• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.27 no.6
• /
• pp.282-288
• /
• 2017

In this paper, GaAs/AlGaAs multi-layer structure was grown by liquid phase epitaxy with graphite sliding boat, which can be used as a device structure of a photocathode image sensor. The multi-layer structure was grown on an n-type GaAs substrate in the sequence as follows: GaAs buffer layer, Zn-doped p-type AlGaAs layer as etching stop layer, Zn-doped p-type GaAs layer, and Zn-doped p-type AlGaAs layer. The Characteristics of GaAs/AlGaAs structures were analyzed by using scanning electron microscope (SEM), secondary ion mass spectrometer (SIMS) and hall measurement. The SEM images shows that the p-AlGaAs/p-GaAs/p-AlGaAs multi-layer structure was grown with a mirror-like surface on a whole ($1.25mm{\times}25mm$) substrate. The Al composition in the AlGaAs layer was approximately 80 %. Also, it was confirmed that the free carrier concentration in the p-GaAs layer can be adjusted to the range of $8{\times}10^{18}/cm^2$ by hall measurement. In the result, it is expected that the p-AlGaAs/p-GaAs/p-AlGaAs multi-layer structure grown by the LPE can be used as a device structure of a photoelectric cathode image sensor.

• Journal of the Korean Vacuum Society
• /
• v.22 no.3
• /
• pp.162-167
• /
• 2013

An epitaxial layer structure for heterojunction p-InGaP/N-InAlGaP solar cell has proposed. Simulation for current density-voltage characteristics has been performed on p-InGaP/N-InAlGaP structure and the simulation results were compared with p-InGaP/p-GaAs/N-InAlGaP structure and homogeneous InGaP pn junction structure. The simulation result showed that the maximum output power and fill factor have greatly increased by replacing n-InGaP with N-InAlGaP. The thicknesses of p-InGaP and n-InAlGaP were optimized for the epitaxial layer structure of p-InGaP/N-InAlGaP.

• Proceedings of the IEEK Conference
• /
• 1998.06a
• /
• pp.401-404
• /
• 1998

Recently, InGaP/GaAs HBTs have been much interested as a potential replacement for AlGaAs/GaAs HBTs because of their superior device and material properties. In this paper, DC characteristics of InGaP/GaAs HBTs and the temperature dependance as well as the reliability were investigated comparing with AlGaAs/GaAs HBTs. As a results InGaP/GaAs HBTs produced the superior performance to AlGaAs/GaAs HBTs.

• Journal of Sensor Science and Technology
• /
• v.8 no.5
• /
• pp.421-426
• /
• 1999

In this paper, we present p-channel GaAs MOSFET having $Al_2O_3$ as gate insulator fabricated on a semi-insulating GaAs substrate, which can be operated in the depletion mode. $1\;{\mu}m$ thick undoped GaAs buffer layer, $4000\;{\AA}$ thick p-type GaAs epi-layer, undoped $500{\AA}$ thick AlAs layer, and $50\;{\AA}$ thick GaAs cap layer were subsequently grown by molecular beam epitaxy(MBE) on (100) oriented semi-insulating GaAs substrate and this wafer was oxidized. AlAs layer was fully oxidized as a $Al_2O_3$ thin film. The I-V, $g_m$, breakdown charateristics of the fabricated GaAs MOSFET showed that wet thermal oxidation of AlAs/GaAs epilayer/S I GaAs was successful in realizing depletion mode p-channel GaAs MOSFET.

• Korean Journal of Materials Research
• /
• v.11 no.8
• /
• pp.655-660
• /
• 2001

Surface photovoltage spectroscopy was used to study $In_{0.5}(Ga_{1-x}Al_x)_{0.5}P/GaAs$ grown by metalorganic chemical vapor deposition(MOCVD). Energy gap related transition in GaAs and $In_{0.5}(Ga_{1-x}Al_x)_{0.5}P$ were observed. By measuring the frequency dependence of $In_{0.5}(Ga_{1-x}Al_x)_{0.5}P/GaAs$, we observed that SPV line shape does not chance, whereas the amplitude change. This results is due to the difference in the lifetimes of the photocarriers in GaAs and in $In_{0.5}(Ga_{1-x}Al_x)_{0.5}P$. We also have evaluated the parameters that describe the temperature dependences of the band gap.

• Journal of the Korean Institute of Telematics and Electronics D
• /
• v.35D no.7
• /
• pp.88-93
• /
• 1998

For the self-aligned AlGaAs/GaAs HBTs, the surface states at the interface between the extrinsic base surface and the passivation nitride is a major cause of degradation of dc characteristics. In this paper the degradation mechanisms of self-aligned AlGaAs/GaAs HBT were analyzed, and GaAs HBTs, which employed an InGaP ledge emitter structure formed by the nonself-aligned process to cover the surface of the extrinsic base and reduce the surface states, produced high reliability. Accoridng to the acceleration lifetime test, the nonself-aligned InGaP/GaAs HBTs produced very reliable dc characteristics comparing with the self-aligned AlGaAs/GaAs HBTs. The activation energy was 1.97eV and MTTF $4.8{\times}10^{8}$ hrs at $140^{\circ}C$ which satisfied the MIL standard.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.07a
• /
• pp.164-165
• /
• 2005

