• 한국진공학회지
• /
• 제7권s1호
• /
• pp.50-56
• /
• 1998

Ion beam assisted deposition (IBAD) was successfully used to produce a dense and ultra-adherent Hydroxyapatite (HA) film on titanium alloy and alumina. Recently it is also proved that the HA coatings on alumina substrate treated with 20 ppm $AgNO_3$ had the structure of $(Ag, Ca)_10(PO_4)6(OH)_2$, which exhibited excellent antimicrobial effects. The present paper aims to morphlogically characterize the adhesion of macrophages on newly developed Ag-HA coated alumina and Ti6A14V substrates and to evaluate the biocompatibility of the coatings in vitro. It can be found that the cell number on alumina of the concentration of $AgNO_3$ in the treatment, the cell number on Ag-HA coatings decreased. Up to 20 ppm $AgNO_3$ by Ag-treatment, the morphological development of the cells on Ag-HA coating was similar to that of the cells on HA coating, suggesting the biotolerance of the Ag-HA coatings.

• 한국표면공학회지
• /
• 제34권3호
• /
• pp.225-230
• /
• 2001

In this study, the effect of surface treatment of CFRP (Carbon Fiber Reinforced Composites) on the shear strength of CFRP/metal composites was investigated. The surface of 14 plied unidirectional (0-dog ) CFRP was treated by an $Ar^{/}$ + ion beam under an oxygen environment. Shear strength tests were performed using SLS (Single Lap Shear) specimens based on the ASTM D906-94a procedure. The shear strength of the surface-treated CFRP/metal composites was compared with that of the untreated CFRP/metal composites. The results showed that the shear strength of surface-treated CFRP/metal composites was 36% greater than that of untreated CFRP/metal composites.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2009년도 제38회 동계학술대회 초록집
• /
• pp.247-247
• /
• 2010

DLC(diamond-like carbon)는 비정질 고상 탄소의 하나로 다이아몬드의 유사한 높은 경도, 내마모성, 윤활성, 전기절연성, 화학적 안정성을 가지고 있는 재료이다. 이러한 우수한 특성 때문에 DLC는 박막의 형태로 여러 종류의 보호코팅에 많이 응용되고 있다. DLC의 광범위한 응용에 있어 가장 큰 문제점은 박막이 갖는 높은 잔류응력과 이에 따른 기판과의 낮은 접착성으로 알려져 있다. 최근 연구에 의하면, plasma pre-treatment를 통해 PTFE기판에 DLC박막의 adhesion strength를 증진 시킬 수 있다고 보고하였다. 또한 ion beam technique를 이용하여 잔류응력을 줄이고 기판과의 접착력을 높일 수 있다는 것도 보고 되었다. 이에 기인하여 pre-treatment가 DLC합성에 잔류응력을 낮추고 기판과의 접착성을 높이는 효과를 보일 것이라고 가정하고 연구하였다. 본 연구에서 pre-treatment가 Diamond-like Carbon의 stainless steel 합성시 stress와 adhesion에 어떤 효과가 있는지 알아보기 위해, pre-treatment시와 synthesis of DLC film시에 13.56MHz 150W RF플라즈마 화학기상 증착 (RF-PECVD) 법을 통해 합성되었다. pre-treatment시에 H2(80 sccm), O2(10 sccm), N2(20 sccm)의 가스 종류를 다르게 하였고, synthesis of DLC film시에는 CH4 (20 sccm), H2 (80 sccm)가스의 유량을 고정하였다. 합성된 DLC 박막은 Contact Angle Analyze, Raman spectroscopy, Scratch tester를 이용하여 접촉각, D peak Position, G peak Position, ID/IG ratio, 접착력을 측정하였다.

