Mixed-mode interlaminar fracture toughness of carbon fabric/epoxy composites, which are applicable to tilting train carbody, was evaluated through the MMB (Mixed-mode bending) test. Specimens were made of CF3327 plain woven fabric with epoxy and a starter delamination at one end was made by inserting Teflon film with the thickness of 12.5 μ m. Mixed-mode interlaminar fracture test was conducted for 6 types of specimens with the mode II ratio of 20 ,35, 50, 65, 80, 90%. Also crack propagating behaviors and fractured surfaces were examined through an optical travelling scope and a scanning electron microscope, respectively.

• Journal of the Korean Society for Railway
• /
• v.8 no.2
• /
• pp.195-201
• /
• 2005

Mode II interlaminar fracture behaviors of carbon fabric/epoxy composites, which are applicable to tilting train carbodies, was investigated by the ENF (End notched flexure) test. The specimens were made of CF3327 plain woven fabric with epoxy and a starter delamination at one end was made by inserting Teflon film with the thickness of 12.5$mu$m or 25.0$mu$m. The equation for mode II interlaminar fracture toughness was suggested based on the effective crack length from the compliance of load-displacement curve. Mode II interlaminar fracture toughness was evaluated for several types of the specimens. Also crack propagating behaviors and fracture surfaces were examined through an optical travelling scope and a scanning electron microscope.

• International Journal of Aeronautical and Space Sciences
• /
• v.12 no.2
• /
• pp.115-133
• /
• 2011

Fiber reinforced polymer composites (FRPs) are being increasingly used for a wide range of engineering applications owing to their high specific strength and stiffness. However, their through-the-thickness performance lacks some of the most demanding physical and mechanical property requirements for structural applications, such as aerospace vehicles and military components. Carbon nanotubes (CNTs) and carbon nanofibers (CNFs), due to their excellent mechanical, thermal and electrical properties, offer great promise to improve the weak properties in the thickness direction and impart multi-functionality without substantial weight addition to FRPs. This paper reviews the progress made to date on i) the techniques developed for integration of CNTs/ CNFs into FRPs, and ii) the effects of the addition of these nanofillers on the interlaminar properties, such as such interlaminar shear strength, interlaminar fracture toughness and impact damage resistance and tolerance, of FRPs. The key challenges and future prospects in the development of multiscale CNT-FRP composites for advanced applications are also highlighted.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.8 no.5
• /
• pp.425-434
• /
• 1984

The concept of intermittent interlaminar bonding is investigated as a means of improving the fracture toughness of cross-ply Gr/Ep composites without significant loss of tensile strength and modulus. The concept of linear elastic fracture mechanics(LEFM)is used to study the effects of strong bonded area and bonding composites. The experimental results indicate that the fracture toughness and notch strength of intermittent interlaminar bonded composities are improved and the tensile strength only decreased by 3-8% in comparison to those of the fully bonded composites. Damage zones around the crack tip are detected by the modified X-Ray non-destructive testing technique and the fractography. The improvement of toughness is explained based on the damage zones. The mechanisms of damage zone are shown to be caused by subcrack along the fiber on the 0.deg. ply, matrix cracking along the fiber on the 90.deg. ply, interlaminar delamination, and ply pull-out of the 0.deg. ply.

• Composites Research
• /
• v.17 no.1
• /
• pp.29-37
• /
• 2004

Honeycomb sandwich composite(HSC) structures have been widely used in aircraft and military industry owing to their light weight and high stiffness. Mechanical properties of honeycomb core materials are needed for accurate analysis of the sandwich composites. In this study. theoretical formula for effective elastic modulus and Poisson's ratio of honeycomb core materials was established using an energy method considering the bending, axial and shear deformations of honeycomb core walls. Finite-element analysis results obtained by using commercial FEA code, ABAQUS 6.3 were comparable to the theoretical ones. In addition, we performed tensile test of HSC plates and analyzed deformation behaviors and interlaminar stresses through its FEA simulation. An increased shear stress along the interface between surface and honeycomb core layers was shown to be the main reason for interfacial delamination in HSC plate under tensile loading.

