used to the general concrete structures. The research need the development of the repair material for a performance enhance of the agricultural underwater concrete structures. This research evaluated the mechanical and durability performance of the latex modified repair mortar for underwater concrete structures which peformed the repair in the underwater according to the characteristic of the agricultural concrete structure. The latex modified repair mortar is a material that minimize the effect of the ecosystem, environment and the segregation. In this research, the construction condition of the latex modified repair mortar for agricultural concrete structures was considered and the test specimens made in the underwater condition. Test results was then compared with target performance and commercial repair mortar. Experimental test results indicated that the mechanical and durability performance of latex modified repair mortar for agricultural underwater concrete structure satisfied all target performance. Also, the latex modified repair mortar resulted in better repair performance than the commercial repair mortar.