• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.13 no.6
• /
• pp.272-278
• /
• 2003

$Bi_4Ti_3O_{12}$ (BIT) and $(Bi_{3.25}La_{0.75})(Ti_{2.97}V_{0.03})O_{12}$ (BLTV) thin films were deposited on ITO/glass substrates by metal organic chemical vapor deposition (MOCVD) using ultrasonic spraying. After deposition of the films in oxygen atmosphere for 30 min, the films were heated by rapid thermal annealing (RTA) method, especially direct insertion, at various temperatures. The films were investigated on phase formation temperature, microstructure and electrical properties. From x-ray diffraction (XRD) patterns, the perovskite phase formation temperature of BLTV thin film was about $600^{\circ}C$ which was lower than that of BIT, $650^{\circ}C$. The leakage current of the BLTV thin film was measured to be $1.52\times 10^{-9}$A/$cm^2$ at an applied voltage of 1 V. The remanent polarization (Pr) and coercive field (Ec) values of the BLTV film deposited at $650^{\circ}C$ were $5.6\muC/cm^2$ and 96.5 kV/cm, respectively.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2011.02a
• /
• pp.97-97
• /
• 2011

산화아연 (ZnO)은 넓은 에너지 밴드갭 (~3.37 eV), 큰 엑시톤 결합 에너지 (~60 meV) 그리고 높은 전자 이동도 (bulk~300 $cm^2Vs^{-1}$, single nanowire~1000 $cm^2Vs^{-1}$)를 갖고 있어, 광전자 소자 및 반도체소자 응용에 매우 널리 사용되고 있다. 특히, 산화아연 나노로드(ZnO nanorod)는 1차원 나노구조로써 더욱 향상된 전자 이동도와 캐리어의 direct path way를 제공하여 차세대 광전자소자 및 태양광 소자의 응용에 대한 연구가 매우 활발하게 이루어지고 있다. 한편, 이러한 산화아연 나노로드를 성장시키기 위하여 VLS (vapor-liquid-solid), 졸-겔 공정(sol-gel process), 수열합성(hydrothermal synthesis), 전기증착(electrodeposition)등 다양한 방법이 보고되었지만, 이러한 산화아연 나노로드의 성장방법은 실제적인 소자응용을 위한 패터닝 형성에 대하여 제약을 받는 문제점이 있다. 이들 중에서 수열합성법과 전극증착법은 ZnO 또는 AZO (Al doped ZnO) seed 층 표면과 성장용액의 화학반응에 의해서 선택적으로 산화아연 나노로드를 성장시킬 수 있다. 이에 본 연구에서는, 광전자소자의 응용을 위한 간단한 패터닝 공정을 위해, 산화인듐주석(ITO) 박막이 증착된 유리기판(glass substrate)위에 수열합성법과 전극증착법을 이용하여 산화아연 나노로드를 선택적으로 성장시켰다. 실험을 위해, ITO glass 위에 RF magnetron 스퍼터를 사용하여 AZO seed 층을 metal shadow mask를 이용하여 패터닝을 형성한 후, 질산아연과 헥사메틸렌테트라아민으로 혼합된 용액에 $85^{\circ}C$ 온도를 유지하여, 패터닝이 형성된 샘플에 전압을 인가하여 성장시켰다. 나노구조 분석을 위해, 전계주사현미경을 이용하여 수열합성법과 전기증착법에 의한 패터닝된 산화아연 나노로드를 비교하여 관찰하였다.

