The present study was conducted to evaluate the effects of dietary formulated feed additive on growth performance and carcass traits of Hanwoo steers. A formulated feed additive reported to reduce heat load in the rumen in our previous research was used (Cho et al., 2014). Total 32 herds of Hanwoo steers were assigned into two groups of control and treatment. Total mixed ration was provided as basal diet for cattle and 100 g of additive was supplemented on diet for treatment. Feeding trial was performed during 120 days before slaughter. For growth performance, 3 periods (0~90 days; 90~120 days; 0~120 days) were allotted and average daily gain, feed requirement and final body weight were determined. Loin meat between $12^{th}$ and $13^{th}$ rib was used for meat quality analysis after slaughtering. Only $1^{st}$ period showed significantly improved growth performance of treatment (P<0.05) and there were no significant difference in other periods. At $3^{rd}$ periods (overall), a trend of increased average daily gain was found at treatment (P=0.075). Carcass performance and quality did not show significant differences between treatment and control (P>0.05). In meat quality, treatment showed significant increment in all measured meat colors (P<0.05) and significantly less sharing force compared to the control (P<0.05). Although no significant difference in growth performance and carcass yield were found, remarkably improved economic status was detected in treatment group. In conclusion, it could be suggested that application of a formulated feed additive specialized in reduction of heat load in the rumen was able to increase economical balance through enhancing heat stress condition of ruminant and growth.

• Journal of the Korean Society for Heat Treatment
• /
• v.9 no.4
• /
• pp.281-288
• /
• 1996

This study has been investigated the influence of solid solution treatment on the microstructure of Mg-6Al-xZn(x=0,1,2) alloys fabricated by squeeze casting process. The products having clean surface and fine microstructure are fabricated by adopting the liquid metal forging method. The microstructures of as-fabricated state show ${\beta}(Mg_{17}Al_{12})$ precipitates between the dendrite boundaries. It is found that the hardness of the alloys is increased with increasing amount of zinc due to the solid solution hardening effect of zinc. In the changes of microstructure upon solid solution treatment time at $405^{\circ}C$, ${\beta}$ phases are dissolved in ${\alpha}$ matrix up to 1hr and the microstructure are coarsened rapidly after 2hrs. The microhardness are decreased rapidly until 1hr of solution treatment time and then stabilized. From the above results, it is concluded that the optimum solid solution treatment condition for Mg-6Al-xZn alloys is at $405^{\circ}C$ for 1hr. The solution treatment time is greatly reduced comparing to conventional casting(at $385{\sim}418^{\circ}C$ for 10~14hrs) due to the formation of the super-saturated solid solution by liquid metal forging.

• Journal of the Korean Society for Heat Treatment
• /
• v.32 no.5
• /
• pp.212-223
• /
• 2019

This study is to investigate the relationship between microstructural factors and tensile properties after aging heat treatment of the 15-5PH stainless steel at the temperature range of $450^{\circ}C$, $500^{\circ}C$ and $550^{\circ}C$ for various time. For the aging time of 2 hours, hardness showed maximum at $450^{\circ}C$ and then decreased with increasing aging temperature. While, hardness decreased gradually during aging $450^{\circ}C$, $500^{\circ}C$ and $550^{\circ}C$ from 1 hour to 5 hours but the hardness nearly unchanged until the 100 hours after 5 hours aging. When aging at $450^{\circ}C$, Cu atoms preferentially aggregated at the prior austenite grain boundaries and martensite lath boundaries, and Cu concentration at those boundaries was nearly unchanged even after aging for 100 hours. Therefore it was suggested that the coherency is still maintained after 100 hours aging at $450^{\circ}C$. Aging at $500^{\circ}C$ and $550^{\circ}C$ results in an increase in the concentration of Ni at the martensite lath boundaries and prior austenite grain boundaries, resulting in the formation of reversed austenite. Especially, when aged at $550^{\circ}C$ for 100 hours, the concentration of Ni remarkably increased at those boundaries, and thus the microstructure of herring bone shape was appeared. Considering the migration of Ni atom to the lath boundaries and prior austenite grain boundaries, Ni atoms contributed greatly to the formation of reversed austenite. On the other hand, it was found that Cu atoms hardly moving to those boundaries may not be contributed to the formation of reversed austenite. When aging at $450^{\circ}C$, the coarsening of the precipitated Cu atoms proceeded very slowly with increasing aging time, therefore the decrease in strengths were small but the reduction area was considerably increased due to the softening of the matrix. At the aging temperature of $500^{\circ}C$ and $550^{\circ}C$, the strengths decreased and the elongation and reduction area increased due to the appearance of the reversed austenite. Especially, the increase of reduction area was remarkable.

