• 제목/요약/키워드: Hot Rolled Stainless Steel

검색결과 17건 처리시간 0.023초

열간압연 클래드강의 맞대기용접부 내식성 및 용접성 평가 (Evaluation of Corrosion Resistance and Weldability for the Butt Welding Zone of Hot Rolled Clad Steel Plates)

  • 박재원;이철구
    • Journal of Welding and Joining
    • /
    • 제31권5호
    • /
    • pp.47-53
    • /
    • 2013
  • We have investigated the traits of clad metals in hot-rolled clad steel plates, including the sensitization and mechanical properties of STS 316 steel plate and carbon steel (A516), under various specific circumstances regarding post heat treatment, multilayered welds, and thick or repeated welds for repair. For evaluations, sectioned weldments and external surfaces were investigated to reveal the degree of sensitization by micro vickers hardness, tensile, and etching tests the results were compared with those of EPR tests. The clad steel plates were butt-welded using FCAW and SAW with the time of heat treatment as the variable, a that was conducted at $625^{\circ}C$, for 80, 160, 320, 640, and 1280 min. Then, the change in corrosion resistance was evaluated in these specimens. With carbon steel (A516), as the heat treatment time increased, the annealing effect caused the tensile strength to decrease. The micro-hardness gradually increased and decreased after 640 min. The elongation and contraction of the area also increased gradually. The oxalic acid etch test and EPR test on STS316 and the clad metal showed STEP structure and no sensitization. From the test results on multi-layered and repair welds, it could be concluded that there is no effect on the corrosion resistance of clad metals. The purpose of this study was to suggest some considerations for developing on-site techniques to evaluate the sensitization of stainless steels.

AISI 316L 클래드강의 맞대기 용접부 입계부식과 예민화 거동에 관한 연구 (The Sensitization and Intergranular Corrosion Behavior of AISI 316L Clad Steel with Butt Welding)

  • 이철구;박재원
    • Journal of Welding and Joining
    • /
    • 제31권2호
    • /
    • pp.49-56
    • /
    • 2013
  • We have investigated traits of clad metals in hot-rolled clad steel plates, sensitization and mechanical properties of STS 316 steel plate and carbon steel(A516). Clad steel plates were butt-weld by SAW+SMAW, and with the time of heat treatment as the variable, heat treatment was conducted at $625^{\circ}C$, for 80, 160, 320, 640, 1280 minutes. As a way to evaluate it, sectioned weldments and external surfaces were investigated to reveal the degree of sensitization by mechanical property, etching and those of EPR test, results were compared with it. In short, the purpose of this study is suggesting some considerations in developing on-site techniques to evaluate the sensitization of stainless steels.

클래드강 맞대기 용접부의 후열처리 유지시간에 따른 델타 페라이트 거동 (δ-Ferrite Behavior of Butt Weld Zone in Clad Steel Plates Depended on Holding Time of PWHT)

  • 박재원;이철구
    • Journal of Welding and Joining
    • /
    • 제32권2호
    • /
    • pp.29-36
    • /
    • 2014
  • Recently, in order to enhance the function and usefulness of products, cladding of dissimilar materials that maximizes the performance of the material is being widely used in all areas of industry as an important process. Clad steel plate, produced by cladding stainless steel plate, an anticorrosive material, on carbon steel plate, is being used to produce pressure vessels. Stainless steel plate has good corrosion resistance, and carbon steel plate has good rigidity and strength; clad steel can satisfy all of these qualities at once. This study aims to find the ${\delta}$-ferrite behavior, mechanical properties, structure change, integrity and reliability of clad steel weld on hot rolled steel plates. For this purpose, multi-layer welding, repair welding and post weld heat treatment were implemented according to welding procedure specifications (WPS). In order to observe the mechanical properties and toughness of clad steel weld zone, post weld heat treatment was carried out according to ASME Sec. VIII Div.1 UW-40 procedure for post weld heat treatment. With heat treatment at $625^{\circ}C$, the hold time was used as the process variable, increased by intervals that were doubled each time, from 80 to 1,280 min. The structure of weld part was typical cast structure; localized primary austenite areas appeared near central vermicular ferrite and fusion line. The heat affected zone showed rough austenite structure created by the weld heat input. Due to annealing effects of heat treatment, the mechanical properties (tensile strength, hardness, impact value) of the heat affected area tended to decrease. From the results of this study, it is possible to conclude the integrity of clad steel welds is not affected much in field welding, repair welding, multi-layer welding, post weld heat treatment, etc.

용접 공정 디자인에 따른 클래드강의 기계적 성질 변화 (Change of Mechanical Properties of Clad Steel According to the Welding Process Design)

  • 이정현;박재원
    • 한국생산제조학회지
    • /
    • 제22권3호
    • /
    • pp.372-379
    • /
    • 2013
  • In this study, we investigated the traits of the clad metals used in hot-rolled clad steel plates. We examined the sensitization and mechanical properties of STS 316 steel plate and carbon steel (A516) under the specific circumstances of post heat treatment and whether a weld was multilayered and thick or repeated because of repairs. The test conditions were as follows. The clad steel plates were butt-welded using FCAW/SAW, and the heat treatment was conducted at $625^{\circ}C$, for 80, 160, 320, 640, or 1280 min. The change in the corrosion resistance was evaluated in these specimens. In the case of the carbon steel (A516), as the heat treatment time increased, the annealing effect caused the tensile strength to decrease. The micro- hardness gradually increased and then decreased after 640 min. The elongation and contraction of the area increased gradually. An oxalic acid etch test and EPR test on STS316, a clad metal, showed a STEP structure and no sensitization. From the test results for the multi-layered and repair welds, it could be concluded that there is no effect on the corrosion resistance of clad metals. In summary, the purpose of this study was to suggest some considerations when developing on-site techniques and evaluate the sensitization of stainless steels.