The dry etch characteristics of GaAs over both AlGaAs and InGaP in planar inductively coupled $BCl_3$-based plasmas(ICP) with additions of $SF_6$ or $CF_4$ were studied. The additions of flourine gases provided enhanced etch selectivities of GaAs/AlGaAs and GaAs/InGaP. The etch stop reaction involving formation of involatile $AlF_3$ and $InF_3$ (boiling points of etch products: $AlF_3\sim1300^{\circ}C$, $InF_3$ > $1200^{\circ}C$ at atmosphere) were found to be effective under high density inductively coupled plasma condition. Decrease of etch rates of all materials was probably due to strong increase of flourine atoms in the discharge, which blocked the surface of the material against chlorine neutral adsorption. The process parameters were ICP source power (0 - 500 W), RF chuck power (0 - 30 W) and variable gas composition. The process results were characterized in terms of etch rate, selectivities of GaAs over AlGaAs and InGaP, surface morphology, surface roughness and residues after etching.

• Journal of the Korean Vacuum Society
• /
• v.19 no.2
• /
• pp.134-140
• /
• 2010

We have investigated the contactless electroreflectance (CER) properties of $In_{0.5}(Ga_{1-x}Al_x)_{0.5}P$/GaAs double heterostructures grown by metal-organic chemical vapour deposition (MOCVD). The CER measurements on the sample were studied as a function of temperature, modulation voltage ($V_{ac}$), and dc bias voltage ($V_{bias}$). Five signals observed at room temperature are related to the GaAs, $In_{0.5}Ga_{0.5}P$, $In_{0.5}(Ga_{0.73}Al_{0.27})_{0.5}P$, $In_{0.5}(Ga_{0.5}Al_{0.5})_{0.5}P$, and $In_{0.5}(Ga_{0.2}Al_{0.8})_{0.5}P$ transitions, respectively. From the temperature dependence of CER spectrum, the Varshni coefficients and broadening parameters were determined and discussed. In addition, we found that the behavior of the CER amplitude for the reverse bias is larger than that of the forward.

• Journal of Surface Science and Engineering
• /
• v.36 no.4
• /
• pp.334-338
• /
• 2003

$BCl_3$고밀도 평판형 유도결합 플라즈마(High Density Planar Inductively Coupled Plasma)를 이용하여 AlGaAs와 InGaP의 건식식각에 대하여 연구하였다. 본 실험에서는 ICP 소스파워(0∼500 W), RIE 척 파워(0-150 W), 공정압력(5∼15 mTorr)의 변화에 따른 AlGaAs와 InGaP의 식각률, 식각단면 그리고 표면 거칠기 등을 분석 하였다. 또, 공정 중 OES(Optical Emission Spectroscopy)를 이용하여 in-situ로 플라즈마를 관찰하였다. $BCl_3$ 유도결합 플라즈마를 이용한 AlGaAs의 식각결과는 우수한 수직측벽도와(>87$^{\circ}$) 깨끗하고 평탄한 표면(RMS roughness = 0.57 nm)을 얻을 수 있었다. 반면, InGaP의 경우에는 식각 후 표면이 다소 거칠어진 것을 확인할 수 있었다. 모든 공정조건에서 AlGaAs의 식각률이 InGaP보다 더 높았다. 이는 $BCl_3$ 유도결합 플라즈마를 이용하여 InGaP을 식각하는 동안 $InCl_{x}$ 라는 휘발성이 낮은 식각부산물이 형성되어 나타난 결과이다. ICP 소스파워와 RIE 척파워가 증가하면 AlGaAs와 InGaP모두 식각률이 증가하였지만, 공정압력의 증가는 식각률의 감소를 가져왔다. 그리고 OES peak세기는 공정압력과 ICP 소스파워의 변화에 따라서는 크게 변화하였지만 RIE 척파워에 따라서는 거의 영향을 받지 않았다.

• Journal of the Korean Vacuum Society
• /
• v.2 no.4
• /
• pp.424-432
• /
• 1993

AlGaAs/InGaAs/GaAs pseudomorphic structures have been grown by atmosheric pressure-MOCVD . The Al incorporation efficiency is constant but slightly exceeds the Ga incorporation during the growth of AlGaAs layers at $650^{\circ}C$ . Meanwhile , the In incorporation efficiency is constant but slightly less than the Ga incorporation in InGAAs layers. InGaAs/GaAs QWs were grown and their optical properties were characterized . $\delta$-doped Al0.24Ga0.76As/In0.16 Ga0.84As p-HEMT structures were successfully grown by MOCVD and their transport properties were characterized by Hall effect and SdH measurements. SdH Measurements at 3.7K show clear magnetoresistance oscillations and plateaus in the quantum Hall effect confirming the existence of a two-dimensional electron gas(2DEG) and a parallel conduction through the GaAs buffer layer. The fabricated $1.5\mu\textrm{m}$gatelength p-HEMTs having p-type GaAs in the buffer layer show a high transconductance of 200 mS/mm and a good pinch-off characteristics.