• Journal of the Korean Wood Science and Technology
• /
• v.37 no.4
• /
• pp.330-339
• /
• 2009

The material properties of Cedar (Cryptomeria japonica) were evaluated according to heat treatment conditions. The special focus was made on the color control of cedar wood by heat treatment. The difference of color between sapwood and heartwood could be reduced by heat treatment at a temperature above $170^{\circ}C$. Long heating time was more effective in reducing the difference. The Equilibrium Moisture Content (EMC) of heat-treated wood was as low as 50 percent. The result obviously indicates that heat-treated wood is more dimensionally stable in the change of moisture condition than the control. The heat-treated wood was also effective in increasing the durability against wood rotting fungi. However, more study is required to develop heat treatment as an environmentally-friendly technology for wood preservation without chemical. The mechanical properties of heat-treated wood showed relatively higher performance than the control in general. Meanwhile the dramatic decrease in impact bending stress due to the loss of ductility may limit uses of heat-treated wood in certain cases. There were no significant changes in microscopic structure which may cause changes in mechanical properties. Further study on the chemical analysis of heat-treated wood is needed to scrutinize the causes of changes of material properties.

• 한국연소학회:학술대회논문집
• /
• 2001.11a
• /
• pp.83-89
• /
• 2001

Most technologies of reduction process used in the heat treatment of existent metal products are related to metals applied to bolts and parts of automobiles, and nonmetal such as copper. Heating conditions and reduction gases produced in above processes depend on types of products to be treated thermally but heating systems employ electricity commonly and the reduction gases are separated into additional production equipment and a gas dryer and inefficiently provided into the system. Electrical heating system has the advantage of convenient temperature-control but is not economical because of disadvantages of high electricity-running cost and extra installation cost of a transformer. Accordingly, development of the system which has economical heating mode in which provision of reduction gas and heating conditions are unified is necessary for improvement of economy and efficiency in current reduction processes. This study aimed to develop a new advanced heat treatment furnace using catalytic combustion. thereby minimizing the cost during heating, supplying heat and reductive gas at the same time and controlling operating condition freely by changing electrical heating system to heating system by the gas combustion and regeneration of wasted heat.

• Journal of the Korean Society for Heat Treatment
• /
• v.26 no.2
• /
• pp.66-71
• /
• 2013

The purpose of this study is to prepare a high-strength Fiberglass Reinforced Metal (FRM). Aluminum covering over carbon fibers (CF) was made to increase their wettability to molten aluminum. A cylindrical sputtering apparatus was used for the covering. One tow of carbon fibers was placed along the central axis of the cylindrical target. Aluminum was uniformly coated around the carbon fiber tow. But in case of CF without sizing treatment, aluminum spread into the inside of the tow. Preforms of carbon fiber/aluminum composite were made by impregnating carbon fiber with molten aluminum. Contact angle of molten aluminum to the aluminum-coated carbon fiber was about $30^{\circ}$. The fractured section of preform was observed by SEM, which showed that molten aluminum wetted the outer part of the tow well but had not penetrated into the center, and that adhesion between CF and aluminum matrix was in good condition.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.19 no.2
• /
• pp.30-37
• /
• 2020

We propose a practical method for increasing formability of a sheet metal plate using laser heat treatment (LHT) and cladding process. In this work, two kinds of process such as laser-induced heat treatment and cladding were utilized to evaluate the effect on formability of SUS316 sheets with different thickness of 1 and 3 mm. By using a vertically line-patterned tensile specimen that was LHTed or cladded on its surface, the process parameters of each surface treating method were studied and optimized. Through the basic test, we knew that the laser power of 900 W and scanning speed of 500 mm/min was the best condition for increase of formability. As the treatment results, ultimate tensile strength and elongation were increased as approximately 2.1 and 7.0%, respectively. To verify the usefulness of this work in industrial cases, we conducted a bulging test using with and without LHTed SUS316 sheet metal blanks. The results show that the bulging height of LHTed sheet was increased by 73% compared to that of the original one.

• Journal of the Korean Society for Heat Treatment
• /
• v.16 no.3
• /
• pp.134-140
• /
• 2003

Effects of cryogenic treatment and tempering temperature on the amount of retained austenite, hardness and wear properties has been investigated using alloy tool steel, STD 11. Cryogenic treatments were performed at the temperatures of $-100^{\circ}C$, $-150^{\circ}C$ and $-196^{\circ}C$, and tempering were performed at $200^{\circ}C$ and $530^{\circ}C$. It was shown that lower hardness value was obtained on high temperature ($530^{\circ}C$) tempering even after cryogenic treatment. And retained austenite was not entirely transformed to martensite after cryogenic treatment even at $-196^{\circ}C$, which was not consistent with the belief that $-80^{\circ}C$ was sufficient to entirely transform any austenite retained in the quenched microstructure. Austenite retained in cryogenic treated condition was completely transformed to martensite only after tempering at $530^{\circ}C$. As far as wear test conditions in this investigation, it was found that cryogenic treatments improved the sliding wear resistance, but improvement of wear resistance was not directly related with retained austenite contents. And it was found that predominent wear mechanisms of STD 11 steel were oxidation wear and adhesive wear In sliding wear conditions.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.14 no.2
• /
• pp.79-87
• /
• 1978

