• Journal of the Korean Wood Science and Technology
• /
• v.24 no.1
• /
• pp.95-99
• /
• 1996

The bending and compression strength properties of two types Rhus verniciflua specimens, which made of no heat-treated wood and heat-treated wood for urushiol extraction, were measured. The heat-treated specimens were finger-jointed with either resorcinol-phenol or polyurethane resin adhesives, and the vertical type bending strength property was also measured in these specimens. The results obtained are as follows ; 1. The correlation coefficient between the compression strength and specific gravity in the specimens of no heat-treated and heat-treated wood was high. However there was no difference in compression strength property as affected by heat treatment. 2 The correlation coefficient between the bending strength and specific gravity in the specimens of no heat-treated and heat-treated wood was also high. However, there was no difference in bending strength property as affected by heat treatment. 3 The bending test showed high correlation between modulus of elasticity and modulus of rupture for the specimens made of no heat-treated and heat-treated wood. However, there was no difference in bending strength property between the specimens made of heat-treated and no heat-treated wood. 4. The efficiencies of bending strength test on the finger-jointed specimens of heat-treated wood with resorcinol-phenol and polyurethane resin adhesives were 0.85, 0.81. respectively.

• Fashion & Textile Research Journal
• /
• v.17 no.2
• /
• pp.295-304
• /
• 2015

This paper investigated wear comfort property of heat storage knitted fabrics for high emotional garment. For this purpose, ZrC imbedded PET knitted fabric was prepared and various physical properties such as thermal, wicking and drying characteristics were measured. In addition, far-infrared emission characteristics of ZrC imbedded PET was analysed and tactile hand property and dye affinity of ZrC imbedded knitted fabric were also studied in comparison with regular and other commercial heat storage PET knitted fabrics. It was observed that Zr imbedded amount in the yarn was 19.29% by ingredient analysis and far-infrared emission energy was $3.65{\times}10^2W/m^2$, emissivity was 0.906 at the range of wavelength $6{\sim}20{\mu}m$. It was found that maximum heat flow (Qmax) of ZrC imbedded PET knitted fabric was lower than that of regular PET one and warmth keepability rate was higher than that of regular PET one, which means ZrC imbedded PET have heat storage property. Drying property of ZrC imbedded knitted fabric was better than that of regular PET one due to heat by far-infrared emitted from ZrC in the core of filament. It revealed that wicking property of the ZrC imbedded fabric was not influenced by far-infrared emission, but affected by fibre physical properties. Tactile hand property of ZrC imbedded knitted fabric was not influenced by imbedding ZrC in the filament but affected preferably by structure of knitted fabric. Dye affinity of ZrC imbedded PET knitted fabric was less influenced by dyeing temperature and time than regular PET knitted one.

• Nuclear Engineering and Technology
• /
• v.33 no.2
• /
• pp.184-191
• /
• 2001

The effects of ${\gamma}$-irradiation on the crosslinking of high density polyethylene (HDPE) was investigated for the purpose of obtaining a suitable formulation for heat shrinkable materials. In this study the HDPE specimens were prepared by blending with cross linking agents and pressed into a 0.2 mm sheet at 18$0^{\circ}C$. ${\gamma}$-irradiation was conducted at 40 to 100 kGy in nitrogen. The heat shrinkable property and thermal mechanical property of the HDPE sheets have been investigated. It was found that the degree of crosslinking of the irradiated HDPE samples were increased with irradiation dose. Compared with the HDPE containing triallylisocyanurate, the HDPE containing trimethylol propane triacrylate shows a slight increase in crosslinking density. The heat transformation and dimension change of HDPE decreased with increasing radiation dose. The heat shrinkage of the samples increased with increasing annealing temperatures. The thermal resistance of HDPE increased upon the crosslinking of HDPE.

• Journal of the Korean Society for Heat Treatment
• /
• v.31 no.1
• /
• pp.12-17
• /
• 2018

We investigated the corrosion behavior of commercially pure cold working processed (CP)-Ti with coarse-grained (CG) microstructure heat-treated at $400^{\circ}C$ and $600^{\circ}C$, respectively. It is observed that corrosion resistance of as-received CP-Ti heat-treated at $400^{\circ}C$, at which recrystallization proceeds, is largely improved. Interestingly, the mechanical property of CP-Ti sample at $400^{\circ}C$ was scarcely deteriorated. It is attributed to the decrease of the defects such as strain variance and dislocation density. On the other hand, the annealing treatment at $600^{\circ}C$ of CP-Ti plate causes to grain growth with the noticeable reduction of mechanical property. Hence, it is considered that defect density such as strain and dislocation density is important microstructural parameter for the improvement of corrosion resistance. The introduction of proper annealing treatment can help to improve corrosion resistance without scarifying mechanical property of CP-Ti.

