• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.25 no.4
• /
• pp.629-636
• /
• 2001

In order to investigate the possibility of impact punching in brittle materials, an experimental setup was developed. In the setup, a long bar as a punch was used to apply the impact load to the specimen plate and measure the applied impact force during the impact punching process. Impact punching tests with various shape of punches were performed in soda-lime glass and silicon wafer under a different level of contact pressure. The damage appearance after the impact punching was examined according to the applied contact pressure. The minimum contact pressure required for a complete punching in glass specimens without development of radial cracks around the punched hole was sought at each condition. The minimum contact pressure increased with increasing the thickness of specimens and decreasing the end radius of punches. The profile of impact forces was measured during the impact punching experiment, and it could explain well the behavior of the punching process in brittle material plates. The measured impact force increased with increasing the contact pressure applied to the plates.

• Journal of the Korean Society for Heat Treatment
• /
• v.9 no.3
• /
• pp.169-176
• /
• 1996

Effect of retained austenite on rolling contact fatigue of nitrocarburized high-carbon chromium bearing steel has been investigated to develop surface-hardened bearing steel with imprved resistance to rolling contact fatigue. Fatigue tests were conducted in elesto-hydrodynamic lubricating conditions at a shaft speed of 5,000rpm, under max, hertzian stress of $492kg/mm^2$. Volume fraction of retained austenite in austenitic nitrocarburized STB2 steel was controlled by tempering at various temperature, $200{\sim}250^{\circ}C$. It was observed using TEM that decomposition of retained austenite during tempering at $250^{\circ}C$ was the highest in quantity, resulted in formation of lower bainite. Rolling contact fatigue life of the specimens with lower bainite, formed by decomposition of retained austenite, was improved in comparison with there of specimens with more amount of retained austenite.

• Transactions of the Korean Society for Noise and Vibration Engineering
• /
• v.16 no.5 s.110
• /
• pp.441-451
• /
• 2006

It is known that ball bearings mounted in housing or on shaft are playing a key role to keep it running smoothly. The roundness of a housing bore on which bearing outer ring is mounted with interference has directly affected the running accuracy of bearing. The running accuracy of bearing, therefore, can extend the significant influence to the rotating machinery as well. In this paper, bearing's vibration and fatigue life considering raceway roundness of ball bearing before and after mounted in housing bore are theoretically estimated. To perform analysis, a simple three degrees of freedom model was proposed and then Newton-Raphson iterative method was introduced to be utilized in the analysis. The results show that the vibration magnitude of ball bearing fitted into housing unit is appeared considerably larger than the one of its pre-assembling. And theoretical $L_{10}$ life which ninety percent of the bearing population will endure decreased in about fifty percent.

• Journal of Powder Materials
• /
• v.5 no.1
• /
• pp.15-21
• /
• 1998

The effect of $\alpha$/$\beta$ phase on the mechanical properties and contact damage of silicon nitrides $Si_3N_4$) was investigated. Silicon nitride materials were prepared from two starting powders, at selective increasing hot-pressing temperatures to coarsen the microstructures: (i) from relatively coarse $\alpha$-phase powder, essentially equiaxed $\alpha$-$Si_3N_4$ grains, with limited, slow transformation to $\beta$-$Si_3N_4$ grain; (ii) from relatively fine $\alpha$-phase powder, a more rapid transformation to $\beta$-$Si_3N_4$, with attendant grain elongation. The resulting micro-structure thereby provided a spectrum of $\alpha$/$\beta$ phase ratios, grain sizes, and grain shapes. Fracture strength, hardness, and toughness were measured, and contact damage and strength degradation after indentation were investigated by Hertzian indentation using spherical indenter. A brittle to ductile transition in $Si_3N_4$ depended on $\alpha$/$\beta$ phase ratio as well as grain size. Silicon nitride with elongated $\beta$ grains showed a superior, contact damage resistance.

• Journal of the Korean Ceramic Society
• /
• v.35 no.1
• /
• pp.48-54
• /
• 1998

The effect of coating thickness on the contact fracture was studied, in Si3N4 coated Si3N4-BN system When the elastic/plastic mismatch is relatively large betwen two layers in bilayer certain critical coating thickness was required to prevent cone crack initiation and this critical thickness was decreased by de-creasing the elastic/plastic mismatch,. In addition the required critical thickness should be increased when higher loads apply. In conclusion an appropriate coating thickness should be designed by elastic/plastic mismatch between two layers and environment (applied load) to prevent the coating fracture

• Proceedings of the Korean Society for Noise and Vibration Engineering Conference
• /
• 2005.11a
• /
• pp.112-118
• /
• 2005

Ball bearings which were fitted between housing and shaft play an important role in rotating shaft system smoothly, Therefore bearing's running accuracy has significant influence on that of rotating machinery. Manufacturing accuracy of bearings as well as that of shaft and housing is main factor to affect bearing running accuracy In this paper, bearing's vibration and fatigue life considering raceway roundness of ball bearing before and after being fitted into housing are theoretically estimated. To perform analysis, a simple three degrees of freedom model was proposed and then these analysis was conducted utilizing the Newton-Raphson iterative method. The results show that vibration magnitude of ball bearing fitted into housing is considerably larger than before assembly, and bearing's theoretical L$_{10}$ fatigue life that ninety percent of the bearing population will endure decreased in about fifty percent.