• 대한방사선치료학회지
• /
• 제28권1호
• /
• pp.77-86
• /
• 2016

목 적 : 방사선 치료 시 Carbon Fiber Couch에 의한 감약이 일어난다. 본 연구에서는 치료계획 시스템(Treatment Planning System: TPS)을 이용해 Varian사의 Varian Standard Couch(VSC)를 모델링 하여 유용성을 평가하고자 한다. 대상 및 방법 : 선형가속기(Clinac IX, VARIAN, USA)의 CBCT(Cone Beam Computed Tomography)를 이용하여 VSC의3가지 조건Side Rail Out Grid(SROG), Side Rail InGrid(SRIG), Side Rail In OutSpine Down Bar(SRIOS)로 스캔 한 후 TPS(Pinnacle9.8, Philips, USA)로 전송하여 Side Rail, Side Bar Upper, Side Bar Lower, Spine Down Bar를 Automatic Contouring하여 모델링 하였다. 전산화 단층촬영(Light Speed RT 16, GE, USA)으로 스캔 한 Cheese Phantom(Middelton, USA) 을 TPS로 전송하여 모델링 한 VSC를 적용하였다. 측정 점은 Cheese Phantom내의 Ion Chamber(A1SL, Standard imaging, USA)이며 Isocenter에 위치시켜 Energy(4, 10MV), Gantry Angle($5^{\circ}$간격으로 측정), Field Size($3{\times}3cm^2$, $10{\times}10cm^2$)에 변화를 주어 각 100MU의 동일한 조건에서 얻은 계산 값과 측정값을 비교하였으며 Side Bar Upper에 의한 감약을 비교하기 위해 SRIG조건에서 $127^{\circ}$를 포함하였다. 결 과 : CBCT를 이용해 얻은 VSC의 Density를 TPS에서 확인한 결과 $0.9g/cm^3$였으며 Spine Down Bar의 경우 $0.7g/cm^3$로 나타났다.Side Rail, Side Bar Upper, Side Bar Lower, Spine Down Bar에서 각 17.49%, 16.49%, 8.54%, 7.59%의 감약이 일어났으며모델링의 정확성을 평가하기 위해 계산 값과 측정값을 비교한 결과 평균 1.13%의 오차가 보였으며 Spine Down Bar를 지나는 $170^{\circ}beam$에서 1.98%로 가장 많은오차를 보였다. 결 론 : TPS이용해 모델링 한 VSC의 유용성을 평가하기 위해계산 값과 측정값을 비교한 결과 최대1.98%의 오차를 보였다. 방사선 치료계획 시 VSC를 모델링 하여 적용한다면선량에 대한 예측이 가능해 더욱 정확한 치료를 하는데 도움이 될 것으로 사료된다.

• 대한치과보철학회지
• /
• 제45권3호
• /
• pp.362-374
• /
• 2007

Statement of problem. The intial stability for osseointegration of implant has been an interesting factor. Especially, in the case of poor bone quality or immediately loaded implant, various strategies have been developed focusing on the surface of materials to improve implant fixation to bone. The microscopic properties of implant surfaces play a major role in the osseous healing of dental implants. Purpose. The aims of this study are to perform a histologic and histomorphometric comparison of the healing characteristics of three different surfaces and the comparison of resonance frequency analysis (RFA) values measured by $Osstell^{TM}$ and perio-test values (PTV) measured by Periotest. Material and methods. A total of 24 screw titanium implants (Dentium Co., Seoul, Korea) with 6mm in length and 3.4mm in diameter, were placed in the mandible of 4 beagle dogs. Implants were divided into three groups following the surface treatment methods: Group I is machined(control group). Group II is anodically oxidized. Group III is coated 500nm in thickness with hydroxyapatite(HA) by ion beam assisted deposition(IBAD) on the anodized oxidization. Bone blocks from 2 dogs were caught after 3 weeks of covered healing and another blocks from 2 dogs after 6 weeks. RFA values and PTV were measured right after insertion and at 3 and 6weeks. Histomorphometric analysis was made with Kappa Image Base System to calculate bone-to-implant contact (BIC) and bone area inside the threads. Pearson's correlation analyses were performed to evaluate the correlation between RFA and PTV, BIC and bone area ratio of three different surfaces at 3 and 6 weeks. Results. 1) In all surface treatment methods, the RFA values decreased and the PTV values increased until 6 weeks in comparison to initial values. 2) At 3 weeks, no significant difference was found from bone-to-implant contact ratio and bone area ratio of three different surface treatment methods(P>0.05). However, at 6 weeks, different surface treatment methods showed significantly different bone-toimplant contact ratio and bone area ratio(P<0.05). 3) In the implants with the IBAD on the anodic oxidization, significant difference was found between the 3 weeks and the 6 weeks bone area ratio(P<0.05). 4) Correlation was found between the RFA values and the bone area ratio at 3 and 6 weeks with significant difference(P<0.05). Conclusions. These results indicate that the implants with the IBAD on the anodic oxidization may have a high influence on the initial stability of implant.

