• Nuclear Engineering and Technology
• /
• v.33 no.4
• /
• pp.386-396
• /
• 2001

Mixtures Of AUC-UO$_2$and Gd$_2$O$_3$ Powders doped With Cr$_2$O$_3$ or Cr$_2$O$_3$-SiO$_2$ were Pressed and sintered at 1730 t in hydrogen gas witk various water-vapor contents. The density of UO$_2$- 6wt% Gd$_2$O$_3$ pellets can be increased from 91% TD to 94.5% TD in 1 vol% $H_2O$-H$_2$ gases by the addition of 0.02wt% Cr$_2$O$_3$-(0.01~0.04) wt% SiO$_2$. The magnitude of density increase is much larger in (1~3 vol%) $H_2O$-H$_2$ gases than in 0.05 vol% $H_2O$-H$_2$ gas. The densification of U0$_2$- Gd$_2$O$_3$ compact is significantly delayed in the temperature range between 1300 and 1500 t , but that of compacts with Cr$_2$O$_3$-SiO$_2$ is not. The role of Cr$_2$O$_3$ and SiO$_2$ in densification is discussed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.11a
• /
• pp.198-198
• /
• 2006

Tin doped $In_2O_3$ sputtering target is widely used to produce a various kinds of flat panel display because of high transmittance in visible region and high electrical conductivity. In2O3 and SnO2 powders were prepared by a homogeneous precipitation method using metal source, respectively, the calcining and sintering behavior of the indium-tin oxide(In2O3-SnO2) composite powders were studied. The tin oxide(SnO2) dispersion condition in ITO sputtering target was improved by increasing calcining temperature. And the tin oxide dispersion was also improved by reducing the tin oxide contents in the ITO target from 30 to 5wt%. SnO2 dispersion and densification of ITO target is very difficult to control due to sublimation of SnO2 at over 1150C.

• Journal of the Korean Ceramic Society
• /
• v.28 no.2
• /
• pp.160-166
• /
• 1991

Microstructure and phase changes during the sintering of ZnO varistors were studied in ZnO-Bi2O3-CoO-Sb2O3 and ZnO-Bi2O3-CoO-Sb2O3-Cr2O3 systems using acanning electron microscopy (SEM) with an energy dispersive X-ray analysis (EDAX), X-ray diffraction (XRD) and differential thermal analysis (DTA). The spinel phase and the Bi2O3 phase were formed by the decomposition of the pyrochlore phase during heating. The spinel particles (2-4$\mu\textrm{m}$), which were formed both along ther grain boundaries and within the ZnO grain, were always found near the pyrochlore phase. Intergranular phases (Bi2O3 and pyrochlore) were precipitated from the liquid phase during cooling. The Bi2O3 phases were located at the triple (or multiple) point of the ZnO grains. Cr2O3 played a role in decreasing the formation temperature of the spinel phase and Bi2O3 phase during sintering, and inhibited the grain growth.

• Korean Journal of Materials Research
• /
• v.13 no.10
• /
• pp.645-650
• /
• 2003

The microstructure and electrical characteristics of $Pr_{6}$ $O_{11}$ -based ZnO varistor ceramics composed of $ZnO-Pr_{6}$ $O_{ 11}$/$-CoO-Cr_2$$O_3$-$Dy_2$$O_3$-based ceramics were investigated with $Dy_2$$O_3$content in the range of 0.0∼2.0 mol%. As $Dy_2$$O_3$content was increased, the average grain size was decreased in the range of 18.6∼4.7 $\mu\textrm{m}$ and the density of the ceramic was decreased in the range of 5.53∼4.34 g/㎤. While, the varistor voltage was increased in the range of 39.4∼436.6 V/mm and the nonlinear exponent was in the range of 4.5∼66.6 with increasing $Dy_2$$O_3$content. The addition of $Dy_2$$O_3$highly enhanced the nonlinear properties of varistors, compared with the varistor without $Dy_2$$O_3$. In particular, the varistor with $Dy_2$$O_3$ content of 0.5 mol% exhibited the highest nonlinearity, in which the nonlinear exponent is 66.6 and the leakage current is 1.2 $\mu\textrm{A}$. The donor concentration and the density of interface states were decreased in the range of $(4.19∼0.33) ${\times}$10^{18}$ //㎤ and $(5.38∼1.74) ${\times}$10^{12}$ $\textrm{cm}^2$, respectively, with increasing $Dy_2$$O_3$content. The minimum dissipation factor of 0.0302 was obtained from 0.5mol% $Dy_2$$O_3$.

• Journal of the Korean Ceramic Society
• /
• v.29 no.10
• /
• pp.797-805
• /
• 1992

Al2O3-20 wt% ZrO2 composite powders to be used as the starting materials of the Al2O3/ZrO2-Spinel composite system were prepared by the use of the emulsion-hot kerosene drying method. The crystalline phase of ZrO2 in the synthesized Al2O3-ZrO2 composite powders was 100% tetragonal but the small amount of t-ZrO2 was transformed into m-ZrO2 after crushing. The hardness, fracture toughness, and flexural strength of the composite, which was sintered at 1650$^{\circ}C$ for 4 hrs after calcining at 1100$^{\circ}C$ for 2 hrs and had the relative density of 99%, were 15.7 GPa, 4.97 MN/m3/2, and 390 MPa, respectively. The fracture form in the sintered composites was found to be the intergranular fracture.

