• Geomechanics and Engineering
• /
• 제33권5호
• /
• pp.453-462
• /
• 2023

Intermediate Geomaterials (IGMs) are natural formation materials that exhibit the engineering behavior (strength and compressibility) between soils and rocks. The engineering behavior of such material is highly unpredictable as the IGMs are stiffer than soils and weaker/softer than rocks. Further, the characterization of such material needs exposure to both soil and rock mechanics. In most conventional designs of geotechnical structures, the engineering properties of the IGMs are either aligned with soils or rocks, and this assumption may end up either in an over-conservative design or under-conservative design. Hence, many researchers have attempted to evaluate its actual engineering properties through laboratory tests. However, the test results are partially reliable due to the poor core recovery of IGMs and the possible sample disturbance. Subsequently, in-situ tests have been used in recent years to evaluate the engineering properties of IGMs. However, the respective in-situ test finds its limitations while exploring IGMs with different geological formations at deeper depths with the constraints of sampling. Standard Penetration Test (SPT) is the strength-based index test that is often used to explore IGMs. Moreover, it was also observed that the coefficient of variation of the design parameters (which represents the uncertainties in the design parameters) of IGMs is relatively high, and also the studies on the probabilistic characterization of IGMs are limited compared with soils and rocks. With this perspective, the present article reviews the laboratory and in-situ tests used to characterize the IGMs and explores the shear strength variation based on their geological origin.

• 한국응용과학기술학회지
• /
• 제18권4호
• /
• pp.273-284
• /
• 2001

A series of microcapsule were synthesized by using several PCM(Phase Change Material) as a core material and gelatin/arabic gum, melamine/formaldehyde as a shell material. Coacervation technique and in situ polymerization were adopted in synthesizing microcapsules. In the microencapsulation by coacervation, tetradecane and octadecane were used as core materials. In the microencapsulation by situ polymerization tetradecane, pentadecane, hexadecane, heptadecane, octadecane, and nonadecane were used as core material. The synthesized microcapsule was examined to observe the shape of the microcapsule. The particle size analysis was performed by particle size analyzer. The thermal properties(e.g. melting point, heat of melting, crystallization temperature, heat of crystallization, differences between melting point and crystallization temperature) were obtained by DSC(Differential Scanning Calorimeter). The stirring rate effect was investigated during the microencapsulation. It was found that with increasing the stirring rate much smaller microcapule was produced. However, this did not necessarily lead to formation of spherical microcapsule.

• Bulletin of the Korean Chemical Society
• /
• 제20권9호
• /
• pp.1049-1055
• /
• 1999

Electrochemical oxidation of silicon (p-type Si(100)) at room temperature in ethylene glycol and in aqueous solutions has been performed by applying constant low current densities for the preparation of thin SiO2 layers. In-situ ac impedance spectroscopic methods have been employed to characterize the interfaces of electrolyte/oxide/semiconductor and to estimate the thickness of the oxide layer. The thicknesses of SiO2 layers calculated from the capacitive impedance were in the range of 25-100Å depending on the experimental conditions. The anodic polarization resistance parallel with the oxide layer capacitance increased continuously to a very large value in ethylene glycol solution. However, it decreased above 4 V in aqueous solutions, where oxygen evolved through the oxidation of water. Interstitially dissolved oxygen molecules in SiO2 layer at above the oxygen evolution potential were expected to facilitate the formation of SiO2 at the interfaces. Thin SiO2 films grew efficiently at a controlled rate during the application of low anodization currents in aqueous solutions.

• Journal of Acupuncture Research
• /
• 제18권5호
• /
• pp.135-146
• /
• 2001

Objective : Bone homeostasis is maintained by balance of bone formation and resorption. Therefore, bone related diseases arose by disturbance of this balance between osteoblast and osteoclast activities. To develop a successful screening system of the therapeutic components based on oriental medicine is essential to set out systematic approach for that purpose. Methods : This study was perforated Sprague-Dawley rat femur for bony defects(${\phi}5mm$) by the fissure bur. And experimetal group were treated with Cervi Pantotricuhum Cornu injection at both $Sh{\grave{e}}nsh{\tilde{u}}$(BL23) & $D{\grave{a}}zh{\grave{u}}(BL11)(0.2m{\ell})$. This was evaluated by radiography and histological analysis with in situ hybridization. Results : Cervi Pantotricuhum Cornu Herbal Acupuncture has weak effect on bony defect healing and this was evaluated by X-ray taking and histological analysis with in situ hybridization. Osteocalcin gene expression was not changed by Cervi Pantotricuhum Cornu Herbal Acupuncture in bony defects animal model. Conclusion : Taken together this study show that the Cervi Pantotricuhum Cornu herbal-acupuncture has a weak effect healing of bony defects, this type of approach might give a good chance to explore the favorable effects of Cervi Pantotricuhum Cornu herbal-acupuncture on bone tissue.

• 한국고분자학회:학술대회논문집
• /
• 한국고분자학회 2006년도 IUPAC International Symposium on Advanced Polymers for Emerging Technologies
• /
• pp.303-303
• /
• 2006

In-situ ring opening polymerization of ${\varepsilon}-caprolactum$ was carried out in the presence of aminoethylaminopropylisobutyl POSS and stoichiometric amount of adipic acid. The covalent bond formation of POSS on the polyamide was confirmed by the appearance of FT-IR peak at $1123\;cm^{-1}$ that corresponds to the Si-O stretching of POSS structures. Gradual decrease in melting endotherm peak was observed on loading POSS in PA6/POSS nanocomposites. Sharp increase in intrinsic viscosity was observed upto 2.5 wt % loading POSS in the polyamide 6 nanocomposites. These nanocomposites were further characterized using nuclear magnetic resonance, melt viscosity and X-ray diffraction.