• 공업화학
• /
• 제16권4호
• /
• pp.527-532
• /
• 2005

이온성고분자-금속복합체(Ionic Polymer Metal Composites, IPMC)는 전기활성 고분자이며, 낮은 구동전압에서도 큰 변위를 나타내는 유연한 스마트 소재(soft smart material)이다. 이온성고분자-금속복합체의 표면전극 제조는 일반적으로 화학적 환원방법(무전해 전기도금)에 의해 제조되고 있지만, 이러한 방법에서는 그 재료가 다공성 고분자 막으로 표면이 균일한 전극을 제조하기에 어려움이 있다. 본 연구에서는 전극의 표면 저항을 감소시켜 응답속도를 증가시킴과 동시에 낮은 전압에서 큰 변위를 낼 수 있는 IPMC 제조방법을 고안하여 수행하였다. 화학적 환원방법으로 이온고분자-금속 복합체를 형성시킨 후, 이온빔보조증착법(Ion Beam Assisted Deposition)으로 균질한 표면 전극 층을 형성시켜 화학적 특성을 개선하여 전기적 자극에 의한 구동반응 속도를 향상시킬 수 있는 구동체 제조방법을 제안하였다.

• 식물조직배양학회지
• /
• 제26권3호
• /
• pp.197-203
• /
• 1999

수분후 담배의 배에 중이온 beam ($^{14}$ N)을 조사하여 얻은 종자로부터 albino식물체를 분리하여 기내 생장과 분화의 특성을 검토하였다. 기내에서 생장시킨 albino식물체는 엽록소함량이 급격한 감소를 나타내었고 기공수는 잎의 이면 및 표면 표피에서 녹색 식물체 보다 많았다 연속광 조건하의 탄소원을 첨가한 MS배지에서 albino개체는 절간이 신장하지 않았으나 10.0mg/L 의 GA$_3$처리로 절간신장이 회복되었다. 잎절편 배양시 albino식물체는 1.0 mg/L 의 BAP와 kinetin의 단용처리로 다수의 신초를 형성하였고, 1.0mg/L의 2,4-D와 NAA의 단용처리로 다량의 캘러스를 형성하였다. 잎절편에서 유도된 albino 캘러스에 1.0mg/L BAP+0.1mg/L NAA를 혼용처리하면 다수의 식물체가 재분화 되었다. 이와같이 albino 식물체는 다경줄기 형성, 캘러스 형성, 캘러스로부터 재분화율 등이 녹색 식물체와 차이가 없었다. 또한 NAA와 BAP를 혼용처리 하였을 때 잎절편으로부터 기관분화의 유형도 정상주와 비슷하였다. 이러한 결과는 본 albino담배 변이체가 색소체 함량의 급감과 같은 광합성과 관련된 기능에서는 결손을 보이고 있음에도 불구하고 조직수준의 기관분화계에는 이상이 없다는 것을 시사한다.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 하계학술대회 논문집 Vol.4 No.2
• /
• pp.723-727
• /
• 2003

