• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2008년도 추계학술대회 논문집 Vol.21
• /
• pp.260-261
• /
• 2008

In this study, we investigated the properties of Indium Zinc Oxide (IZO) films prepared in facing targets sputtering (FTS) system at room temperature as function of oxygen contents. As as-deposited films were rapidly thermal annealing on air atmosphere of $400^{\circ}C$ for 30s. As a result, the transmittance of IZO films increased with increasing oxygen flow in the visible range. After rapidly thermal annealing to films, the optical properties of films improved than films deposited at R.T, but the electrical properties decreased. Before RTA treatment, the lowest resistivity IZO is $5.4\times10^{-4}[\Omega{\cdot}cm]$ at oxygen gas flow. But, after RTA treatment, IZO films have the value of lowest resistivity at the lower oxygen gas ratio in compare with before RTA treatment. The resistivity of IZO films is $7.29\times10^{-4}[\Omega{\cdot}cm]$ at pure argon atmosphere.

• 전기학회논문지
• /
• 제59권11호
• /
• pp.2016-2020
• /
• 2010

Indium-zinc-oxide (IZO) films were deposited at room temperature via RF sputtering with varying the flow rate of additive nitrogen gas ($N_2$). Thin film transistors (TFTs) with an inverted staggered configuration were fabricated by employing the various IZO films, such as $N_2$-added and pure (i.e., w/o $N_2$-added), as active channel layers. For all the deposited IZO films, effects of additive $N_2$ gas on their deposition rates, electrical resistivities, optical transmittances and bandgaps, and chemical structures were extensively investigated. Transfer characteristics of the IZO-based TFTs were measured and characterized in terms of the flow rate of additive $N_2$ gas. The experimental results indicated that the transistor action occurred when the $N_2$-added (with $N_2$ flow rate of 0.4-1.0 sccm) IZO films were used as the active layer, in contrast to the case of using the pure IZO film.

• 한국전기전자재료학회논문지
• /
• 제30권7호
• /
• pp.432-436
• /
• 2017

IZO transistors with $Al_2O_3$ as gate dielectrics have been investigated. To improve permittivity in an ambient dielectric layer, we grew $Al_2O_3$ by atomic layer deposition directly onto the substrates. Then, we prepared IZO semiconductor solutions with 0.1 M indium nitrate hydrate [$In(NO_3)_3{\cdot}xH_2O$] and 0.1 M zinc acetate dehydrate [$Zn(CH_3COO)_2{\cdot}2H_2O$] as precursor solutions; the IZO solution made with a molar ratio of 7:3 was then prepared. It has been found that these oxide transistors exhibit low operating voltage, good turn-on voltage, and an average field-effect mobility of $0.90cm^2/Vs$ in ambient conditions. Studies of low-voltage driving of IZO transistors with atomic layer-deposited high-k $Al_2O_3$ as gate dielectric provide data of relevance for the potential use of these materials and this technology in transparent display devices and displays.

• 한국전기전자재료학회논문지
• /
• 제30권8호
• /
• pp.484-490
• /
• 2017

We investigated the rewritable operation of a non-volatile memory device composed of Al (top)/$TiO_2$/indium-zinc-oxide (IZO)/Al (bottom). The oxygen-deficient IZO layer of the device was spin-coated with 0.1 M indium nitrate hydrate and 0.1 M zinc acetate dehydrate as precursor solutions, and the $TiO_2$ layer was fabricated by atomic layer deposition. The oxygen vacancies IZO layer of an active component annealed at $400^{\circ}C$ using thermal annealing and it was proven to be in oxygen vacancies and oxygen binding environments with OH species and heavy metal ions investigated by X-ray photoelectron spectroscopy. The device, which operates at low voltages (less than 3.5 V), exhibits non-volatile memory behavior consistent with resistive-switching properties and an ON/OFF ratio of approximately $3.6{\times}10^3$ at 2.5 V.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2007년도 춘계학술대회A
• /
• pp.215-219
• /
• 2007

In this work, the indium zinc oxide (IZO) films had been deposited on the glass substrate coated with the SiO film. Based on a comparative investigation of the IZO monolayer and IZO/SiO multilayer, it is shown that the thickness of SiO film has a great effect on the mechanical properties of the thin films. The AFM images of the IZO thin film included the SiO film were shown smoother surfaces than monolayer. Resistivity was in inverse proportion to Mobility. If it deposited the SiO film on the substrate, the layer of change was generated between two layer(SiO and substrate). The layer of change influenced resistance because of oxygen content was more than the IZO monolayer.

