• Tunnel and Underground Space
• /
• v.5 no.3
• /
• pp.240-250
• /
• 1995

Microcrack development in the macheon gabbro, the Sangju sandstone and the Jungsun marble due to fatigue stresses was investigated using differential strain analysis and microscopic observations from fluorescent-dyed thin sections. In the Macheon gabbro, various types of cracks, including gran boundary cracks, cleavage cracks, intragranular cracks adn intergranular cracks were developed. However, only grain boundary cracks were produced in the Sangju sandstone and the Jungsun marble due to fatigue stress. Many microcracks were produced due to fatigue stresses in the macheon gabbro. However, few microcracks were produced in the Sangju sandstone and the Jungsun marble. Fatigue stresses produced new microcracks in the Junngsun marble and the Macheon gabbro, but only pre-existing grain boundary cracks were lengthened in the Sangju snadstone. Most microcracks were produced within a few tens of numbers of cyclic loading, indicating that rocks under fatigue stresses will be damaged at the early stage of cyclic loading.

• Nuclear Engineering and Technology
• /
• v.51 no.5
• /
• pp.1381-1389
• /
• 2019

Stress corrosion cracking (SCC) widely found in both primary and secondary sides of steam generator (SG) tubing in pressurized water reactors (PWR) has become an important safety issue. Using eddy-current tests (ECTs), non-destructive evaluations are performed for the integrity management of SG tubes against intergranular SCC. To enhance the reliability of ECT, this study investigates the effects of oxide films on ECT's detection capabilities for SCC in laboratory-degraded SG tubing in high temperature and high pressure aqueous environment.

• Journal of the Korean Society of Industry Convergence
• /
• v.23 no.1
• /
• pp.73-81
• /
• 2020

This study analyzed the causes of failure of SCM435 bolts that fix the springs of automobile air brakes that have been fractured during use. The cause of failure was analyzed using SEM, EDS, metallogical microscope and Vickers hardness tester. In the fracture, the ratchet mark began at the outer boundary of crack origin, and the grains at crack origin were found to have clear intergranular corrosion. One SCM435 bolt was subjected to a stress of 398 MPa, it's a stress of about 80% of the fatigue limit. As a result of such a large applied stress, cracks occurred at the corrosion origin and were fractured. In order to prevent the SCM435 bolt from fracture, it is necessary to use the correct composition, the accuracy of heat treatment, preventing damage by external impact, preventing corrosion of the damage part by moisture, and introduction a compressive residual stress by peening.

• Journal of the Korean Society for Heat Treatment
• /
• v.10 no.3
• /
• pp.198-208
• /
• 1997

The-steady-state creep mechanism and behavior of Zircaloy-4 used as cladding materials in PWR have been investigated in air environment over the temp, ranges from 600 to $645^{\circ}C$ and stress ranges from 4 to $7kg/mm^2$. The stress exponents for the creep deformation of this alloy, n were decreased 4.81, 4.71, 4.64, and 4.56 at 600, 615, 630 and $645^{\circ}C$, respectively; the stress exponents decreased with increasing the temperature and got closer to about 5. The apparent activation energies, Q, were 62.1, 60.0, 57.9 and 55.4 kcal/mole at stresses of 4, 5, 6, $7kg/mm^2$, respectively; the activation energies decreased with increasing the stress and were close to those of volume self diffusion of Zr in Zr-Sn-Fe-Cr system. In results, it can be considered that the creep deformation for Zircaloy-4 was controlled by the dislocation climb over the ranges of this experimental conditions. Larson-Miller parameter, P, for the crept specimens was obtained as P=(T+460)(logt,+23). The failure plane observed by SEM slightly showed up intergranular fracture at this experiment ranges. However, it was essentially dominated by the dimple phenomenon, which was a characteristics of the transgranular fracture.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.6 no.2
• /
• pp.34-41
• /
• 2010

This work is concerned with the analysis of stress corrosion cracking(SCC) behavior of Alloy 600 nozzle penetration mock-up according to a residual stress induced by a dissimilar metal welding(DMW) in a nuclear reactor pressure vessel. The effects of the dimension and materials of the nozzle penetration on the deformation and the residual stress induced by DMW were investigated using a finite element analysis(FEA). The inner diameter(ID) change of the nozzle by DMW and its dependance on the design variables, calculated by FEA, were well consistent with those measured from the mock-up. Accelerated SCC tests were performed for three mock-ups with different wall thicknesses in a highly acidic solution to investigate mainly the effect of the residual stress on the SCC behavior of Alloy 600 nozzle. From a destructive examination of the mock-up after the tests, the SCC behavior of the nozzle was fairly related with the residual stress induced by DMW : axial cracks were found in the ID surface of the nozzle within the J-weld region where the highest tensile hoop stress was predicted by FEA, while circumferential cracks were observed beyond both J-weld root and toe where the highest tensile axial stress was expected.