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient and a nonlinear electro-optic coefficient value. In spite of its advantages, SBN has not been investigated well compared to other ferroelectric materials with perovskite structure. In this study, SBN thin film was manufactured by ion beam sputtering technique using the prepared SBN target in $Ar/O_2$ atmosphere. SBN30 thin film of $1000{\AA}$ was pre-deposited as a seed layer on $Pt(100)/TiO_2/SiO_2/Si$ substrate followed by SBN60 deposition up to $3000{\AA}$ in thickness. As-deposited SBN60/SBN30 layer was heat-treated at different temperatures of 650, 700, 750, and $800^{\circ}C$ in air, respectively The crystallinity and orientation behavior as well as electric properties of SBN60/SBN30 multi-layer were examined. The deposited layer was uniform and the orientation was shown primarily along (001) plane from XRD pattern. There was no difference in the crystal structure with heat-treatment temperature, but the electric properties depended on the heating temperature and was the best at $750^{\circ}C$. In electric properties of Pt/SBN60/SBN30/Pt thin film capacitor prepared, the remnant polarization (2Pr) value was $15{\mu}C/cm^2$, the coercive field (Ec) 75 kV/cm, and the dielectric constant 1075, respectively.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2003년도 추계학술대회 논문집 Vol.16
• /
• pp.271-274
• /
• 2003

[ $Sr_xBa_{1-x}Nb_2O_6$ ] (SBN, $0.25{\leq}x{\leq}0.75$) ceramic is a ferroelectric material with tetragonal tungsten bronze (TTB) type structure, which has a high pyroelectric coefficient and a nonlinear electro-optic coefficient value. In spite of its advantages, SBN has not been investigated well compared to other ferroelectric materials with perovskite structure. In this study, SBN thin film was manufactured by ion beam sputtering technique using the prepared SBN target in $Ar/O_2$ atmosphere. SBN30 thin films of different thickness were pre-deposited as a seed layer on $Pt(100)/TiO_2/SiO_2/Si$ substrate followed by SBN60 deposition up to $4500\;{\AA}$ in thickness. As-deposited SBN60/SBN30 layer was heat-treated at different temperatures of 650, 700, 750, and $800\;^{\circ}C$ in air, respectively, The crystallinity and orientation behavior as well as electric properties of SBN60/SBN30 multi-layer were examined. The deposited layer was uniform and the orientation was shown primarily along (001) plane from XRD pattern. There was difference in the crystal structure with heat-treatment temperature, and the electric properties depended on the heating temperature and the seed-layer thickness. In electric properties of Pt/SBN60/SBN30/Pt thin film capacitor prepared, the remnant polarization (2Pr) value was $15\;{\mu}C/cm^2$, the coercive field (Ec) 65 kV/cm, and the dielectric constant 1492, respectively.

• 식물조직배양학회지
• /
• 제25권2호
• /
• pp.103-107
• /
• 1998

중이온 빔을 이용한 방사선 돌연변이의 기초자료를 얻고자 담배의 수분ㆍ수정 직후의 원배에 100 Gy의 중이온빔을 조사하여 $\textrm{M}_{1}$세대의 종자를 얻었다. NaCl 20과 25%를 포함된 MS배지에 $\textrm{M}_{1}$세대의 종자를 파종하여 17개통의 NaCl저항성 식물체를 선발하였다. 저항성 식물체는 BY-4품종에 $^{14}\textrm{N}$빔을 조사한 처리구에서만 관찰되었다. $\textrm{M}_{1}$세대의 저항성 식물체의 경우 영양생장기간 중에는 외형적 변이가 관찰되지 않았으나 생식생장기의 화기에 있어서는 다양한 변이가 관찰되었다. 특히 암술 수술의 길이의 변화, 꽃잎의 변화, 불완전 화분립, 줄기당 꽃의 착생수 감소 등의 변이가 발생하였다. $\textrm{M}_{1}$세대에서 17개의 NaCl저항성 계통 중에서 8계통은 $\textrm{M}_{2}$ 세대에도 저항성형질이 발현되었고, 또한 $\textrm{M}_{2}$세대의 3계통은 Mannitol이 포함된 배지에서 저항성을 보여주었다.