• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.5
• /
• pp.256-261
• /
• 2009

Hydrophilic and transparent $TiO_2$ thin film was fabricated by sol-gel method and the properties of contact angle, surface morphology, and transmittance were measured. In addition, surfactant Tween 80 was used for increasing the hydrophilic property of thin film. When the contents of Tween 80 in $TiO_2$ solution was 0, 10, 30, 50wt%, the contact angles of $TiO_2$ thin film were $41.4^{\circ}$, $18.2^{\circ}$, $16.0^{\circ}$, $13.2^{\circ}$, respectively. Fabricated $TiO_2$ thin film showed the photocatalytic property that decomposed methylene blue and decreased the absorbance of solution after UV irradiation. $TiO_2$ thin films fabricated with the solution of 30 wt% Tween 80 were deposited on glass (bare), antimony tin oxide (ATO), fluorine tin oxide (FTO), indium tin oxide (ITO) coated glass substrates, and the contact angle and transmittance of thin film was measured. The contact angles of thin films deposited on four substrates were $16.2\sim27.1^{\circ}$ and was decreased to the range of $13.2\sim17.6^{\circ}$ after UV irradiation, Especially, the thin films coated on ATO and FTO glass substrate showed high transmittance of 74.6% in visible range, respectively, and low transmittance of 54.2% and 40.4% in infrared range, respectively.

• Journal of the Korean Ceramic Society
• /
• v.31 no.11
• /
• pp.1315-1322
• /
• 1994

In this study, stable PbTiO3 coating solution was prepared using diethanolamine(DEA) complexing agent and deposited on indium-tin oxide(ITO) coated glass substrate. Prepared thin films were dense and crack-free. Perovskite-type PbTiO3 thin films could be obtained above 50$0^{\circ}C$, while the films heat-treated above $650^{\circ}C$ showed undesired properties due to interface reactions between films and substrates and warpage phenomena of substrates. Measured maximum dielectric constant and loss tangent were found to be 144 and 0.0163 at 1 kHz, 55$0^{\circ}C$ heat-treatment, respectively.

• Korean Journal of Materials Research
• /
• v.18 no.10
• /
• pp.521-528
• /
• 2008

We present the structural, optical, and electrical properties of amorphous silicon suboxide (a-$SiO_x$) films grown on indium tin oxide glass substrates with a radio frequency magnetron technique from a polycrystalline silicon oxide target using ambient Ar. For different substrate-target distances (d = 8 cm and 10 cm), the deposition temperature effects were systematically studied. For d = 8cm, oxygen content in a-$SiO_x$ decreased with dissociation of oxygen onto the silicon oxide matrix; temperature increased due to enlargement of kinetic energy. For d = 10 cm, however, the oxygen content had a minimum between $150^{\circ}\;and\;200^{\circ}$. Using simple optical measurements, we can predict a preferred orientation of liquid crystal molecules on a-$SiO_x$ thin film. At higher oxygen content (x > 1.6), liquid crystal molecules on an inorganic liquid crystal alignment layer of a-$SiO_x$ showed homogeneous alignment; however, in the lower case (x < 1.6), liquid crystals showed homeotropic alignment.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.788-791
• /
• 2002

Tin doped indium oxide(ITO) films are highly conductive and transparent in the visible region whose property leads to the applications in solar cell, liquid crystal display, thermal heater, and other sensors. This paper investigated ITO films as a transparent conducting films for application of PDP. ITO films were grown on glass substrate by RF magnetron sputtering method. To achieve high transmittance and low resistivity, we examined the various film deposition such as substrate temperature, gas pressure, annealing temperature, and deposition time. We recommend the substrate temperature of $500^{\circ}C$ and post annealing of $200^{\circ}C$ in $O_2$ atmosphere for good conductivity and transmittance. From XRD examination, ITO films showed a preferred(222) orientation. As substrate temperature increased from RT to $500^{\circ}C$, the intensity of the (222) peak increased. The highest peak intensity was observed at a substrate temperature of $500^{\circ}C$. with the optimum growth conditions, ITO films showed resistivity of $1.04{\times}10^{-4}{\Omega}-cm$ and transmittance of 81.2% for a film 300nm thick in the wavelength range of the visible spectrum.