MICROSTRUCTURAL OBSERVATION AND TENSILE ISOTROPY OF AN AUSTENITIC ODS STEEL

  • Kim, Tae-Kyu;Bae, Chang-Soo;Kim, Do-Hyang;Jang, Jin-Sung;Kim, Sung-Ho;Lee, Chan-Bock;Hahn, Do-Hee
    • Nuclear Engineering and Technology
    • /
    • 제40권4호
    • /
    • pp.305-310
    • /
    • 2008
  • Based on a composition of 99.4 wt% AISI 316L stainless steel, 0.3wt% Ti and 0.3 wt% $Y_2O_3$, an austenitic ODS steel was fabricated by a process of mechanical alloying, hot isostatic pressing and rolling. Fine oxide particles were observed in the matrix, and their chemical formulations were determined to be $Y_2Si_2O_7$ and TiO. Heat treatment of the cold-rolled sample at $1200^{\circ}C$ induced an isotropic tensile behavior at room temperature and at $700^{\circ}C$. This result would be mainly attributed to the equiaxed grains that form as a result of the heat treatment for recrystallization.

0.04% Gd-이상 스테인레스 강의 부식 및 마모성에 대한 집합조직 효과 (Effect of Texture on the Corrosion and Wear Behaviors of 0.04% Gd-Duplex Stainless Steels)

  • 백열;최용;문병문;손동성
    • 한국표면공학회:학술대회논문집
    • /
    • 한국표면공학회 2014년도 추계학술대회 논문집
    • /
    • pp.212-212
    • /
    • 2014
  • 0.04% Gd-duplex stainless steels (Gd-DSTSs) for neutron absorbing materials were inert arc-melted and poured into a Y-shape block with the size of $100{\times}100{\times}20[mm]$. The Gd-DSTS was hot rolled at $1200^{\circ}C$ followed by cold rolling to have 33% reduction. The average grain sizes of the rolling (RD), transverse (TD) and short transverse (ST) directions were 6, 7, $11{\mu}m$, respectively. The micro-hardnesses of the RD, TD and ST directions were 258.5, 292.3, 314.7 $H_V$, respectively. Corrosion potential and corrosion rate of the cold rolled Gd-duplex stainless steel in aerated artificial sea water and 0.1M $H_2SO_4$ solution were $0.2216V_{SHE}$, $0.0106A/cm^2$, $-0.0825V_{SHE}$, $0.0168A/cm^2$ for RD, $0.2210V_{SHE}$, $0.0077A/cm^2$, $0.0817V_{SHE}$, $0.0092A/cm^2$ for TD, $0.1056V_{SHE}$, $0.0059A/cm^2$, $0.0475V_{SHE}$, $0.0069A/cm^2$ for ST, respectively. The corrosion behavior depended on the texture, which were due to mainly grain boundary and minorly crystallographic texture. Friction coefficient and wear resistance were 2.07 and 0.48 mm, respectively.

  • PDF

직접 에너지 적층을 통한 STS316L 소재의 보수 공정에서 그루브 형상이 기계적 특성에 미치는 효과 (Effect of Groove Shapes on Mechanical Properties of STS316L Repaired by Direct Energy Deposition)

  • 오욱진;손용;손종윤;신광용;심도식
    • 소성∙가공
    • /
    • 제29권2호
    • /
    • pp.103-112
    • /
    • 2020
  • This study explores the effects of different pre-machining conditions on the deposition characteristics and mechanical properties of austenitic stainless steel samples repaired using direct energy deposition (DED). In the DED repair process, defects such as pores and cracks can occur at the interface between the substrate and deposited material. In this study, we varied the shape of the pre-machined zone for repair in order to prevent cracks from occurring at the slope surface. After repairs by the DED process, macro-scale cracks were observed in samples that had been pre-machined with elliptic and trapezoidal grooves. In addition, it was not possible to completely prevent micro-crack generation on the sloped interfaces, even in the capsule-type grooved sample. From observation of the fracture surfaces, it was found that the cracks around the inclined interface were due to a lack of fusion between the substrate and the powder material, which led to low tensile properties. The specimen with the capsule-type groove provided the highest tensile strength and elongation (respective of 46% and 571% compared to the trapezoidal grooved specimen). However, the tensile properties were degraded compared to the non-repaired specimen (as-hot rolled material). The fracture characteristics of the repaired specimens were determined by the cracks at the sloped interfaces. These cracks grew and coalesced with each other to form macro-cracks, they then coalesced with other cracks and propagated to the substrate, causing final fracture.