• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.19 no.6
• /
• pp.277-281
• /
• 2009

Superhydrophobic $SiO_2$ thin films were successfully fabricated on a glass substrate by sol-gel method. To fabricate $SiO_2$ thin film with a high roughness, $SiO_2$ nano particles were added into tetraethoxysilane (TEOS) solution. The prepared $SiO_2$ thin film without an addition of $SiO_2$ nano particles showed a very flat surface with ca. 1.27 nm of root mean square (RMS) roughness. Otherwise, the $SiO_2$ thin films fabricated by using coating solutions added $SiO_2$ nano particles of 1.0, 2.0 and 3.0 wt% showed a RMS roughness of ca. 44.10 nm, ca. 69.58 nm, ca. 80.66 nm, respectively. To modify the surfaces of $SiO_2$ thin films to hydrophobic surface, a hydrophobic treatment was carried out using a fluoroalkyltrimethoxysilane (FAS). The $SiO_2$ thin films with a high rough surface were changed from hydrophilic to hydrophobic surface after the FAS treatment. Especially, the prepared $SiO_2$ thin film with a RMS roughness of 80.66 nm showed a water contact angle of $163^{\circ}$.

• Journal of Conservation Science
• /
• v.22
• /
• pp.61-76
• /
• 2008

We examined characterizations of Paraloid B72 films when it dissolved in four different solvents-acetone, MEK, toluene and xylene. The surface before and after coating were observed by optical microscope and AFM. Thickness and contact angle of films was measured and surface energy was calculated for grasping properties of films. We also tested adhesive strength of films by scratch tester and durability of films by performing yellowing test. The result was that xylene has better coating property than other solvents. Because 10% Paraloid B72 in xylene film is even, non-mottled, thin, stabilized in yellowish and has proper hydrophobic, we confirmed xylene is good solvent for bronze artifact conservation. However, other tests will need for finding appropriate concentration of Paraloid B72.

• Journal of Pharmaceutical Investigation
• /
• v.27 no.4
• /
• pp.323-329
• /
• 1997

Ipriflavone is non-hormonal antiosteoporotic drug which inhibits bone resorption by reducing recruitment and/or differentiation of osteoclasts, and stimulates proliferation and differentiation of osteoblast, and also enhances calcitonin secretion in the presence of estrogen. Although some kinds of immediately-released preparation of ipriflavone are available in commercial market, in present study, we tried to formulate sustained-release tablet using coating method with hydrophobic and hydrophilic coating materials. In vitro dissolution test was applied to evaluate sustained-release patterns of several test preparations (Test tablet A, B and C) designed using different preparation method or different compositions. From the results of dissolution test, test tablet A which showed suitable dissolution profile was selected as the candidate of new product. Pharmacokinetic evaluation of test drug, ipriflavone sustained-release tablets, was conducted in 6 beagle dogs weighing $11.5{\pm}0.5\;Kg$ compared with $Theobon^{\circledR}$ tablet, immediately-released tablet (Kukjae Pharm. Co.) as reference drug. Two products were randomly administered to 6 beagle dogs, and after 1 week, cross-over study was conducted. From the present study, AUC and $T_{max}$ of test product were significantly different from those of reference product (p<0.05), respectively$(AUC\;:\;3646.28{\pm}472.56\;vs\;3646.28{\pm}472.56\;ng{\cdot}hr/ml,\;T_{max}\;:\;4.33{\pm}1.03\;vs\;1.42{\pm}0.38\;hr)$. But $C_{max}$ was not significantly different between two products (p>0.05) $(\;512.52{\pm}48.18\;vs\;443.97{\pm}140.53\;ng/ml)$. From the results of pharmacokinetic evaluations, it was noted that absorption amount of test product was increased, but absorption rate was delayed and $C_{max}$ of two products were not changed. And it was concluded that redesign of the sustained-release preparation which has a lower content of iprifavone rather than test tablet A must be considered.

• Composites Research
• /
• v.32 no.6
• /
• pp.388-394
• /
• 2019

Inherited the excellent electrical and mechanical properties based on the low dimensional structure of graphene, three-dimensional graphene nanostructures have gathered great attention as electrochemical energy storage electrodes owing to their high porosity and large specific surface area. Also, having the catecholamine structure, dopamine has been regarded as a multifunctional material to possess high affinity to various organic/inorganic materials and to modify a hydrophobic surface to a hydrophilic one. In this work, through coating dopamine on the three-dimensional graphene nanostructure, we tried to increase the specific capacitance by enhancing the wettability with electrolyte and to improve the mechanical compressive property by strengthening the nano-architecture. As a result, the dopamine-coated nanostructure exhibited significant improvement on the specific capacitance (51.5% increase) and compressive stress (59.6% increase).

• Membrane Journal
• /
• v.24 no.4
• /
• pp.276-284
• /
• 2014

In this study, a hydrophobic polyvinylidene fluoride (PVDF) membrane was modified by coating neutral hydrophilic poly(vinyl alcohol). The flux of pure water was measured and then fouling test was conducted with bovin serum albumin (BSA) as model protein foulant. As a result, the experiments showed that pure water flux was decreased but anti-fouling property was significantly enhanced. Pure water flux with increasing molecular weights of the polymer was decreased and fouling resistance was enhanced. Also, Pure water flux with increasing solution concentration was decreased and fouling resistance was enhanced. It is probably due to the increase in hydrophilicity and decrease in roughness of the membrane surface, as revealed by contact angle and AFM analysis.

