• 연구논문집
• /
• 통권33호
• /
• pp.175-182
• /
• 2003

In this study, the wear resistance of the complex powder diffusion treated KS STD 61 has been investigatived. KS STD 61 tool steel was pretreated in quenching and tempering processes to obtain the tempered martensitic microstructure. The samples were packed with complex powder in steel pot($\Phi$90x60mm) and heated in a box furnace. the complex powder diffusion treatment are carried out at $540^{\circ}C$, $520^{\circ}C$, $500^{\circ}C$ for 40min, 1.5hr and 2.5hr. The microstructure, microhardness, wear resistance, and coating layer thickness of the complex powder diffusion treated samples were investigation. The weight loss of as heat treated sample was 0.4mg and that of the complex powder treated at $540^{\circ}C$ for 2.5hr was 0.17mg. These result means that the wear resistance of tool steels can be easily improved by the powder diffusion process at conventional tempering treatment temperature.

• 설비공학논문집
• /
• 제15권10호
• /
• pp.828-834
• /
• 2003

A diffusion absorption refrigerator is a heat-generated refrigeration system. It uses a three-component working fluid consisting of the refrigerant (ammonia), the absorbent (water) and the auxiliary gas (hydrogen or helium). In this study, experimental investigations have been carried out to examine the effects of charging conditions of working fluids on the evaporating temperature for diffusion absorption refrigerator. Experimental parameters considered in the present experiments are charging concentration, solution charge and system pressure determined by auxiliary gas charged. As a result, in the charging condition of 35% of concentration and 20 kg$_{f}$cm$^2$ of system pressure, the system has the lowest evaporating temperature. It was found that there exists a minimum value of solution charge for the operation of diffusion absorption refrigerator.r.

• 한국재료학회지
• /
• 제16권10호
• /
• pp.614-618
• /
• 2006

The thermal stability of Cu/Ti(or Ta)/NiSi contacts was investigated. Ti(Ta)-capping layers deposited to form NiSi was utilized as the Cu diffusion barrier. Ti(Ta)/NiSi contacts was thermally stable upto $600^{\circ}C$. However when Cu/Ti(Ta)/NiSi contacts were furnace-annealed at $300{\sim}400^{\circ}C$ for 40 min., the Cu diffusion was found to be effectively suppressed, but NiSi was dissociated and then Ni diffused into the Cu layer to form Cu-Ni solutions. On the other hand, the Ni diffusion did not occur for the Al/Ti/NiSi system. The thermal instability of Cu/Ti(Ta)/NiSi contacts was attributed to the high heat of solution of Ni in Cu.

• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2021년도 가을 학술논문 발표대회
• /
• pp.127-128
• /
• 2021

In this study, a study was conducted to analyze thermal diffusion according to the depth of concrete exposed to high temperatures. For thermal diffusion analysis, a test specimen in which K-type sheath thermocouples were poured in 0, 10, 20, 30, and 40 mm sections was manufactured, and thermal diffusion measurement was performed through one-sided heating for 180 minutes under heating conditions. As a result of the review, it was shown that as the temperature condition increased, the heat diffusion increased as the depth increased.

• 한국수학사학회지
• /
• 제15권3호
• /
• pp.59-64
• /
• 2002

This paper investigates a history of Fourier Series for the heat equation and how deeply it is related to modern famous three equations, Navier-Stokes equations in fluid dynamics, drift-diffusion equations in semiconductor, and Black-Scholes equation in finance. We also propose improved models for the heat equation with finite propagation speeds.

• 한국세라믹학회지
• /
• 제36권11호
• /
• pp.1266-1273
• /
• 1999

• 대한기계학회논문집B
• /
• 제30권9호
• /
• pp.905-912
• /
• 2006

Experiments in low strain rate methane-air counterflow diffusion flames diluted with $CO_2$ have been conducted to investigate the flame extinction behavior and edge flame oscillation in which flame length is less than the burner diameter and thus lateral conductive heat loss in addition to radiative loss could be remarkable at low global strain rates. The critical mole fraction at flame extinction is examined in terms of velocity ratio and global strain rate. It is seen that flame length is closely relevant to lateral heat loss, and this sheets flame extinction and edge flame oscillation considerably. Lateral heat loss causes flame oscillation even at fuel Lewis number less than unity. Edge flame oscillations are categorized into three: a growing-, a harmonic- and a decaying-oscillation mode. Onset conditions of the edge flame oscillation and the relevant modes are examined with global strain rate and $CO_2$ mole fraction in fuel stream. A flame stability map based on the flame oscillation modes is also provided at low strain rate flames.

• 설비공학논문집
• /
• 제14권2호
• /
• pp.161-167
• /
• 2002

In this study, external condensation heat transfer coefficients (HTCs) of two non-azeotropic refrigerant mixtures of HFC32/HFC134a and HF0134a/HCF0123 at various compositions were measured on both low fin and Turbo-C enhanced tubes of 19.0 mm outside diameter All data were taken at the vapor temperature of 39$^{\circ}C$ with a wall subcooling of 3- 8 K. Test results showed that HTCs of the tested mixtures on the enhanced tubes were much lower than the ideal values calculated by the mass fraction weighting of the pure compo- nents'HTCs. Also the reduction of HTCs due to the diffusion vapor film was much larger than that of a plain tube. Unlike HTCs of pure fluids, HTCs of the mixtures measured on enhanced tubes increased as the wall subcooling increased, which was due to the sudden break up of the vapor diffusion film with an increase in wall subcooling. Finally, heat transfer enhancement ratios for mixtures were found to be much lower than those of pure fluids.

• 콘크리트학회논문집
• /
• 제11권4호
• /
• pp.31-41
• /
• 1999

Blended Low Heat type cement is ground granulated blast furnace slag and fly ash mixed ternary with ordinary portland cement. From the viewpoint of X-ray patterns of domestic LHC, the main components of cement such as $C_2$S, $C_3$A, $C_3$S are considerably reduced. Therefore the heat evolution of LHC paste is 42cal/g lower than of OPC paste. At early age, the compressive strength development of LHC concrete is delayed, but the slump loss ratio of fresh concrete is reduced more than 20% with elapsed time. The penetrability of LHC is lower than that of OPC by 1/7.8 with the penetrability of chloride ion into the concrete until the age of 120 days. And the PD Index value of LHC is 0.44$\times$10-6 $\textrm{cm}^2$/s, which indicates only 39.3% of OPC. From the Mercury Intrusion Porosimetry test of cement past, we know that the pore size of LHC is more dense than that of OPC by production of C-S-H.

• Journal of the Korean Wood Science and Technology
• /
• 제22권2호
• /
• pp.61-70
• /
• 1994

This study was executed to find the applicability of press drying of tree disk by investigating the shrinkage and drying defect and to form appropriate model by comparing the actual moisture content(MC) and internal temperature in respect of drying time with calculated values based computer simulation to which was applied finite difference method. In press drying disk, heating period, constant drying rate period maintained plateau temperature at 100$^{\circ}C$ and falling drying rate period were significantly distinguished. Actual MC and internal temperature were analogous to those calculated at comparing points. Heat transfer model formed by Fourier's law using specific heat of moist wood and conduction coefficient considering fractional volume of each element of wood cell wall, bound water, free water and air showed applicability as basic data to developing heat expansion, shrinkage and drying stress during press drying. Also mass transfer model formed by Fick's diffusion law using water vapor diffusion coefficient showed applicability. Longitudinal shrinkage was developed by pressure of hot press and tangential shrinkage was restrained by hygrothermal recovery. The heart check, surface check and ring failure were occurred differently in species, but V-shaped crack didn't develop.