• Resources Recycling
• /
• v.30 no.2
• /
• pp.14-23
• /
• 2021

To investigate the potential for leaching of heavy metals by bacteria from ores stacked on actual mining sites, leaching tests of a complex metallic ore (Pb-Zn-As ore) were conducted over 60 days using acidophile bacteria Acidithiobacillus ferrooxidans and Acidithiobacillus thiooxidans under initial acidic conditions. Initially, a small amount of heavy metals was leached due to the initial acidic conditions. After 20 days, when A. thiooxidans in the reactor was adapted to the ore, the amount of leached heavy metals rapidly increased; the concentrations of leached arsenic, iron, and zinc reached a maximum of 2800, 3700, and 2500 mg/L, respectively. On the other hand, in the presence of A. ferrooxidans or in the control test without bacteria, heavy metals, except zinc, were barely detected in leaching. Through this study, it was confirmed that (i) bacteria could leach heavy metals at mining sites under acidic conditions and (ii) leaching of heavy metals from a high arsenic-containing ore by A. thiooxidans was more significant than that by A. ferrooxidans.

• Resources Recycling
• /
• v.30 no.4
• /
• pp.11-19
• /
• 2021

Arsenic (As) oxidation followed by precipitation from a high-As(III)-containing leaching solution derived from a sulfidic ore was investigated in this study to remove aqueous As from the solution using activated carbon (AC) with air injection as an oxidant. To obtain the initial leaching solution, a domestic sulfidic ore was leached in a sulfuric acid solution at pH 1 and 50℃ for 95 h, and approximately 7 g/L of Fe and 3 g/L of As were leached out. To determine the effect of the oxidative reaction utilizing AC with air injection, the leaching solution was tested under the following five oxidative conditions at an initial pH of 1 and 90℃ for 72 h: air-only injection; air injection with 1, 5, and 10 w/v% of AC addition; and H₂O₂ addition. The tests in the presence of both air and AC revealed that the oxidation kinetics and As removal were improved by the reaction between the metallic species and the surface group formed on the AC surface. In addition, the greater the amount of AC added, the better was the reaction efficiency, removing 93-94% of As with more than 5 w/v% of AC addition. Finally, X-ray diffraction analysis confirmed that the precipitate formed from the oxidative reaction was scorodite (FeAsO₄·2H₂O).