• Journal of the Korean Vacuum Society
• /
• v.5 no.4
• /
• pp.348-353
• /
• 1996

Rapid thermal annealing (RTA) was applied to polycrystalline CdTe thin films evaporated on CdS/ITO/glass substrate and the effect of the annealing temperatures and the atmosphere on physical properties of polycrystalline CdTe thin films and CdTe/CdS solar cell characteristics were studied. Results obtained by EDX showed that the bulk composition of CdTe remained stoichiometric after annealing at $550^{\circ}C$ in the air but the surface composition became Cd-rich. Cross-sectional TEM and micro EDX showed that columnar grains and micro-twins remained even after RTA, however, and the sulfur content in the annealed CdTe (added by sulfur diffusion from CdS during the annealing) was much smaller than that by furnace annealing. Among the investigated RTA temperatures and gas environments, the cell made with CdTe annealed at $550^{\circ}C$ in air showed the best solar energy conversion efficiency.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.06a
• /
• pp.407-407
• /
• 2008

무기EL 디스플레이는 고체재료에 전계를 가했을 때 발광하는 현상을 이용한소자로서, 급속도로 발전을 거듭하고 있으나, 유전체층에 강한전계를 가하여 발광하여야 하므로 낮은 Breakdown voltage와 효율의 한계로 인하여 휘도가 낮고 풀 컬러화 디스플레이 등 의 응용에는 적용되고 있지 못하는 실정이다. 본 연구에서는 강유전체 Perovskite 구조를 가지는 ABO3 물질 중 PMN(Lead Magnesium niobate) 과 PZT (Lead Zirconate titanate) 후막을 제조하여 Inorganic EL(Electro Luminance)에 적용하고 소자의 광전특성을 평가하였다. 소자에 사용된 기판은 고온소성에 알맞은 알루미나(Al2O3)기판을 채택 하였으며, 그 위 하부전극으로는 고온소성에 따른 화학적 안정성이 우수한 Au전극을 Screen Printing 하였다. 제조 되어진 PMN후막 페이스트는 PMN(Pb(Mg1/2 Nb2/3)O3) + Glass Frit(Pb-Zn-B) + BaTiO3(99.99%) 로 합성되었으며 하부전극위에 인쇄하였다. 그 다음 PZT sol-gel을 Spin coating으로 도포 하였다. 형광체로 ZnS:Cu.Cl 을 Screen Printing을로 형성하였으며, 평탄화를 위하여 유기물 충을 Screen Printing 공정으로 성막 하였다. 상부전극으로는 DC sputter로 ITO를 증착하여 EL소자 완성 후 Spectro - Chroma meter로 소자특성을 측정하였다. 평탄화를 통한 유기물층에 변화되는 Capacitance를 Oscilloscope로 전압 전류 pulse의 변화에 따른 opto-electronic 특성을 평가하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2009.06a
• /
• pp.203-204
• /
• 2009

The Indium Zinc Tin Oxide (IZTO) thin films for flexible display electrode were deposited on poly carbonate (PC) and polyethersulfone(PES) and glass substrates at room temperature by facing targets sputtering (FTS). Two different kinds of targets were installed on FTS system. One is ITO ($In_2O_3$ 90 wt.%, $SnO_2$ 10 wt.%), the other is IZO ($In_2O_3$ 90 wt.%, ZnO 10 wt.%). As-deposited IZTO thin films were investigated by a UV/VIS spectrometer, an X-ray diffractometer (XRD), an atomic force microscope (AFM) and a Hall Effect measurement system. As a result, we could prepare the IZTO thin films with the resistivity of under $10^{-4}\;[{\Omega}{\cdot}cm]$ and IZTO thin films deposited on glass substrate showed an average transmittance over 80% in visible range (400~800 nm) in all IZTO thin films except in IZTO thin film deposited at $O_2$ gas flow rate of 0.1[sccm].