• Journal of the Korean Solar Energy Society
• /
• v.22 no.4
• /
• pp.35-43
• /
• 2002

This research makes that quantitative radiation property of an actual town ward is obtained in quest of the parameter with regard to a radiation heat transfer property and set up several town ward models that reproduced a solid form of a city along the attribute of the city. A regular trend possibility that is able to evaluate a radiation characteristics of a town ward quantitatively from a town ward guideline and confirmation that is produced about each parameter as a result of a numerical value simulation it obtained. This research shot a coefficient of Gebhart's emission absorption. sky radiation absorption rate direct solar radiation absorption rate the parameter with regard to a radiation heat transfer characteristics of a town ward in each town ward model and a volume rate of a town ward advances case study under regular such condition and shot the absorption rate, direct and others days and calculated an absorption rate and checked about the relation between a town ward and each radiation heat transfer property of a city.

• Korean Journal of Metals and Materials
• /
• v.47 no.3
• /
• pp.195-201
• /
• 2009

This paper is concerned with effects of Mn and heat-input on the mechanical properties of EGW welds. Four different kinds of welding consumables were fabricated by varying Mn contents such as 1.3, 1.5, 1.7, 2.0%Mn and each consumable was welded for EGW on four heat-input conditions between 190 and 340 KJ/Cm. Mn contents were decreased as heat-input increases and alloy elements (C, Si, Ti, B, Al) to deoxidize easily also revealed similar tendency to Mn. Their microstructure, Charpy impact property and strength were investigated, and it is found that Charpy impact property and strength exhibit a strong dependence on change of microstructure by Mn contents and heat-input. The increase of Mn contents or the decrease of heat-input made the microstructure fine and increase volume fraction of acicular ferrite, thereby leading to the great improvement of Charpy impact property and strength. In case of single EGW, optimum Mn contents are over 1.7% for the toughness and strength.

• KSCE Journal of Civil and Environmental Engineering Research
• /
• v.29 no.5A
• /
• pp.531-541
• /
• 2009

The research analyzes and investigates conventional concrete, hydration heat, set, and mechanical properties by making high flowing self-compacting concretes of binary blend and ternary blend as one of evaluations about the properties of the hydration heat of high flowing self-compacting concrete with a strength of 30, 50, and 70 MPa. In addition, it estimates concrete adiabatic temperatures by calculating a thermal property value of powder obtained by measuring a heat evolution amount for powder used in concrete, a thermal property value of concrete obtained by conducting a simple adiabatic temperature test, and a normal thermal property value of material used in concrete, using a simple equation. Moreover, it analyzes and investigates the hydration heat property of high flowing self-compacting concrete and the thermal stress caused by hydration heat by conducting a 3D temperature stress analysis for the hydration heat and the adiabatic temperature obtained by temperature analysis, using MIDAS CIVIL 06 program.

• Journal of Advanced Marine Engineering and Technology
• /
• v.23 no.6
• /
• pp.806-813
• /
• 1999

The effect of Post-Weld Heat Treatment(PWHT) of SS400 Steel was investigated with parameters such as micro vickers hardness corrosion potential polarization behaviors galvanic current Al anode generating current Al anode weight loss etc. Hardness of each parts(HAZ, BM, WM)by PWHT is lower than that of each parts by Non Post-Weld Heat Treatment(NPWHT) However hardness of WM of HAZ part was the highest among those three parts and HAZ area were also acted as cathode without any case of heat treatment. Potential difference between each three parts by PWHT was also smaller compared to NPWHT. Therefore it is suggested that Corrosion resistance property is increased by PWHT. However both Al anode generating current and anode weight loss was also decreased by PWHT compared to NPWHT when SS400 steel is cathodically protected by Al anode.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.10a
• /
• pp.150-153
• /
• 2007

Apply electromagnetic stirring system to making rheology slurry of Al7075. This experiment has important element which is the relation between solid fraction percent and melt temperature of Al7075. The rheology slurry of Al7075 eliminated liquid phase to include alloying element of copper and zinc by squeeze casting process. In result the most structure was composed entirely of globular primary $\alpha$. Used this material for this study. This study made a comparison of mechanical property according to heat treatment T6 at each melt temperature ($619^{\circ}C$ and $615^{\circ}C$). The microstructure and component are observed how heat treatment T6 weight with the mechanical property by SEM-EDS.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2014.11a
• /
• pp.47-48
• /
• 2014

This study is to hydration property of low carbon type recycled cement from waste cementitious powder and cement raw materials. Waste cementitious powder possible to low carbon type recycled cement in small part of additive materials. Also, low carbon type recycled cement using waste cementitious powder is suitable for low heat type cement.