• Transactions on Electrical and Electronic Materials
• /
• v.1 no.2
• /
• pp.23-27
• /
• 2000

Indium in oxide(ITO) films have been deposited on PET and glass substrates by DC reactive magnetron sputtering without post-deposition thermal treatment, The high quality for microstructure, electrical and optical properties of the as-deposited ITO films on unheated substrates is dominated by the sputtering parameters, The influence of the working gas pressure, DC power and oxygen partial pressure has been systematically investigated, The lowest DC power, and oxygen partial pressure has been systematically investigated, The lowest resistivity of ITO films deposited on PET substrates was 6$\times$10$^{-4}$ $\Omega$cm. It has been obtained at a working pressure of 3 mTorr and DC power of 30 W. The sheet resistance and optical transmittance of these film were 22 $\Omega$/square and 84% respectively. The best values of figures of merit for the electrical and optical characteristics such as T/ $R_{sh}$ and $T^{10}$ / $R_{sh}$ are approximately 38.1 and 7.95($\times$10$^{-3}$ $\Omega$$^{-1}$ ), respectively.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.8
• /
• pp.715-718
• /
• 2008

An in-line wet etch/cleaning system was established for the research and development in wet etch process. The system was equipped with a reverse moving system for the reduction in the size of the in-line wet etch/cleaning system and it was possible for the glass substrate to be moved back and forth and alternated in a wet etch bath. For the comparison of the effect of the normal motion and that of the alternating motion on the in-line wet etch process, indium tin oxide(ITO) pattern was obtained through both wet etch process conditions. The results showed that the alternating motion is not inferior to the normal motion in etch rate and in etch uniformity. It is concluded that the alternating motion is possible to be applied to the in-line etch process.

• Journal of Korean Vacuum Science & Technology
• /
• v.3 no.1
• /
• pp.54-58
• /
• 1999

We deposited diamond-like carbon (DLC) films using ion beam sputtering of a graphite target on flat substrates for use as a thin film field emitter. An n-type silicon wafer, titanium-coated silicon, and indium tin oxide (ITO) coated glass were used as a substrate. All films exhibited a sudden increase in the emission after a breakdown occurred at high voltage. The morphology of the films after the breakdown depended on the substrate. On ITO and Ti substrates, the DLC film peeled off upon breakdown, but on the Si substrate the surface melting due to breakdown resulted in the formation of various structures such as a sharp point, mound, and crater. By scanning the deformed surface with a tip anode, we found that the emission was concentrated at the deformed sites, indicating that the field enhancement due to the morphology change was responsible for the increased emission.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.5
• /
• pp.377-380
• /
• 2012

Laser direct patterning of indium tin oxide(ITO) is one of new methods of direct etching process to replace the conventional photolithography. A diode pumped Q-switched Nd:$YVO_4$ (${\lambda}$= 1,064 nm) laser was used to produce ITO electrode on various transparent oxide semiconductor films such as zinc oxide(ZnO). The laser direct etched ITO patterns on ZnO were compared with those on glass substrate and were considered in terms of the overlapping rate of laser beam. In case of the laser etching on double-layer, it was possible to obtain the higher overlapping rate of laser beam.

• The Transactions of the Korean Institute of Electrical Engineers C
• /
• v.53 no.4
• /
• pp.231-236
• /
• 2004

A normally open thermopneumaticc-actuated microvalve has been fabricated and their properties are investigated. The advantages of the proposed microvalve are of the low cost fabrication process and the transparent optical property using polydimethylsiloxane (PDMS) and indium tin oxide (ITO) glass. The fabricated microvalves with in-channel configuration are easily integrated with other microfluidic devices on the same substrate. The fabrication process of thermopneumatic-actuated microvalvesusing PDMS is very simple and its performance is very suitable for a disposable lab-on-a-chip. The PDMS membrane deflection increases and the flow rates of the microchannel with microvalvels decrease as the applied power to the ITO heater increases. The powers at flow-off are dependent on the membrane thickness and the applied inlet pressure but are independent of the channel width of microvalves. The flow rate is well controlled by the switching function of ITO heater and the closing/opening times are around 20 sec and 25 sec, respectively.

• Journal of the Semiconductor & Display Technology
• /
• v.17 no.2
• /
• pp.71-75
• /
• 2018

In this study, we prepared OLED cell with ITO (Indium Tin Oxide) films grown on the glass substrate by facing targets sputtering. Before fabrication of OLED cells, we investigated properties of ITO films deposited at various sputtering conditions. To investigate properties of as-prepared films, we employed four-point probe, UV-VIS spectrometer, X-ray diffractometer (XRD), field emission scanning electron microscopy (FE-SEM), hall-effect measurement. As a results, as-prepared ITO films have high transmittance of over 85 % in the visible range (300-800 nm) and a resistivity of under $10^{-4}$ (${\Omega}-cm$). Their resistivity increased as a function of oxygen gas flow and substrate temperature. OLED cell with ITO films were fabricated by thermal evpoeartor. Properties of OLEDs cell referring to properties of ITO films.