• Journal of the Korean Society of Safety
• /
• v.25 no.3
• /
• pp.34-39
• /
• 2010

Unidirectional Carbon Fiber Reinforced Plastics (CFRP) are advanced materials which combine the characteristics of the light weight, high stiffness and strength. For those reasons, the use of the unidirectional CFRP has increased in jet fighters, aerospace structures. However, unidirectional CFRP composites have a lot of problems, especially delamination, compared with traditional materials such as steels and aluminums, and so forth. Therefore, the interlaminar fracture toughness for a laminate CFRP composite is very important. In this study, The mode II interlaminar fracture toughness was measured by using center notched flexure(CNF) test specimen. The CNF specimens using unidirectional carbon prepreg were fabricated by a hot-press with the gage pressure and temperature controller. And three kinds of a/L ratio was applied to these specimens. Here, we discuss the relations of the crack growth and the mode II interlaminar fracture under the four point bending CNF test. From the results, we shows that mode II interlaminar was occurred when the more $a_0$/L ratio, the less load. And $G_{IIC}$ also were obtained as 5.33, 2.9 and $0.58kJ/m^2$ according to $a_0$/L ratio=0.2, 0.3 and 0.4.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.12 no.5
• /
• pp.944-951
• /
• 1988

Global-Local Laminate Variational Model is utilized to investigate the characteristics of interlaminar stresses in thick composite laminates under uniform axial extension. Various laminates with different fiber orientation and stacking sequences are analyzed to observe the behavior of interlaminar normal stresses. From this result, the interlaminar normal stress distribution along the laminate interfaces is examined and discussed with an existing approximation model. The repeated stacking of Poisson's ratio symmetric sublaminates is found to be the best stacking method of thick composite laminates to reduce the interlaminar normal stresses for the prevention of the free-edge delamination.

• Journal of the Korean Society for Aeronautical & Space Sciences
• /
• v.41 no.8
• /
• pp.665-672
• /
• 2013

One of the major causes of stiffness and strength degradations in laminated composite structures is the delamination between composite layers. In most engineering applications, laminated composite structures have certain curvatures. If the curved composite structure is subjected to bending that tends to flatten the composite structures, through the thickness stresses can be generated in the thickness direction of the composites. Under normal operation open mode delamination could occur at the sites of peak interlaminar stress. This paper describes a technique to determine radial direction stress of a laminated composite structure using a curved beam. Stacking sequence effects of interlaminar stress were studied. The radial location and intensity of the open mode delamination stress were calculated and compared with the results obtained from the analytical solution and finite element method.

• Journal of the Korean Society for Precision Engineering
• /
• v.22 no.2
• /
• pp.164-171
• /
• 2005

This study aims to examine an effect of stacking sequence and curvature on the penetration characteristic of a composite laminated shell. For the purpose, we manufactured specimens with different stacking sequences and curvatures, and conducted a penetration test using an air-gun. To examine an influence according to stacking sequence, as flat plate and curvature specimen had more plies, their critical penetration energy was higher, Critical penetration energies of specimen A and C with less interfaces somewhat higher than those of B and D with more interfaces. The reason that with less interfaces, critical penetration energy was higher is pre-impact bending stiffness of composite laminated shell with less interfaces was lower than that of laminated shell with more interfaces, but bending stiffness after impact was higher. And it is because interface, the weakest part of the composite laminated shell, was influenced by transverse impact. As curvature increases, critical penetration energy increases linearly. It is because as curvature increases, resistance to in-plane deformation as well as bending deformation increases, which need higher critical penetration energy. Patterns of cracks caused by penetration of composite laminated shells include interlaminar crack, intralaminar crack, and laminar fracture. A 0$^{\circ}$ply laminar had a matrix crack, a 90$^{\circ}$ply laminar had intralaminar crack and laminar fracture, and interface between 0$^{\circ}$and 90$^{\circ}$laminar had a interlaminar crack. We examined crack length and delamination area through a penetration test. For the specimen A and C with 2 interface, the longest circumferential direction crack length and largest delamination area were observed on the first interface from the impact point. For the specimen B and D with 4 interface, the longest crack length and largest delamination area were observed on the third interface from the impact point.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.21 no.2
• /
• pp.317-326
• /
• 1997

An investigation was performed to study the matrix cracking and delamination in laminated composite plates due to transverse impact. A model was developed for predicting the initiation of the matrix cracking and the shape and size of impact-induced delamination in laminated composite plates resulting from the ballistic impact. The model consists of a stress analysis and a failure analysis. A transient finite element analysis which was based on the higher-order shear deformation theory was adopted for calculating the stresses inside the laminated composite plates during impact. A failure analysis was used to predict the initial intraply matrix cracking and the shape and size of the interface delamination in the laminates. As a results, a shear matrix cracking which was governed by the transverse interlaminar shear stress occured at the middle layer near the midplane of laminates and a bending matrix cracking which was governed by the transverse inplane stress occured at the bottom layer near the surface of laminates. In a thick laminates, a shear matrix cracking generated first at the middle layer of laminates, but in a thin laminates, a bending matrix cracking generated first at the bottom layer of laminates.