• Journal of Korean Society for Atmospheric Environment
• /
• v.20 no.3
• /
• pp.291-302
• /
• 2004

The CuO/$3AL_2O_3{\cdot}2SiO_2$ catalyst impregnated ceramic candle filters for nitrogen oxides removal were prepared by porous mullite($3AL_2O_3{\cdot}2SiO_2$) support and CuO catalyst deposited on this support to achieve uniformly dispersed CuO deposition, which are impregnated into the pores of available alumino-silicate ceramic candle filter. The CuO/3$AL_2O_3{\cdot}2SiO_2$ catalyst impregnated ceramic candle filters were characterized by XRD, BET, air permeability, pore size, SEM and catalytic tests in the reduction of NOx by NH$_3$. The observed effects of CuO/3$AL_2O_3{\cdot}2SiO_2$ impregnated ceramic candle filters in SCR reaction are as follows : (1) when the content of CuO catalyst increased further, activity of NO increased. (2) NO conversion at first increased with temperature and then decreased at high temperatures (above 40$0^{\circ}C$), possibly due to the occurrence of the ammonia oxidation reaction. (3) In pilot plant test for 3 months, NO conversion was greater than 90%.

• Journal of the Korean Ceramic Society
• /
• v.26 no.2
• /
• pp.187-194
• /
• 1989

Synthesis of spinel pigment on ZnO-Fe2O3 system. The object of this research is the synthesis of new spinel pigments on the basic of ZnO-Fe2O3 system which was substituted by ZnO-Fe2O3 by MgO-Al2O3. This research was progressed by measuring the X-ray diffraction and the reflectances of the substitued ZnO-Fe2O3 group. Which was obtained by sintering at the temperature of 1,00$0^{\circ}C$, 1,10$0^{\circ}C$, 1,20$0^{\circ}C$ and 1,25$0^{\circ}C$ and them by regrinding. In order to coloring test, here basic compositions of Barium glaze, Zinc glaze, Lime glaze, Lead glaze and Talc glaze used in this experiment are obtained from the ceramic work. Adding synthetic stains in these basic glazes with 3%, mixing and glazing on the specimen. The specimens was fired at 1,28$0^{\circ}C$ in reducing and oxidizing atmosphere in the gas kiln. The results of the research as follow. 1. Many kinds of spinel pigment was produced on ZnO-Fe2O3 system that is to say, not always only spinel. 2. Spinel peak was observed strongly on the ZnO-Fe2O3 system withsubstituting by MgO-Fe2O3 and MgO-Al2O3 group(the ratio of MgO, Al2O3 being increased, observed more strongly). 3. The most effective temperature ranges was 1,20$0^{\circ}C$~1,25$0^{\circ}C$. 4. The color of spinel pigments on this system was observed by "stable YR". 5. It was yellow red in oxidizing and green in reducing atmosphere on the coloring test.ring test.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2003.07a
• /
• pp.836-839
• /
• 2003

We have synthesized some phosphors in the system $CaO-Y_{2}O_3-Al_{2}O_{3}$ by combinatorial polymerized-complex method. Composition and synthetic temperature of phosphors in the liblary was screened from the emission intensities of individual samples under VUV excitation. In $Tb^{3+}$-activated $CaO-Y_{2}O_3-Al_{2}O_{3}$, green phosphors showing good intensity were found to be $CaYAl_{3}O_{7}$, $CaYalO_{4}$, $YAlO_{3}$, $Y_{3}Al_{5}O_{12}$, $Y_{4}Al_{2}O_{9}$, $Ca_{3}Al_{2}O6$.

• Journal of the Korean Ceramic Society
• /
• v.34 no.1
• /
• pp.88-94
• /
• 1997

The oxidation behavior of the NiCrAlY bond coat and thermal fatigue failure in the plasma-sprayed thermal barrier coating system, ZrO2.8wt%Y2O3 top coat/Ni-26Cr-5Al-0.5Y bond coat/Hastelloy X superalloy substrate, in commercial use for finned segment of gas turbine burner were investigated. The main oxides formed in the bond coat were NiO, Cr2O3, and Al2O3. It divided the oxide distribution at this interface into two types whether an Al2O3 thin layer existed beneath ZrO2/bond coat interface before operation at high temperature or not. While a continuous layer of NiO was formed mainly in the region where the Al2O3 thin layer was present, the absence of it resulted in the formation of mixture of Cr2O3 and Al2O3 beneath NiO layer. Analyses on the fracture surface of specimen spalled by thermal cycling showed that spalling occurred mainly along the ceram-ic coat near ZrO2/bond coat oxide layer interface, but slightly in the oxide layer region.

• Journal of the Korean Ceramic Society
• /
• v.30 no.8
• /
• pp.615-622
• /
• 1993

In order to increase chemical durability of thin films in binary system B2O3-SiO2 and Al2O3-SiO2 on the slide glass by the dip-coating technique from TEOS(Tetraethyl Orthosilicate) and boric acid or aluminum nitrate, phosphoric acid(5~20mol%) was added, respectively. Corrosion of acid and alkali of samples treated with 1N, HCl, NaOH and distilled water at 10$0^{\circ}C$ for 15 minute, were measured IR transmittance and variance of transmittance at visible range. Surface structure of thin film was investigated with SEM and formation of crystal phase according to additiion of phosphoric acid was measrued with XRD. In Al2O3-SiO2 system, change of remarkable characteristic was not obtained at the addition of P2O5 but transmittance of thin film was decreased with addition of P2O5 in B2O3-SiO2 system.