• Journal of Power System Engineering
• /
• v.17 no.5
• /
• pp.78-85
• /
• 2013

A high thermal conductivity material, namely graphene is treated by planetary ball milling machine to transport the heat by increasing the temperature. Experiments were performed to assess the heat transfer enhancement benefits of coating the bottom wall of copper substrate with graphene. It is well known that the graphene is unable to disperse into base fluid without any treatment, which is due to the several reasons such as attachment of hydrophobic surface, agglomeration and impurity. To further improve the dispersibility and thermal characteristics, planetary ball milling approach is used to grind the raw samples at optimized condition. The results are examined by transmission electron microscopy, x-ray diffraction, Raman spectrometer, UV-spectrometer, thermal conductivity and thermal imager. Thermal conductivity measurements of structures are taken to support the explanation of heat transfer properties of different samples. As a result, it is found that the planetary ball milling approach is effective for improvement of both the dispersion and heat carriers of carbon based material. Indeed, the heat transfer of the ground graphene coated substrate was higher than that of the copper substrate with raw graphene.

• Tribology and Lubricants
• /
• v.21 no.3
• /
• pp.107-113
• /
• 2005

Micro/nano adhesion and friction properties of self-assembled monolayers (SAMs) with different head- and end-group were experimentally studied according to the coating methods. Various kinds of SAM having different spacer chains (C10 and C18), head-group and end-group were deposited onto Si-wafer by dipping and chemical vapour deposition (CVD) methods under atmospheric pressure, where the deposited SAM resulted in the hydrophobic nature. The adhesion and friction properties between tip and SAM surfaces under nano scale applied load were measured using an atomic force microscope (AFM) and also those under micro scale applied load were measured using a ball-on-flat type micro-tribotester. Surface roughness and water contact angles were measured with SPM (scanning probe microscope) and contact anglemeter respectively. Results showed that water contact angles of SAMs with the end-group of fluorine show higher relatively than those of hydrogen. SAMs with the end-group of fluorine show lower nano-adhesion but higher micro/nanofriction than those with hydrogen. Water contact angles of SAMs coated by CVD method show high values compared to those by dipping method. SAMs coated by CVD method show the increase of nano-adhesion but the decrease of nano-friction. Nano-adhesion and friction mechanism of SAMs with different end-group was proposed in a view of size of fluorocarbon molecule.

• Elastomers and Composites
• /
• v.39 no.4
• /
• pp.301-308
• /
• 2004

Three types of parylene (PA-N, PA-C, PA-D) were used for coating the surface on natural latex rubbers in order to improve surface characteristics including mechanical properties and biocompatibility. The parylene coating was the CVD (chemical vapor deposition) method, and the surface properties of the modified latex were measured. Annealing effects on the mechanical properties of the coated latex were also investigated. The adhesion between latex and parylene was good for all the types of parylene used. As annealing temperature was increased, latex modified with PA-N became more hydrophobic, while the latex treated with PA-C and PA-D became more hydrophilic. As the annealing temperature was raised, the tensile strength was increased, and the elongation was decreased. The biocompatibility was noticeably improved on the latex surface modified with the parylenes through CVD method.

• Journal of Adhesion and Interface
• /
• v.20 no.2
• /
• pp.66-70
• /
• 2019

The surface of hydrophobic polypropylene (PP) fibers (spun-bonded fabric) was treated by an atmospheric plasma treatment method. These pre-treated hydrophilic PP fabrics were dip-coated in the aqueous poly(N-vinyl pyrrolidone) (PVP) solution. PVP layers on the surface of PP fiber were crosslinked by an irradiation of electron beam. The thickness of PVP hydrogels coated on the surface was easily controlled by changing the concentration of PVP in coating solution. The stepwise surface treatment, PVP coating, and hydrogel formation via electron beam irradiation were analyzed by the measurement of contact angle, scanning electron microscopy, and optical microscopy.

• Corrosion Science and Technology
• /
• v.18 no.6
• /
• pp.228-231
• /
• 2019

Aluminum and its alloys have been widely used in various fields because of low weight, high strength, good conductivity, and low price. It is well known that aluminum alloys that cause natural oxide film can inhibit corrosion in wet, salty environments. However, these oxides are so thin that corrosion occurs in a variety of environments. To prevent this problem, an electrochemical anodizing technique was applied to the aluminum alloy surface to form a thick layer of oxide and a unique oxide shape, such as a hierarchical pore structure simultaneously combining large and small pores. The shape of the structures was implemented using stepwise anodization voltages such as 40 V for mild anodizing and 80 V for hard anodizing, respectively. To maximize water repellency, it is crucial to the role of surface structures shape. And a hydrophobic thin film was coated by 1H, 1H, 2H, 2H-Perfluorodecyltrichlorosilane (FDTS) to minimize surface energy of the structure surface. Thus, such nanoengineered superhydrophobic surface exhibited a high water contact angle and excellent corrosion resistance such as low corrosion current density and inhibition efficiency.