• 공업화학
• /
• 제17권6호
• /
• pp.644-647
• /
• 2006

Indium zinc oxide (IZO) 박막이 radio frequency reactive magnetron sputtering 방법을 이용하여 증착되었으며 여러 가지 공정변수 중에서 $O_{2}$ 농도와 증착 후에 열처리 온도를 선택하여 박막의 광학적, 전기적 그리고 구조적인 특성을 조사하였다. $O_{2}$ 농도가 증가할수록 IZO 박막의 증착속도는 감소하였고 저항도는 증가하였으며 투과도는 약간 증가하는 경향을 보였다. Atomic force microscopy 분석의 결과로부터, 순수한 아르곤에서 증착된 박막의 표면이 가장 거칠었고 $O_{2}$가 첨가된 조건에서 증착된 박막들은 덜 거칠었다. 순수한 아르곤의 조건에서 증착된 IZO 박막들을 각각 250, 350, 그리고 $450^{\circ}C$에서 열처리하였다. 투과도와 저항도는 순수한 아르곤 조건에서 증착된 시료에서 가장 낮게 나타났고 $250^{\circ}C$의 열처리 온도까지 낮은 저항도가 유지되었다. 박막의 표면은 높은 온도에서 열처리된 시료일수록 더 매끄러운 표면을 가졌다. X-ray diffraction 결과를 통해서 높은 온도에서 열처리된 시료일수록 박막의 결정화가 잘 이루어진 것을 알 수 있었다.

• 한국표면공학회지
• /
• 제41권1호
• /
• pp.6-11
• /
• 2008

An Indium Zinc Oxide(IZO) transparent conductive layer was deposited on a large size glass substrate by using magnetron dc sputtering method with varying a deposition temperature. As the deposition temperature decreased to a room temperature, the sheet resistance of IZO film increased. But this deposition temperature range is included in an applicable to a device. From a standpoint of the sheet resistance, the differences of the sheet resistance were not great and the uniformity of the layer was uniformed around 10%. Crystallization particles were shown on the surface of the layer as deposition temperature increased, but these particles were not shown on the surface of the layer as deposition temperature decreased to the room temperature. It didn't make a scrap of difference in a transmittance of varying deposition temperature. Therefore, it is concluded that IZO thin film manufactured by the room temperature deposition condition can be used as a large size transparent conductive layer of a liquid crystal display device.

• 한국전기전자재료학회논문지
• /
• 제19권5호
• /
• pp.442-449
• /
• 2006

Electrical, optical, and structural properties of indium zinc oxide (IZO) films grown by a box cathode sputtering (BCS) were investigated as a function of oxygen flow ratio. A sheet resistance of $42.6{\Omega}/{\Box}$, average transmittance above 88% in visible range, and root mean spare roughness of $2.7{\AA}$ were obtained even in the IZO layers grown at room temperature. In addition, it is shown that electrical characteristics of the top-emitting organic light emitting diodes (TOLEDs) with the BCS grown-IZO top cathode layer is better than that of TOLEDs with DC sputter grown IZO top cathode, due to absence of plasma damage effect. Furthermore the effects of oxygen flow ratio in IZO films are investigated, based on x-ray photoelectron spectroscopy (XPS), ultra violet/visible (UV/VIS) spectro-meter, scanning electron microscopy (SEM), and atomic force microscopy (AFM) analysis results.

• 한국진공학회:학술대회논문집
• /
• 한국진공학회 2016년도 제50회 동계 정기학술대회 초록집
• /
• pp.278-278
• /
• 2016

Solution-processed metal-oxide semiconductors have been considered as the next generation semiconducting materials for transparent and flexible electronics due to their high electrical performance. Moreover, since the oxide semiconductors show high sensitivity to light illumination and possess persistent photoconductivity (PPC), these properties can be utilized in realizing optical memory devices, which can transport information much faster than the electrons. In previous works, metal-oxide semiconductors are utilized as a memory device by using the light (i.e. illumination does the "writing", no-gate bias recovery the "reading" operations) [1]. The key issues for realizing the optical memory devices is to have high photoconductivity and a long life time of free electrons in the oxide semiconductors. However, mono-layered indium-zinc-oxide (IZO) and mono-layered indium-gallium-zinc-oxide (IGZO) have limited photoconductivity and relaxation time of 570 nA, 122 sec, 190 nA and 53 sec, respectively. Here, we boosted up the photoconductivity and relaxation time using a double-layered IZO/IGZO active layer structure. Solution-processed IZO (top) and IGZO (bottom) layers are prepared on a Si/SiO2 wafer and we utilized the conventional thermal annealing method. To investigate the photoconductivity and relaxation time, we exposed 9 mW/cm2 intensity light for 30 sec and the decaying behaviors were evaluated. It was found that the double-layered IZO/IGZO showed high photoconductivity and relaxation time of 28 uA and 1048 sec.

• Journal of Information Display
• /
• 제13권3호
• /
• pp.113-118
• /
• 2012

Metal oxide semiconductors were considered promising materials as backplanes of future displays. Moreover, the adoption of carrier-suppressing metal into indium-zinc oxide (IZO) has become one of the most important themes in the metal oxide research field. In this paper, efforts to realize and optimize IZO with diverse types of carrier suppressors are summarized. Properties such as the band gap of metal in the oxidized form and its electronegativity were examined to confirm their relationship with the metal's carrier-suppressing ability. It was concluded that those two properties could be used as indicators of the carrier-suppressing ability of a material. As predicted by the properties, the alkali earth metals and early transition metals used in the research effectively suppressed the carrier and optimized the electrical properties of the metal oxide semiconductors. With the carrier-suppressing metals, IZO-based thin-film transistors with high (above $1cm^2/V{\cdot}s$) mobility, a lower than 0.6V/dec sub-threshold gate swing, and an over $3{\times}10^6$ on-to-off current ratio could be achieved.