• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07a
• /
• pp.58-61
• /
• 2002

SBT thin films were etched at different content of Cl$_2$in Cl$_2$/Ar plasma. We obtained the maximum etch rate of 883 ${\AA}$/min at Cl$_2$(20%)/Ar(80%). As Cl$_2$ gas increased in Cl$_2$/Ar plasma, the etch rate decreased. The maximum etch rate may be explained by variation of volume density for Cl atoms and by the concurrence of two etching mechanisms such as physical sputtering and chemical reaction with formation of low-volatile products, which can be desorbed only by ion bombardment. The variation of volume density for Cl, F and Ar atoms and ion current density were measured by the optical emission spectroscopy and Langmuir probe. To evaluate the physical damage due to plasma, X-ray diffraction and atomic force microscopy analysis carried out. After etching process, P-E hysteresis loops were measured by ferroelectric workstation.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2010.06a
• /
• pp.385-385
• /
• 2010

In this work, we have investigated the etching characteristics of $TiO_2$ and selectivity of $TiO_2$ over $SiO_2$ thin films as resistance in ReRAM using the inductively coupled plasma. The etch rate and selectivity were measured by varying the $BCl_3$ addition into Ar plasma. The maximum etchrate was obtained at 110.1nm/min at $BCl_3$/Ar=5sccm/10sccm, 500W for RFpower, -100v for DC-bias voltage, and 2Pa for the process pressure. The etched $TiO_2$ surface was investigated with X-ray photo electron spectroscopy. We explained the etching mechanism in two etch mechanisms, physiclas puttering and chemical reaction.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11b
• /
• pp.26-29
• /
• 2001

$SrBi_2Ta_2O_{9}$ thin films were etched at high-density $Cl_2/CF_4/Ar$ in inductively coupled plasma system. The etching of SBT thin films in $Cl_2/CF_4/Ar$ were chemically assisted reactive ion etching. The maximum etch rate was 1300 $\AA$/min at 900W in $Cl_2(20)/CF_4(20)/Ar(80)$. As rf power increase, radicals (F, Cl) and ion(Ar) increase. The influence of plasma induced damage during etching process was investigated in terms of the surface morphology and th phase of X-ray diffraction. The chemical residue was investigated with secondary ion mass sperometry.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.15 no.12
• /
• pp.1011-1015
• /
• 2002

In this study, Au thin films were etched with a Cl$_2$/Ar gas combination in an inductively coupled plasma. The highest etch rate of the Au thin film was 3500 A/min at a Cl$_2$/(Cl$_2$+Ar) gas mixing ratio of 0.2. The surface reaction of the etched Au thin films was investigated using x-ray photoelectron spectroscopy (XPS) analysis. There is Au-Cl bonding by chemical reaction between Cl and Au. During the etching of Au thin films in Cl$_2$/Ar plasma, Au-Cl bond is formed, and these products can be removed by the physical bombardment of Ar ions[l].

• Transactions on Electrical and Electronic Materials
• /
• v.10 no.1
• /
• pp.1-4
• /
• 2009

Dry etching characteristics of indium tin oxide films and etch selectivities over photoresist films were investigated using $Cl_2/HBr$ inductively coupled plasma. From a Langmuir probe diagnostic system, it was observed that while the plasma temperature was kept nearly constant in spite of the change of the HBr mixing ratio, the positive ion density decreases rapidly with increasing the mixing ratio. On the other hand, a quadrupole mass spectrometer showed that the neutral HBr and Br species increased. The etching mechanism in the $HBr/Cl_2$ plasma was analyzed.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2001.11a
• /
• pp.26-29
• /
• 2001

SrBi$_2$Ta$_2$$O_{9}$ thin films were etched at high-density C1$_2$/CF$_{4}$/Ar in inductively coupled plasma system. The etching of SBT thin films in C1$_2$/CF$_{4}$/Ar were chemically assisted reactive ion etching. The maximum etch rate was 1300 $\AA$/min at 900W in Cl$_2$(20)/CF$_4$(20)/Ar(80). As f power increase, radicals (F, Cl) and ion(Ar) increase. The influence of plasma induced damage during etching process was investigated in terms of the surface morphology and th phase of X-ray diffraction. The chemical residue was investigated with secondary ion mass spectrometry.y.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.824-827
• /
• 2000

