• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2016.05a
• /
• pp.34-35
• /
• 2016

Most of the construction adhesive may contain harmful component to the human body with an organic adhesive. In addition, when the adhesive caused hydroquinone, alkyl benzophenone, etc, also it raises the skin diseases to workers. Therefore, the inorganic adhesive development is necessary. This study was a study to know adhesive strength properties that adhesive using a magnesium oxide according to the addition ratio of the retarder. It has experiments to two types of magnesium oxide and type and ratio of retarder differently.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2018.11a
• /
• pp.48-49
• /
• 2018

Recently the old buildings have been increasing and increasing reconstruction. As a result, the frequency of use of architectural adhesives has increased. Adhesives are not only used for bonding but also for building materials used in various fields. However, since the adhesive is made of an organic material, it causes various skin diseases and sick house syndrome, and when a fire occurs, harmful substances are generated, and incomplete combustion may cause personal injury. Therefore, in this study, to solve the disadvantages of conventional adhesives, we tried to develop inorganic adhesives using inorganic materials.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2013.05a
• /
• pp.78-79
• /
• 2013

As a part of study to maximize the amount used of the ground granulated blast-furnace slag, the study deals with setting properties of paste that is mixed the ground granulated blast-furnace slag with CaO-Al₂O₃ based inorganic blinder. The results of the experiment show that the setting time is most fast in the mix of 25% rate of CaO-Al₂O₃ based inorganic blinder. It is generally needed 2 hours for work time in precast concrete products. In this study, this requirement is achieved when using the retarder of 0.5%.

• Journal of the Korean Ceramic Society
• /
• v.39 no.4
• /
• pp.401-408
• /
• 2002

The influence of $H_3BO_3$ in one of inorganic retarder for the hydration of OPC was investigated. The shape of needdle Ettringite formed in few minitues for a no addition of $H_3BO_3$ but, retarded to form of Ettringite and $Ca(OH)_2$ according to addition of $H_3BO_3$. Hydration was retarded for tranquil of Al ion by to be low of pH.

• Journal of Ceramic Processing Research
• /
• v.19 no.5
• /
• pp.407-412
• /
• 2018

In this study, we have made a cement based inorganic insulation material and added CSA (Hauyne Clinker) to reduce the demolding time and enhance the handling workability. CSA contents were varied by 0%, 1%, 3%, 5% and the atmospheric steam curing was tried for enhancing the compressive strength. As the CSA contents are increased to 5%, a rapid reaction of hydration caused the sinking of the slurry. So, the setting-retarder was added to control the reaction of hydration. By this, the sinking of the slurry was controlled but the height of the green body after expansions was a little bit lowered. In the CSA-added slurry, it was possible to demold within 24 hours and in case of CSA 5%-added, the sufficient workability was secured. Atmospheric steam curing (temperatures $-40{\sim}80^{\circ}C$, for 6~10 hrs.) was attempted to improve the compressive strength and found that an excellent strength of 0.25 MPa was achieved at $80^{\circ}C$ for 8 hrs. Specific gravity was about $0.12{\sim}0.13g/cm^3$ and heat conductivity was about 0.045 W/mK in all specimens. This strategy significantly improves the compressive strength of CSA 5%-added specimen up to 25% compared to without CSA added specimen.

• Journal of the Korean Ceramic Society
• /
• v.56 no.5
• /
• pp.468-473
• /
• 2019

This study focused on manufacturing an inorganic insulation material set with various amounts of calcium-sulfoaluminate (CSA) (hauyne) content for enhancing both workability (demolding, handling) and the high thermal insulating property. To carry out the experiment, the amounts of CSA utilized were 5%, 10%, 15%, and 20%, with anhydrous gypsum added in equal proportion to produce a stable formation. As the content of CSA increased, a sinking phenomenon occurred because of the hydration reaction from the slurry, so it was difficult to utilize a retarder normally used in the cement manufacturing process. However, an RCOOM surfactant was able to solve the local clumping problem from cement and CSA and obtain a rapid retarding effect, so it was included in this process at 0.3%. Furthermore, the cement fineness was not 7000 ㎠/g but rather 3300 ~ 4000 ㎠/g to prevent a rapid temperature increase in the slurry. The specific gravity of the sample manufactured with 20% CSA was approximately 0.11 g/㎤, and its thermal conductivity was 0.041 W/m·K, providing an excellent insulating property.

• Journal of the Korea Institute of Building Construction
• /
• v.19 no.4
• /
• pp.289-297
• /
• 2019

Epoxy resin adhesives are currently used as adhesives in buildings. Epoxy resin adhesives, which are organic materials, generate harmful substances when producing adhesives, and toxic substances are high in the residential space after installation. In addition, a large amount of carbon monoxide generated from organic materials in the case of a building fire leads to personal injury. This study evaluates the feasibility of inorganic adhesives using pure inorganic materials such as magnesia, phosphate, and borax as inorganic adhesives to replace existing organic adhesives. As a result of the experiment on the selection of adequate phosphate and the characteristics of the addition rate of borax used as a retarder, the potassium phosphate monobasic was obtained as a suitable phosphate and the characteristics according to the borax addition rate were compared with the quality standard of KS F 4923 The hardening shrinkage and heat change rate satisfied the quality standards. The tensile strength was satisfactory when the borax addition rate was 4% or more, but the adhesive strength did not meet the quality standards. Further studies are needed to improve adhesion strength.

• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.8 no.2
• /
• pp.343-349
• /
• 1998

The effect of pH on the dehydration reaction of $TiCL_4$ solution. KOH and HC1 were used as a accelerater and retarder in dehydration. Results are follow. Neutralization point is pH 7.4 in the system of $TiCL_4$- KOH and the production which is produced at acidic side is Ti -gel of poly metatitanic acid. The production which is produced at alkalic side is aligomer and crystalline potasium titanate is not detected.

• Journal of the Korean Ceramic Society
• /
• v.33 no.3
• /
• pp.307-312
• /
• 1996

In following addition of 0.3, -0.6, 0.8, 1.0 and 5 weight percent MgSiF66H2O studies have been made of the setting and hardening characteristics of ordinary portland cement. MgSiF66H2O retarded the setting time of ordinary portland cement and extended the induction pariod of the hydration. In ordinary portland cement the setting characteristics were drastically altered especially at high MgSiF66H2O contents. Evidence was also obtained by the formation of a KSiF6 which was very fine particle. The results wee as follows. 1. Slump was slightly decreased when MgSiF66H2O added. 2. Setting time was retarded depending on the amount of retarding agent 2 to 8 hours 3. Compressive strength was almost same or some increased in comparision with opc. 4. When MgSiF66H2O was added to cement paste K2SiF6 were formed It was fine-sized distributed uniformly in cement grain and caused retardation of cement setting.