• Journal of the Computational Structural Engineering Institute of Korea
• /
• v.16 no.2
• /
• pp.141-151
• /
• 2003

Railway bridges are subject to dynamic loads generated by the interaction between moving vehicles and the bridge structures. These dynamic loads result in response fluctuations in bridge members. To investigate the real dynamic behavior of the bridge, therefore, a number of analytical and experimental Investigations should be carried out. In this paper, a train/track/bridge interaction analysis program for evaluating the dynamic characteristics of bridges due to KTX operation in terms of structural safety, operational safety and passenger comfort is developed. To build a practical model of train/track/bridge, Hertzian spring for wheel/rail contact modeling and Winkler element for ballast are applied. This program also used torsional degree of freedom and constraint equation based on geometrical relationship in order to take into consideration three-dimensional eccentricity effect due to the operation on double track through quasi-three dimensional analysis. To verify the developed Program, comparison has been made between the measured results and those of simulation of the typical PSC box bridge(2@40m=80m) of the KHSR bridges.

• Tribology and Lubricants
• /
• v.31 no.1
• /
• pp.1-5
• /
• 2015

In this study, we apply an ultrasonic nanocrystal surface modification (UNSM) technique to radial journal bearings (JBs) and disks made of SUJ2 and SCM440, respectively. We investigate frictional properties of untreated and UNSM-treated specimens using a ball-on-disk tester. We construct the Stribeck curve at the boundary, under mixed and full hydrodynamic lubrication conditions for the specimens using friction data obtained from JB tests. The friction at the boundary lubrication condition and the transition period to mixed lubrication condition on the UNSM-treated specimens is reduced, which improves the service life of JBs. The major effects of this reduction in the three lubrication regimes can be explained in the terms of improved mechanical properties and the presence of micro dimples. Moreover, we estimate the friction and fatigue properties of SCM440 specimens using a ball-on-disk specimen under dry and oil-lubricated conditions. Friction test results reveal that the UNSM-treated specimens show lower friction coefficient than the untreated specimens under both dry and oil-lubricated conditions. We evaluate the fatigue properties of SCM440 specimens by calculating the Hertzian stress with respect to the failure cycles. Fatigue tests results also reveal that the UNSM-treated specimens possess a longer fatigue life than the untreated specimens. The improved properties are effective in increasing the energy efficiency of bearings.

• Journal of Korean Society of Steel Construction
• /
• v.11 no.1 s.38
• /
• pp.33-42
• /
• 1999

In the present study, crack initiation criteria, static failure and tensile mode fatigue behavior for a rail steel are evaluated to assure the railway vehicle's safety. The transverse fissure, which is the most critical damage in the rail, is initiated by the maximum shear stress and its location is subsurface. In addition, the possibility of transition from the shear mode to the mixed mode increases with increasing the length of subsurface crack. Because of the brittleness by the welding, the fracture toughness of the welded part is lower than of the base metal. For low ${\Delta}K$, the stage II fatigue crack growth rates of the welded part is slower than of the base metal but, for high ${\Delta}K$, this different behavior for fatigue crack growth rate is nearly diminished. These trends are more remarkable for low stress ratio, R=0.1. It is believed that this behavior is caused by the change of the microstructure which that of the welded part is coarser than of base metal.

• Journal of the Korean Ceramic Society
• /
• v.42 no.8 s.279
• /
• pp.554-560
• /
• 2005

The engineering ceramic needs the properties of high strength, hardness, corrosion-resistance and heat-resistance in order to withstand thermal shock or applied nonuniform stresses without failure. The densely coated porous ceramics can be used for machine component, electromagnetic component, bio-system component and energy-system component by their high-performances from superior coating properties and light-weight characteristics due to the structure including pore by itself. In this study we controlled the porosity of silica and alumina, $8.2\~25.4\%$ and $23.4\~36.0\%$, respectively, by the control of sintering temperature and starting powder size. We made bilayer structures, consisting of a transparent glass coating layer bonded to a thick substrate of different porous ceramics by a thin layer of epoxy adhesive, facilitated observations of crack initiation and propagation. The elastic modulus mismatch could be controlled using different porous ceramics as the substrate layer. Then we applied 150 N force using WC sphere with a radius of 3.18 mm by Hertzian indentation. As a result, the crack initiation in the coating layer was delayed at lower porosity in the substrate layer, and the damage in the coating layer was relatively smaller at the bilayer structure coated on higher elastic substrate.