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.22 no.11
• /
• pp.961-968
• /
• 2009

In this work, transparent conductive oxide(TCO) films such as $In_2O_3-SnO_2$(ITO) and $In_2O_3-ZnO$(IZO) were prepared on polyethylene naphthalene(PEN) and glass substrates by using rf-magnetron sputtering system. The TCO films deposited on PEN substrate show very poor conductivity as compared to that of the TCO films deposited on glass substrates. From the results of the residual gas analysis(RGA) test, this poor stability of plastic substrate is presumed to be caused by the deteriorated adhesion between the TCO films and the plastic substrate due to outgassing from the plastic substrate during deposition of TCO films. From our experiment, it is found that the vaporization of some defects in the plastic substrates deteriorate the adhesion of the TCO films to the plastic substrate, because the most plastic substrates containing the water vapor and/or other adsorbed particles such as organic solvents. Mixing of these gases vaporized in the sputtering process will also affect the electrical property of the deposited TCO films. Inorganic thin composite $(SiO_2)_{40}(ZnO)_{60}$ film as a gas barrier layer is coated on the PEN substrate to protecting the diffusion of vapors from the substrate, so that the TCO films with an improved quality can be obtained.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.7
• /
• pp.599-602
• /
• 2008

Growth of well-aligned ZnO nanostructures on various substrates such as GaN, ITO/glass, and sapphire was realized via a simple aqueous solution method at low temperature of $90^{\circ}C$. Morphology of ZnO nanostructures grown on various substrates as function of substrate was studied. It was found that ZnO nanostructures is a strong function of substrate. It was clearly observed that the morphology of ZnO nanostructures could be varied by change of substrate. Morphology, crystallinity, and crystal characteristics were carried out by FE-SEM, synchrotron x-ray scattering measurements, and high-resolution electron microscopy, respectively.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2006.05a
• /
• pp.671-672
• /
• 2006

We have investigated the behavior of the ultrafast laser ablation of chromium films (200nm) on the silicon and pyrex-glass(corning 7740) substrate with respect to the laser fluence and the number of laser pulses. In addition, several experiments about ITO thin film were carried out with femto-second Ti:Sapphire laser (150fs). Finally, we introduce the ablation characteristic in accordance with materials of thin film and substrate.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2018.06a
• /
• pp.57-57
• /
• 2018

Zinc-oxide (ZnO), II-VI semiconductor with a wide and direct band gap (Eg: 3.2~3.4 eV), is one of the most potential candidates to substitute for ITO due to its excellent chemical, thermal stability, specific electrical and optoelectronic property. However, the electrical resistivity of un-doped ZnO is not low enough for the practical applications. Therefore, a number of doped ZnO films have been extensively studied for improving the electrical conductivities. In this study, Ti-doped ZnO films were successfully prepared by atomic layer deposition (ALD) techniques. ALD technique was adopted to careful control of Ti doping concentration in ZnO films and to show its feasible application for 3D nanostructured TCO layers. Here, the structural, optical and electrical properties of the Ti-doped ZnO depending on the Ti doping concentration were systematically presented. Also, we presented 3D nanostructured Ti-doped ZnO layer by combining ALD and nanotemplate processes.

• Journal of the Microelectronics and Packaging Society
• /
• v.2 no.1
• /
• pp.35-48
• /
• 1995

마이크로회로내에서 티탄산바륨 중 바륨의 일부가 납으로 치환됨에 따른 전기적 특 성의 변화를 확인하기 위하여 MOD(금속유기화합물 분해법)공정에 의 barum 2-ethylhexanoate, barium neodecanoate, lead 2-ethylhexanoate 및 titanium dimethoxy 야 -2-ethylhexanoate 와 같은 MOC(금속 유기화합물) 들을 합성하고 공통 용매에 대한 용해 도를 시험하였다. 그 결과 barium 2-ethylhexanoate 만 p-xylene에 대한 용해도가 낮았으며 그 외의 다른 MOC들은 모두 p-xylene 단일 용매에 매우 잘 용해되었다. 바륨의 일부가 납 으로 치환된 티탄산 납바륨 박막은 MOC 혼합용액을 ITO/glass, Pt/SiO2/Si 및 Pt/Ti/SiO2/Si 웨이퍼 기판 위에 spin coating 하고 소성하여 얻었다. 이와 같이 얻어진 박막 의 전기적 특성을 측정하고 그 결과를 비교 고찰하였다.