• Proceedings of the Korean Nuclear Society Conference
• /
• 1996.05c
• /
• pp.145-150
• /
• 1996

Acoustic Emission (AE) technique was applied to stress corrosion cracking of Inconel 600 to investigate the AE capability of detecting crack growth and to obtain the relation between AE characteristics and crack mechanism. The specimens were heat-treated in two conditions (600$^{\circ}C$ for 30 hrs or 700 $^{\circ}C$ for 1 hr) and undergone CERT at two extension rates ( 2.5${\times}$10$^{-5}$ or 1.25${\times}$10$^{－4}$(mm/s)). It was found that the AE peak amplitude from plastic deformation was generally smaller than about 48dB (0.25mV), while Intergranular stress corrosion cracking (IGSCC) and ductile fracture produced higher values of 49 to 70dB (0.3mV to 3mV). The slopes of cumulative amplitude distribution (b-values) were linearly dependent on IGSCC susceptibility and the higher the susceptibility, the smaller the b-value. The monitoring of combined AE parameters such as event rate, amplitude, count and energy can provide effective means to clearly identify the transition from crack initiation and small crack growth to rapid growth of dominant cracks.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.19 no.4
• /
• pp.1-8
• /
• 2020

Mechanical components that support structures in aerospace and power generation industries require high-strength materials. Particularly, in the aerospace industry, aluminum alloys, titanium alloys, and composite materials are increasingly used due to their high maneuverability and durability to withstand low temperature extreme environments; however, ultra-high-strength steel is still used in key components under heavy loads such as landing gears. In this paper, the fault cause analysis and troubleshooting of aircraft parts made of ultra-high-strength steel (300M) broken during normal operation are described. To identify the cause of the defect, a temporary inspection of the same aircraft was performed, and material testing, non-destructive inspection, microstructure examination, and fracture area inspection of the damaged parts were performed. Fracture analysis results showed that a crack in the shape of a branch developed from the tool mark in the direction of the intergranular strain. Based on the results, the cause of fracture was confirmed to be stress corrosion.

• Nuclear Engineering and Technology
• /
• v.50 no.1
• /
• pp.1-17
• /
• 2018

This article reviews the multiscale nature of stress corrosion cracking (SCC) observed by high-resolution characterizations in austenite stainless steels and Ni-base superalloys in light water reactors (including boiling water reactors, pressurized water reactors, and supercritical water reactors) with related opinions. A new statistical summary and comparison of observed degradation phenomena at different length scales is included. The intrinsic causes of this multiscale nature of SCC are discussed based on existing evidence and related opinions, ranging from materials theory to practical processing technologies. Questions of interest are then discussed to improve bottom-up understanding of the intrinsic causes. Last, a multiscale modeling and simulation methodology is proposed as a promising interdisciplinary solution to understand the intrinsic causes of the multiscale nature of SCC in light water reactors, based on a review of related supporting application evidence.

• Korean Journal of Materials Research
• /
• v.26 no.7
• /
• pp.353-358
• /
• 2016

The hydrogen embrittlement of two austenitic high-manganese steels was investigated using tensile testing under high-pressure gaseous hydrogen. The test results were compared with those of different kinds of austenitic alloys containing Ni, Mn, and N in terms of stress and ductility. It was found that the ultimate tensile stress and ductility were more remarkably decreased under high-pressure gaseous hydrogen than under high-pressure gaseous argon, unlike the yield stress. In the specimens tested under high-pressure gaseous hydrogen, transgranular fractures were usually observed together with intergranular cracking near the fracture surface, whereas in those samples tested under high-pressure gaseous argon, ductile fractures mostly occurred. The austenitic high-manganese steels showed a relatively lower resistance to hydrogen embrittlement than did those with larger amounts of Ni because the formation of deformation twins or microbands in austenitic high-manganese steels probably promoted planar slip, which is associated with localized deformation due to gaseous hydrogen.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.24 no.3 s.174
• /
• pp.603-612
• /
• 2000

Corrosion characteristics on the 12Cr alloy steel of turbine blade was electro-chemically investigated in 3.5wt% NaCI and 12.7wt% Na2S04 solution, respectively. Electro-chemical polarization test, Huey test and Oxalic acid etching test were previously conducted to estimate corrosion susceptibility of the material. And, using the horizontal corrosion fatigue tester, corrosion fatigue characteristics of 12Cr alloy steel in distilled water, 3.5wt% NaCI solution, and 12.7wt%(1M) Na2S04 solution were also fracture-mechanically estimated and compared their results. Parameter considered was room temperature, 60'C and 90'C. Corrosion fatigue crack length was measured by DC potential difference method.Obtained results are as follows,1) 12Cr alloy steel showed high corrosion rate in 3.5wt% NaCI solution and Na2S04 solution at high tempratue.2) Intergranular corrosion sensitivity of 12 Cr alloy was smaller than austenitic stainless steel.3) Corrosion fatigue crack growth rate in 3.5wt% NaCI and 12.7wt%(IM) Na2S04 solution is entirely higher than in the distilled water, and also increased with the temperature increase.