This is an experimental study on friction welding and heat treatment of engine exhaust valve materials whose welding combination is SCr4 as stem to 21-4N as head and SUH3 to 21-4N. In this study, not only the experiments of friction welding under the selected optimum welding condition and the examination of the mechanical properties were carried out, but also the heat treatment of friction welded specimens under the two selected conditions was taken to obtain the better welding character, eliminating the latent stress and the hardness peak which appeared at the welded zones of heat resisting steel(21-4N, SUH3) and low alloyed steel ($SCr_4$) friction weldments. The results obtained by the experiments and consideration in this study are as follows: I) It was experimentally proved quite reasonable that 'speed=3,OOO rpm, heating pressure Pl=8 kg/ mm2, upsetting pressure p, = 20 kg/mm', heating time $t_1$ = 3 see, upsetting time TEX>$t_2$ = 2.5 sec' was selected as the optimum welding condition for friction-welding the engine exhaust valve materials $SCr_4$ to 21-4 Nand SUH 3 to 21-4 N. 2) The results of the previous study and this one on friction welding of such dissimilar materials as SUH 3-SUH 31, SCr 4-SUH 31, SCr 4-SUH 3, SUH 3-CRK 22, SCr4-21-4 Nand SUH3-21-4 N agreed with each other substantially in the friction welding characteristics at welded interface zones. 3) It was also certified quite satisfactory that '600\ulcornerCX30 min. Xroom air cooling' as an optimum heat treatment condition of the friction welded materials SCr 4-21-4 Nand SUH 3-21-4 N was experimentally determined to eliminate the latent stress and the hardness peak at welded zones. 4) About 20% of the tensile strength before heat treatment of friction welded specimens was decreased after heat treatment 600\ulcornerCX30 min. Xair cooling, but the location of fracture was moved from heat affected zone to parent $SCr_4$ & SUH3. 5) Microscopic examination of the weld joints friction-welded and heat-treated under the above mentioned conditions revealed that the weld zone is very narrow and has a fine grained intermixed structure without any welding defects. 6) The above mentioned conditions can be also utilized as friction welding parameters of the other dissimiar materials for engine valve production.

• Restorative Dentistry and Endodontics
• /
• v.19 no.1
• /
• pp.135-147
• /
• 1994

This study was conducted to evaluate whether the fatigue toughness of visible light cured composite resins could be improved and how much percentage of polymerzation shrinkage could be affected by additional heat treatment. 7 materials were investigated for this study: P-50, Lite-fil CR inlay, Pekafil, Clearfil CR inlay, Clearfil photo posterior, Z -100 and Progress. Diametral tensile strengths and linear shrinkages of composite resins were taken under visible light cured and additional post-cure heated condition and compared each other. A fatigue toughness of above materials was evaluated by measuring diametral tensile strength after they were repeatedly loaded with 120kgf/$cm^2$ up to 3000 cycles. The results obtained were as follows : 1. When composite resins were cured just by visible light, Lite fil CR inlay, Z -100 and Progress showed respectively higher diametral tensile strength than the other materials. Clearfil CR inlay, Clearfil photo posterior and Progress exhibited strong fatigue toughness compared to P-50 and Pekafil. 2. Post-cure heat treated composite resins had higher diametral tensile strengths than visible light cured composite resins at fatigue toughness test as well as no fatigue toughness test. 3. When Composite resins were additionally polymerized by post-cure heat treatment, P-50 showed weak fatigue toughness, on the contrary, Clearfil CR inlay, Z-100, Progress showed strong one. 4. When composite resins were cured just by visible light, percentage of polymerization linear shrinkage was the lowerest in Clearfil CR inlay, followed by, in ascending order, Clearfil photo posterior, Lite-fil CR inlay, Progress, Pekafil, P-50, and Z-100. In the case of post- cure heat treated composite resins, percentage of linear shrinkage was the lowest in Clearfil photo posterior, followed by, in ascending order, Lite-til CR inlay, Clearfil CR inlay, Progress, P-50, Pekafil and Z-100. 5. Percentage of polymerization linear shrinkage was greater in the post-cure heat treated composite resins than in the visible light cured composite resins and linear shrinkage increased significantly in Pekafil, Clearfil CR inlay, and Clearfil photo posterior between at the visible light cured and at the post-cure heat treated condition. The above results is saying that additional post-cure heat treatment on the composite resins for posterior restoration is able to affect on improvement of strength and fatigue toughness and lead to increase polymerization of composite resins.