• 한국분말재료학회지
• /
• 제10권4호
• /
• pp.275-280
• /
• 2003

Synthesis and characteristics of Cu nanopowder were considered by in-situ characterization method using SMPS in pulsed wire evaporation process. With increasing pressure in chamber, particle size and degree of agglomeration increased by increase of collision frequency. Also, it was found from the XRD analyses and BET measurements that crystallite size and particle size decreased with elevating applied voltage. However, SMPS measurements and TEM observation revealed the increase of particle size and degree of agglomeration with increase of applied voltage. These results suggested that particle growth and agglomeration depend on overheating factor in chamber at the early stage and thermal coagulation in filtering system during powder formation until collection.

• 한국재료학회지
• /
• 제22권4호
• /
• pp.202-206
• /
• 2012

$CoSi_2$ was formed through annealing of atomic layer deposition Co thin films. Co ALD was carried out using bis(N,N'-diisopropylacetamidinato) cobalt ($Co(iPr-AMD)_2$) as a precursor and $NH_3$ as a reactant; this reaction produced a highly conformal Co film with low resistivity ($50\;{\mu}{\Omega}cm$). To prevent oxygen contamination, $ex-situ$ sputtered Ti and $in-situ$ ALD Ru were used as capping layers, and the silicide formation prepared by rapid thermal annealing (RTA) was used for comparison. Ru ALD was carried out with (Dimethylcyclopendienyl)(Ethylcyclopentadienyl) Ruthenium ((DMPD)(EtCp)Ru) and $O_2$ as a precursor and reactant, respectively; the resulting material has good conformality of as much as 90% in structure of high aspect ratio. X-ray diffraction showed that $CoSi_2$ was in a poly-crystalline state and formed at over $800^{\circ}C$ of annealing temperature for both cases. To investigate the as-deposited and annealed sample with each capping layer, high resolution scanning transmission electron microscopy (STEM) was employed with electron energy loss spectroscopy (EELS). After annealing, in the case of the Ti capping layer, $CoSi_2$ about 40 nm thick was formed while the $SiO_x$ interlayer, which is the native oxide, became thinner due to oxygen scavenging property of Ti. Although Si diffusion toward the outside occurred in the Ru capping layer case, and the Ru layer was not as good as the sputtered Ti layer, in terms of the lack of scavenging oxygen, the Ru layer prepared by the ALD process, with high conformality, acted as a capping layer, resulting in the prevention of oxidation and the formation of $CoSi_2$.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 2001년도 춘계학술대회 논문집 반도체재료
• /
• pp.79-83
• /
• 2001

In order to compare the barrier properties of Ta-N/Si(001) with those of Ta-N/Ta/Si(001), we studied structural properties of films grown by RF magnetron sputtering with various $Ar/N_2$ ratios. To evaluate the barrier properties, the samples were annealed in a vacuum chamber. Ex-situ x-ray scattering measurements were done using an in-house x-ray system. With increasing nitrogen ratio in Ta-N/Si(001), the barrier property of Ta-N/Si(001) was enhanced, finally failed at $750^{\circ}C$ due to the crystallization and silicide formation. Compared with Ta-N/Si(001), Ta-N/Ta/Si(001) forms silicides at $650^{\circ}C$. However it does not crystallize even at $750^{\circ}C$. With increasing nitrogen composition in Ta-N/Ta/Si(001), the formation of tantalum silicide was reduced and the surface roughness was improved. To observe the surface morphology of Ta-N/Ta/Si(001) during annealing, we performed an in-situ x-ray scattering experiment using synchrotron radiation of the 5C2 at Pohang Light Source(PLS). Addition of Ta layer between Ta-N and Si(001) improved the surface morphology and reduced the surface degradation at high temperatures. In addition, increasing $N_2/Ar$ flow ratio reduced the formation of tantalum silicide and enhanced the barrier properties.

• Korea-Australia Rheology Journal
• /
• 제12권3_4호
• /
• pp.143-149
• /
• 2000

In this article, we considered shear-induced microstructure and rheological behavior of micellar solutions of cationic surfactant, cetylpyridinium chloride (CPC) in the presence of a structure-forming additive, sodium salicylate (NaSal). Shear viscosity, shear moduli and flow birefringence were measured as functions of the surfactant and additive concentrations. In the presence of NaSal, the micellar solution exhibited the non-linear rheological behavior due to the formation of supramolecular structures when the molar ratio of NaSal to CPC exceeded a certain threshold value. Flow birefringence probed the change in micelle alignment under shear flow. At low shear rates, the flow birefringence increased as the shear rate increased. On the other hand, fluctuation of flow birefringence appeared from the shear rate near the onset of shear thickening, which was caused by shear-induced coagulation or aggregation. These results were confirmed by the SEM images of in situ gelified micelle structure through sol-gel route.

• 한국전기전자재료학회:학술대회논문집
• /
• 한국전기전자재료학회 1994년도 추계학술대회 논문집
• /
• pp.106-108
• /
• 1994

Electromigration(EM) tests were carried out on Al and Cu films in HV systems to study surface migration. The Al films were made on oxidized silicon wafers by thermal evaporation, in-situ annealed at 300$^{\circ}C$, patterned, and EM tested at 260$^{\circ}C$ and 4.5MA/$\textrm{cm}^2$. SEM observation with back scattered electron mode on the EM tested Al films disclosed that thinning took place under the native Al oxide. In the case of Cu films, tested using in-situ TEM, thinning was also observed at the early stage of void formation even though the thinned areas were much less than those of the Al films.