Fabrication of InP-based photonic devices by dry etch Process is important for clear formation of waveguide mesa structure. We have developed more efficient etch process of the inductively coupled plasma (ICP) with low damages and less polymeric deposits for the InP-based photonic devices than the reactive ion etching (RIE) technique. We report the tendency of etch rate variation by the process parameters of the RF power, pressure, gas flow rate, and the gas mixing ratio. The surface roughness of InP-based waveguide structure was more improved by the light wet etching in the mixed solution of H$_2$SO$_4$:H$_2$O (1:1)

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.145-145
• /
• 2008

High-k materials have been paid much more attention for their characteristics with high permittivity to reduce the leakage current through the scaled gate oxide. Among the high-k materials, $ZrO_2$ is one of the most attractive ones combing such favorable properties as a high dielectric constant (k= 20 ~ 25), wide band gap (5 ~ 7 eV) as well as a close thermal expansion coefficient with Si that results in good thermal stability of the $ZrO_2$/Si structure. During the etching process, plasma etching has been widely used to define fine-line patterns, selectively remove materials over topography, planarize surfaces, and trip photoresist. About the high-k materials etching, the relation between the etch characteristics of high-k dielectric materials and plasma properties is required to be studied more to match standard processing procedure with low damaged removal process. Among several etching techniques, we chose the inductively coupled plasma (ICP) for high-density plasma, easy control of ion energy and flux, low ownership and simple structure. And the $BCl_3$ was included in the gas due to the effective extraction of oxygen in the form of $BCl_xO_y$ compounds. During the etching process, the wafer surface temperature is an important parameter, until now, there is less study on temperature parameter. In this study, the etch mechanism of $ZrO_2$ thin film was investigated in function of $Cl_2$ addition to $BCl_3$/Ar gas mixture ratio, RF power and DC-bias power based on substrate temperature increased from $10^{\circ}C$ to $80^{\circ}C$. The variations of relative volume densities for the particles were measured with optical emission spectroscopy (OES). The surface imagination was measured by scanning emission spectroscope (SEM). The chemical state of film was investigated using energy dispersive X-ray (EDX).

• Journal of the Korean institute of surface engineering
• /
• v.42 no.6
• /
• pp.251-255
• /
• 2009

In this study, the plasma etching of the TaN thin film with $O_2/BCl_3$/Ar gas chemistries was investigated. The equipment for the etching was an inductively coupled plasma (ICP) system. The etch rate of the TaN thin film and the selectivity of TaN to $SiO_2$ and PR was studied as a function of the process parameters, including the amount of $O_2$ added, an RF power, a DC-bias voltage and the process pressure. When the gas mixing ratio was $O_2$(3 sccm)/$BCl_3$(6 sccm)/Ar(14 sccm), with the other conditions fixed, the highest etch rate was obtained. As the RF power and the dc-bias voltage were increased, the etch rate of the TaN thin film was increased. X-ray photoelectron spectroscopy (XPS) was used to investigate the chemical states of the surface of the TaN thin film.

• Proceedings of the Korean Institute of Navigation and Port Research Conference
• /
• 2000.11a
• /
• pp.21-24
• /
• 2000

Ferroelectric YMnO$_3$thin films are excellent dielectric materials for high integrated ferroelectric random access memory (FRAM) with metal-ferroelectric-silicon field effect transistor (MFSFET) structure. In this study, YMnO$_3$thin films were etched with Cl$_2$/Ar gas chemistries in inductively coupled plasma (ICP). The maximum etch rate of YMnO$_3$thin films is 285 $\AA$/min under Cl$_2$/Ar of 10/0, 600 W/-200 V and 15 mTorr. The selectivities of YMnO$_3$over CeO$_2$and $Y_2$O$_3$are 2.85, 1.72, respectively. The results of x-ray photoelectron spectroscopy (XPS) reflect that Y is removed dominantly by chemical reaction between Y and Cl, while Mn is removed more effective by Ar ion bombardment than chemical reaction. The results of secondary ion mass spectrometer (SIMS) were equal to these of XPS. The etch profile of the etched YMnO$_3$film is approximately 65$^{\circ}$and free of residues at the sidewall.